A Study of the Synergistic Interaction of Konjac Glucomannan/Curdlan Blend Systems under Alkaline Conditions

Characterizations of konjac glucomannan/curdlan edible coatings and the preservation effect on cherry tomatoes

In this study, konjac glucomannan (KGM) and curdlan were used to fabricate composite coating (KC). The coating solutions were investigated using a rheological method, and the coatings were characterized by water solubility tests, water vapor permeability (WVP), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). The preservation effect of KC coating on cherry tomatoes stored at room temperature was determined. Results indicated that the curdlan addition can adjust the hydrophilicity/hydrophobicity of KGM coatings. Curdlan addition enhanced intermolecular entanglement and film-forming property. Increasing curdlan content in KC coatings significantly decreased the moisture content, dissolution and swelling ratio, and WVP. The KGM-curdlan composites behaved as high-performance coatings with good compatibility and uniformity. The K₃C₂ coating showed the best uniformity, water barrier, and thermal stability. The application of K₃C₂ coating significantly reduced the weight loss, decay loss, and delayed the decreases of firmness, soluble solids, total acid, and VC contents of cherry tomatoes. The KGM/curdlan edible coatings have promising potential for prolonging the shelf life of cherry tomatoes and applications in fruits preservation in the future.

The alleviative effect of curdlan on the quality deterioration of konjac glucomannan thermo-irreversible gels after commercial sterilization at 121 °C

This work employed different curdlan concentrations (0.00 %, 1.00 %, 1.50 %, 2.00 %, and 2.50 %) to alleviate the quality degradation of konjac glucomannan (KGM) gels after commercial sterilization at 121 °C for 15 min. The results showed that all levels of curdlan could retard the deterioration of KGM gels, with the best effect at 2.00 %. After commercial sterilization, incorporating curdlan into KGM gels greatly reduced the Tan σ (G"/ G'), total relaxation time and half-free water from 0.52, 89.85 ms and 98.26 % to 0.27, 38.48 ms and 21.42 %, respectively. Moreover, the addition of curdlan imparted a better texture to KGM gels, as reflected in the increase of hardness, springiness, water-holding capacity and whiteness value from 1400.85 g, 0.42, 87.92 % and 33.33 to 3461.68 g, 0.80, 96.50 % and 49.27, respectively. Furthermore, SEM images revealed that curdlan endowed KGM gels with a tighter structure and smaller pores, and the pore size distribution was reduced from 113.46 μm to17.91 μm, indicating a stronger interaction among molecules, as evidenced by XRD and FTIR results. KGM gels with curdlan possessed less proportion of complete crystallites and crystalline region. These findings suggested that curdlan can be the potently protectant for improving the quality of commercially sterilized KGM gel-based products.

Preparation and characterization of konjac glucomannan (KGM) and deacetylated KGM (Da-KGM) obtained by sonication

BACKGROUND

Konjac glucomannan (KGM) has been widely applied in the food industry as a thickening and gelation agent because of its unique colloidal properties of viscosity enhancement and gelling ability. The current study aimed to prepare and characterize KGM and deacetylated KGM (Da-KGM) samples obtained by sonication in neutral and alkali ethanol-water solutions.

RESULTS

The results showed that the deacetylation degree (DD) of Da-KGM increased exponentially with alkali concentration. Fourier transform infrared spectrometry further confirmed the deacetylation reaction through the dramatic decrease in the acetyl group band at 1740 cm^-1 . Besides, the high similarity among the tested groups in terms of X-ray diffraction (XRD) spectra implied a similar crystalline structure, while differential scanning calorimetry (DSC) curves revealed that the water binding capacity and decomposition temperature of KGM changed slightly with alkali and sonication treatment. The rheological profiles indicated that apparent viscosity (η₀ ) of sonicated KGM samples was unchanged except for the T60 group (60 min sonication treatment). Particularly, ultrasonic treatment under high alkaline conditions (0.10 mol L^-1 NaOH) was noted to promote the deacetylation reaction, and the obtained samples showed decreased apparent viscosity and weakened the gelation process in aqueous solution. Partial correction analysis indicated that alkali rather than ultrasonic treatment resulted in the change of DD and η₀ in Da-KGM. Moreover, sonication contributed to off-white color by reducing the browning caused by alkali in Da-KGM products.

CONCLUSION

Ultrasound-mediated heterogeneous deacetylation reaction is a feasible way to prepare Da-KGM samples with lightened browning and controllable DD. © 2022 Society of Chemical Industry.

Gelation of konjac glucomannan by acetylmannan esterases from Aspergillus oryzae

Konjac glucomannan (KGM) is a principal component of the gelatinous food Konjac. Konjac production through alkali treatment releases an undesirable amine-odor. Two acetylesterases (AME1 and AME2) active against konjac glucomannan (polymer or oligomer) were purified from the supernatant of Aspergillus oryzae RIB40 culture. We cloned the genes encoding AME1 and AME2 based on the genomic information of A. oryzae, constructed their expression systems in A. oryzae, and obtained the recombinant enzymes (rAME1 and rAME2). rAME1 did not act on the KGM polymer but only on the KGM oligomer, releasing approximately 60% of the acetic acid in the substrate. However, rAME2 was active against both KGM substrates, releasing approximately 80% and 100% of acetic acid from the polymer and oligomer, respectively. Both enzymes were active against xylan and exhibited a trace activity on ethyl ferulate. The acetyl group position specificities of both enzymes were analyzed via heteronuclear single quantum correlation NMR using oligosaccharides of glucomannan prepared from Aloe vera (AGM), which has a higher acetyl group content than KGM. rAME1 acted specifically on single-substituted acetyl groups and not on double-substituted ones. In contrast, rAME2 appeared to act on all the acetyl groups in AGM. Treatment of 3% KGM with rAME2 followed by heating to 90 °C resulted in gel formation under weakly acidic conditions. This is the first study to induce gelation of KGM under these conditions. A comparison of the breaking and brittleness properties of gels formed by alkaline and enzymatic treatments revealed similar texture of the two gels. Furthermore, scanning electron microscopy of the surface structure of both gels revealed that both formed a fine mesh structure. Our findings on enzymatic gelation of KGM should lead to the development of new applications in food manufacturing industry.