UHMWPE-Based Glass-Fiber Composites Fabricated by FDM. Multiscaling Aspects of Design, Manufacturing and Performance

Cyclic Impact Compaction of an Ultra High Molecular Weight Polyethylene (UHMWPE) Powder and Properties of the Compacts

Experiments on Cyclic Impact Compaction (CIC) of UHMWPE powder GUR 4120 were carried out on a laboratory hydro-pneumatic impact device. This device provides impact energies of up to 1 kJ with a frequency of impacts of 9 s^-1 and enables producing dense and robust compacts in the form of disks with a diameter of up to 60 mm and a height of up to 24 mm. The optimal parameters of the CIC were determined, which are the preheating temperature of the powder, the impact energy and the number of impacts. The strength, Brinell hardness and elongation of the resulting compacts with a diameter of 40 mm and a height of 15 mm were 37.5 MPa, 49.0 MPa and 470%, respectively. The possibility of activating UHMWPE powder by explosive loading was studied. It was found that the explosive pretreatment reduces the mechanical properties of the resultant compacts. The CIC method is suitable for the manufacture of UHMWPE-based composites with nano-additives, as evidenced by the successful production of compacts containing nanoscale detonation carbon as an additive. The results of the present study show that the CIC method is promising for the industrial production of small-sized UHMWPE parts.

Effect of Borpolymer on Mechanical and Structural Parameters of Ultra-High Molecular Weight Polyethylene

The paper presents the results of studying the effect of borpolymer (BP) on the mechanical properties, structure, and thermodynamic parameters of ultra-high molecular weight polyethylene (UHMWPE). Changes in the mechanical characteristics of polymer composites material (PCM) are confirmed and complemented by structural studies. X-ray crystallography (XRC), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), and infrared spectroscopy (IR) were used to study the melting point, morphology and composition of the filler, which corresponds to the composition and data of the certificate of the synthesized BP. Tensile and compressive mechanical tests were carried out in accordance with generally accepted standards (ASTM). It is shown that BP is an effective modifier for UHMWPE, contributing to a significant increase in the deformation and strength characteristics of the composite: tensile strength of PCM by 56%, elongation at break by 28% and compressive strength at 10% strain by 65% compared to the initial UHMWPE, due to intensive changes in the supramolecular structure of the matrix. Structural studies revealed that BP does not chemically interact with UHMWPE, but due to its high adhesion to the polymer, it acts as a reinforcing filler. SEM was used to establish the formation of a spherulite supramolecular structure of polymer composites.