Characterization, Antimicrobial Effects, and Cytocompatibility of a Root Canal Sealer Produced by Pozzolan Reaction between Calcium Hydroxide and Silica

Comparative bioactivity and immunomodulatory potential of the new Bioroot Flow and AH Plus Bioceramic sealer: An in vitro study on hPDLSCs

OBJECTIVES

To evaluate the cytocompatibility, bioactivity, and anti-inflammatory potential of the new pre-mixed calcium silicate cement-based sealers Bioroot Flow (BrF) and AH Plus Bioceramic Sealer (AHPbcs) on human periodontal ligament stem cells (hPDLSCs) compared to the epoxy resin-based sealer AH Plus (AHP).

MATERIALS AND METHODS

Standardized discs and 1:1, 1:2, and 1:4 eluates of BrF, AHPbcs and AHP after setting were prepared. The following assays were performed: cell attachment and morphology via SEM, cell viability via a MTT assay, cell migration/proliferation via a wound-healing assay, cytoskeleton organization via immunofluorescence staining; cytokine release via ELISA; osteo/cemento/odontogenic marker expression via RT-qPCR, and cell mineralized nodule formation via Alizarin Red S staining. HPDLSCs were isolated from extracted third molars from healthy patients. Comparisons were made with hPDLSCs cultured in unconditioned (negative control) or osteogenic (positive control) culture media. Statistical significance was established at p < 0.05.

RESULTS

Both BrF and AHPbcs showed significantly positive results in the cytocompatibility assays (cell metabolic activity, migration, attachment, morphology, and cytoskeleton organization) compared with a negative control group, while AHP showed significant negative results. BrF exhibited an upregulation of at least one osteo/cementogenic marker compared to the negative and positive control groups. BrF showed a significantly higher calcified nodule formation than AHPbcs, the negative and positive control groups, while AHPbcs was higher than the negative control group. Both were also significantly higher than AHP group.

CONCLUSION

BrF and AHPbcs exhibit adequate and comparable cytocompatibility on hPDLSCs. BrF also promoted the osteo/cementogenic differentiation of hPDLSCs. Both calcium silicate-based sealers favored the downregulation of the inflammatory cytokine IL-6 and the calcified nodule formation from hPDLSCs. BrF exerted a significantly higher influence on cell mineralization than AHPbcs.

CLINICAL RELEVANCE

This is the first study to elucidate the biological properties and immunomodulatory potential of Bioroot Flow and AH Plus Bioceramic Sealer. The results act as supporting evidence for their use in root canal treatment.

Physicochemical properties of AH plus bioceramic sealer, Bio-C Sealer, and ADseal root canal sealer

BACKGROUND

The aim of this study was to evaluate the physicochemical properties of two newly introduced premixed calcium silicate-based root canal sealers (AH Plus Bioceramic Sealer and Bio-C Sealer) compared to a resin-based root canal sealer (ADseal root canal sealer).

METHODS

Solubility, pH analysis, calcium ion release, and film thickness of each sealer were evaluated following ISO guidelines. The data were examined using the two-way ANOVA test. Furthermore, X-ray diffraction (XRD) examination was performed to investigate the crystalline phase of each type of sealer. X-ray fluorescence (XRF) analysis was done for the chemical elemental analysis of each sealer.

RESULTS

The least film thickness, highest alkalinity, and highest calcium ion release were all displayed by AH Plus Bioceramic Sealer. High solubility, high alkalinity, intermediate calcium ion release, and intermediate film thickness were all displayed by Bio-C Sealer. While ADseal root canal sealer displayed the greatest film thickness, least solubility, alkalinity, and calcium ion release.

CONCLUSIONS

Both AH Plus Bioceramic Sealer and Bio-C Sealer represented adequate properties to be considered a good sealer that could be used as a potential alternative to resin-based root canal sealers.

Novel antibacterial and apatite forming restorative composite resin incorporated with hydrated calcium silicate

Background

White Portland cement is a calcium silicate material. It exhibits antibacterial properties and is biocompatible. In addition, calcium silicate-based materials are known to release calcium ions and form apatite. The purpose of this study was to develop a novel bioactive restorative resin composite with antibacterial and apatite forming properties to prevent tooth caries at the interface of teeth and restorative materials, by incorporation of hydrated calcium silicate (hCS) derived from white Portland cement.

Methods

To prepare the experimental composite resins, a 30 wt% light-curable resin matrix and 70 wt% filler, which was mixed with hCS and silanized glass powder were prepared in following concentrations: 0, 17.5, 35.0, and 52.5 wt% hCS filler. The depth of cure, flexural strength, water sorption, solubility, and antibacterial effect were tested. After immersion in artificial saliva solution for 15, 30, 60, and 90 days, ion concentration by ICP-MS and apatite formation using SEM-EDS, Raman spectroscopy and XRD from experimental specimens were analyzed.

Results

All experimental groups showed clinically acceptable depths of cure and flexural strength for the use as the restorative composite resin. Water sorption, solubility, released Ca and Si ions increased with the addition of hCS to the experimental composite resin. Experimental groups containing hCS showed greater antibacterial effects compared with the 0 wt% hCS filler group (p < 0.05). The 52.5 wt% hCS filler group produced precipitates mainly composed of Ca and P detected as hydroxyapatite after immersion in artificial saliva solution for 30, 60, and 90 days.

Conclusions

This results show that composite resins containing hCS filler is effective in antibacterial effects. hCS has also apatite formation ability for reducing gap size of microleakage by accumulating hydroxyapatite precipitates at the restoration-tooth interface. Therefore, novel composite resin containing hCS is promising bioactive resin because of its clinically acceptable physiochemical properties, antibacterial properties, and self-sealing potential for prevention of microleakage for longer usage of restorations.