Influence of Build Orientation, Geometry and Artificial Saliva Aging on the Mechanical Properties of 3D Printed Poly(ε-caprolactone)

3D Printing for Dental Applications

Due to increased life expectancy and greater concern among populations regarding oral health problems and aesthetics, in the last few years, there has been a growing demand for dental structures and devices to replace/restore missing/damaged teeth [...].

A Study of the Mechanical Properties of Naturally Aged Photopolymers Printed Using the PJM Technology

Additive manufacturing is being increasingly used both for rapid prototyping as well as the fabrication of finished components. It is important to determine how the properties of 3D printed materials change over time and how they affect the durability and usability of products. The aim of the research presented in this article was to find out what influence the natural aging period had on the mechanical properties, especially the tensile strength and modulus of elasticity, of specimens made from the selected photocurable resins using the PolyJet Matrix (PJM) technology. The tests involved determining the tensile strength and modulus of elasticity of specimens fabricated in 2013 and 2014 using two types of photosensitive resins, i.e., FullCure 720 and VeroWhite, respectively. Some of the specimens were stored under laboratory conditions until July 2022 and then tested using a universal testing machine. The experimental data obtained in 2022 for the naturally aged models were compared with those reported for the as-printed specimens. One of the main findings of this study was that the tensile strength and modulus of elasticity of the naturally aged specimens were largely dependent on the printing direction (model orientation on the build tray). The test results show that aging generally decreased the tensile strength of the specimens. In one case, however, an increase in this property was observed. For the X and Y printing directions, R_m declined by 27.1% and 30.7%, respectively. For the Z direction, a decrease of only 5.5% was reported, for Full Cure 720. The modulus of elasticity of the models tested in 2022 differed considerably from that reported for the as-printed objects. Higher values of the modulus of elasticity implied that the material stiffness increased over time, and this is a common phenomenon in polymers. Interesting results were obtained for VeroWhite specimens. The modulus of elasticity decreased significantly by 25.1% and 42.4% for the specimens printed in the X and Z directions, respectively. However, for the models built in the Y direction, it increased by 27.4%. The experimental data may be of significance to users of products manufactured using the PJM method as well as to researchers dealing with the durability and reliability of such materials.

3D Printing of Polymeric Bioresorbable Stents: A Strategy to Improve Both Cellular Compatibility and Mechanical Properties

One of the leading causes of death is cardiovascular disease, and the most common cardiovascular disease is coronary artery disease. Percutaneous coronary intervention and vascular stents have emerged as a solution to treat coronary artery disease. Nowadays, several types of vascular stents share the same purpose: to reduce the percentage of restenosis, thrombosis, and neointimal hyperplasia and supply mechanical support to the blood vessels. Despite the numerous efforts to create an ideal stent, there is no coronary stent that simultaneously presents the appropriate cellular compatibility and mechanical properties to avoid stent collapse and failure. One of the emerging approaches to solve these problems is improving the mechanical performance of polymeric bioresorbable stents produced through additive manufacturing. Although there have been numerous studies in this field, normalized control parameters for 3D-printed polymeric vascular stents fabrication are absent. The present paper aims to present an overview of the current types of stents and the main polymeric materials used to fabricate the bioresorbable vascular stents. Furthermore, a detailed description of the printing parameters' influence on the mechanical performance and degradation profile of polymeric bioresorbable stents is presented.

3D Printing for Cartilage Replacement: A Preliminary Study to Explore New Polymers

The use of additive manufacturing technologies for biomedical applications must begin with the knowledge of the material to be used, by envisaging a very specific application rather than a more general aim. In this work, the preliminary study was focused on considering the cartilaginous tissue. This biological tissue exhibits different characteristics, such as thickness and mechanical properties, depending on its specific function in the body. Due to the lack of vascularization, cartilage is a supporting connective tissue with limited capacity for recovery and regeneration. For this reason, any approach, whether to repair/regenerate or as a total replacement, needs to fulfill the adequate mechanical and chemical properties of the surrounding native cartilage to be successful. This work aims to explore the possibility of using new polymers for cartilage total replacement approaches with polymeric materials processed with the specific 3D printing technique of fused filament fabrication (FFF). The materials studied were Nylon^® 12 (PA12), already described for this purpose, and LAY-FOMM^® 60 (FOMM). FOMM has not been described in the literature for biomedical purposes. Therefore, the chemical, thermal, swelling capacity, and mechanical properties of the filaments were thoroughly characterized to better understand the structure–properties–application relationships of this new polymer. In addition, as the FFF technology is temperature based, the properties were also evaluated in the printed specimens. Due to the envisaged application, the specimens were also characterized in the wet state. When comparing the obtained results with the properties of native cartilage, it was possible to conclude that: (i) PA12 exhibits low swelling capacity, while FOMM, in its dry and wet forms, has a higher swelling capacity, closer to that of native cartilage; (ii) the mechanical properties of the polymeric materials, especially PA12, are higher than those of native cartilage; and (iii) from the mechanical properties evaluated by ultra-micro hardness tests, the values for FOMM indicate that this material could be a good alternative for cartilage replacement in older patients. This preliminary study, essentially devoted to expanding the frontiers of the current state of the art of new polymeric materials, provides valuable indications for future work targeting the envisaged applications.