Development of New Experimental Dental Enamel Resin Infiltrants-Synthesis and Characterization

Properties of Nanohybrid Dental Composites-A Comparative In Vitro Study

(1) Background: the current study investigated three nanohybrid composites: two commercial products ClearfilMajestyTM (CM) and HarmonizeTM (HU), compared with an experimental product PS2. (2) Methods: Two sample types were molded using Teflon dies. The first sample type was represented by standard discs (20 mm diameter and 2 mm thickness) (n = 60, 20/each material), used for surface conditioning investigation, specifically roughness monitoring and color stability analysis using AFM and the CIELab test, respectively. The second sample type was a standard cylindrical specimen (4 mm diameter and 6 mm height) for compression testing (n = 60, 20/each material). After complete polymerization, the samples were ground with sandpaper and further polished. The filler size and distribution in the polymer matrix were investigated with SEM. Data were statistically analyzed using the Anova Test followed by Tukey's post hoc test on the Origin Lab 2019 software produced by OriginLab Corporation, Northampton, MA, USA. (3) Results: A mono-disperse system was identified in HU samples, while CM and PS2 revealed both nano- and microfiller particles. The samples' observation after immersion in coffee and tea indicated that a lower roughness combined with optimal filler lamination within the polymer matrix assured the best color preservation. The compression strength was lower for the HU sample, while higher values were obtained for the complex filler systems within CM and PS2. (4) Conclusions: the behavior of the investigated nanohybrid composites strongly depends on the microstructural features.

An Insight into Enamel Resin Infiltrants with Experimental Compositions

Resin infiltration is a conservative treatment of initial enamel carious lesions. Only one infiltrant material is available on the market (Icon, DMG), and research is now investigating new chemical compositions so as to further exploit the benefits of the resin infiltration technique. A literature search of the articles testing the effects of different formulations on mechanical properties, resin penetration ability, remineralizing, and antibacterial activities was conducted. Of 238 articles, 29 resulted in being eligible for the literature review. The formulations investigated were all different and consisted in the inclusion of hydrophobic monomers (i.e., BisEMA, UDMA), solvents (ethanol, HEMA), alternative etchants (PAM) or molecules with antibacterial or bioactivity features (i.e., AgNP, YbF_3, MTZ, chitosan, DMAMM, HAp, MC-IL, NACP, PUA, CHX) and microfilled resins. Information on the long-term performances of the tested experimental materials were scarce. The combination of TEGDMA with hydrophobic monomers and the inclusion of a solvent alternative to ethanol reinforced mechanical properties of the materials. Hybrid-glass materials demonstrated an enhanced remineralization capacity. Techniques such as tunnelization increased the penetration depth and preserved the recourse to less-conservative treatments. Combining the min-invasive infiltrant approach with remineralizing and bacteriostatic properties would be beneficial for therapeutic and economical aspects, according to the principles of minimally invasive dentistry.

Resin Infiltration of Non-Cavitated Enamel Lesions in Paediatric Dentistry: A Narrative Review

The resin infiltration (RI) technique was introduced as one of the minimal intervention dentistry strategies in addressing dental caries among the paediatric population. This technique used the low-viscosity resin monomer to infiltrate the non-cavitated carious lesion and other developmental enamel porosities, thus allowing the conservation of the tooth structure. This narrative review aims to explore the value of RI in Paediatric Dentistry. Through our search of the literature, the development of the material, their clinical applications and shortcomings, as well as the innovation that has been carried out to improve the current RI, were discussed. There are number of high-level evidence supporting the use of RI in arresting non-cavitated proximal caries lesions in primary and permanent teeth, but its efficacy in managing anterior white spot lesions is still unclear. Limited penetration depth, not radiopaque and questionable long-term colour and material stability were among the limitation of the material. Various laboratory-based studies have been conducted to improve the current properties of RI. Nevertheless, RI has emerged as one of the important micro-invasive techniques in addressing non-cavitated and anterior white-spot enamel lesions in children and adolescents with great success.

Novel dental resin infiltrant containing smart monomer dodecylmethylaminoethyl methacrylate

Objectives

White spot lesions (WSLs) are prevalent and often lead to aesthetic problems and progressive caries. The objectives of this study were to: (1) develop a novel resin infiltrant containing smart monomer dodecylmethylaminoethyl methacrylate (DMAEM) to inhibit WSLs, and (2) investigate the effects of DMAEM incorporation on cytotoxicity, mechanical properties, biofilm-inhibition and protection of enamel hardness for the first time.

Methods

DMAEM was synthesized using 1-bromododecane, 2-methylamino ethanol and methylmethacrylate. DMAEM with mass fractions of 0%, 1.25%, 2.5% and 5% were incorporated into a resin infiltant containing BisGMA and TEGDMA. Cytotoxicity, mechanical properties and antibacterial effects were tested. After resin infiltration, bovine enamel was demineralized with saliva biofilm acids, and enamel hardness was measured.

Result

DMAEM infiltration did not increase the cytotoxicity or compromise the physical properties when DMAEM mass fraction was below 5% (p > 0.05). Biofilm metabolic activity was reduced by 90%, and biofilm lactic acid production was reduced by 92%, via DMAEM (p < 0.05). Mutans streptococci biofilm CFU was reduced by 3 logs (p < 0.05). When demineralized in acid and then under biofilms, the infiltrant + 5% DMAEM group produced an enamel hardness (mean ± sd; n = 6) of 2.90 ± 0.06 GPa, much higher than 0.85 ± 0.12 GPa of the infiltrant + 0% DMAEM group (p < 0.05).

Significance

A novel resin infiltrant with excellent mechanical properties, biocompability, strong antibacterial activity and anti-demineralization effect was developed using DMAEM for the first time. The DMAEM resin infiltrant is promising for inhibiting WSLs, arresting early caries, and protecting enamel hardness.

Impact of Dentistry Materials on Chemical Remineralisation/Infiltration versus Salivary Remineralisation of Enamel-In Vitro Study

The aim of this study is to evaluate salivary remineralisation versus chemical remineralisation/infiltration of enamel, using different dentistry materials. The enamel changes were studied using confocal laser scanning microscopy (CLSM), and the depth of lesions and demineralisation/remineralisation/infiltration percentage were calculated. Additionally, the macro elemental composition of the teeth was performed using atomic absorption spectroscopy (AAS). Two studies were performed: (i) demineralisation of enamel in 3% citric acid and infiltration treatment with infiltration resin (Icon, DMG), remineralisation with Fluor Protector (Ivoclar Vivadent) and artificial saliva pH 8; and (ii) enamel demineralisation in saliva at pH 3 and remineralisation at salivary pH 8. The results showed that, firstly, for the remineralisation of demineralised enamel samples, Fluor Protector (Ivoclar Vivadent) was very effective for medium demineralised lesions followed by saliva remineralisation. In cases of deep demineralisation lesions where fluoride could not penetrate, low viscosity resin (Icon, DMG, Hamburg) effectively infiltrated to stop the demineralisation process. Secondly, remineralisation in salivary conditions needed supplementary study over a longer period, to analyse the habits, diet and nutrition of patients in detail. Finally, demineralisation/remineralisation processes were found to influence the macro elemental composition of enamel demineralisation, with natural saliva proving to be less aggressive in terms of decreasing Ca and Mg content.