Influence of EDC on Dentin-Resin Shear Bond Strength and Demineralized Dentin Thermal Properties

Effect of applying carbodiimide combined with a two-step self-etch adhesive durability

BACKGROUND

This study investigated the effect of carbodiimide (EDC) combined with Clearfil SE self-etch adhesive on the shear bond strength (SBS), crosslinking degree, denaturation temperature, and enzyme activity of dentin in vitro.

MATERIALS AND METHODS

Collected human sound third molars were randomly divided into different groups with or without EDC treatment (0.01-1 M). The specimens (n = 16)were stored for 24 h (immediate) or 12 months (aging) before testing the SBS. Fine dentin powder was obtained and treated with the same solutions. Then the crosslinking degree, denaturation temperature (Td), and enzyme activity were tested. Statistical analysis was performed using a one-way analysis of variance (ANOVA) to compare the differences of data between groups (α = 0.05).

RESULTS

There was a significant drop in immediate SBS and more adhesive fracture of 1.0 M EDC group, while there were no significant differences among the other groups. SEM showed a homogeneous interface under all treatments. After 12 months of aging, the SBS significantly decreased. Less decreases of SBS in the 0.3 and 0.5 M groups were found. Due to thermal and enzymatical properties consideration, the 0.3 and 0.5 M treatments also showed higher cross-link degree and Td with lower enzyme activity.

CONCLUSION

0.3 and 0.5 M EDC may be favorable for delaying the aging of self-etch bond strength for 12 months. But it is still needed thoroughly study.

Crosslinking Improve Demineralized Dentin Performance and Synergistically Promote Biomimetic Mineralization by CaP_PILP

OBJECTIVE

to explore the effects of optimal crosslinking (chemical treatment) on demineralized dentin matrix and the possible synergism with calcium phosphate polymer-induced liquid precursor (CaP-PILP) bionic remineralization (physical treatment), and offer benefit to the clinic of resin-dentin bonding and dentin hypersensitivity.

METHODS

demineralized dentin was treated with glutaraldehyde (GA), carbodiimide (EDC), and procyanidin (PA) for crosslinking, followed by CaP-PILP biomimetic remineralization. The morphology, surface mechanical and physio-chemical properties, and enzymatic resistance were evaluated regardless of the modification.

RESULTS

the collagen fibers appeared morphologically complete with higher surface microhardness and characteristic peaks of amide I-III bands were visible after GA, PA, and EDC crosslinking. Collagen collapse and dissolution were seen in untreated demineralized dentin with enzyme attack, while the collagen fiber structure remained intact in GA- and PA-treated specimens. The lamellar mineral phase was visible at 2 days and the dentin tubules were almost completely enclosed at 4-6 days after PA crosslinking and mineralization. However, demineralized collagen fibers and open tubules were still visible between the dentinal tubules on day 8 in the control group.

CONCLUSION

the structure integrity, enzyme resistance, and mechanical properties of the collagen fiber network could be significantly preserved by GA and PA crosslinking than EDC and no treatment. While, strongest synergistic effects were observed in PA on bionic remineralization by CaP-PILP, and further significantly improve the quality and shorten the duration of mineralization. These findings would be beneficial for dental clinical practice of resin-dentin bonding and dentin hypersensitivity.

Dual function of quercetin as an MMP inhibitor and crosslinker in preventing dentin erosion and abrasion: An in situ/in vivo study

OBJECTIVE

The aim of the present study was to evaluate the in situ/in vivo effect of quercetin on dentin erosion and abrasion.

METHODS

Human dentin blocks (2 × 2 × 2 mm) were embedded and assigned to 6 groups: 75 μg/mL, 150 μg/mL and 300 μg/mL quercetin (Q75, Q150, Q300); 120 μg/mL chlorhexidine (CHX, positive control); and deionized water and ethanol (the negative controls). The specimens were treated with the respective solutions for 2 min and then subjected to in situ/in vivo erosive/abrasive challenge for 7 d as follows: in vivo erosion 4 times a day and then in vivo toothbrush abrasion after the first and last erosive challenges of each day. Dentin loss was assessed by profilometry. An additional dentin specimen was used to evaluate the penetration depth of quercetin into dentin by tracking the spatial distribution of its characteristic Raman peak. Moreover, dentin blocks (7 × 1.7 × 0.7 mm) were used to detect the impact of quercetin on dentin-derived matrix metalloproteinase (MMP) inhibition by in situ zymography, and the inhibition percentage (%) was calculated. Additionally, the potential collagen crosslinking interactions with quercetin were detected by Raman spectroscopy, and the crosslinking degree was determined with a ninhydrin assay. Fully demineralized dentin beams (0.5 × 0.5 × 10 mm) were used to evaluate the impact of quercetin on the mechanical properties of dentin collagen fibre by the ultimate micro-tensile strength test (μUTS). The data were analysed by one-way analysis of variance and Tukey's test (α = 0.05).

RESULTS

Compared to the negative controls, all treatment solutions significantly reduced dentin loss. The dentin loss of Q150 and Q300 was significantly less than that of CHX (all P < 0.05). The amount of quercetin decreased with increasing dentin depth, and the maximum penetration depth was approximately 25-30 µm. In situ zymography showed that quercetin significantly inhibited the activities of dentin-derived MMPs. The inhibitory percentages of Q75 and Q150 were significantly lower than that of CHX (all P < 0.05), but no significant difference was found between Q300 and CHX (P = 0.58). The collagen crosslinking interactions with quercetin primarily involved hydrogen bonding and the degree of crosslinking increased in a concentration-dependent manner. Statistically significant increases in μUTS values were observed for demineralized dentin beams after quercetin treatment compared with those of the control treatments (all P < 0.05).

SIGNIFICANCE

This study provides the first direct evidence that quercetin could penetrate approximately 25-30 µm into dentin and further prevent dentin erosion and abrasion by inhibiting dentin-derived MMP activity as well as crosslinking collagen of the demineralized organic matrix.

Effect of Collagen Crosslinkers on Dentin Bond Strength of Adhesive Systems: A Systematic Review and Meta-Analysis

This study aimed to identify the role of crosslinking agents in the resin–dentin bond strength (BS) when used as modifiers in adhesives or pretreatments to the dentin surface through a systematic review and meta-analysis. This paper was conducted according to the directions of the PRISMA 2020 statement. The research question of this review was: “Would the use of crosslinkers agents improve the BS of resin-based materials to dentin?” The literature search was conducted in the following databases: Embase, PubMed, Scielo, Scopus, and Web of Science. Manuscripts that reported the effect on the BS after the use of crosslinking agents were included. The meta-analyses were performed using Review Manager v5.4.1. The comparisons were performed by comparing the standardized mean difference between the BS values obtained using the crosslinker agent or the control group. The subgroup comparisons were performed based on the adhesive strategy used (total-etch or self-etch). The immediate and long-term data were analyzed separately. A total of 50 articles were included in the qualitative analysis, while 45 articles were considered for the quantitative analysis. The meta-analysis suggested that pretreatment with epigallocatechin-3-gallate (EGCG), carbodiimide, ethylenediaminetetraacetic acid (EDTA), glutaraldehyde, and riboflavin crosslinking agents improved the long-term BS of resin composites to dentin (p ≤ 0.02). On the other hand, the use of proanthocyanidins as a pretreatment improved both the immediate and long-term BS values (p ≤ 0.02). When incorporated within the adhesive formulation, only glutaraldehyde, riboflavin, and EGCG improved the long-term BS to dentin. It could be concluded that the application of different crosslinking agents such as carbodiimide, EDTA, glutaraldehyde, riboflavin, and EGCG improved the long-term BS of adhesive systems to dentin. This effect was observed when these crosslinkers were used as a separate step and when incorporated within the formulation of the adhesive system.

Effect of pretreatment with matrix metalloproteinase inhibitors on the durability of bond strength of fiber posts to radicular dentin

Objectives

Application of matrix metalloproteinases inhibitors has been suggested to improve the durability of resin–dentin bonding. The purpose of this study was to evaluate the effect of dimethyl sulfoxide (DMSO), carbodiimide (EDC), and chlorhexidine (CHX) treatment on the push‐out bond strength of fiber posts to radicular dentin.

Materials and Methods

24 extracted premolars were assigned randomly to 4 groups after root canal treatment and post space preparation (n = 6). In the first, second, and third groups, radicular dentin was treated with 1 ml of 5% DMSO, 0.3 M EDC, and 2% CHX, respectively. The fourth group (control) received no treatment. The root canals were primed with ED primer II, and the fiber posts were cemented with Panavia F2.0. In each group, half of the specimens were subjected to the push‐out test and the other half to 3000 thermal cycles before testing. Data were analyzed using two‐way analysis of variance via SPSS version 20 (p < .05).

Results

Among the nonthermocycled specimens, the values of push‐out bond strength were observed in the control, EDC, CHX, and DMSO groups, in decreasing order. Among the thermocycled specimens, the values were observed in the control, EDC, DMSO, and CHX groups in decreasing order. Thermocycling had a significant adverse effect on the push‐out bond strength (p = .015), but the effect of material (p = .375), and the interaction effect of material and thermocycling (p = .998) were not significant.

Conclusions

Application of CHX, DMSO, and EDC had no significant effect on the bond strength of fiber posts to radicular dentin.

Physicochemical properties, bond strength and dual-species biofilm inhibition effect of dental resin composites with branched silicone methacrylate

Dental resin composites (DRCs) with 15 wt% (EC-15%) and 20 wt% (EC-20%) synthesized branched silicone methacrylate (BSM) in resin matrix have showed anti-adhesion effect against Streptococcus mutans. With the aim to evaluate the BSM containing DRCs further, water sorption (WS), solubility (SL), mechanical properties before and after water immersion, anti-adhesion effect against dual-species, bonding strength to adhesive treated dentin, and cytotoxicity of BSM containing DRCs were investigated. DRC without BSM was used as control. The WS and SL were obtained until the mass variation of composite in distilled water kept stable. Three-point bending test was used to evaluate flexural strength (FS) and modulus (FM) of composite before and after water immersion. Mixture of Streptococcus mutans and Lactobacillus acidophilus was used to study the anti-adhesion effect against dual-species. Bonding strength of composite to adhesive treated dentin was measured through macro-shear test. Extract of composite was used to evaluate its cytotoxicity effect on L-929 mouse fibroblasts, and cell viability was obtained by MTT assay. The results showed that EC-15% and EC-20% had similar WS and SL as control (p < 0.05); After water immersion, FS and FM of all composites decreased (p < 0.05), but there was no significant difference in value of FS and FM between different groups (p > 0.05); More bacteria were recovered from the surface of control than those from the surface of EC-15% and EC-20% (p < 0.05); Extract of EC-15% was less cytotoxic (higher cell viability) than those EC-20% and control (p < 0.05). All of results revealed that incorporation of 15 wt% or 20 wt% BSM in resin matrix could endow DRC with inhibition effect on dual-species biofilm formation without impairing physiochemical properties, bonding strength to adhesive treated dentin, and cytotoxicity of DRC.

Effects of Collagen Crosslinkers on Dentine: A Literature Review

This aim of this review is to explore the current research related to crosslinking agents used on dentine. A systematic search of publications in PubMed and Web of Science databases was performed. Further retrieval was conducted using the search terms of specific names of crosslinkers. Reviews, conference abstracts, dissertation and theses, non-English articles, studies of intrinsic crosslinking of dentine, studies of adhesives without specific crosslinker components, studies of crosslinker applications in other collagenous tissues or tooth-like structures and irrelevant studies were excluded. Manual screening was conducted on the bibliographies of remaining papers to identify other relevant articles. One hundred and one articles were included in this systematic review and full texts were retrieved. Both synthetic and naturally derived crosslinkers have been found to exhibit significant effects in biomodification of dentine via their multiple interactions with the dentine matrix. A stable matrix network or a durable hybrid layer in dentine bonding could be achieved, where the dentine collagen fibrils show improved biochemical and biomechanical properties and enzymatic biodegradation is reduced. Although no crosslinkers have been tested in clinical trials, extensive research has been conducted in laboratory studies to investigate their potential applicability for inhibition of demineralisation and/or promotion of remineralisation, caries prevention as well as improvement of bonding performance of adhesive systems. Further studies are needed to develop the feasibility for clinical use, reduce side effects as well as explore mechanisms of action and long-term effectiveness.