Microstructural Investigation and On-Site Repair of Thin Pd-Ag Alloy Membranes

Gas-Transport Characteristics of PdCu–Nb–PdCu Membranes Modified with Nanostructured Palladium Coating

A method for obtaining composite gas-diffusion PdCu–Nb–PdCu membranes modified with a nanostructured crystalline coating was developed to increase the performance of Nb-based membranes. A modifying functional layer with a controlled size and composition was synthesized by electrochemical deposition, which made it possible to determine a certain geometric shape for palladium nanocrystallites. Developed PdCu–Nb–PdCu membranes have demonstrated flux values up to 0.232 mmol s⁻¹ m⁻² in the processes of diffusion purification of hydrogen at 400 °C. A very significant difference in the hydrogen fluxes through the modified and non-modified composite PdCu–Nb–PdCu membranes reached 1.73 times at the lower threshold temperature of 300 °C. Cu doping of protective layer did not affect the selective properties of the membranes, which was confirmed by the obtained high selectivity values up to 1323, and made it possible to reduce the noble metal content. The research data indicate that the modification of the membrane surface significantly accelerates the hydrogen transfer process at sufficiently low temperatures due to the acceleration of dissociative–associative processes on the surface. The reported approach demonstrates new possibilities for creating productive and cost-efficient membranes based on niobium.

Promising Isotope Effect in Pd77Ag23 for Hydrogen Separation

Pd–Ag alloys are largely used as hydrogen separation membranes and, as a consequence, the Pd–Ag–H system has been intensively studied. On the contrary, fewer information is available for the Pd–Ag–D system; thus, the aim of this work is to improve the knowledge of the isotope effect on the commercial Pd77Ag23 alloy, especially for temperature above 200 °C. In particular, deuterium absorption measurements are carried out in the Pd77Ag23 alloy in the temperature range between 79 and 400 °C and in the pressure range between 10−2 and 16 bar. In this exploited pressure (p) and composition (c) range, above 300 °C the pc isotherms display the typical shape of materials where only a solid solution of deuterium is present while at lower temperatures these curves seem to be better described by the coexistence of a solid solution and a deuteride in a large composition range. The obtained results are compared and discussed with the ones previously measured with the lightest hydrogen isotope. Such a comparison shows that the Pd77Ag23 alloy exhibits a clear inverse isotope effect, as the equilibrium pressure of the Pd–Ag–D system is higher than in Pd–Ag–H by a factor of ≈2 and the solubility of deuterium is about one half of that of hydrogen. In addition, the absorption measurements were used to assess the deuteration enthalpy that below 300 °C is ΔHdeut = 31.9 ± 0.3 kJ/mol, while for temperatures higher than 300 °C, ΔHdeut increases to 43 ± 1 kJ/mol. Additionally, in this case a comparison with the lighter isotope is given and both deuteration enthalpy values result lower than those reported for hydrogenation. The results described in this paper are of practical interest for applications operating above 200 °C, such as membranes or packing column, in which Pd77Ag23 has to interact with a gas stream containing both hydrogen isotopes.