Drying Regimes on Regenerated Cellulose Films Characteristics and Properties

Wood cellulose films with different foldabilities triggered by dissolution and regeneration from concentrated H2SO4 and NaOH/urea aqueous solutions

Forests are a major source of wealth for Canadians, and cellulose makes up the "skeleton" of wood fibers. Concentrated H2SO4 and NaOH/urea aqueous solutions are two efficient solvents that can rapidly dissolve cellulose. Our preliminary experiment obtained regenerated wood cellulose films with different mechanical properties from these two solvents. Therefore, herein, we aim to investigate the effects of aqueous solvents on the structure and properties of wood cellulose films. Regenerated cellulose (RC) films were produced by dissolving wood cellulose in either 64 wt% H2SO4 solution (RC-H4) or NaOH/urea aqueous solution (RC-N4). RC-H4 showed the higher tensile strength (109.78 ± 2.14 MPa), better folding endurance (20-28 times), and higher torsion angle (42°) than RC-N4 (62.90 ± 2.27 MPa, un-foldable, and 12°). The increased cellulose contents in the H2SO4 solutions from 3 to 5 wt% resulted in an improved tensile strength from 102.61 ± 1.99 to 132.93 ± 5.64 MPa and did not affect the foldability. RC-H4 also exhibited better water vapor barrier property (1.52 ± 0.04 × 10-7 g m-1 h-1 Pa-1), superior transparency (~90 % transmittance at 800 nm), but lower thermal stability compared to RC-N4. This work provides special insights into the regenerated wood cellulose from two aqueous solvents and is expected to facilitate the development of high-performance RC films from abundant forestry resources.

Near-Infrared (NIR) Silver Sulfide (Ag2S) Semiconductor Photocatalyst Film for Degradation of Methylene Blue Solution

A silver sulfide (Ag₂S) semiconductor photocatalyst film has been successfully synthesized using a solution casting method. To produce the photocatalyst films, two types of Ag₂S powder were used: a commercialized and synthesized powder. For the commercialized powder (CF/comAg₂S), the Ag₂S underwent a rarefaction process to reduce its crystallite size from 52 nm to 10 nm, followed by incorporation into microcrystalline cellulose using a solution casting method under the presence of an alkaline/urea solution. A similar process was applied to the synthesized Ag₂S powder (CF/syntAg₂S), resulting from the co-precipitation process of silver nitrate (AgNO₃) and thiourea. The prepared photocatalyst films and their photocatalytic efficiency were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and UV-visible spectroscopy (UV-Vis). The results showed that the incorporation of the Ag₂S powder into the cellulose films could reduce the peak intensity of the oxygen-containing functional group, which indicated the formation of a composite film. The study of the crystal structure confirmed that all of the as-prepared samples featured a monoclinic acanthite Ag₂S structure with space group P₂₁/C. It was found that the degradation rate of the methylene blue dye reached 100% within 2 h under sunlight exposure when using CF/comAg₂S and 98.6% for the CF/syntAg₂S photocatalyst film, and only 48.1% for the bare Ag₂S powder. For the non-exposure sunlight samples, the degradation rate of only 33-35% indicated the importance of the semiconductor near-infrared (NIR) Ag₂S photocatalyst used.