An In-Situ LSCM Study on Bainite Formation in a Fe-0.2C-1.5Mn-2.0Cr Alloy

In Situ High-Temperature EBSD and 3D Phase Field Studies of the Austenite-Ferrite Transformation in a Medium Mn Steel

In this research, in situ high-temperature electron backscattered diffraction (EBSD) mapping is applied to record and analyze the migration of the α/γ interfaces during cyclic austenite-ferrite phase transformations in a medium manganese steel. The experimental study is supplemented with related 3D phase field (PF) simulations to better understand the 2D EBSD observations in the context of the 3D transformation events taking place below the surface. The in situ EBSD observations and PF simulations show an overall transformation behavior qualitatively similar to that measured in dilatometry. The behavior and kinetics of individual austenite-ferrite interfaces during the transformation is found to have a wide scatter around the average interface behavior deduced on the basis of the dilatometric measurements. The trajectories of selected characteristic interfaces are analyzed in detail and yield insight into the effect of local conditions in the vicinity of interfaces on their motion, as well as the misguiding effects of 2D observations of processes taking place in 3D.

Study on Bainitic Transformation by Dilatometer and In Situ LSCM

This study investigates the bainitic transformation kinetics of carbide-free bainitic steel with Si + Al and carbide-bearing bainitic steel without Si + Al, as well as the phase transformation and microstructure through in situ high-temperature laser scanning confocal microscopy. Results show that bainitic ferrite plates preferentially nucleate at the grain boundary. New plates nucleate on previously formed ones, including two dimensions which appear on a plane where a three-dimensional space of bainitic ferrite forms. Nucleation on the formed bainitic ferrite is faster than that at the grain boundary in some grains. The bainitic ferrite growth at the austenite grain boundary is longer and has a faster transformation rate. The bainitic ferrite growth on the formed bainitic ferrite plate is shorter and has a slower transformation rate. The location and number of nucleation sites influence the thickness of the bainitic ferrite. The higher the number of plates preferentially nucleating at the original austenite grain boundary, the greater the thickness of the bainitic ferrite.

Exploring the Difference in Bainite Transformation with Varying the Prior Austenite Grain Size in Low Carbon Steel

The simulation welding thermal cycle technique was employed to generate different sizes of prior austenite grains. Dilatometry tests, in situ laser scanning confocal microscopy, and transmission electron microscopy were used to investigate the role of prior austenite grain size on bainite transformation in low carbon steel. The bainite start transformation (Bs) temperature was reduced by fine austenite grains (lowered by about 30 °C under the experimental conditions). Through careful microstructural observation, it can be found that, besides the Hall–Petch strengthening effect, the carbon segregation at the fine austenite grain boundaries is probably another factor that decreases the Bs temperature as a result of the increase in interfacial energy of nucleation. At the early stage of the transformation, the bainite laths nucleate near to the grain boundaries and grow in a “side-by-side” mode in fine austenite grains, whereas in coarse austenite grains, the sympathetic nucleation at the broad side of the pre-existing laths causes the distribution of bainitic ferrite packets to be interlocked.