Nanostructured Fe,Co-Codoped MoO₃ Thin Films

Synthesis and Characterization of Highly Photocatalytic Active Ce and Cu Co-Doped Novel Spray Pyrolysis Developed MoO3 Films for Photocatalytic Degradation of Eosin-Y Dye

The current work deals with the fabrication of novel MoO3 nanostructured films with Ce and Cu co-doping through the spray pyrolysis route on a glass substrate maintained at 460 °C for the first time. The phase of developed films was approved by an X-ray diffraction study, and the crystallite size was determined between 82 and 92 nm. The optical transmission of the developed films was noticed to be reduced with doping and found between 45 and 90% for all films, and the absorption edge shifted to a higher wavelength with doping. The optical energy gap of the fabricated films was found to be reduced from 3.85 to 3.28 eV with doping. The developed films were used to degrade the harmful Eosin-Y dye under UV light. The system with 2% Ce and 1% Cu-doped MoO3 turned out to be the most effective catalyst for photodegradation of the dye in a period of 3H and almost degrade it. Hence, the MoO3 films prepared with 2% Ce and 1% Cu will be highly applicable as photocatalysts for the removal of hazardous dye from wastewater.

Effect of Mg Doping on the Physical Properties of Fe2O3 Thin Films for Photocatalytic Devices

Undoped and Mg-doped (y = [Mg²⁺]/[Fe³⁺] = 1, 2, 3, and 4 at.%) Fe₂O₃ thin films were synthesized by a simple spray pyrolysis technique. The thin films were extensively characterized. X-ray diffraction (XRD) and energy-dispersive spectroscopy (EDS) analysis confirmed the successful insertion of Mg in the rhombohedral structure of Fe₂O₃. In addition, scanning electronic microscope (SEM) and confocal microscope (CM) images showed a homogenous texture of the film, which was free of defects. The rough surface of the film obtained by spray pyrolysis is an important feature for photocatalysis and gas sensor applications. The direct band gap of the doped Fe₂O₃ films obtained for [Mg²⁺]/[Fe³⁺] = 3 at.% was E_dir = 2.20 eV, which recommends the Mg-doped iron oxide as an optical window or buffer layer in solar cell devices. The photodegradation performance of Mg-doped Fe₂O₃ was assessed by studying the removal of methylene blue (MB) under sunlight irradiation, with an effective removal efficiency of 90% within 180 min. The excellent photodegradation activity was attributed to the strong absorption of Mg-doped Fe₂O₃ in the UV and most of the visible light, and to the effective separation of photogenerated charge carriers.

Synthesis and Characterization of MgO Thin Films Obtained by Spray Technique for Optoelectronic Applications

Magnesium oxide (MgO) thin films with different magnesium concentrations ([Mg²⁺] = 0.05, 0.1, 0.15 and 0.2 mol·L^-1) in a spray solution have been successfully grown using a spray pyrolysis technique. X-ray diffraction (XRD), Maud software, FTIR spectroscopy, a confocal microscope, Wien2k software, spectrophotometry and a Photoluminescence spectrometer were used to investigate the structural, morphological and optical properties. XRD analysis revealed a better crystalline quality of the MgO thin layer synthesized with [Mg²⁺] = 0.15 mol·L^-1, which crystallized into a face-centered cubic structure along the preferred orientation (200) lattice plan. The enhancement of the crystalline quality for the MgO thin film ([Mg²⁺] = 0.15 mol·L^-1) was obtained, which was accompanied by an increment of 94.3 nm of the crystallite size. No secondary phase was detected and the purity phase of the MgO thin film was confirmed using Maud software. From the transmission spectra results, high transparent and antireflective properties of the MgO thin film were observed, with an average transmission value of about 91.48% in the visible range, which can be used as an optical window or buffer layer in solar cell applications. The films also have a high reflectance value in the IR range, which indicates that the highly reflective surface will prevent an increase in surface temperature under solar irradiation, which could be beneficial in solar cell applications. A direct band gap type was estimated using the Tauc relation which is close to the experimental value of 4.0 eV for optimal growth. The MgO material was tested for the degradation of methylene blue (MB), which reached a high photodegradation rate of about 83% after 180 min under sunlight illumination. These experimental trends open a new door for promising the removal of water contaminants for photocatalysis application.

An Investigation on the Synthesis of Molybdenum Oxide and Its Silica Nanoparticle Composites for Dye Degradation

The molybdenum oxide (MoO₃) and MoO₃@SiO₂ nanoparticles were successfully prepared using the chemical bath deposition (CBD) method. The photocatalytic activities of molybdenum oxide (MoO₃), SiO₂, and MoO₃@SiO₂ nanoparticles composite have shown a synergistic photocatalytic effect of SiO₂ combined with MoO₃. The first-order degradation rate constants for MoO₃, SiO₂, and MoO₃@SiO₂ nanocomposite were 10.3 × 10⁻³ min⁻¹, 15.1 × 10⁻³ min⁻¹, and 16.3 × 10⁻³ min⁻¹, respectively. The MoO₃@SiO₂ composite showed degradation efficiencies in the methylene blue solution close to 100% after 60 min of UV irradiation. The X-ray diffraction (XRD) showed that the MoO₃ powder has a hexagonal crystal structure and the silica is the tridymite type of SiO₂. The crystallite size was about 94 nm, 32 nm, and 125 nm for MoO₃, silica, and MoO₃@SiO₂, respectively, as calculated by the Scherrer equation. The scanning electron microscopy (SEM) images revealed that the MoO₃ powder consisted of a uniform hexagonal structure; the silica showed a rod-like micro-flake morphology and the MoO₃@SiO₂ composite had the appearance of coral-like structures.