Influence of Electrochemical Pretreatment Conditions of PtCu/C Alloy Electrocatalyst on Its Activity

The Effect of Pretreatment on a PtCu/C Catalyst's Structure and Functional Characteristics

This research focuses on studying the effects of various pretreatment types on a PtCu/C catalyst synthesized by the co-deposition of metal precursors. The treatment in a 1 M HNO₃ solution for 1 h is shown to result in a slight increase in activity in the oxygen electroreduction reaction (both the mass activity and specific activity calculated for the value of the electrochemically active surface area). The sample obtained after the thermal treatment, which is carried out at 350 °C under an argon atmosphere for 1 h, demonstrates 1.7 times higher specific activity than the sample before the treatment. The durability testing results obtained by the stress testing method in a potential range of 0.6-1.4 V during 2000 cycles show that the PtCu/C catalysts after both the acid treatment and the thermal treatment are characterized by higher residual activity than the sample in the "as-prepared" state.

Electrochemical Activation and Its Prolonged Effect on the Durability of Bimetallic Pt-Based Electrocatalysts for PEMFCs

The present study, concerned with high-performance ORR catalysts, may be a valuable resource for a wide range of researchers within the fields of nanomaterials, electrocatalysis, and hydrogen energy. The objects of the research are electrocatalysts based on platinum–copper nanoparticles with onion-like and solid-solution structures. To evaluate the functional characteristics of the catalysts, the XRD, XRF, TEM, HAADF-STEM, and EDX methods, as well as the voltammetry method on a rotating disk electrode have been used. This work draws the attention of researchers to the significance of applying a protocol of electrochemically activating bimetallic catalysts in terms of the study of their functional characteristics on the rotating disk electrode. The choice of the potential range during the pre-cycling stage has been shown to play a crucial role in maintaining the durability of the catalysts. The activation of the PtCu/C catalyst during cycling of up to 1.0 V allows for an increase in the durability of the catalysts with onion-like and solid-solution structures of nanoparticles by 28% and 23%, respectively, as compared with activation of up to 1.2 V.

Architecture Evolution of Different Nanoparticles Types: Relationship between the Structure and Functional Properties of Catalysts for PEMFC

This review considers the features of the catalysts with different nanoparticle structures architecture transformation under the various pre-treatment types. Based on the results of the publications analysis, it can be concluded that the chemical or electrochemical activation of bimetallic catalysts has a significant effect on their composition, microstructure, and catalytic activity in the oxygen reduction reaction. The stage of electrochemical activation is recommended for use as a mandatory catalyst pre-treatment to obtain highly active de-alloyed materials. The literature is studied, which covers possible variants of the structural modification under the influence of thermal treatment under different processing conditions. Additionally, based on the literature data analysis, recommendations are given for the thermal treatment of catalysts alloyed with various d-metals.

Free-Standing, Interwoven Tubular Graphene Mesh-Supported Binary AuPt Nanocatalysts: An Innovative and High-Performance Anode Methanol Oxidation Catalyst

Pt-based alloy or bimetallic anode catalysts have been developed to reduce the carbon monoxide (CO) poisoning effect and the usage of Pt in direct methanol fuel cells (DMFCs), where the second metal plays a role as CO poisoning inhibitor on Pt. Furthermore, better performance in DMFCs can be achieved by improving the catalytic dispersion and using high-performance supporting materials. In this work, we introduced a free-standing, macroscopic, interwoven tubular graphene (TG) mesh as a supporting material because of its high surface area, favorable chemical inertness, and excellent conductivity. Particularly, binary AuPt nanoparticles (NPs) can be easily immobilized on both outer and inner walls of the TG mesh with a highly dispersive distribution by a simple and efficient chemical reduction method. The TG mesh, whose outer and inner walls were decorated with optimized loading of binary AuPt NPs, exhibited a remarkably catalytic performance in DMFCs. Its methanol oxidation reaction (MOR) activity was 10.09 and 2.20 times higher than those of the TG electrodes with only outer wall immobilized with pure Pt NPs and binary AuPt NPs, respectively. Furthermore, the catalyst also displayed a great stability in methanol oxidation after 200 scanning cycles, implying the excellent tolerance toward the CO poisoning effect.

Platinum-Containing Nanoparticles on N-Doped Carbon Supports as an Advanced Electrocatalyst for the Oxygen Reduction Reaction

New highly active electrocatalysts were obtained by depositing bimetallic Pt-Cu nanoparticles on the surface of an N-doped carbon support. The structural–morphological characteristics and electrochemical behavior of the catalysts were studied. Using current stress testing protocols, their resistance to degradation was assessed in comparison with that of a commercial Pt/C material. A combined approach to catalyst synthesis that consists in alloying platinum with copper and doping the support makes it possible to obtain catalysts with a uniform distribution of bimetallic nanoparticles on the carbon surface. The obtained catalysts exhibit high activity and durability.

Gas-Transport Characteristics of PdCu–Nb–PdCu Membranes Modified with Nanostructured Palladium Coating

A method for obtaining composite gas-diffusion PdCu–Nb–PdCu membranes modified with a nanostructured crystalline coating was developed to increase the performance of Nb-based membranes. A modifying functional layer with a controlled size and composition was synthesized by electrochemical deposition, which made it possible to determine a certain geometric shape for palladium nanocrystallites. Developed PdCu–Nb–PdCu membranes have demonstrated flux values up to 0.232 mmol s⁻¹ m⁻² in the processes of diffusion purification of hydrogen at 400 °C. A very significant difference in the hydrogen fluxes through the modified and non-modified composite PdCu–Nb–PdCu membranes reached 1.73 times at the lower threshold temperature of 300 °C. Cu doping of protective layer did not affect the selective properties of the membranes, which was confirmed by the obtained high selectivity values up to 1323, and made it possible to reduce the noble metal content. The research data indicate that the modification of the membrane surface significantly accelerates the hydrogen transfer process at sufficiently low temperatures due to the acceleration of dissociative–associative processes on the surface. The reported approach demonstrates new possibilities for creating productive and cost-efficient membranes based on niobium.

Cyanogel-Derived Synthesis of Porous PdFe Nanohydrangeas as Electrocatalysts for Oxygen Reduction Reaction

It is important to develop cost-efficient electrocatalysts used in the oxygen reduction reaction (ORR) for widespread applications in fuel cells. Palladium (Pd) is a promising catalyst, due to its more abundant reserves and lower price than platinum (Pt), and doping an earth-abundant 3d-transition metal M into Pd to form Pd-M bimetallic alloys may not only further reduce the use of expensive Pd but also promote the electrocatalytic performance of ORR, owing to the synergistic effect between Pd and M. Here we report a cyanogel-derived synthesis of PdFe alloys with porous nanostructure via a simple coinstantaneous reduction reaction by using K2PdIICl4/K4FeII(CN)6 cyanogel as precursor. The synthesized PdFe alloys possess hydrangea-like morphology and porous nanostructure, which are beneficial to the electrochemical performance in ORR. The onset potential of the porous PdFe nanohydrangeas is determined to be 0.988 V, which is much more positive than that of commercial Pt/C catalyst (0.976 V) and Pd black catalyst (0.964 V). Resulting from the unique structural advantages and synergetic effect between bimetals, the synthesized PdFe nanohydrangeas with porous structure have outstanding electrocatalytic activity and stability for ORR, compared with the commercial Pd black and Pt/C.

Influence of PtCu/C Catalysts Composition on Electrochemical Characteristics of Polymer Electrolyte Fuel Cell and Properties of Proton Exchange Membrane

The present work aimed to investigate the influence of “weakly bound“ copper dissolution from the surface of bimetallic PtCux/C catalysts on the properties of proton exchange membrane and the membrane electrode assembly (MEA) in general. A number of PtCux/C materials have been obtained by the simultaneous reduction in copper and platinum precursors in the course of liquid-phase synthesis with a varying ratio of metals from PtCu2.0/C to PtCu0.3/C. All bimetallic PtCux/C electrocatalysts after the activation stage exhibit high activity in the oxygen electroreduction reaction. The PtCux/C catalysts in “as prepared” state were tested in MEA. The increase in Cu content in PtCux/C catalysts led to a decrease in current density of MEA while its resistance was almost independent of the Cu fraction in the catalyst. The membrane saturation degree by Cu2+-ions after MEA testing did not exceed 40%, even in the case of the PtCu2.0/C material. The main reason for the degradation of membrane electrode assembly with PtCux/C materials is the transport limitation caused by the contamination of Nafion in three catalytic layer by “weakly bound” copper ions.