Synthesis and Characterization of Indium Tin Oxide Nanowires with Surface Modification of Silver Nanoparticles by Electrochemical Method

Synthesis and Physical Characteristics of Undoped and Potassium-Doped Cubic Tungsten Trioxide Nanowires through Thermal Evaporation

We report an efficient method to synthesize undoped and K-doped rare cubic tungsten trioxide nanowires through the thermal evaporation of WO₃ powder without a catalyst. The WO₃ nanowires are reproducible and stable with a low-cost growth process. The thermal evaporation processing was conducted in a three-zone horizontal tube furnace over a temperature range of 550-850 °C, where multiple substrates were placed at different temperature zones. The processing parameters, including pressure, temperature, type of gas, and flow rate, were varied and studied in terms of their influence on the morphology, aspect ratio and density of the nanowires. The morphologies of the products were observed with scanning electron microscopy. High resolution transmission electron microscopy, X-ray photoelectron spectroscopy, and X-ray diffraction studies were conducted to further identify the chemical composition, crystal structure and growth direction of the nanostructures. Additionally, the growth mechanism has been proposed. Furthermore, we investigated the potassium doping effect on the physical properties of the nanostructures. Photoluminescence measurements show that there were shorter emission bands at 360 nm and 410 nm. Field emission measurements show that the doping effect significantly reduced the turn-on electric field and increased the enhancement factor. Furthermore, as compared with related previous research, the K-doped WO₃ nanowires synthesized in this study exhibited excellent field emission properties, including a superior field enhancement factor and turn-on electric field. The study reveals the potential of WO₃ nanowires in promising applications for sensors, field emitters and light-emitting diodes.

Controlled Synthesis and Enhanced Gas Sensing Performance of Zinc-Doped Indium Oxide Nanowires

Indium oxide (In2O3) is a widely used n-type semiconductor for detection of pollutant gases; however, its gas selectivity and sensitivity have been suboptimal in previous studies. In this work, zinc-doped indium oxide nanowires with appropriate morphologies and high crystallinity were synthesized using chemical vapor deposition (CVD). An accurate method for electrical measurement was attained using a single nanowire microdevice, showing that electrical resistivity increased after doping with zinc. This is attributed to the lower valence of the dopant, which acts as an acceptor, leading to the decrease in electrical conductivity. X-ray photoelectron spectroscopy (XPS) analysis confirms the increased oxygen vacancies due to doping a suitable number of atoms, which altered oxygen adsorption on the nanowires and contributed to improved gas sensing performance. The sensing performance was evaluated using reducing gases, including carbon monoxide, acetone, and ethanol. Overall, the response of the doped nanowires was found to be higher than that of undoped nanowires at a low concentration (5 ppm) and low operating temperatures. At 300 °C, the gas sensing response of zinc-doped In2O3 nanowires was 13 times higher than that of undoped In2O3 nanowires. The study concludes that higher zinc doping concentration in In2O3 nanowires improves gas sensing properties by increasing oxygen vacancies after doping and enhancing gas molecule adsorption. With better response to reducing gases, zinc-doped In2O3 nanowires will be applicable in environmental detection and life science.

Chemical Vapor Deposition-Fabricated Manganese-Doped and Potassium-Doped Hexagonal Tungsten Trioxide Nanowires with Enhanced Gas Sensing and Photocatalytic Properties

Owing to its unique and variable lattice structure and stoichiometric ratio, tungsten oxide is suitable for material modification; for example, doping is expected to improve its catalytic properties. However, most of the doping experiments are conducted by hydrothermal or multi-step synthesis, which is not only time-consuming but also prone to solvent contamination, having little room for mass production. Here, without a catalyst, we report the formation of high-crystallinity manganese-doped and potassium-doped tungsten oxide nanowires through chemical vapor deposition (CVD) with interesting characterization, photocatalytic, and gas sensing properties. The structure and composition of the nanowires were characterized by transmission electron microscopy (TEM) and energy-dispersive spectroscopy (EDS), respectively, while the morphology and chemical valence were characterized by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), respectively. Electrical measurements showed that the single nanowires doped with manganese and potassium had resistivities of 1.81 × 0-5 Ω·m and 1.93 × 10-5 Ω·m, respectively. The doping contributed to the phase transition from monoclinic to metastable hexagonal for the tungsten oxide nanowires, the structure of which is known for its hexagonal electron channels. The hexagonal structure provided efficient charge transfer and enhanced the catalytic efficiency of the tungsten oxide nanowires, resulting in a catalytic efficiency of 98.5% for the manganese-doped tungsten oxide nanowires and 97.73% for the potassium-doped tungsten oxide nanowires after four hours of degradation of methylene blue. Additionally, the gas sensing response for 20 ppm of ethanol showed a positive dependence of doping with the manganese-doped and potassium-doped responses being 14.4% and 29.7%, respectively, higher than the pure response at 250 °C. The manganese-doped and potassium-doped tungsten oxide nanowires are attractive candidates in gas sensing, photocatalytic, and energy storage applications, including water splitting, photochromism, and rechargeable batteries.