Transparent PC/PMMA Blends Via Reactive Compatibilization in a Twin-Screw Extruder

Segregation Behavior of Miscible PC/PMMA Blends during Injection Molding

Miscible blends composed of bisphenol-A polycarbonate (PC) and poly(methyl methacrylate) (PMMA), in which one of them has low molecular weight, were employed to study the surface segregation behavior during flow. The blend samples showed typical rheological behaviors, such as simple polymer melts without a long-time relaxation mechanism ascribed to phase separation, demonstrating that they were miscible. After injection molding, the amounts of a low molecular weight component on the blend surface were found to be larger than the actual blend ratio. Because the injection-molded products were transparent despite a huge difference in refractive indices between PC and PMMA, they showed no phase separation. This result demonstrated that surface segregation of a low molecular weight component occurred under flow field, which expands the material design such as tough plastics with good scratch resistance and optical fibers with tapered refractive index.

Transparent PC/PMMA Blends with Enhanced Mechanical Properties via Reactive Compounding of Functionalized Polymers

Reactive compounding of terminally phenolic OH-functionalized polycarbonate (PC) with epoxy-functionalized polymethylmethacrylate (PMMA) prepared by copolymerization with glycidyl methacrylate was investigated. It was spectroscopically demonstrated that a PC/PMMA copolymer was formed during the melt reaction of the functional groups. Zirconium acetylacetonate could catalytically accelerate this reaction. Correlations of the phenomenological (optical and mechanical) properties with the molecular level and mesoscopic (morphological) structure were discussed. By the investigated reactive compounding process, transparent PC/PMMA blends with two-phase morphologies were obtained in a continuous twin-screw extruder, which, for the first time, combined the high transmission of visible light with excellent mechanical performance (e.g., synergistically improved tensile and flexural strength and high scratch resistance). The transparency strongly depended on (a) the degree of functionalization in both PC and PMMA, (b) the presence of the catalyst, and (c) the residence time of the compounding process. The in-situ-formed PC/PMMA copolymer influenced the observed macroscopic properties by (a) a decrease in the interphase tension, leading to improved and stabilized phase dispersion, (b) the formation of a continuous gradient of the polymer composition and thus of the optical refractive indices in a diffuse mesoscopic interphase layer separating the PC and PMMA phases, and (c) an increase in the phase adhesion between PC and PMMA due to mechanical polymer chain entanglement in this interphase.

Post-chemical grafting poly(methyl methacrylate) to commercially renewable elastomer as effective modifiers for polylactide blends

A novel poly(epichlorohydrin-co-ethylene oxide)-g-poly(methyl methacrylate) copolymer (ECO-g-PMMA) was successfully synthesized from a commercially renewable elastomer via the ATRP method. The graft copolymer was investigated as a toughening agent and compatibilizer for polylactide (PLA) and PLA/ECO blends, respectively. Binary blending PLA with the copolymers (5-15 wt%) significantly improved the strain at break of PLA above 200% without a great strength loss. More importantly, the ternary PLA/ECO/ECO-g-PMMA copolymer blends exhibited a remarkably high impact strength of 96.9 kJ/m² with non-broken behaviors. An interesting phase structure transformation from a typical sea-island structure to a unique quasi-continuous network structure was observed with varying the content of ECO-g-PMMA from 0 to 15 wt% in the ternary blends. The native toughening mechanism analysis indicated the synergistic toughening effect of the good interfacial adhesion and unique quasi-continuous morphology endowed the ternary blends with excellent mechanical performance.