Non-Woven Fabrics Based on Nanocomposite Nylon 6/ZnO Obtained by Ultrasound-Assisted Extrusion for Improved Antimicrobial and Adsorption Methylene Blue Dye Properties

Functional Technical Textile-Based Polymer Nanocomposites with Adsorbent Properties of Toxins and Dyes also Have Antibacterial Behavior

This is the first study of non-woven fabrics elaborated by melt-blowing from polymer nanocomposites made of Nylon 6 and nanoclay (Cloisite 20A) modified with an amine (1,4 diaminobutane dihydrochloride). Morphological and physical characteristics, adsorption capacity, and antibacterial properties are presented. From the X-ray diffraction (XRD) results, it was possible to observe a displacement of the signals to other 2θ angles, due to an α to ϒ phase shift. The scanning electron microscopy (SEM) images showed that the mean diameter of fiber decreased as the content of nanoclay increased. The mechanical tests showed that the tear strength force of neat nylon was 1.734 N, but this characteristic increased to 2.135 N for the sample with 0.5% modified nanoclay. The inulin adsorption efficiency of the Nylon 6/C20A 1.5% and Nylon 6/C20A 2% samples at 15 min was 75 and 74%, respectively. The adsorption capacity of Nylon 6/C20A 1.5% and Nylon 6/C20A 2% for methylene blue and methyl orange remained above 90% even after four adsorption cycles. In addition, non-woven fabrics present antibacterial activity against E. coli.

Green Nanomaterials for Smart Textiles Dedicated to Environmental and Biomedical Applications

Smart textiles recently reaped significant attention owing to their potential applications in various fields, such as environmental and biomedical monitoring. Integrating green nanomaterials into smart textiles can enhance their functionality and sustainability. This review will outline recent advancements in smart textiles incorporating green nanomaterials for environmental and biomedical applications. The article highlights green nanomaterials' synthesis, characterization, and applications in smart textile development. We discuss the challenges and limitations of using green nanomaterials in smart textiles and future perspectives for developing environmentally friendly and biocompatible smart textiles.

Influence of Modified Carbon Black on Nylon 6 Nonwoven Fabric and Performance as Adsorbent Material

The number of chronic kidney disease (CKD) persons continues to rise in Mexico. They require renal replacement therapy, and in the absence of it, hemodialysis is the major option for their survival. The uremic toxins present in the blood are removed by hemodialysis, which involve membranes. In this study, nonwoven fabrics with modified carbon black nanoparticles in a matrix polymer of Nylon 6 were obtained and evaluated as an adsorbent material of uremic toxins. All nonwoven fabrics were characterized by FTIR, XRD, TGA, SEM, and contact angle measurements and were evaluated as an adsorbent material for the urea toxin and as an albumin retainer. The findings suggest their potential application as a hemodialysis membrane. Nanocomposites had a higher hydrophilic characteristic compared to pure Nylon 6. The average diameter size of the fibers was in the range of 5 to 50 μm. All nanocomposites nonwoven fabrics showed high removal percentages of inulin in a range of 80-85% at 15 min of contact. Most Ny6 Zytel/CB nanocomposites showed a high percentage of urea removal (80 to 90%).

Surface modification of TiO2/ZnO nanoparticles by organic acids with enhanced methylene blue and rhodamine B dye adsorption properties

The United Nations Organization (UNO) has revealed that approximately 2.1 billion people do not have access to treated water. Methylene blue (MB) and rhodamine B are produced as water pollutants in textile, plastic, and dye industries. In this study, oxalic acid or lactic acid surface-modification were applied to TiO₂/ZnO nanoparticles aiming to improve antibacterial and adsorption properties. The mixtures containing the corresponding acid and nanoparticles in 0.25 : 1/0.5 : 1 ratios of ZnO and TiO₂ correspondingly were subjected to ultrasonic treatment with a catenoidal ultrasonic probe coupled to a homemade ultrasonic generator with an output power of 750 W, wave amplitude of 50% and variable frequency in the range of 15-50 kHz. To verify the influence of the ultrasonic treatment, different treatment times of 30, 45, 60, and 90 min were applied. Unmodified and modified TiO₂/ZnO nanoparticles were characterized by FTIR, TGA, XRD, SEM, and XPS. From the results, obtained from the physicochemical characterization, in the ZTO90 and ZTL90 samples a greater modification was shown. The SEM images showed that a coating was present on the surface of the ceramic particles of the ZTL90 sample. The O 1s deconvolution in the XPS spectra indicates a greater presence of C[double bond, length as m-dash]O bonds in the ZTL90 sample. In parallel, the sample ZTL90 presented 85 and 89% adsorption efficiency for MB and rhodamine B dyes in a time of 12 min, and important antibacterial activity against E. coli and S. epidermis could be evidenced.

Nanocomposite PLA/C20A Nanoclay by Ultrasound-Assisted Melt Extrusion for Adsorption of Uremic Toxins and Methylene Blue Dye

Design of functional materials it is of great importance to address important problems in the areas of health and environment. In the present work, the synthesis and application of poly-meric nanocomposite materials with poly (lactic acid) (PLA) and modified nanoclay (cloisite 20A) with 1,4-diaminobutane dihydrochloride at different reaction times were studied. The concentra-tions of the nanoclays in the PLA matrix were 0.5, 1 and, 5% by weight (wt%). TGA showed that sample C20AM 120 (120 min of treatment) obtained the highest degree of modification considering the weight losses of the analyzed samples. An FT-IR signal at 1443 cm⁻¹ suggests that the organic modifier is intercalated between the galleries of the clay. XRD, SEM and XPS suggest good disper-sion at low concentrations of the nanoclay. Adsorption tests revealed that the highest percentage of removal of uremic toxins and methylene blue was the sample with 5% wt/wt chemically modified nanoclay, suggesting good affinity between the modified nanoclays in the PLA matrix with the nitrogenous compounds.