Mechanical and Thermal Properties of Functionally Graded Polyolefin Elastomer Foams

Current Trend and New Opportunities for Multifunctional Bio-Scaffold Fabrication via High-Pressure Foaming

Biocompatible and biodegradable foams prepared using the high-pressure foaming technique have been widely investigated in recent decades as porous scaffolds for in vitro and in vivo tissue growth. In fact, the foaming process can operate at low temperatures to load bioactive molecules and cells within the pores of the scaffold, while the density and pore architecture, and, hence, properties of the scaffold, can be finely modulated by the proper selection of materials and processing conditions. Most importantly, the high-pressure foaming of polymers is an ideal choice to limit and/or avoid the use of cytotoxic and tissue-toxic compounds during scaffold preparation. The aim of this review is to provide the reader with the state of the art and current trend in the high-pressure foaming of biomedical polymers and composites towards the design and fabrication of multifunctional scaffolds for tissue engineering. This manuscript describes the application of the gas foaming process for bio-scaffold design and fabrication and highlights some of the most interesting results on: (1) the engineering of porous scaffolds featuring biomimetic porosity to guide cell behavior and to mimic the hierarchical architecture of complex tissues, such as bone; (2) the bioactivation of the scaffolds through the incorporation of inorganic fillers and drugs.

Morphological, Mechanical and Thermal Properties of Rubber Foams: A Review Based on Recent Investigations

During recent decades, rubber foams have found their way into several areas of the modern world because these materials have interesting properties such as high flexibility, elasticity, deformability (especially at low temperature), resistance to abrasion and energy absorption (damping properties). Therefore, they are widely used in automobiles, aeronautics, packaging, medicine, construction, etc. In general, the mechanical, physical and thermal properties are related to the foam's structural features, including porosity, cell size, cell shape and cell density. To control these morphological properties, several parameters related to the formulation and processing conditions are important, including foaming agents, matrix, nanofillers, temperature and pressure. In this review, the morphological, physical and mechanical properties of rubber foams are discussed and compared based on recent studies to present a basic overview of these materials depending on their final application. Openings for future developments are also presented.

Polyurethane Foam Waste Upcycling into an Efficient and Low Pollutant Gasification Syngas

Waste treatment has attracted much attention and, in this regard, gasification processes offer an efficient thermochemical technique that can produce a syngas rich in hydrogen. This technique has been well developed for solid waste and biomass while investigations on gasification of polymeric foam are rare. Therefore, this study explores the treatment of polyurethane foam waste with different gasifying agents, based on thermodynamic modeling. The polymeric foam gasification was developed using the best model for estimating higher heating value (gross calorific value). As the results indicated, models based on both ultimate and proximate analyses had better performance in predicting higher heating value. As one of the main objectives and novelties, the steam and air gasification performance of flexible and rigid polyurethane foam wastes was investigated and compared from efficiency and CO₂ emission viewpoints. Polyurethane foam gasification by steam resulted in higher hydrogen efficiency, led to lower energy efficiency and produced lower CO₂ emissions compared to gasification by air. A hydrogen efficiency of 41.4% was obtained for gasification of waste flexible polyurethane foam by steam. An energy efficiency of 76.6% and CO₂ emission of 7.43 g per mole of feedstock were attained for waste flexible polyurethane foam gasified by air.

Experimental and Finite Element Simulation of Polyolefin Elastomer Foams Using Real 3D Structures: Effect of Foaming Agent Content

In this study, polyolefin elastomer (POE) foams were prepared without any curing agent using a single-step foaming technique. The effect of azodicarbonamide (ADC) content as a chemical foaming agent on the foams’ morphology and mechanical properties was studied using scanning electron microscopy (SEM), mechanical properties (tension and compression) and hardness. The results showed that increasing the ADC content from 2 to 3, 4 and 5 phr (parts per hundred rubber) decreased the foam density from 0.75 to 0.71, 0.65 and 0.61 g/cm3, respectively. The morphological analysis revealed that increasing the ADC content from 2 to 4 phr produced smaller cell sizes from 153 to 109 µm (29% lower), but a higher cell density from 103 to 591 cells/mm3 (470% higher). However, using 5 phr of ADC led to a larger cell size (148 µm) and lower cell density (483 cells/mm3) due to cell coalescence. The tensile modulus, strength at break, elongation and hardness properties continuously decreased by 28%, 21%, 16% and 14%, respectively, with increasing ADC content (2 to 5 phr). On the other hand, the compressive properties, including elastic modulus and compressive strength, increased by 20% and 64%, respectively, with increasing ADC content (2 to 5 phr). The tensile and compression tests revealed that the former is more dependent on foam density (foaming ratio), while the latter is mainly controlled by the cellular structure (cell size, cell density and internal gas pressure). In addition, 2D SEM images were used to simulate the foams’ real 3D structure, which was used in finite element methods (FEM) to simulate the stress–strain behavior of the samples at two levels: micro-scale and macro-scale. Finally, the FEM results were compared to the experimental data. Based on the information obtained, a good agreement between the macro-scale stress–strain behavior generated by the FEM simulations and experimental data was obtained. While the FEM results showed that the sample with 3 phr of ADC had the lowest micro-scale stress, the sample with 5 phr had the highest micro-scale stress due to smaller and larger cell sizes, respectively.