Nano-Hydroxyapatite from White Seabass Scales as a Bio-Filler in Polylactic Acid Biocomposite: Preparation and Characterization

Enhanced chlorobenzene removal by internal magnetic field through initial cell adhesion and biofilm formation

Magnetic fields (MF) have been proven efficient in bioaugmentation, and the internal MFs have become competitive because they require no configuration, despite their application in waste gas treatment remaining largely unexplored. In this study, we firstly developed an intensity-regulable bioaugmentation with internal MF for gaseous chlorobenzene (CB) treatment with modified packing in batch bioreactors, and the elimination capacity increased by up to 26%, surpassing that of the external MF. Additionally, the microbial affinity to CB and the packing surface was enhanced, which was correlated with the ninefold increased secreted ratio of proteins/polysaccharides, 43% promoted cell surface hydrophobicity, and half reduced zeta potential. Furthermore, the dehydrogenase content was promoted over 3 times, and CB removal steadily increased with the rising intensity indicating enhanced biofilm activity and reduced CB bioimpedance; this was further supported by kinetic analysis, which resulted in improved cell adhesive ability and biological utilisation of CB. The results introduced a novel concept of adjustable magnetic bioaugmentation and provided technical support for industrial waste gas treatments. KEY POINTS: • Regulable magnetic bioaugmentation was developed to promote 26% chlorobenzene removal • Chlorobenzene mineralisation was enhanced under the magnetic field • Microbial adhesion was promoted through weakening repulsive forces.

Osseointegration enhancement by controlling dispersion state of carbonate apatite in polylactic acid implant

Osteoconductive ceramics (OCs) are often used to endow polylactic acid (PLA) with osseointegration ability. Conventionally, OC powder is dispersed in PLA. However, considering cell attachment to the implant, OCs may be more favorable when they exist in the form of aggregations, such as granules, and are larger than the cells rather than being dispersed like a powder. In this study, to clarify the effects of the dispersion state of OCs on the osseointegration ability, carbonate apatite (CAp), a bone mineral analog that is osteoconductive and bioresorbable, powder-PLA (P-PLA), and CAp granule-PLA (G-PLA) composite implants were fabricated via thermal pressing. The powder and granule sizes of CAp were approximately 1 and 300-600 µm, respectively. G-PLA exhibited a higher water wettability and released calcium and phosphate ions faster than P-PLA. When cylindrical G-PLA, P-PLA, and PLA were implanted in rabbit tibial bone defects, G-PLA promoted bone maturation compared to P-PLA and pure PLA. Furthermore, G-PLA bonded directly to the host bone, whereas P-PLA bonded across the osteoid layers. Consequently, the bone-to-implant contact of G-PLA was 1.8- and 5.6-fold higher than those of P-PLA and PLA, respectively. Furthermore, the adhesive shear strength of G-PLA was 1.9- and 3.0-fold higher than those of P-PLA and PLA, respectively. Thus, G-PLA achieved earlier and stronger osseointegration than P-PLA or PLA. The findings of this study highlight the significance of the state of dispersion of OCs in implants as a novel strategy for material development.

Fluoride Release and Rechargeability of Poly(lactic acid) Composites with Glass Ionomer Cement

This study investigates the fluoride release, rechargeability and degradation behaviors of newly developed anticariogenic poly(lactic acid) (PLA) composites. The PLA composite with various concentrations (0%, 5%, 10%, 15% and 20% by weight) of glass ionomer cement (GIC) and sodium fluoride (NaF) were prepared using solvent casting method. The fluoride release, fluoride rechargeability and degradation behavior were evaluated. All experimental groups demonstrated fluoride-releasing ability. The highest level of fluoride ions released was found in PLA composite with sodium fluoride (PLA/NaF). Following the 28-day period, both groups showed a gradual reduction in fluoride ion released, ranging between 0.03 ± 0.01 and 0.53 ± 0.06 ppm, although remaining within the effective range for tooth remineralization. However, the rechargeability was only observed in PLA composite with GIC (PLA/GIC). Following an eight-week in vitro degradation test, all PLA/NaF groups displayed a significantly higher percentage of weight change and water absorption compared to the PLA/GIC and the control group. In SEM analysis, the formation of surface porosities was clearly noticed in all PLA/NaF. All specimens retained their structural integrity throughout the study. In conclusion, the newly developed PLA/GIC displays promising possibilities as an anticariogenic material. Furthermore, the rechargeability of these ions are repeatable, ensuring their long-term utility.

Biodegradable Polylactic Acid-Polyhydroxyalkanoate-Based Nanocomposites with Bio-Hydroxyapatite: Preparation and Characterization

Biodegradable polymers play a significant role in medical applications, especially internal devices because they can be broken down and absorbed into the body without producing harmful degradation products. In this study, biodegradable polylactic acid (PLA)-polyhydroxyalkanoate (PHA)-based nanocomposites with various PHA and nano-hydroxyapatite (nHAp) contents were prepared using solution casting method. Mechanical properties, microstructure, thermal stability, thermal properties, and in vitro degradation of the PLA-PHA-based composites were investigated. PLA-20PHA/5nHAp was shown to give the desired properties so it was selected to investigate electrospinnability at different applied high voltages. PLA-20PHA/5nHAp composite shows the highest improvement of tensile strength at 36.6 ± 0.7 MPa, while PLA-20PHA/10nHAp composite shows the highest thermal stability and in vitro degradation at 7.55% of weight loss after 56 days of immersion in PBS solution. The addition of PHA in PLA-PHA-based nanocomposites improved elongation at break, compared to the composite without PHA. PLA-20PHA/5nHAp solution was successfully fabricated into fibers by electrospinning. All obtained fibers showed smooth and continuous fibers without beads with diameters of 3.7 ± 0.9, 3.5 ± 1.2, and 2.1 ± 0.7 µm at applied high voltages of 15, 20, and 25 kV, respectively.

Preparation and Characterization of Acrylonitrile Butadiene Rubber Reinforced with Bio-Hydroxyapatite from Fish Scale

This work aims to enhance the mechanical properties, oil resistance, and thermal properties of acrylonitrile butadiene rubber (NBR) by using the Nile tilapia fish scales as a filler and using bis(triethoxysilylpropyl)tetrasulfide (TESPT) as a coupling agent (CA). The prepared fish scale particles (FSp) are B-type hydroxyapatite and the particle shape is rod-like. The filled NBR with FSp at 10 phr increased tensile strength up to 180% (4.56 ± 0.48 MPa), reduced oil absorption up to 155%, and increased the decomposition temperature up to 4 °C, relative to the unfilled NBR. The addition of CA into filled NBR with FSp at 10 phr increased tensile strength up to 123% (5.62 ± 0.42 MPa) and percentage of elongation at break up to 122% relative to the filled NBR with FSp at 10 phr. This work demonstrated that the prepared FSp from the Nile tilapia fish scales can be used as a reinforcement filler to enhance the NBR properties for use in many high-performance applications.