Stick-slip behaviour on Au(111) with adsorption of copper and sulfate

Nanoscale Electron Transfer Variations at Electrocatalyst-Electrolyte Interfaces Resolved by in Situ Conductive Atomic Force Microscopy

Rational innovation of electrocatalysts requires detailed knowledge of spatial property variations across the solid-electrolyte interface. We introduce correlative atomic force microscopy (AFM) to simultaneously probe, in situ and at the nanoscale, electrical conductivity, chemical-frictional, and morphological properties of a bimetallic copper-gold system for CO₂ electroreduction. In air, water, and bicarbonate electrolyte, current-voltage curves reveal resistive CuO_x islands in line with local current contrasts, while frictional imaging indicates qualitative variations in the hydration layer molecular ordering upon change from water to electrolyte. Nanoscale current contrast on polycrystalline Au shows resistive grain boundaries and electrocatalytically passive adlayer regions. In situ conductive AFM imaging in water shows mesoscale regions of low current and reveals that reduced interfacial electric currents are accompanied by increased friction forces, thus indicating variations in the interfacial molecular ordering affected by the electrolyte composition and ionic species. These findings provide insights into how local electrochemical environments and adsorbed species affect interfacial charge transfer processes and support building in situ structure-property relationships in catalysis and energy conversion research.

In situ friction study of Ag Underpotential deposition (UPD) on Au(111) in aqueous electrolyte

The electrodeposition of silver on Au(111) was investigated using lateral force microscopy (LFM) in Ag+ containing sulfuric acid. Friction force images show that adsorbed sulfate forms3 × 7 R 19 . 1 ∘ structure (θ s u l f a t e = 0 . 2 ) on Au(111) prior to Ag underpotential deposition (UPD) and ( 3 × 3 R 30 ∘ ) structure (θ s u l f a t e = 0 . 33 ) on a complete monolayer or bilayer of Ag. Variation of friction with normal load shows a non-monotonous dependence, which is caused by increasing penetration of the tip into the sulfate adlayer. In addition, the friction force is influenced by the varying coverage and mobility of Ag atoms on the surface. Before Ag coverage reaches the critical value, the deposited silver atoms may be mobile enough to be dragged by the movement of AFM tip. Possible penetration of the tip into the UPD layer at very high loads is discussed as a model for self-healing wear. However, when the coverage of Ag is close to 1, the deposited Ag atoms are tight enough to resist the influence of the AFM tip and the tip penetrates only into the sulfate adlayer.