Effect of mechanochemical surface preparation on bonding to zirconia of a tri-n-butylborane initiated resin

Zirconia bond strength durability following artificial aging: A systematic review and meta-analysis of in vitro studies

The present study systematically reviewed the literature regarding the bond strength durability of zirconia ceramics to resin-based luting cements after application of different bonding protocols and aging conditions. Electronic searches in PubMed, Scopus, and Web of Science databases were performed for relevant literature published between January 1st 2015 and November 15th 2022. Ninety-three (93) English language in-vitro studies were included. The percentage of the mean bond strength change was recorded prior to and after artificial aging, and the weighted mean values and 95% confidence intervals were calculated. Bonding protocols were classified based on the combination of MDP/non-MDP containing cement/primer and surface pretreatment, as well as the level of artificial aging performed. Alumina sandblasting (SA) was identified as the most frequently used surface pre-treatment while an insufficient number of studies was identified for each category of alternative surface treatments. The combination of MDP cement with tribochemical silica coating (TSC) or SA yielded more durable results after aging, while the application of SA and TSC improved bond durability when a non-MDP cement and a non-MDP primer were used. TSC may lead to increased bond durability compared to SA, whereas MDP cements may act similarly when combined with SA or TSC.

Bond durability and surface states of titanium, Ti-6Al-4V alloy, and zirconia for implant materials

PURPOSE

Screw-retained implant crowns used as dental implants comprise a zirconia coping and titanium base bonded using resin cement. These devices are prone to debonding failures. This study investigated the bond characteristics of implant materials based on shear bond strength (SBS) and surface characteristics.

METHODS

Chemically pure (CP) titanium grade-4 (Ti), Ti-6Al-4V alloy (Ti-6Al-4V), and tetragonal polycrystalline zirconia (zirconia) were evaluated as adherent materials. Plates of each material were polished, primed for the respective resin cements, and cemented using either methyl methacrylate-based resin cement (Super-Bond) or composite-based resin cement (Panavia). The cemented samples were subjected to 10,000 thermocycles alternating between 5 and 55 °C, and the SBS were obtained before and after thermocycling. The sample surfaces were characterized based on surface observations, roughness, and free energy (SFE).

RESULTS

The SBSs of all materials bonded using Panavia were significantly compromised during thermocycling and reached zero. Although the SBSs of Ti and Ti-6Al-4V bonded using Super-Bond were not significantly affected by thermocycling, those of zirconia decreased significantly. The bond durability between zirconia and Super-Bond was improved via alumina air-abrasion, which caused no significant loss of SBS after thermocycling. Surface analyses of the air-abraded zirconia validated these results and confirmed that its surface roughness and SFE were significantly increased.

CONCLUSIONS

The bond durability between resin cement and zirconia was lower than that between Ti and Ti-6Al-4V. The alumina air-abrasion pretreatment of zirconia improved the SFE and surface roughness, thereby enhancing bond durability.

Bonding and Thermal Cycling Performances of Two (Poly)Aryl-Ether-Ketone (PAEKs) Materials to an Acrylic Denture Base Resin

Poly(aryl–ether–ketone) materials (PAEKs) are gaining interest in everyday dental practices because of their natural properties. This study aims to analyze the bonding performance of PAEKs to a denture acrylic. Testing materials were pretreated by grinding, sandblasting, and priming prior to polymerization with the denture acrylic. The surface morphologies were observed using a scanning electron microscope and the surface roughness was measured using atomic force microscopy. The shear bond strength (SBS) values were determined after 0 and 2500 thermal cycles. The obtained data were analyzed using a paired samples t-test and Tukey’s honestly significant difference (HSD) test (α = 0.05). The surface characteristics of testing materials after different surface pretreatments showed obvious differences. PAEKs showed lower surface roughness values (0.02–0.03 MPa) than Co-Cr (0.16 MPa) and zirconia (0.22 MPa) after priming and sandblasting treatments (p < 0.05). The SBS values of PAEKs (7.60–8.38 MPa) met the clinical requirements suggested by ISO 10477 (5 MPa). Moreover, PAEKs showed significantly lower SBS reductions (p < 0.05) after thermal cycling fatigue testing compared to Co-Cr and zirconia. Bonding performance is essential for denture materials, and our results demonstrated that PAEKs possess good resistance to thermal cycling fatigue, which is an advantage in clinical applications. The results imply that PAEKs are potential alternative materials for the removable of prosthetic frameworks.

Cement Type (Adhesive vs. Conventional) May Not Affect Clinical Performance of Zirconia and Lithium Disilicate Tooth-Supported Crowns

ARTICLE TITLE AND BIBLIOGRAPHIC INFORMATION

Effect of cement type on the clinical performance and complications of zirconia and lithium disilicate tooth-supported crowns: A systematic review. Report of the Committee on Research in Fixed Prosthodontics of the American Academy of Fixed Prosthodontics. Maroulakos G, Thompson GA, Kontogiorgos ED. J Prosthet Dent 2019;121:754-65.

SOURCE OF FUNDING

Unknown.

TYPE OF STUDY/DESIGN

Systematic review.

Adhesion to Zirconia: A Systematic Review of Current Conditioning Methods and Bonding Materials

Background. Reliable bonding between resin composite cements and high strength ceramics is difficult to achieve because of their chemical inertness and lack of silica content that makes etching impossible. The purpose of this review is to classify and analyze the existing methods and materials suggested to improve the adhesion of zirconia to dental substrate by using composite resins, in order to explore current trends in surface conditioning methods with predictable results. Methods. The current literature, examining the bond strength of zirconia ceramics, and including in vitro studies, clinical studies, and a systematic review, was analyzed. The research in the literature was carried out using PubMed and Cochrane Library databases, only papers in English, published online from 2013 to 2018. The following keywords and their combinations were used: Zirconia, 3Y-TZP, Adhesion, Adhesive cementation, Bonding, Resin, Composite resin, Composite material, Dentin, Enamel. Results. Research, in PubMed and Cochrane Library databases, provided 390 titles with abstracts. From these, a total of 93 publications were chosen for analysis. After a full text evaluation, seven articles were discarded. Therefore, the final sample was 86, including in vitro, clinical studies, and one systematic review. Various adhesive techniques with different testing methods were examined. Conclusions. Airborne-particle abrasion and tribo-chemical silica coating are the pre-treatment methods with more evidence in the literature. Increased adhesion could be expected after physico-chemical conditioning of zirconia. Surface contamination has a negative effect on adhesion. There is no evidence to support a universal adhesion protocol.

Chemical alteration of Ag-Pd-Cu-Au alloy surface by alumina air-abrasion and its effect on bonding to resin cement

The goal of this study was to investigate the chemical alteration of a dental alloy surface by alumina air-abrasion and its effect on bonding to resin cement. Alumina air-abrasion was carried out on an Ag-Pd-Cu-Au alloy. The surface morphology and chemical state of the abraded alloy were characterized. The effect of the air-abrasion on the shear bond strength between the alloy and a methyl methacrylate/tri-n-butyl borane (MMA/TBB) resin cement with some primers was evaluated. The surface characterization revealed that the alumina air-abrasion mechanically roughened and chemically altered the surface. The chemical alterations had two effects: (1) abraded alumina particles remained on the alloy surface and (2) copper ions were oxidized in the alloy surface. As the result, the shear bond strength test indicated that 10-methacryloyloxydecyl dihydrogen phosphate (MDP) contained primer worked with the abraded alloy surface, whereas it did not work with the non-abraded alloy surface.

The effect of subpressure on the bond strength of resin to zirconia ceramic

Objective

This study was conducted to investigate the effect of subpressure on the bond strength of resin to zirconia ceramic. The subpressure would create a pressure gradient which could clean out the bubbles in the adhesives or bonding interface.

Methods

Twenty-eight pre-sintered zirconia discs were fabricated. Half of them were polished (group P, n = 14), and the rest were sandblasted (group S, n = 14). After sintered,the surface roughness of the zirconia discs was measured. Then, they were randomly divided into two subgroups (n = 7). The groups were named as follows: PC: P + no additional treatments; PP: P + 0.04 MPa after application of adhesives; SC: S + no additional treatments; and SP: S + 0.04 MPa after application of adhesives. Resin columns were bonded to the zirconia specimens to determine shear bond strength (SBS). The bonding interfaces were observed and the fracture modes were evaluated. Statistical analysis was performed on all data.

Results

The surface roughness of group S was significantly higher than that of group P (P<0.05). The SBS values were PC = 13.48 ± 0.7 MPa, PP = 15.22 ± 0.8 MPa, SC = 17.23 ± 0.7 MPa and SP = 21.68 ± 1.4 MPa. There were significant differences among the groups (P<0.05). Scanning electron microscopy (SEM) results showed that the adhesives of group SP and PP were closer and denser to the zirconia ceramic than that of group PC and SC. The proportion of the mixed fracture mode significantly increased after adding subpressure (P< 0.05).

Conclusion

Subpressure can improve the shear bond strength of resin to zirconia ceramics and increase micro-infiltration between the adhesives and the zirconia ceramics, especially on the rough surfaces.