Monomer conversion, biaxial flexural strength, apatite forming ability of experimental dual-cured and self-adhesive dental composites containing calcium phosphate and nisin

Comparative analysis of self-cure and dual cure-dental composites on their physico-mechanical behaviour

BACKGROUND

Clinical practitioners may have become familiar with the rapid transformation of dental composites. However, they may not scientifically understand the factors influencing the mechanical and physical properties. Scientific knowledge of filler-resin interaction can significantly improve clinical understanding of resin composites. Several independent studies have examined the mechanical and physico-mechanical properties of dental resin composites; however, no comprehensive study has examined the influence of fillers and resin materials on the physico-mechanical properties of both self-cure and dual-cure composites.

METHODS

This study performed investigations on the physico-mechanical behaviour of four commercially available dual-cure dental composites (Bioactive, Fill Up!, Surefil One, Cention N) and two commercially available self-cure dental composites (Stela Capsule and Stela Automix). Test specimens for flexural and compressive strength, microhardness, fracture toughness, and hydrolytic behaviour were prepared and tested as per respective standards. The data sets were statistically analysed using one-way ANOVA and Tukey's post-hoc comparison.

RESULTS

There was a substantial variation in flexural strength and modulus values in this study, ranging from 32.0 to 113.4 MPa and 2.36 to 12.07 GPa, respectively. Similarly, there were significant differences in compressive strength between the materials in this study, ranging from 119.3 to 223.5 MPa. The highest fracture toughness value was found to be 1.41 MPa.m0.5, while the lowest value was 0.43 MPa.m0.5. Variations in surface microhardness were significant (24.11-68.0 N/mm2), which correlated with the filler content. Water sorption and solubility demonstrated high variations among materials, with Surefil One exceeding ISO 4049 thresholds significantly.

CONCLUSIONS

A linear correlation can be established between surface microhardness (HV) and flexural and compressive moduli, as well as filler content (wt.%). However, both flexural and compressive strengths are impacted by the resin's constituent monomers and the resin-filler matrix's cross-linking capability. Additionally, factors such as filler size, shape, and the cross-linking ability of the resin-filler matrix play a crucial role in fracture toughness and the propagation of cracks within the restoration. Also, resin monomers and filler particle size affect the hydrolytic degradation characteristics of composites, which can also affect their mechanical properties. © 2023 Australian Dental Association.

Addition of nisin to high-viscosity glass-ionomer cement: a comparative in vitro study on antibacterial and physical properties

PURPOSE

Nisin is a lantibiotic effective against Gram-positive microorganisms such as Streptococcus mutans. The study aimed to determine the effect of the addition of nisin to high-viscosity glass-ionomer cement (HVGIC) on its antibacterial activity, setting time, surface microhardness, and compressive strength.

METHODS

1 and 3% w/w nisin were added to HVGIC before mixing. Unmodified HVGIC was the control. Agar disc diffusion, direct contact test, and scanning electron microscopy (SEM) analysis were used to evaluate antibacterial activity against S. mutans. Setting time, surface microhardness, and compressive strength were measured using Gilmore needle apparatus, digital microhardness tester, and universal testing machine, respectively. Statistical analysis included Student's t test, one-way ANOVA with Tamhane's post hoc test, and repeated-measures ANOVA.

RESULTS

As evidenced by the agar disc diffusion (p < 0.001), direct contact tests (p = 0.025), and SEM analysis of the S. mutans cell count and cell surface area (p = 0.049 and 0.003), 3% nisin had the strongest antibacterial activity. There was a dose-dependent increase in setting time (p = 0.005) and surface microhardness (p = 0.006), with no significant difference in compressive strength compared to control.

CONCLUSION

The addition of 3% nisin to HVGIC enhances the antibacterial action against S. mutans and surface microhardness without adversely affecting setting time and compressive strength.

Assessment of physical/mechanical properties and cytotoxicity of dual-cured resin cements containing Sr-bioactive glass nanoparticles and calcium phosphate

The aim was to develop dual-cured resin cements containing Sr-bioactive glass nanoparticles (Sr-BGNPs; 5 or 10 wt%) and monocalcium phosphate monohydrate (MCPM; 3 or 6 wt%). Effects of additives on degree of monomer conversion (DC), biaxial flexural strength/modulus, shear bond strength (SBS), mass/volume change, color stability, ion release, and cytotoxicity were examined. Controls included material without reactive fillers and Panavia SA Plus (PV). Experimental cements showed higher DC than PV regardless of light activation (p<0.05). Mean SBS and color stability were comparable between experimental cements and PV. Cell viability upon the exposure to sample extracts of experimental cements was 80%-92%. High additive concentrations led to lower strength and modulus than PV (p<0.05). The additives increased mass change, reduced color stability, and promoted ion release. The experimental resin cements demonstrated acceptable mechanical/chemical properties and cytotoxicity. The additives reduced the strength but provided ion release, a desirable action to prevent recurrent caries.

Assessment of Physical/Mechanical Performance of Dental Resin Sealants Containing Sr-Bioactive Glass Nanoparticles and Calcium Phosphate

The aim of this study was to assess the chemical/mechanical properties of ion-releasing dental sealants containing strontium-bioactive glass nanoparticles (Sr-BGNPs) and monocalcium phosphate monohydrate (MCPM). Two experimental sealants, TS1 (10 wt% Sr-BGNPs and 2 wt% MCPM) and TS2 (5 wt% Sr-BGNPs and 4 wt% MCPM), were prepared. Commercial controls were ClinproXT (CP) and BeautiSealant (BT). The monomer conversion (DC) was tested using ATR−FTIR (n = 5). The biaxial flexural strength (BFS) and modulus (BFM) were determined (n = 5) following 24 h and 7 days of immersion in water. The Vickers surface microhardness (SH) after 1 day in acetic acid (conc) versus water was tested (n = 5). The bulk and surface calcium phosphate precipitation in simulated body fluid was examined under SEM-EDX. The ion release at 4 weeks was analyzed using ICP-MS (n = 5). The DC after 40 s of light exposure of TS1 (43%) and TS2 (46%) was significantly lower than that of CP (58%) and BT (61%) (p < 0.05). The average BFS of TS1 (103 MPa), TS2 (123 MPa), and BT (94 MPa) were lower than that of CP (173 MPa). The average BFM and SH of TS1 (2.2 GPa, 19 VHN) and TS2 (2.0 GPa, 16 VHN) were higher than that of CP (1.6 GPa, 11 VHN) and BT (1.3 GPa, 12 VHN). TS1 showed higher Ca, P, and Sr release than TS2. Bulk calcium phosphate precipitation was detected on TS1 and TS2 suggesting some ion exchange. In conclusion, the DC of experimental sealants was lower than that of commercial materials, but their mechanical properties were within the acceptable ranges. The released ions may support remineralizing actions.

Effects of Sr/F-Bioactive Glass Nanoparticles and Calcium Phosphate on Monomer Conversion, Biaxial Flexural Strength, Surface Microhardness, Mass/Volume Changes, and Color Stability of Dual-Cured Dental Composites for Core Build-Up Materials

This study prepared composites for core build-up containing Sr/F bioactive glass nanoparticles (Sr/F-BGNPs) and monocalcium phosphate monohydrate (MCPM) to prevent dental caries. The effect of the additives on the physical/mechanical properties of the materials was examined. Dual-cured resin composites were prepared using dimethacrylate monomers with added Sr/F-BGNPs (5 or 10 wt%) and MCPM (3 or 6 wt%). The additives reduced the light-activated monomer conversion by ~10%, but their effect on the conversion upon self-curing was negligible. The conversions of light-curing or self-curing polymerization of the experimental materials were greater than that of the commercial material. The additives reduced biaxial flexural strength (191 to 155 MPa), modulus (4.4 to 3.3), and surface microhardness (53 to 45 VHN). These values were comparable to that of the commercial material or within the acceptable range of the standard. The changes in the experimental composites’ mass and volume (~1%) were similar to that of the commercial comparison. The color change of the commercial material (1.0) was lower than that of the experimental composites (1.5–5.8). The addition of Sr/F-BGNPs and MCPM negatively affected the physical/mechanical properties of the composites, but the results were satisfactory except for color stability.

Effects of Silver Diamine Nitrate and Silver Diamine Fluoride on Dentin Remineralization and Cytotoxicity to Dental Pulp Cells: An In Vitro Study

Silver diamine nitrate (SDN) is expected to help control caries similar to silver diamine fluoride (SDF). The aim of this study was to determine the mineral precipitation in demineralized dentin and the cytotoxicity of SDN and SDF to dental pulp cells. Demineralized dentin specimens were prepared, and SDF, SDN, or water (control) was applied. The specimens were then remineralized in simulated body fluid for 2 weeks. The mineral precipitation in the specimens was examined using FTIR-ATR, SEM-EDX, and synchrotron radiation X-ray tomographic microscopy (SRXTM). Additionally, the cytotoxicity of SDF and SDN to human dental pulp stem cells was analyzed using an MTT assay. The increase in FTIR spectra attributable to apatite formation in demineralized dentin in the SDF group was significantly higher compared to the SDN and control groups (p < 0.05). Dentinal tubule occlusion by the precipitation of silver salts was detected in both SDF and SDN groups. The mineral density as shown in SRXTM images and cytotoxicity of both SDN and SDF groups were comparable (p > 0.05). In conclusion, SDF demonstrated superior in vitro apatite formation compared to SDN. However, the degree of mineral precipitation and cytotoxic effects of both were similar.

Comparison of the effect of preheating on the flexural strength of giomer and nanohybrid composite resin

Background. Considering the increased use of preheating and novel resin-based materials to restore teeth, the present study investigated the impact of preheating on the flexural strength of a giomer and compared it with a nanohybrid composite resin. Methods. Two restorative materials (Beautifil II giomer and Alpha III nanohybrid composite resin) were used. Thirty rod-shaped samples (adding up to 60 samples) were prepared from the materials above and divided into two subgroups: with and without preheating (n=15). Before sample preparation, the giomer and nanohybrid composite resin tubes were preheated at 68ºC for 15 minutes in the preheating subgroups. In the subgroups without preheating, the tubes were kept in a room at 25ºC. Then the flexural strength was compared between the two groups with two-way ANOVA at a significance level of P<0.05. Results. The results showed significantly higher flexural strength in the preheated subgroups than in the non-preheated subgroups (P<0.001). In addition, the mean flexural strength values were significantly higher in the giomer groups than in the nanohybrid composite resin groups (P<0.001). Conclusion. Preheating increased the studied materials' flexural strengths significantly. The flexural strength of the giomer restorative material was higher than that of the nanohybrid composite resin, irrespective of preheating.

Physical/Mechanical and Antibacterial Properties of Orthodontic Adhesives Containing Calcium Phosphate and Nisin

Enamel demineralization around orthodontic adhesive is a common esthetic concern during orthodontic treatment. The aim of this study was to prepare orthodontic adhesives containing monocalcium phosphate monohydrate (MCPM) and nisin to enable mineralizing and antibacterial actions. The physicomechanical properties and the inhibition of S. mutans growth of the adhesives with added MCPM (5, 10 wt %) and nisin (5, 10 wt %) were examined. Transbond XT (Trans) was used as the commercial comparison. The adhesive containing a low level of MCPM showed significantly higher monomer conversion (42–62%) than Trans (38%) (p < 0.05). Materials with additives showed lower monomer conversion (p < 0.05), biaxial flexural strength (p < 0.05), and shear bond strength to enamel than those of a control. Additives increased water sorption and solubility of the experimental materials. The addition of MCPM encouraged Ca and P ion release, and the precipitation of calcium phosphate at the bonding interface. The growth of S. mutans in all the groups was comparable (p > 0.05). In conclusion, experimental orthodontic adhesives with additives showed comparable conversion but lesser mechanical properties than the commercial material. The materials showed no antibacterial action, but exhibited ion release and calcium phosphate precipitation. These properties may promote remineralization of the demineralized enamel.

Effects of Color Modifier on Degree of Monomer Conversion, Biaxial Flexural Strength, Surface Microhardness, and Water Sorption/Solubility of Resin Composites

Color modifiers can be mixed with resin composites to mimic the shade of severely discolored tooth. The aim of this study was to assess the effects of a color modifier on the physical and mechanical properties of a resin composite. The composite was mixed with a color modifier at 0 wt% (group 1), 1 wt% (group 2), 2.5 wt% (group 3), or 5 wt% (group 4). The degree of monomer conversion (DC) was examined after light curing for 20 or 40 s. Biaxial flexural strength (BFS)/modulus (BFM), surface microhardness (SH), and water sorption (W_sp)/solubility (W_sl) were also tested. The DC of group 1 was significantly higher than that of groups 3 and 4. The increase in curing time from 20 to 40 s increased the DC by ~10%. The BFS, BFM, W_sp, and W_sl of all the groups were comparable. A negative correlation was detected between the concentration of color modifier and the BFS and DC, while a positive correlation was observed with W_sp. In conclusion, the color modifier reduced the DC of composites, but the conversion was improved by extending the curing time. The increase in color modifier concentration also correlated with a reduction in strength and the increase in the water sorption of the composites.

Monomer Conversion, Dimensional Stability, Biaxial Flexural Strength, Ion Release, and Cytotoxicity of Resin-Modified Glass Ionomer Cements Containing Methacrylate-Functionalized Polyacids and Spherical Pre-Reacted Glass Fillers

The aim of this study was to prepare RMGICs for pulp protection that contain polyacids functionalized with methacrylate groups (CMs) to enable light-activated polymerization without the need for toxic 2-hydroxyethyl methacrylate (HEMA) monomers. The effects of using CM liquids with 0 or 5 wt% HEMA on the physical/mechanical properties and cytotoxicity of the experimental RMGICs were assessed. Spherical pre-reacted glass fillers (SPG) were used as the powder phase. The experimental RMGICs were prepared by mixing SPG with CM liquid (0 wt% HEMA, F1) or CMH liquid (5 wt% HEMA, F2). Commercial materials (Vitrebond, VB; TheraCal LC, TC) were used for the comparisons. The degree of monomer conversion and fluoride release of both F1 and F2 were significantly lower than those of VB. F1 showed comparable biaxial flexural strength with VB but higher strength than TC. The dimensional stability (mass/volume changes) of the experimental materials was comparable with that of the commercial materials. F1 and F2 exhibited higher Sr/Ca ion release and relative cell viability than VB. The use of CMH liquid reduced the strength but enhanced the fluoride release of the experimental RMGICs. In conclusion, the experimental RMGICs showed comparable strength but lower cytotoxicity compared to the commercial RMGICs. These novel materials could be used as alternative materials for pulp protection.

Effects of Different Application Times of Silver Diamine Fluoride on Mineral Precipitation in Demineralized Dentin

Silver diamine fluoride (SDF) is a cost-effective method for arresting active dental caries. However, the limited cooperation of patients may lead to an SDF application time that is shorter than the recommended 1-3 min for carious lesions. Therefore, the aim of this study was to assess the effect of different application times of SDF on the degree of mineral precipitation in demineralized dentin. Demineralized dentin specimens from permanent maxillary molars were treated by applying 38% SDF for 30, 60, or 180 s. Water was applied in the control group. The specimens were immersed in simulated body fluid for 2 weeks, and the mineral precipitation in demineralized dentin was then analyzed using FTIR-ATR, SEM-EDX, and synchrotron radiation X-ray tomographic microscopy (SRXTM). The FTIR-ATR results showed a significant increase in mineral precipitation in the 180 s group after 1 week. However, after 2 weeks, the SRXTM images indicated comparable mineral density between the 30, 60, and 180 s groups. The precipitation of silver chloride and calcium phosphate crystals that occluded dentinal tubules was similar in all experimental groups. In conclusion, an application time of either 30, 60, or 180 s promoted a comparable degree of mineral precipitation in demineralized dentin.