Mechanical and chemical characterization of contemporary occlusal splint materials fabricated with different methods: a systematic review

OBJECTIVE

To systematically review studies on various occlusal splint materials and describe their mechanical and chemical properties.

METHODS

MEDLINE (PubMed), Scopus, and Web of Science searches were conducted for in vitro studies focusing on occlusal splint materials. Two reviewers performed an assessment of the identified studies and data abstraction independently, and this was complimented by an additional hand search. The articles were limited to those in the English language that were published between January 1st, 2012, and December 1st, 2022.

RESULTS

The initial search yielded 405 search results of which 274 were selected for full-text review following abstract evaluation. 250 articles that did not meet the inclusion criteria were excluded, and the remaining 25 articles (with 1 article identified from the reference lists of included articles) providing mechanical and chemical values were used in this review. Poly methyl methacrylate (PMMA) -based occlusal splint materials showed the highest values in terms of hardness, wear resistance, flexural strength, flexural modulus, e-modulus, and fracture toughness. The material group with the highest water sorption and water solubility was 3D printed (PR) splint materials. In addition, the lowest degree of double bond conversion was also observed in this group of materials.

CONCLUSIONS

The outcome of this review suggests that mechanically and chemically acceptable properties can be attained with PMMA-based occlusal splint materials using both conventional and digital production methods. PR splint materials should not be considered as the primary choice for long-term treatments due to their low mechanical and chemical properties.

CLINICAL RELEVANCE

This review provides clinical recommendations for selecting the appropriate material and fabrication method for occlusal splints while taking the patients' needs and the materials´ mechanical and chemical properties into account.

Bioactive Glass-Enhanced Resins: A New Denture Base Material

BACKGROUND

The creation of the denture base material with bioactive properties that releases ions and produces hydroxyapatite.

METHODS

Acrylic resins were modified by the addition of 20% of four types of bioactive glasses by mixing with powders. Samples were subjected to flexural strength (1, 60 days), sorption and solubility (7 days), and ion release at pH 4 and pH 7 for 42 days. Hydroxyapatite layer formation was measured using infrared.

RESULTS

Biomin F glass-containing samples release fluoride ions for a period of 42 days (pH = 4; Ca = 0.62 ± 0.09; P = 30.47 ± 4.35; Si = 22.9 ± 3.44; F = 3.1 ± 0.47 [mg/L]). The Biomin C (contained in the acrylic resin releases (pH = 4; Ca = 41.23 ± 6.19; P = 26.43 ± 3.96; Si = 33.63 ± 5.04 [mg/L]) ions for the same period of time. All samples have a flexural strength greater than 65 MPa after 60 days.

CONCLUSION

The addition of partially silanized bioactive glasses allows for obtaining a material that releases ions over a longer period of time.

CLINICAL SIGNIFICANCE

This type of material could be used as a denture base material, helping to preserve oral health by preventing the demineralization of the residual dentition through the release of appropriate ions that serve as substrates for hydroxyapatite formation.

Characterization of occlusal splint materials: CAD-CAM versus conventional resins

AIM

The aim of this in vitro study was to assess the mechanical properties of five commercially available subtractive computer-aided design and computer-aided manufacturing (CAD-CAM) milled splint materials, as well as to compare them with conventional heat-polymerized and autopolymerizing resins used in the construction of conventional splints.

MATERIAL AND METHODS

Five CAD-CAM milled (ProArt CAD Splint, Therapon Transpa, Temp Premium Flexible Transpa, Cast, and Aqua), one autopolymerizing (Palapress), and one heat-polymerized (Paladon 65) resin materials were evaluated. Flexural strength, E-modulus, Vickers hardness, fracture toughness, fracture work, water sorption, and water solubility were measured. Samples were evaluated after dry and water storage for 30 days at 37 °C. Data were collected and statistically analyzed.

RESULTS

Under both storage circumstances, the flexural strength values of Paladon 65, Therapon Transpa, Temp Premium Flexible Transpa, and Aqua were statistically non-significant (P=0.055). The polycarbonate-based CAD-CAM material Temp Premium Flexible Transpa had the highest statistically significant values of the fracture toughness and fracture work (P<0.001). Moreover, it exhibited the lowest percentages of water sorption and water solubility among the investigated materials (P<0.001). All of the CAD-CAM materials exhibited dry elastic moduli greater than Palapress and lower than Paladon 65. One of the CAD-CAM materials, Cast, had the highest dry Vickers hardness value, which was non-significant when compared to Therapon Transpa (P=0.762).

CONCLUSION

CAD-CAM polycarbonate-based splint materials exhibit higher fracture toughness and fracture work as well as lower water sorption and solubility than polymethyl methacrylate-based ones. The mechanical characteristics of the assessed CAD-CAM milled splint materials were not typically superior to those of the conventional heat-polymerized resin. However, some of them outperformed the autopolymerizing acrylic resin in terms of flexural strength, surface microhardness, water sorption, and water solubility.