Which is the best bearing surface for primary total hip replacement? A New Zealand Joint Registry study

Pseudotumor from ceramic-on-ceramic total hip arthroplasty

INTRODUCTION AND IMPORTANCE

Total hip arthroplasty is one of the most performed surgical interventions in the world. Adverse local tissue reactions and pseudotumors are infrequent but dangerous eventualities, which are often related with metal-on-metal or metal-on-polyethylene implants. This study wants to highlight how adverse local tissue reactions and pseudotumors must be taken into consideration during the diagnostic process.

CASE PRESENTATION

We report the case of a patient with ceramic-on-ceramic modular total hip arthroplasty with titanium neck. 12 years after surgery, he complained of pain and swelling on the hip. Diagnostic tests revealed the presence of a bulky pseudotumor. During the revision surgery biopsy samples were taken and microscopical analysis revealed the presence of fibrous tissue, fibrin hemorrhagic collections, histiocytes and chronic inflammation due to foreign body, with dark refractive material of an exogenous nature.

CLINICAL DISCUSSION

The possible formation of pseudotumor and metallosis reactions in hip prostheses with metal-on-metal coupling or in couplings with polyethylene is known. Many cases of pseudotumor are reported after revision of prostheses due to the breakage of ceramic components, but we did not observe any damage or corrosion of the prosthetic elements; on the other hand, we noticed an excessive retroversion of the femoral neck. It may be possible that an accurate microscopic analysis could clarify the failure of this implant.

CONCLUSION

To date ceramic-ceramic coupling remains the gold standard in terms of resistance and durability for hip arthroplasty but there is still a gap of knowledge in the field of tribology and individual immune response mechanisms.

The utility of cemented femoral stems in modern THA: a 10-year comparative analysis of the Charnley and Exeter stems

BACKGROUND

Total hip replacement (THR) is one of the most common surgical procedures performed worldwide. The controversy surrounding the relative merits of a cemented composite beam or cemented taper-slip stem in total hip replacement continues. Our aims primarily were to assess the 10-year outcomes of cemented stems using Charnley and Exeter prostheses with regional registry data and secondarily to assess the main predictors of revision.

METHODS

We prospectively collected registry data for procedures performed between January 2005 and June 2008. Only cemented Charnley and Exeter stems were included. Patients were prospectively reviewed at 6 months, 2, 5 and 10 years. The primary outcome measure was a 10-year all-cause revision. Secondary outcomes included 're-revision', 'mortality' and functional 'Western Ontario and McMaster Universities Osteoarthritis Index' (WOMAC) scores.

RESULTS

We recorded a total of 1351 cases in the cohort, 395 Exeter and 956 Charnley stems. The overall all-cause revision rate at 10 years was 1.6%. The revision rate for Charnley stem was 1.4% and 2.3% revision rate for all Exeter stems with no significant difference noted between the two cohorts (p = 0.24). The overall time to revision was 38.3 months. WOMAC scores at 10 years were found to be insignificantly higher for Charnley stems (mean 23.8, σ = 20.11) compared to Exeter stems (mean 19.78, σ = 20.72) (p = 0.1).

CONCLUSION

There is no significant difference between cemented Charnley and Exeter stems; they both perform well above the international average. The decline in the use of cemented THA is not fully supported by this regional registry data.

National Registry Data Analysis on a Unique Highly-Crosslinked Polyethylene for Total Hip Arthroplasty

Background

Several types of highly-crosslinked polyethylene with different manufacturing processes and mechanical properties are commercially available, including HIGHCROSS (Medacta). The aim of this registry study is to ascertain the long-term safety of the HIGHCROSS liners in total hip arthroplasty and compare the revision rates with its contemporaries using real-world data to establish their safety and generalizability when used by multiple surgeons.

Methods

The Australian Orthopaedic Association National Joint Replacement Registry (AOANJRR) and the Swiss National Joint Registry (SIRIS) were selected for the large number of users of Medacta implants and the availability of long-term results. Three reports from SIRIS and 4 reports from AOANJRR were examined to establish the overall and Kaplan-Meier (KM) cumulative revision rate.

Results

According to SIRIS, the HIGHCROSS liner was the most commonly used bearing surface with Medacta stems with overall revision rates for wear/osteolysis at 9.7 years of 0.04% and 0.03%, respectively, for AMIStem and Quadra. Based on AOANJRR, the KM cumulative revision rate for any reason of Medacta stems with HIGHCROSS liners was lower than that with ceramic liners at 3 years for MasterLoc and at 10 years for Quadra. The KM cumulative revision rate for any reasons of Medacta cementless cups with HIGHCROSS liners at 12 years was lower than the comparator made of all other implants and tribological couplings (1.6% vs 2.1%).

Conclusions

This real-world data proves that long-term HIGHCROSS survival rates are comparable to other modern bearing surfaces.

Head, acetabular liner composition, and rate of revision and wear in total hip arthroplasty: a Bayesian network meta-analysis

Total hip arthroplasty (THA) is a common procedure for patients suffering from hip pain e.g. from osteoarthritis, osteonecrosis, or hip fractures. The satisfaction of patients undergoing THA is influenced by the choice of implant type and material, with one key factor being the selection of the appropriate material combination for the bearing surface. In this Bayesian network meta-analysis, we investigated the impact of material combinations for the bearing surface on the longevity of hip implants. The wear penetration rate per year and the total wear penetration in the liner resulting from different material combinations, as well as the survival rate at last follow-up, were examined. We analyzed a total of 663,038 THAs, with 55% of patients being women. Mean patient age was 59.0 ± 8.1 years and mean BMI 27.6 ± 2.6 kg/m2. The combination of an aluminium oxide (Al2O3) head and an Al2O3 liner demonstrated the lowest wear penetration at last follow-up and the lowest rate of wear penetration per year. Additionally, the combination of a crosslinked polyethylene (XLPE) liner and a zircon oxide (ZrO2) head demonstrated the lowest rate of revision at last follow-up. These findings underscore the importance of careful material selection for hip implant bearing surfaces to optimize their longevity and patient satisfaction after THA.

Synchrotron-based characterization of arthroprosthetic CoCrMo particles in human bone marrow

Particles released from cobalt-chromium-molybdenum (CoCrMo) alloys are considered common elicitors of chronic inflammatory adverse effects. There is a lack of data demonstrating particle numbers, size distribution and elemental composition of bone marrow resident particles which would allow for implementation of clinically relevant test strategies in bone marrow models at different degrees of exposure. The aim of this study was to investigate metal particle exposure in human periprosthetic bone marrow of three types of arthroplasty implants. Periprosthetic bone marrow sections from eight patients exposed to CoCrMo particles were analyzed via spatially resolved and synchrotron-based nanoscopic X-ray fluorescence imaging. These analyses revealed lognormal particle size distribution patterns predominantly towards the nanoscale. Analyses of particle numbers and normalization to bone marrow volume and bone marrow cell number indicated particle concentrations of up to 1 × 10¹¹ particles/ml bone marrow or 2 × 10⁴ particles/bone marrow cell, respectively. Analyses of elemental ratios of CoCrMo particles showed that particularly the particles' Co content depends on particle size. The obtained data point towards Co release from arthroprosthetic particles in the course of dealloying and degradation processes of larger particles within periprosthetic bone marrow. This is the first study providing data based on metal particle analyses to be used for future in vitro and in vivo studies of possible toxic effects in human bone marrow following exposure to arthroprosthetic CoCrMo particles of different concentration, size, and elemental composition. Graphical abstract.

How to Prevent Aseptic Loosening in Cementless Arthroplasty: A Review

Aseptic loosening is the main late postoperative complication of cementless total hip arthroplasties (THAs), leading to pain and functional impairment. This article aims to update the orthopedic surgeon on the various methods by which the aseptic loosening rate can be reduced. We performed a systematic review by searching the PubMed database for hip aseptic loosening. We included meta-analysis, randomized controlled trials, reviews, and systematic reviews in the last 10 years, which provided information on techniques that can prevent aseptic loosening in total hip arthroplasty. From a total of 3205 articles identified, 69 articles (2%) met the inclusion criteria, leading to a total of 36 recommendations. A lot of research has been conducted in terms of septic loosening in the last decade. Currently, we have various techniques by which we can reduce the rate of aseptic loosening. Nevertheless, further randomized clinical trials are needed to expand the recommendations for aseptic loosening prevention.

Vitamin E-Enhanced Liners in Primary Total Hip Arthroplasty: A Systematic Review and Meta-Analysis

Objective

Adding vitamin E to highly cross-linked polyethylene liners is frequently performed in clinical practice, aiming at reducing liner wear, increasing liner survival, and delaying revision surgery. This study is aimed at evaluating the revision rate, total femoral head penetration, and postoperative clinical function of highly cross-linked polyethylene liners with and without vitamin E in total hip arthroplasty.

Methods

We conducted a systematic literature search to identify the use of highly cross-linked vitamin E liners compared to other liners in patients who received total hip arthroplasty (THA) before April 2021. The study quality assessment and data collection were conducted by two independent reviewers. Studies were artificially grouped, and vitamin E-enhanced liners (VE-PE) were compared with vitamin E-free liners (non-VE-PE). Analyses were executed using Review Manager version 5.4.1.

Results

From the preliminary screening of 568 studies, fourteen studies met the research criteria. Compared to non-VE-PE, using VE-PE reduced the all-cause revision rate (odds ratio = 0.54; 95% confidence interval (CI) 0.40, 0.73; P < 0.0001). The total femoral head penetration of the VE-PE was lower than that of the non-VE-PE (mean difference = −0.10; 95% CI -0.17, -0.03; P = 0.007). However, there was no difference in clinical function, including the Harris Hip Score and EuroQol Five-Dimension Questionnaire scores.

Conclusion

Compared to the liners without vitamin E, the addition of vitamin E to liners could reduce the all-cause revision rate by approximately 46% in the short-term follow-up. In addition, even though addition of vitamin E could also slow down femoral head penetration, there is no contribution to clinical function.

Is Surface Metastability of Today’s Ceramic Bearings a Clinical Issue?

Recent studies on zirconia-toughened alumina (ZTA) evidenced that in vivo aged implants display a much higher monoclinic zirconia content than expected from in vitro simulations by autoclaving. At the moment, there is no agreement on the source of this discrepancy: Some research groups ascribe it to the effect of mechanical impact shocks, which are generally not implemented in standard in vitro aging or hip walking simulators. Others invoke the effect of metal transfer, which should trigger an autocatalytic reaction in the body fluid environment, accelerating the kinetics of tetragonal-to-monoclinic transformation in vivo. Extrapolations of the aging kinetics from high (autoclave) to in vivo temperature are also often disputed. Last, Raman spectroscopy is by far the preferred method to quantify the amount of monoclinically transformed zirconia. There are, however, many sources of errors that may negatively affect Raman results, meaning that the final interpretation might be flawed. In this work, we applied Raman spectroscopy to determine the monoclinic content in as-received and in vitro aged ZTA hip joint implants, and in one long-term retrieval study. We calculated the monoclinic content with the most used equations in the literature and compared it with the results of X-ray diffraction obtained on a similar probe depth. Our results show, contrary to many previous studies, that the long-term surface stability of ZTA ceramics is preserved. This suggests that the Raman technique does not offer consistent and unique results for the analysis of surface degradation. Moreover, we discuss here that tetragonal-to-monoclinic transformation is also necessary to limit contact damage and wear stripe extension. Thus, the surface metastability of zirconia-containing ceramics may be a non-issue.

Benchmarking total hip replacement constructs using noninferiority analysis: the New Zealand joint registry study

BACKGROUND

The aim of this study was to compare the relative performance of total hip replacement constructs and discern if there is substantial variability in performance in currently commonly used prostheses in the New Zealand Joint Registry (NZJR) using a noninferiority analysis.

METHODS

All patients who underwent a primary total hip replacement (THR) registered in the NZJR between 1st January 1999 to June 2020 were identified. Using a noninferiority analysis, the performance of hip prostheses were compared with the best performing contemporary construct. Construct failure was estimated using the 1-Kaplan Meier survival function method to estimate net failure. The difference in failure between the contemporary benchmark and other constructs was examined.

RESULTS

In total 135,432 THR were recorded comprising 1035 different THR constructs. Notably 328 constructs were used just once. Forty-eight constructs (62,251 THR) had > 500 procedures at risk at 3 years post-primary of which 28 were inferior by at least 20% relative risk of which, 10 were inferior by at least 100% relative risk. Sixteen constructs were identified with > 500 procedures at risk at 10 years with 9 inferior by at least 20%, of which one was inferior by > 100% relative risk. There were fewer constructs noninferior to the best practice benchmark when we performed analysis by gender. In females at 10 years, from 5 constructs with > 500 constructs at risk, 2 were inferior at the 20% margin. In males at 10 years, there were only 2 eligible constructs of which one was inferior at the 20% margin.

CONCLUSIONS

We discerned that there is substantial variability in construct performance and at most time points, just over half of constructs are inferior to the best performing construct by at least 20%. These results can facilitate informed decision-making when considering THR surgery.

Does vitamin E highly-crosslinked polyethylene convey an advantage in primary total hip replacement? A systematic review and meta-analysis

BACKGROUND

Vitamin E highly cross-linked polyethylene (HXLPE) was developed to reduce wear in total hip replacement (THR). This formal systematic review and meta-analysis aimed to provide independent synthesis of wear characteristics of Vitamin E treated HXLPE compared to HXPLE/UHMWPE. Secondary outcome measures were differences in revision rates and functional scores.

METHODS

We performed a formal systematic review as per PRISMA guidelines; literature searches were conducted on 14 November 2017 (MEDLINE, Embase on Ovid, and the Cochrane Library). We included randomised controlled trials, analyses of joint registries, and case-controlled studies of primary THR comparing cups with a vitamin E HXLPE bearing with bearing surfaces made from other types of polyethylene. Initial screening was performed by 2 independent assessors; disagreement resolved in discussion with a third reviewer. Studies were evaluated using the Cochrane risk of bias tool. Data extraction permitted meta-analysis.

RESULTS

372 studies were identified on initial screening, 5 studies met the eligibility criteria. There was no significant heterogeneity between studies. There was variable risk of bias. At a mean of 35 (range 20-60) months, Vitamin E HXLPE had significant advantages over highly cross-linked polyethylene with regards total femoral head penetration (p = 0.004). Given the RSA measurement errors this may not be clinically significant.There were neither significant differences in revision rates nor Harris Hip Scores (p = 0.06).

CONCLUSION

At a minimum of 3 years follow-up there was reduced total femoral head penetration for vitamin E HXLPE over HXLPE. This bearing surface does not, as yet, have clinically significant advantages in terms of revision rates or patient function over HXLPE.