Design of percutaneous transluminal coronary angioplasty balloon catheters

BACKGROUND

Eight commercially available percutaneous transluminal coronary angioplasty (PTCA), including semi-compliant and non-compliant balloons, have been assessed in detail on their tip, balloon, shaft, RX-Port, and hypotube design. Important performance characteristics such as tip deformation, balloon elongation, and deflation rate have been quantified.

METHODS

Five catheters of each model were evaluated during various tests. The robustness of the tips was evaluated through compression, measuring any occurrence of damage. The longitudinal growth of the balloons was recorded during inflation up to Rated Burst Pressure (RBP). The forces required to move the catheter forward and retract it into the guide catheter were measured in a simulated use test setup. The deflation behavior was studied by measuring extracted contrast media over time. Furthermore, balloon compliance and catheter dimensions were investigated.

RESULTS

The outer dimensions of the catheter were found to be smallest at the hypotube (0.59-0.69 mm) and highest at the balloon, respectively, the crossing profile (0.9-1.2 mm). The tip diameter increased after compression by 1.7-22%. Cross-sections of the folded balloons revealed a tri- and two-fold, respectively. The measured balloon elongation ranged from 0.6 to 2.0 mm. After the inflation of the balloon, an increase in friction between the guide wire and the catheter was observed on four catheters. A maximum increase of 0.12 N to 1.07 N was found. Cross-sections of the RX-Port revealed a semicircular-shaped inflation lumen and a circular guide wire lumen. The measured deflation rate ranged from 0.004 to 0.013 µL/s, resulting in an estimated balloon deflation time of 10.2-28.1 s.

CONCLUSION

This study provides valuable insights into the design characteristics of RX PTCA balloon catheters, which can contribute to facilitating the development of improved catheter designs and enhancing clinical outcomes. Distinctions between SC and NC catheters, such as balloon performance and dimensions, are evident. It is important to note that no single catheter excels in all aspects, as each possesses unique strengths. Therefore, it is essential to consider individual intervention requirements when selecting a catheter. The research also identifies specific catheter weaknesses, such as reduced wall thickness, fringes at the tip, and reduced performance characteristics.

Temperature-dependent tensile properties of polyamide 12 for the use in percutaneous transluminal coronary angioplasty balloon catheters

BACKGROUND

Percutaneous transluminal coronary angioplasty (PTCA) balloon catheters must withstand high pressures required for the lesion treatment, pushing loads during insertion, and pulling loads during withdrawal. These loads pose a challenge especially for polymeric tubular shafts with small cross sections. In order to enable new design innovations and to better understand the mechanics of current catheter technologies, the tensile properties of polyamide (PA) 12 were investigated. PA 12 dog bone specimens and medical PA 12 tubes were either stored at ambient temperature and humidity or conditioned in water, and subjected to tensile loads at different temperatures. In addition, the effect on the tensile properties of the necking process, a forming process to reduce the wall thickness of the tubes, was determined.

RESULTS

The tested tubes showed a reduction in both Young's Modulus (- 41.5%) and yield stress (- 29.2%) compared to standardized specimens. Furthermore, an increase in temperature and water absorption softens the material and reduces the mechanical properties like the Young's Modulus and the yield stress. It was found that the material strengthens during the necking process. Likely due to the orientation of the polymers chain molecules in load direction (Rösler et al., 2007), the Young's Modulus of the material could be increased by 43.5%. Furthermore, the absence of a yield point after necking allows for a greater loading capacity of the material without unstable neck growth. Besides the strengthening, the ultimate strain is reduced by 50%. This indicates that the necking process induces plastic deformation.

CONCLUSION

The investigation showed that the environmental conditions like temperature and humidity can influence mechanical properties. It could also be shown that pre-forming processes such as necking can enhance the mechanical properties, such as the Young's Modulus, while reducing the wall thickness. These findings suggest possible further development of catheters with a small cross section and higher mechanical strength and highlight the importance to account for the targeted operating temperature during the design process.

Energy harvesting from the beating heart by a mass imbalance oscillation generator

Energy-harvesting devices attract wide interest as power supplies of today's medical implants. Their long lifetime will spare patients from repeated surgical interventions. They also offer the opportunity to further miniaturize existing implants such as pacemakers, defibrillators or recorders of bio signals. A mass imbalance oscillation generator, which consists of a clockwork from a commercially available automatic wrist watch, was used as energy harvesting device to convert the kinetic energy from the cardiac wall motion to electrical energy. An MRI-based motion analysis of the left ventricle revealed basal regions to be energetically most favorable for the rotating unbalance of our harvester. A mathematical model was developed as a tool for optimizing the device's configuration. The model was validated by an in vitro experiment where an arm robot accelerated the harvesting device by reproducing the cardiac motion. Furthermore, in an in vivo experiment, the device was affixed onto a sheep heart for 1 h. The generated power in both experiments-in vitro (30 μW) and in vivo (16.7 μW)-is sufficient to power modern pacemakers.