Synthesis and characterization of MXene (Ti3C2Tx)/Iron oxide composite for ultrasensitive electrochemical detection of hydrogen peroxide

Due to the widespread usage of hydrogen peroxide (H₂O₂) in various consumer and industrial products (Examples: fuel cells and antibacterial agents), it became important to accurately detect H₂O₂ concentration in environmental, medical and food samples. Herein, titanium carbide Ti₃C₂T_x (MXene) was synthesized by using Ti, Al and C powders at high-temperature. Then, nanocrystalline iron oxide (α-Fe₂O₃) was obtained from a single solid-phase method. Using Ti₃C₂T_x and Fe₂O₃ powders, Ti₃C₂T_x-Fe₂O₃ nanocomposite was prepared by ultrasonication. As-synthesized, Ti₃C₂T_x-Fe₂O₃ composite had been characterized by UV-Visible (UV-Vis), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD) and Raman spectroscopy. The Fe₂O₃ nanoparticles (NPs) were decorated on the surface of Ti₃C₂T_x as observed by high resolution scanning electron microscopy (HR-SEM) and high resolution transmission electron microscopy (HR-TEM). The Ti₃C₂T_x nanosheets were formed with the average size of 400-500 nm. HR-SEM images of α-Fe₂O₃ showed that the coral-like particles with the average length ~5 μm were obtained_. The electrochemical properties of the individual (Ti₃C₂T_x and α-Fe₂O₃) and composite materials (Ti₃C₂T_x-Fe₂O₃) were investigated by cyclic voltammetry (CV). Ti₃C₂T_x-Fe₂O₃ nanocomposite modified electrode had exhibited potent electro-catalytic activity for H₂O₂ reduction by reducing the overpotential about 320 mV and a linear response was recorded from 10 nM to 1 μM H₂O₂. The optimization of various parameters such as material composition ratio, amount of catalyst, effects of pH, scan rate and interference effects with other biomolecules were carried out. In addition, the kinetic parameters such as rate constant, diffusion coefficient and the active surface area of the electrodes were calculated. Moreover, the Ti₃C₂T_x-Fe₂O₃ composite modified electrode was used successfully to detect H₂O₂ in food and urine samples. We believe that Ti₃C₂T_x-Fe₂O₃ composite based materials could be used for the fabrication of non-enzymatic H₂O₂ sensors for medical diagnosis, food safety and environmental monitoring applications.

Recent trends in the applications of thermally expanded graphite for energy storage and sensors - a review

Carbon nanomaterials such as carbon dots (0D), carbon nanotubes (1D), graphene (2D), and graphite (3D) have been exploited as electrode materials for various applications because of their high active surface area, thermal conductivity, high chemical stability and easy availability. In addition, due to the strong affinity between carbon nanomaterials and various catalysts, they can easily form metal carbides (examples: ionic, covalent, interstitial and intermediate transition metal carbides) and also help in the stable dispersion of catalysts on the surface of carbon nanomaterials. Thermally expanded graphite (TEG) is a vermicular-structured carbon material that can be prepared by heating expandable graphite up to 1150 °C using a muffle or tubular furnace. At high temperatures, the thermal expansion of graphite occurred by the intercalation of ions (examples: SO4 2-, NO3 -, Li+, Na+, K+, etc.) and oxidizing agents (examples: ammonium persulfate, H2O2, potassium nitrate, potassium dichromate, potassium permanganate, etc.) which helped in the exfoliation process. Finally, the obtained TEG, an intumescent form of graphite, has been used in the preparation of composite materials with various conducting polymers (examples: epoxy, poly(styrene-co-acrylonitrile), polyaniline, etc.) and metal chlorides (examples: FeCl3, CuCl2, and ZnCl2) for hydrogen storage, thermal energy storage, fuel cells, batteries, supercapacitors, sensors, etc. The main features of TEG include a highly porous structure, very lightweight with an apparent density (0.002-0.02 g cm-3), high mechanical properties (10 MPa), thermal conductivity (25-470 W m-1 K-1), high electrical conductivity (106-108 S cm-1) and low-cost. The porosity and expansion ratio of graphite layers could be customized by controlling the temperature and selection of intercalation ions according to the demand. Recently, TEG based composites prepared with metal oxides, chlorides and polymers have been demonstrated for their use in energy production, energy storage, and electrochemical (bio-) sensors (examples: urea, organic pollutants, Cd2+, Pb2+, etc.). In this review, we have highlighted and summarized the recent developments in TEG-based composites and their potential applications in energy storage, fuel cells and sensors with hand-picked examples.

Selective Chemistry-Based Separation of Semiconducting Single-Walled Carbon Nanotubes and Alignment of the Nanotube Array Network under Electric Field for Field-Effect Transistor Applications

Semiconducting single-walled carbon nanotubes (s-SWCNTs) are considered as a replacement for silicon in field-effect transistors (FETs), solar cells, logic circuits, and so forth, because of their outstanding electronic, optical, and mechanical properties. Herein, we have studied the reaction of pristine SWCNTs dispersed in a pluronic F-68 (PF-68) polymer solution with para-amino diphenylamine diazonium sulfate (PADDS) to separate nanotubes based on their metallicity. The preferential selectivity of the reactions was monitored by changes in the semiconducting (S22 and S33) and metallic (M11) bands by ultraviolet-visible-near infrared spectroscopy. Metallic selectivity depended on the concentrations of PADDS, reaction time, and the solution pH. Furthermore, separation of pure s-SWCNTs was confirmed by Raman spectroscopy and Fourier-transform infrared spectroscopy. After the removal of metallic SWCNTs, direct current electric field was applied to the pure s-SWCNT solution, which effectively directed the nanotubes to align in one direction as nanotube arrays with a longer length and high density. After that, electrically aligned s-SWCNT solution was cast on a silicon substrate, and the length of the nanotube arrays was measured as ∼2 to ∼14 μm with an areal density of ∼2 to ∼20 tubes/μm of s-SWCNTs. Next, electrically aligned s-SWCNT arrays were deposited on the channel of the FET device by drop-casting. Field-emission scanning electron microscopy and electrical measurements have been carried out to test the performance of the aligned s-SWCNTs/FETs. The fabricated FETs with a channel length of 10 μm showed stable electrical properties with a field-effect mobility of 30.4 cm2/Vs and a log10 (I on/I off) current ratio of 3.96. We envisage that this new chemical-based separation method and electric field-assisted alignment could be useful to obtain a high-purity and aligned s-SWCNT array network for the fabrication of high-performance FETs to use in digital and analog electronics.