Prolonged post-washing in ethanol decreases bond strength of additively manufactured crown materials

OBJECTIVES

This study aimed to investigate the effect of post-washing duration and crown thickness on the bond strength between additively manufactured crown materials and dental cement in vitro.

METHODS

Rectangular-shaped specimens of two thicknesses (1.5 and 2.0 mm) were additively manufactured from permanent VarseoSmile Crown (VC) and long-term temporary NextDent (ND) materials. The specimens were post-washed (n = 160) in ethanol for 5 min, 10 min, 1 h, and 8 h then cemented with dual-cure resin cement. Twenty PMMA (TC) were milled as a control. A chevron-notch test was performed to measure the maximum load until failure (N). Interfacial bond strength (J/m2) was calculated and statistically analysed. The mode of failure was analysed by scanning electron microscopy (SEM).

RESULTS

There was a significant difference in the bond strength between all groups (p < 0.01). VC at 1.5mm thickness post-washed for 10 min showed the highest mean bond strength (1.77 ±0.96 J/m2) while VC at 2.0mm thickness post-washed for 8 h showed the lowest (0.22 ±0.10 J/m2). Exposure to ethanol for 8 h resulted in lower bond strength. Within the type of material, there were no differences in bond strength between the thicknesses when post-washed for the same duration.

CONCLUSIONS

Prolonged post-washing of AM crown materials can significantly decrease the bond strength to resin cement. There were no differences between the permanent and long-term temporary AM materials. When post-washed for 5 min, AM materials observed comparable or higher bond strength values compared to PMMA.

CLINICAL SIGNIFICANCE

The output of this research serves as a guide for dental practitioners, emphasising the importance of adhering to correct post-washing procedures for optimal bond strength of additively manufactured crown materials.

Factors influencing the bond strength of additively manufactured crown materials in dentistry: A systematic review of in vitro studies

OBJECTIVE

The purpose of this systematic review was to investigate how different interventions can impact the bond strength of additively manufactured crown materials after cementation.

DATA/SOURCES

Four online databases Ovid MEDLINE, Scopus, Web of Science and Google Scholar were searched up to January 2023. Inclusion criteria were English-language publications, full-text, and in vitro studies only. Exclusion criteria were studies that did not assess the bonding of an additively manufactured crown material to cement or did not conduct any bond strength tests. An assessment of risk of bias was done in accordance with a modified Consolidated Standards of Reporting Trials (CONSORT) checklist. Each study was analysed and compared based on the interventions and bond strength results.

STUDY SELECTION

Six studies satisfied the inclusion and exclusion criteria, five of which evaluated photopolymerised resin and one that tested zirconia manufacturing via 3D printing. All studies observed a low risk of bias. The interventions applied included the type of surface pretreatments, airborne-particle abrasion pressure, cement type, taper of crown, and artificial aging. Three studies compared the bonding performance to milled materials.

CONCLUSIONS

The bond strength of crown materials additively manufactured from photopolymers presented high values and are comparable to milled materials. The systematic review demonstrated there was no definite superior cement type, but airborne-particle abrasion with alumina was generally recommended. There is a clear gap in the literature regarding the bond strength of additively manufactured crowns. Therefore, further research is necessary to evaluate its clinical applicability for permanent restorations.

CLINICAL SIGNIFICANCE

Factors influencing the bond strength of additively manufactured crown materials should be evaluated so dental professionals can adopt procedures that promote the strongest bond.