Facile Synthesis of Surfactant-Induced Platinum Nanospheres with a Porous Network Structure for Highly Effective Oxygen Reduction Catalysis

Developing a facile and eco-friendly method for the large-scale synthesis of the highly active and stable catalysts toward oxygen reduction reaction (ORR) is very important for the practical application of proton exchange membrane fuel cells (PEMFCs). In this paper, a mild aqueous-solution route has been successfully developed for the gram-scale synthesis of three-dimensional porous Pt nanospheres (Pt-NSs) that are composed of network-structured nanodendrites and/or oval multipods. In comparison with the commercial Pt/C catalyst, X-ray photoelectron spectroscopy (XPS) demonstrates the dominant metallic-state of Pt and electrochemical impedance spectroscopy (EIS) indicates the substantial improvement of conductivity for the Pt-NSs/C catalyst. The surfactant-induced porous network nanostructure improves both the catalytic ORR activity and durability. The optimal Pt-NSs/C catalyst exhibits a half-wave potential of 0.898 V (vs. RHE), leading to the mass activity of 0.18 A mgPt-1 and specific activity of 0.68 mA cm-2 which are respectively 1.9 and 5.7 times greater than those of Pt/C. Moreover, the highly-active Pt-NSs/C catalyst shows a superior stability with the tenable morphology and the retained 78% of initial mass activity rather than the severe Pt aggregation and the only 58% retention of the commercial Pt/C catalyst after 10000 cycles.

A bimetallic nanocoral Au decorated with Pt nanoflowers (bio)sensor for H2O2 detection at low potential

In this work, we have developed for the first time a method to make novel gold and platinum hybrid bimetallic nanostructures differing in shape and size. Au-Pt nanostructures were prepared by electrodeposition in two simple steps. The first step consists of the electrodeposition of nanocoral Au onto a gold substrate using hydrogen as a dynamic template in an ammonium chloride solution. After that, the Pt nanostructures were deposited onto the nanocoral Au organized in pores. Using Pt (II) and Pt (IV), we realized nanocoral Au decorated with Pt nanospheres and nanocoral Au decorated with Pt nanoflowers, respectively. The bimetallic nanostructures showed better capability to electrochemically oxidize hydrogen peroxide compared with nanocoral Au. Moreover, Au-Pt nanostructures were able to lower the potential of detection and a higher performance was obtained at a low applied potential. Then, glucose oxidase was immobilized onto the bimetallic Au-Pt nanostructure using cross-linking with glutaraldehyde. The biosensor was characterized by chronoamperometry at +0.15V vs. Ag pseudo-reference electrode (PRE) and showed good analytical performances with a linear range from 0.01 to 2.00mM and a sensitivity of 33.66µA/mMcm². The good value of K_m^app (2.28mM) demonstrates that the hybrid nanostructure is a favorable environment for the enzyme. Moreover, the low working potential can minimize the interference from ascorbic acid and uric acid as well as reducing power consumption to effect sensing. The simple procedure to realize this nanostructure and to immobilize enzymes, as well as the analytical performances of the resulting devices, encourage the use of this technology for the development of biosensors for clinical analysis.