Surface Characteristics and Microbiological Analysis of a Vat-Photopolymerization Additive-Manufacturing Dental Resin

The wide application of additive manufacturing in dentistry implies the further investigation into oral micro-organism adhesion and biofilm formation on vat-photopolymerization (VP) dental resins. The surface characteristics and microbiological analysis of a VP dental resin, printed at resolutions of 50 μm (EG-50) and 100 μm (EG-100), were evaluated against an auto-polymerizing acrylic resin (CG). Samples were evaluated using a scanning electron microscope, a scanning white-light interferometer, and analyzed for Candida albicans (CA) and Streptococcus mutans (SM) biofilm, as well as antifungal and antimicrobial activity. EG-50 and EG-100 exhibited more irregular surfaces and statistically higher mean (Ra) and root-mean-square (rms) roughness (EG-50-Ra: 2.96 ± 0.32 µm; rms: 4.05 ± 0.43 µm/EG-100-Ra: 3.76 ± 0.58 µm; rms: 4.79 ± 0.74 µm) compared to the CG (Ra: 0.52 ± 0.36 µm; rms: 0.84 ± 0.54 µm) (p < 0.05). The biomass and extracellular matrix production by CA and SM and the metabolic activity of SM were significantly decreased in EG-50 and EG-100 compared to CG (p < 0.05). CA and SM growth was inhibited by the pure unpolymerized VP resin (48 h). EG-50 and EG-100 recorded a greater irregularity, higher surface roughness, and decreased CA and SM biofilm formation over the CG.

Novel Poly(Methyl Methacrylate) Containing Nanodiamond to Improve the Mechanical Properties and Fungal Resistance

Herein we evaluate the effect of nanodiamond (ND) incorporation on the mechanical properties of poly(methyl methacrylate) (PMMA) nanocomposite. Three quantities of ND (0.1, 0.3, and 0.5 wt.%) were tested against the control and zirconium oxide nanoparticles (ZrO). Flexural strength and elastic modulus were measured using a three-point bending test, surface hardness was evaluated using the Vickers hardness test, and surface roughness was evaluated using atomic force microscopy (AFM), while fungal adhesion and viability were studied using Candida albicans. Samples were also analyzed for biofilm thickness and biomass in a saliva-derived biofilm model. All groups of ND-PMMA nanocomposites had significantly greater mean flexural strengths and statistically improved elastic modulus, compared to the control and ZrO groups (P < 0.001). The Vickers hardness values significantly increased compared to the control group (P < 0.001) with 0.3% and 0.5% ND. ND addition also gave significant reduction in fungal adhesion and viability (P < 0.001) compared to the control group. Finally, salivary biofilm formation was markedly reduced compared to the ZrO group. Hence, the incorporation of 0.1–0.5 wt.% ND with auto- polymerized PMMA resin significantly improved the flexural strength, elastic modulus, and surface hardness, and provided considerable fungal resistance.

Improving Polymethyl Methacrylate Resin Using a Novel Titanium Dioxide Coating

PURPOSE

The objective of this study was to improve the surface characteristics of poly (methyl methacrylate) (PMMA) by developing a novel, thin film coating process and to characterize the resulting coated surface.

MATERIALS AND METHODS

An atomic layer deposition (ALD) technique was developed to deposit a titanium dioxide (TiO₂ ) nano-thin film on PMMA. The surface wettability for both coated and uncoated PMMA was determined by measuring water contact angle. Wear resistance was assessed using a mechanical tooth-brushing device with a 50 g load for 6000 strokes after 5 months of water storage. A denture cleanser challenge test was performed by using sonication in 3.8% sodium perborate for 1 hour with aged specimens. X-ray photoelectron spectroscopy (XPS) was used before and after the brushing test and challenge test to analyze the PMMA surface chemical composition. The mechanical strength of coated and uncoated PMMA was measured using a three-point bending test. Surface microbial interactions were also evaluated by assessing Candida albicans biofilm attachment.

RESULTS

Nano-TiO₂ coating (30 nm thick) was successfully deposited on PMMA at 65°C. After coating, water contact angle decreased from 70° to less than 5°. After brushing test, the coating remained intact. XPS analysis revealed no loss of TiO₂ from coated specimens following brushing and denture cleanser sonication for 1 hour. There was no statistically significant difference in mechanical strength (MPa) (mean ± SD) between PMMA (139.4 ± 11.3) and TiO₂ -PMMA (160.7 ± 37.1) (p = 0.0995). C. albicans attachment decreased by 63% to 77% on the coated PMMA surface.

CONCLUSIONS

ALD is a promising technique to modify surface properties of PMMA and resulted in a stable adherent thin film. By depositing a TiO₂ coating, PMMA surface properties may lead to significantly reduced microorganism adhesion and easier pathogen removal from PMMA. For patients who wear dentures, reducing the oral microbial biofilm burden using a TiO₂ -coated PMMA surface could positively impact their oral and systemic health.