Flexibility in zeolites: origin, limits, and evaluation

Numerous pieces of evidence in the literature suggest that zeolitic materials exhibit significant intrinsic flexibility as a consequence of the spring-like behavior of Si-O and Al-O bonds and the distortion ability of Si-O-Si and Al-O-Si angles. Understanding the origin of flexibility and how it may be tuned to afford high adsorption selectivity in zeolites is a big challenge. Zeolite flexibility may be triggered by changes in temperature, pressure, or chemical composition of the framework and extra-framework compounds, as well as by the presence of guest molecules. Therefore, zeolite flexibility can be classified into three categories: (i) temperature and pressure-induced flexibility; (ii) guest-induced flexibility; and (iii) compositionally-induced flexibility. An outlook on zeolite flexibility and the challenges met during the precise experimental evaluations of zeolites will be discussed. Overcoming these challenges will provide an important tool for designing novel selective adsorbents.

Interplay between alkali-metal cations and silanol sites in nanosized CHA zeolite and implications for CO2 adsorption

Silanols are key players in the application performance of zeolites, yet, their localization and hydrogen bonding strength need more studies. The effects of post-synthetic ion exchange on nanosized chabazite (CHA), focusing on the formation of silanols, were studied. The significant alteration of the silanols of the chabazite nanozeolite upon ion exchange and their effect on the CO₂ adsorption capacity was revealed by solid-state nuclear magnetic resonance (NMR), Fourier-transform infrared (FTIR) spectroscopy, and periodic density functional theory (DFT) calculations. Both theoretical and experimental results revealed changing the ratio of extra-framework cations in CHA zeolites changes the population of silanols; decreasing the Cs⁺/K⁺ ratio creates more silanols. Upon adsorption of CO₂, the distribution and strength of the silanols also changed with increased hydrogen bonding, thus revealing an interaction of silanols with CO₂ molecules. To the best of our knowledge, this is the first evidence of the interplay between alkali-metal cations and silanols in nanosized CHA.

Application of BPH zeolite for the transesterification of glycerol to glycerol carbonate: effect of morphology, cation type and reaction condition

The valorization of glycerol (Gly) to high-value chemicals is the key to unlocking economic and sustainable biodiesel production. Transesterification of Gly with dimethyl carbonate (DMC) to glycerol carbonate (GC) requires...

The role of mixed alkali metal cations on the formation of nanosized CHA zeolite from colloidal precursor suspension

A clear understanding of the crystal formation pathways of zeolites remains one of the most challenging issues to date. Here we investigate the synthesis of nanosized chabazite (CHA) zeolites using organic template-free colloidal suspensions by varying the time of aging at room temperature and the time of hydrothermal treatment at 90 °C. The role of mixed alkali metal cations (Na⁺, K⁺, Cs⁺) on the formation of CHA in the colloidal suspensions was studied. Increasing the aging time of the precursor colloidal suspension from 4 to 17 days resulted in faster crystallization of CHA nanocrystals (3 h instead of 7 h at 90 °C) to afford significantly smaller particles (60 nm vs 600 nm). During the crystallization a considerable change in the content of inorganic cations in the recovered solid material was observed to coincide with the formation of the CHA nanocrystals. The Na⁺ cations were found to direct the formation of condensed and pre-shaped aluminosilicate particles in the colloidal precursor suspensions, while K⁺ cations facilitated the formation of secondary building units (SBUs) of the CHA type framework structure such as d6r and cha cages, and the Cs⁺ cations promoted the long-range crystalline order facilitating the crystallization of stable zeolite nanocrystals.