Yang B, Aregawi W, Chen R, Zhang L, Wang Y, Fok A. Accelerated Fatigue Model for Predicting Composite Restoration Failure. J Dent Res 2022; 101:1606-1612. [PMID: 36199249 PMCID: PMC9703530 DOI: 10.1177/00220345221126928] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [What about the content of this article? (0)] [Affiliation(s)] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/17/2022] Open
Abstract
An empirical method is proposed to predict the clinical performance of resin composite dental restorations by using laboratory data derived from simple specimens subjected to chemical degradation and accelerated cyclic fatigue. Three resin composites were used to fill dentin disks (2-mm inner diameter, 5-mm outer diameter, and 2 mm thick) made from bovine incisor roots. The specimens (n = 30 per group) were aged with different durations of a low-pH challenge (0, 24, and 48 h under pH 4.5) before being subjected to diametral compression with either a monotonically increasing load (fast fracture) or a cyclic load with a continuously increasing amplitude (accelerated fatigue). The data from 1 material were used to establish the relationship between laboratory time (number of cycles) and clinical time to failure (years) via the respective survival probability curves. The temporal relationship was then used to predict the clinical rates of failure for restorations made of the other 2 materials, and the predictions were compared with the clinical data to assess their accuracy. Although there were significant differences in the fast fracture strength among the groups of materials or durations of chemical challenge, fatigue testing was much better at separating the groups. Linear relationships were found between the laboratory and clinical times to failure for the first material (R2 = 0.90, 0.90, and 0.62 for the 0-, 24-, and 48-h low-pH groups, respectively). The clinical life of restorations made of the other 2 materials was best predicted with data from the 48-h low-pH groups. In conclusion, an accelerated fatigue model was successfully calibrated and applied to predict the clinical failure of resin composite restorations, and the predictions based on data obtained from chemically aged specimens provided the best agreement with clinical data.
Collapse
Affiliation(s)
- B. Yang
- Hospital of Stomatology, Guanghua School of Stomatology, Sun Yat-sen University; Guangdong Provincial Key Laboratory of Stomatology, Guangzhou, China
| | - W. Aregawi
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| | - R. Chen
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| | - L. Zhang
- Divison of Biostatistics, School of Public Health, University of Minnesota, Minneapolis, MN, USA
| | - Y. Wang
- Hospital of Stomatology, Guanghua School of Stomatology, Sun Yat-sen University; Guangdong Provincial Key Laboratory of Stomatology, Guangzhou, China
| | - A.S.L. Fok
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| |
Collapse
|
2
|
Zhang A, Lima B, Chen R, Aregawi W, Rudney J, Aparicio C, Fok A. Verification of Collagenase Production by Streptococcus Mutans. Dent Mater 2022. [DOI: 10.1016/j.dental.2021.12.113] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [What about the content of this article? (0)] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/03/2022]
|
3
|
Zhang A, Ye N, Aregawi W, Zhang L, Salah M, VanHeel B, Chew HP, Fok ASL. A Review of Mechano-Biochemical Models for Testing Composite Restorations. J Dent Res 2021; 100:1030-1038. [PMID: 34365857 DOI: 10.1177/00220345211026918] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [What about the content of this article? (0)] [Affiliation(s)] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/17/2022] Open
Abstract
Due to the severe mechano-biochemical conditions in the oral cavity, many dental restorations will degrade and eventually fail. For teeth restored with resin composite, the major modes of failure are secondary caries and fracture of the tooth or restoration. While clinical studies can answer some of the more practical questions, such as the rate of failure, fundamental understanding on the failure mechanism can be obtained from laboratory studies using simplified models more effectively. Reviewed in this article are the 4 main types of models used to study the degradation of resin-composite restorations, namely, animal, human in vivo or in situ, in vitro biofilm, and in vitro chemical models. The characteristics, advantages, and disadvantages of these models are discussed and compared. The tooth-restoration interface is widely considered the weakest link in a resin composite restoration. To account for the different types of degradation that can occur (i.e., demineralization, resin hydrolysis, and collagen degradation), enzymes such as esterase and collagenase found in the oral environment are used, in addition to acids, to form biochemical models to test resin-composite restorations in conjunction with mechanical loading. Furthermore, laboratory tests are usually performed in an accelerated manner to save time. It is argued that, for an accelerated multicomponent model to be representative and predictive in terms of both the mode and the speed of degradation, the individual components must be synchronized in their rates of action and be calibrated with clinical data. The process of calibrating the in vitro models against clinical data is briefly described. To achieve representative and predictive in vitro models, more comparative studies of in vivo and in vitro models are required to calibrate the laboratory studies.
Collapse
Affiliation(s)
- A Zhang
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| | - N Ye
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| | - W Aregawi
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| | - L Zhang
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA.,The State Key Laboratory Breeding Base of Basic Science of Stomatology (Hubei-MOST) & Key Laboratory of Oral Biomedicine Ministry of Education, School & Hospital of Stomatology, Wuhan University, Wuhan, China
| | - M Salah
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA.,Faculty of Dentistry, Ain-Shams University, Cairo, Egypt
| | - B VanHeel
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| | - H P Chew
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| | - A S L Fok
- Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA
| |
Collapse
|