Slow release fertilizer prepared with lignin and poly(vinyl acetate) bioblend

Controlled or slow release fertilizers have been recommended to enhance crop yield, while minimizing environmental and economic issues related from current fertilizer applications. However, alternative biodegradable and non-toxic coating material should be suggested to produce biocoated fertilizers. Here we propose the use of lignin and poly(vinyl acetate) (PVAc) as biocoating materials for preparing slow release urea fertilizer. The blend of PVAc and lignin at a mass ratio of 75:25 improved the characteristics of the formed film and increased the nitrogen release time if compared to the pure polymers. The nitrogen release time from urea granules coated with a polymeric layer of 154.3 ± 5.5 μm formed by lignin and PVAc was 36 times greater than from bare urea. The increase in the polymeric coating from 52.6 ± 5.2 to 80.2 ± 6.1 μm decreased the curvature of the nitrogen release data by a factor of at least 1.7, while the curvature was decreased in at least 1.3 with the increase in the polymeric coating from 80.2 ± 6.1 to 158.9 ± 10.6 μm. The adjustment of nitrogen release data to the Peppas-Sahlin model indicated the Fickian diffusion is more predominant than relaxation contributions, since the used polymers did not present considerable swelling. Thus, the blending of PVAc and lignin at 25 wt% of lignin and 75 wt% of PVAc is suggested as a biocoating material for producing slow release fertilizers.

Heterogeneous nucleation of polymorphs on polymer surfaces: polymer-molecule interactions using a heterogeneous dielectric solvation model

We have investigated the mechanism of the nucleation of acetaminophen on poly(methyl-methacrylate) and poly(vinyl-acetate) utilizing a combination of quantum mechanical computations and electrostatic models. We have used a heterogeneous dielectric solvation model to determine the stability of different orientations of acetaminophen on polymer surfaces. We find that for the nucleation of acetaminophen on the polymer surfaces in vacuum, the most stable orientation is a flat orientation. For the nucleation process in solution where acetaminophen and the polymer surface are surrounded by a solvent, we find that the heterogeneous dielectric solvation model predicts that a sideways orientation is the most stable orientation.

Curing mechanism of flexible aqueous polymeric coatings

The objective of this study was to explain curing phenomena for pellets coated with a flexible polymeric coating based on poly(vinyl acetate) (Kollicoat® SR 30D) with regard to the effect of starter cores, thickness of drug layer, adhesion of coating to drug-layered-cores as well as coating properties. In addition, appropriate approaches to eliminate the curing effect were identified. Sugar or MCC cores were layered with the model drugs carbamazepine, theophylline, propranolol HCl, tramadol HCl and metoprolol HCl using HPMC (5 or 25% w/w, based on drug) as a binder. Drug-layered pellets were coated with Kollicoat® SR 30D in a fluidized bed coater using TEC (10% w/w) as plasticizer and talc (35-100% w/w) as anti-tacking agent. Drug release, pellet properties (morphology, water uptake-weight loss and osmolality) and adhesion of the coating to the drug layer were investigated as a function of curing at 60°C or 60°C/75% RH for 24h. The film formation of the aqueous dispersion of Kollicoat® SR 30D was complete, and therefore, a strong curing effect (decrease in drug release) at elevated temperature and humidity (60°C/75% RH) could not be explained by the well-known hydroplasticization and the further gradual coalescence of the colloidal polymer particles. According to the provided mechanistic explanation, the observed curing effect was associated with (1) high flexibility of coating, (2) adhesion between coating and drug layer, (3) water retaining properties of the drug layer, and (4) osmotically active cores. Unwanted curing effects could be minimized/eliminated by the addition of talc or/and pore-forming water soluble polymers in the coating, increasing binder amount or applying an intermediate coating, by increasing the thickness of drug layer or using non-osmotic cores. A new insight into curing phenomena mainly associated with the adhesion between drug layer and coating was provided. Appropriate approaches to avoid unwanted curing effect were identified.