26
|
Łosiewicz B, Osak P, Maszybrocka J, Kubisztal J, Bogunia S, Ratajczak P, Aniołek K. Effect of Temperature on Electrochemically Assisted Deposition and Bioactivity of CaP Coatings on CpTi Grade 4. MATERIALS 2021; 14:ma14175081. [PMID: 34501171 PMCID: PMC8433821 DOI: 10.3390/ma14175081] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 07/13/2021] [Revised: 09/01/2021] [Accepted: 09/02/2021] [Indexed: 01/11/2023]
Abstract
Calcium phosphate (CaP) coatings are able to improve the osseointegration process due to their chemical composition similar to that of bone tissues. Among the methods of producing CaP coatings, the electrochemically assisted deposition (ECAD) is particularly important due to high repeatability and the possibility of deposition at room temperature and neutral pH, which allows for the co-deposition of inorganic and organic components. In this work, the ECAD of CaP coatings from an acetate bath with a Ca:P ratio of 1.67, was developed. The effect of the ECAD conditions on CaP coatings deposited on commercially pure titanium grade 4 (CpTi G4) subjected to sandblasting and autoclaving was presented. The physicochemical characteristics of the ECAD-derived coatings was carried out using SEM, EDS, FTIR, 2D roughness profiles, and amplitude sensitive eddy current method. It was showed that amorphous calcium phosphate (ACP) coatings can be obtained at a potential −1.5 to −10 V for 10 to 60 min at 20 to 70 °C. The thickness and surface roughness of the ACP coatings were an increasing function of potential, time, and temperature. The obtained ACP coatings are a precursor in the process of apatite formation in a simulated body fluid. The optimal ACP coating for use in dentistry was deposited at a potential of −3 V for 30 min at 20 °C.
Collapse
|
27
|
Suspension of Amorphous Calcium Phosphate Nanoparticles Impact Commitment of Human Adipose-Derived Stem Cells In Vitro. BIOLOGY 2021; 10:biology10070675. [PMID: 34356530 PMCID: PMC8301486 DOI: 10.3390/biology10070675] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 06/22/2021] [Accepted: 07/14/2021] [Indexed: 12/18/2022]
Abstract
Amorphous calcium phosphate (aCaP) nanoparticles may trigger the osteogenic commitment of adipose-derived stem cells (ASCs) in vitro. The ASCs of three human donors are investigated using basal culture medium DMEM to either 5 or 50 µg/mL aCaP nanoparticles suspension (control: no nanoparticles). After 7 or 14 days, stem cell marker genes, as well as endothelial, osteogenic, chondrogenic, and adipogenic genes, are analyzed by qPCR. Free calcium and phosphate ion concentrations are assessed in the cell culture supernatant. After one week and 5 µg/mL aCaP, downregulation of osteogenic markers ALP and Runx2 is found, and averaged across the three donors. Our results show that after two weeks, ALP is further downregulated, but Runx2 is upregulated. Endothelial cell marker genes, such as CD31 and CD34, are upregulated with 50 µg/mL aCaP and a 2-week exposure. Inter-donor variability is high: Two out of three donors show a significant upregulation of ALP and Runx2 at day 14 with 50 µg/mL aCaP compared to 5 µg/mL aCaP. Notably, all changes in stem cell commitment are obtained in the absence of an osteogenic medium. While the chemical composition of the culture medium and the saturation status towards calcium phosphate phases remain approximately the same for all conditions, gene expression of ASCs changes considerably. Hence, aCaP nanoparticles show the potential to trigger osteogenic and endothelial commitment in ASCs.
Collapse
|
28
|
Pantović Pavlović MR, Stanojević BP, Pavlović MM, Mihailović MD, Stevanović JS, Panić VV, Ignjatović NL. Anodizing/Anaphoretic Electrodeposition of Nano-Calcium Phosphate/Chitosan Lactate Multifunctional Coatings on Titanium with Advanced Corrosion Resistance, Bioactivity, and Antibacterial Properties. ACS Biomater Sci Eng 2021; 7:3088-3102. [PMID: 34152124 DOI: 10.1021/acsbiomaterials.1c00035] [Citation(s) in RCA: 7] [Impact Index Per Article: 2.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 01/09/2023]
Abstract
The aim of this work was to investigate corrosion resistivity, bioactivity, and antibacterial activity of novel nano-amorphous calcium phosphate (ACP) potentially multifunctional composite coatings with and without chitosan oligosaccharide lactate (ChOL), ACP + ChOL/TiO2 and ACP/TiO2 ACP + ChOL/TiO2, respectively, on the titanium substrate. The coatings were obtained by new single-step in situ anodization of the substrate to generate TiO2 and the anaphoretic electrodeposition process of ACP and ChOL. The obtained coatings were around 300 ± 15 μm thick and consisted of two phases, namely, TiO2 and hybrid composite phases. Both ACP/TiO2 and ACP + ChOL/TiO2 have improved corrosion stability, whereas the ACP + ChOL/TiO2 coating showed better corrosion stability. It was shown that at the very start of the deposition process, the formation of the ChOL/TiO2 layer takes place predominantly, which is followed by the inclusion of ChOL into ACP with simultaneous growth of TiO2. This deposition mechanism resulted in the formation of strongly bonded uniform stable coating with high corrosion resistance. In vitro bioactivity was investigated by immersion of the samples in simulated body fluid (SBF). There is in-bone-like apatite formation on both ACP/TiO2 and ACP + ChOL/TiO2 surfaces upon immersion into SBF, which was proven by X-ray diffraction and Fourier transform infrared spectroscopy. While ACP/TiO2 shows no antibacterial activity, ACP + ChOL/TiO2 samples exhibited three- to fourfold decreases in the number of Staphylococcus aureus and Pseudomonas aeruginosa, respectively, after 420 min. The probable mechanism is binding ChOL with the bacterial cell wall, inhibiting its growth, altering the permeability of the cell membrane, and leading to bacterial death.
Collapse
|
29
|
Ruiz-Agudo E, Ruiz-Agudo C, Di Lorenzo F, Alvarez-Lloret P, Ibañez-Velasco A, Rodriguez-Navarro C. Citrate Stabilizes Hydroxylapatite Precursors: Implications for Bone Mineralization. ACS Biomater Sci Eng 2021; 7:2346-2357. [PMID: 33973778 PMCID: PMC8479724 DOI: 10.1021/acsbiomaterials.1c00196] [Citation(s) in RCA: 9] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/06/2021] [Accepted: 04/16/2021] [Indexed: 11/30/2022]
Abstract
Mineralization of hydroxylapatite (HAp), the main inorganic phase in bone, follows nonclassical crystallization routes involving metastable precursors and is strongly influenced by organic macromolecules. However, the effect of small organic molecules such as citrate on the formation of HAp is not well constrained. Using potentiometric titration experiments and titration calorimetry, in combination with a multianalytical approach, we show that citrate stabilizes prenucleation species as well as a liquid-like calcium phosphate precursor formed before any solid phase nucleates in the system. The stabilization of a liquid-like precursor phase could facilitate infiltration into the cavities of the collagen fibrils during bone mineralization, explaining the enhancement of collagen-mediated mineralization by citrate reported in previous studies. Hence, citrate can influence bone mineralization way before any solid phase (amorphous or crystalline) is formed. We also show that HAp formation after amorphous calcium phosphate (ACP) in the absence and presence of citrate results in nanoplates of about 5-12 nm thick, elongated along the c axis. Such nanoplates are made up of HAp nanocrystallites with a preferred c axis orientation and with interspersed ACP. The nanoplatelet morphology, size, and preferred crystallographic orientation, remarkably similar to those of bone HAp nanocrystals, appear to be an intrinsic feature of HAp formed from an amorphous precursor. Our results challenge current models for HAp mineralization in bone and the role of citrate, offering new clues to help answer the long-standing question as to why natural evolution favored HAp as the mineral phase in bone.
Collapse
|
30
|
Habelitz S, Bai Y. Mechanisms of Enamel Mineralization Guided by Amelogenin Nanoribbons. J Dent Res 2021; 100:1434-1443. [PMID: 34009057 DOI: 10.1177/00220345211012925] [Citation(s) in RCA: 6] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/15/2022] Open
Abstract
The nanofibrous nature and its intricate structural organization are the basis for the extraordinary ability of sound enamel to outlive masticatory forces at minimal failure rates. Apatite nanofibers of several hundreds of micrometers to possibly millimeters in length originate during the secretory stage of amelogenesis as 2-nm-thin and 15-nm-wide ribbons that develop and grow in length under the guidance of a dynamic mixture of specialized proteins, the developing enamel matrix (DEM). A critical role in the unidirectional and oriented growth of enamel mineral ribbons has been attributed to amelogenin, the major constituent of the DEM. This review elaborates on recent studies on the ability of ribbon-like assemblies of amelogenin to template the formation of an amorphous calcium phosphate precursor that transforms into apatite mineral ribbons similar to the ones observed in developing enamel. A mechanistic model of the biological processes that drive biomineralization in enamel is presented in the context of a comparative analysis of enamel mouse models and earlier structural data of the DEM emphasizing a regulatory role of the matrix metalloproteinase 20 in mineral deposition and the involvement of a process-directing agent for the templated mineral growth directed by amelogenin nanoribbons.
Collapse
|
31
|
Osak P, Maszybrocka J, Kubisztal J, Ratajczak P, Łosiewicz B. Long-Term Assessment of the In Vitro Corrosion Resistance of Biomimetic ACP Coatings Electrodeposited from an Acetate Bath. J Funct Biomater 2021; 12:12. [PMID: 33562425 PMCID: PMC7930999 DOI: 10.3390/jfb12010012] [Citation(s) in RCA: 8] [Impact Index Per Article: 2.7] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/15/2021] [Revised: 02/02/2021] [Accepted: 02/04/2021] [Indexed: 12/31/2022] Open
Abstract
Calcium phosphate coatings are able to improve the osseointegration process due to their chemical composition, which is similar to that of bone tissues. In this work, to increase the long-term corrosion resistance and to improve the osseointegration process of commercially pure titanium Grade 4 (CpTi G4), biomimetic amorphous calcium phosphate (ACP) coatings were electrodeposited for the first time from an acetate bath with a pH level of 7.0 and a Ca:P ratio of 1.67. ACP coatings were obtained on CpTi G4 substrate subjected to sandblasting and autoclaving using electrochemically assisted deposition at a potential of -3 V relative to the open circuit potential for 30 min at room temperature. SEM, EDS, 2D roughness profiles, amplitude-sensitive eddy current method, and Kelvin scanning probe were used for the surface characterization of the biomaterial under study. In vitro corrosion resistance tests were conducted for 21 days in artificial saliva using open circuit potential, polarization curves, and electrochemical impedance spectroscopy measurements. The passive-transpassive behavior was revealed for the obtained ACP coatings. The long-term corrosion resistance test showed a deterioration of the protective properties for CpTi G4 uncoated and coated with ACP with immersion time. The mechanism and kinetics of the pitting corrosion on the CpTi G4|TiO2|ACP coating system are discussed in detail.
Collapse
|
32
|
Yamashita M, Nomura Y, Ishikawa M, Shimoda S, Hanada N. Oxidized Low-Density Lipoprotein Promotes In Vitro Calcification. MATERIALS 2020; 13:ma13225120. [PMID: 33202824 PMCID: PMC7697660 DOI: 10.3390/ma13225120] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 10/16/2020] [Revised: 11/10/2020] [Accepted: 11/11/2020] [Indexed: 11/16/2022]
Abstract
Calcification plays an important role in the human body in maintaining homeostasis. In the human body, the presence of a high amount of oxidized low-density lipoprotein (ox-LDL) is a consistent feature of the local areas that are common sites of ectopic calcification, namely dental calculus, renal calculus, and the areas affected by arteriosclerosis. Hence, ox-LDL may have some effect on calcification. Scanning electron microscopy (SEM) observation revealed a high amount of amorphous calcium phosphate (ACP) when ox-LDL was included in the solution. In the in vitro experiment, the highest amount of precipitation of calcium phosphate was observed in the solution containing ox-LDL compared to the inclusion of other biomaterials and was 4.2 times higher than that of deionized water for 4.86 mM calcium and 2.71 mM phosphate. The morphology of calcium phosphate precipitates in the solution containing ox-LDL differed from that of the precipitates in solutions containing other biomaterials, as determined by transmission electron microscopy (TEM). Through the time course observation of the sediments using TEM, it was observed that the sediments changed from spherical or oval shape to a thin film shape. These results indicate that sediments acquired a long-range order array, and the phase transitioned from non-crystalline to crystalline with an increased time and density of ACP. Thus, it is concluded that ox-LDL promoted ACP precipitation and it plays an important role in ectopic calcification.
Collapse
|
33
|
Berg C, Unosson E, Engqvist H, Xia W. Amorphous Calcium Magnesium Phosphate Particles for Treatment of Dentin Hypersensitivity: A Mode of Action Study. ACS Biomater Sci Eng 2020; 6:3599-3607. [PMID: 33463162 DOI: 10.1021/acsbiomaterials.0c00262] [Citation(s) in RCA: 9] [Impact Index Per Article: 2.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/28/2022]
Abstract
Occlusion of exposed dentin tubules may eliminate or reduce dentin hypersensitivity by hindering fluid movements within the tubules. In this study, the mode of action of spherical particles of amorphous calcium magnesium phosphate (180-440 nm in diameter) was studied. A degradation study of the particles in Tris-HCl buffer showed that the particles continuously released Ca2+, Mg2+, and phosphate, and XRD analysis revealed the formation of hydroxyapatite (HA) after 1 week. The occluding effect and efficacy of the spherical particles as an occluding agent were evaluated in an in vitro study. The ACMP particles were incorporated in a gel intended for at-home use and tested on extracted human molars. Application of the particles followed by incubation in artificial saliva resulted in occlusion of exposed tubules, and examination with SEM showed that the particles could penetrate the tubules down to 100 μm from the dentin surface. Transformation of the particles into nanocrystalline HA-structures (nanoHA) was initiated at the dentin surface within 12 h of application, and tubule penetration of the particles, accompanied by further ion release and diffusion of ions, resulted in deep intratubular occlusion in the majority of the tubules within 3 days from application. NanoHA was tightly adhered to the tubule walls, filling the entire tubule volume after 7 days. The results of this study demonstrate the mode of action of the amorphous calcium magnesium phosphate particles in occluding exposed dentin tubules. Interaction with saliva and transformation of the particles within the tubules inducing further mineralization indicate that the particles may be used as an effective treatment to reduce dentin hypersensitivity.
Collapse
|
34
|
Biomineralization Precursor Carrier System Based on Carboxyl-Functionalized Large Pore Mesoporous Silica Nanoparticles. Curr Med Sci 2020; 40:155-167. [PMID: 32166678 DOI: 10.1007/s11596-020-2159-3] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/28/2019] [Revised: 11/20/2019] [Indexed: 12/15/2022]
Abstract
Bone and teeth are derived from intrafibrillarly mineralized collagen fibrils as the second level of hierarchy. According to polymer-induced liquid-precursor process, using amorphous calcium phosphate precursor (ACP) is able to achieve intrafibrillar mineralization in the case of bone biomineral in vitro. Therefore, ACP precursors might be blended with any osteoconductive scaffold as a promising bone formation supplement for in-situ remineralization of collagens in bone. In this study, mesoporous silica nanoparticles with carboxyl-functionalized groups and ultra large-pores have been synthesized and used for the delivery of liquid like biomimetic precursors (ACP). The precursor delivery capacity of the nanoparticles was verified by the precursor release profile and successful mineralization of 2D and 3D collagen models. The nanoparticles could be completely degraded in 60 days and exhibited good biocompatibility as well. The successful translational strategy for biomineralization precursors showed that biomineralization precursor laden ultra large pore mesoporous silica possessed the potential as a versatile supplement in demineralized bone formation through the induction of intrafibrillar collagen mineralization.
Collapse
|
35
|
Baras BH, Melo MAS, Thumbigere-Math V, Tay FR, Fouad AF, Oates TW, Weir MD, Cheng L, Xu HHK. Novel Bioactive and Therapeutic Root Canal Sealers with Antibacterial and Remineralization Properties. MATERIALS (BASEL, SWITZERLAND) 2020; 13:E1096. [PMID: 32121595 PMCID: PMC7084849 DOI: 10.3390/ma13051096] [Citation(s) in RCA: 18] [Impact Index Per Article: 4.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 01/15/2020] [Revised: 02/20/2020] [Accepted: 02/21/2020] [Indexed: 02/07/2023]
Abstract
According to the American Dental Association Survey of Dental Services Rendered (published in 2007), 15 million root canal treatment procedures are performed annually. Endodontic therapy relies mainly on biomechanical preparation, chemical irrigation and intracanal medicaments which play an important role in eliminating bacteria in the root canal. Furthermore, adequate obturation is essential to confine any residual bacteria within the root canal and deprive them of nutrients. However, numerous studies have shown that complete elimination of bacteria is not achieved due to the complex anatomy of the root canal system. There are several conventional antibiotic materials available in the market for endodontic use. However, the majority of these antibiotics and antiseptics provide short-term antibacterial effects, and they impose a risk of developing antibacterial resistance. The root canal is a dynamic environment, and antibacterial and antibiofilm materials with long-term effects and nonspecific mechanisms of action are highly desirable in such environments. In addition, the application of acidic solutions to the root canal wall can alter the dentin structure, resulting in a weaker and more brittle dentin. Root canal sealers with bioactive properties come in direct contact with the dentin wall and can play a positive role in bacterial elimination and strengthening of the root structure. The new generation of nanostructured, bioactive, antibacterial and remineralizing additives into polymeric resin-based root canal sealers are discussed in this review. The effects of these novel bioactive additives on the physical and sealing properties, as well as their biocompatibility, are all important factors that are presented in this article.
Collapse
|
36
|
Yang T, Xie P, Wu Z, Liao Y, Chen W, Hao Z, Wang Y, Zhu Z, Teng W. The Injectable Woven Bone-Like Hydrogel to Perform Alveolar Ridge Preservation With Adapted Remodeling Performance After Tooth Extraction. Front Bioeng Biotechnol 2020; 8:119. [PMID: 32154241 PMCID: PMC7047753 DOI: 10.3389/fbioe.2020.00119] [Citation(s) in RCA: 6] [Impact Index Per Article: 1.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/09/2019] [Accepted: 02/06/2020] [Indexed: 02/05/2023] Open
Abstract
Grafting bone substitute is paramount to prevent the alveolar ridge resorption after tooth extraction and facilitate the subsequent implant treatment. An ideal bone substitute should acquire the excellent osteogenic property, more importantly, possess the suitable remodeling rate in balance with bone formation and desirable clinical manageability. However, none of bone substitute is simultaneously characterized by these features, and currently, the limited remodeling property leads to the excessive waiting time before implantation. Enlightened by woven bone, the transitional tissue that is able to induce osteogenesis during bone healing could be easily remodeled within a short period and depend on the favorable injectability of hydrogel, an injectable woven bone-like hydrogel (IWBLH) was constructed in this study to address the above problems. To mimic the component and hierarchical structure of woven bone, amorphous calcium phosphate (ACP) and mineralized collagen fibril were synthesized and compounded with alginate to form IWBLHs with various ratio. Screened by physiochemical characterization and in vitro biological assays, an optimal IWBLH was selected and further explored in rat model of tooth extraction. Compared with the most widely used bone substitute, we showed that IWBLH could be easily handled to fully fill the tooth socket, perform a comparable function to prevent the alveolar bone resorption, and completely remodeled within 4 weeks. This IWBLH stands as a promising candidate for alveolar ridge preservation (ARP) in future.
Collapse
|
37
|
Tsai YL, Kao MW, Huang SJ, Lee YL, Lin CP, Chan JCC. Characterization of Phosphorus Species in Human Dentin by Solid-State NMR. Molecules 2020; 25:E196. [PMID: 31947753 PMCID: PMC6983145 DOI: 10.3390/molecules25010196] [Citation(s) in RCA: 8] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/12/2019] [Revised: 12/30/2019] [Accepted: 12/31/2019] [Indexed: 11/16/2022] Open
Abstract
The rat has been considered as an appropriate animal model for the study of the mineralization process in humans. In this work, we found that the phosphorus species in human dentin characterized by solid-state NMR spectroscopy consist mainly of orthophosphate and hydrogen phosphate. Some orthophosphates are found in a disordered phase, where the phosphate ions are hydrogen-bonded to structural water, some present a stoichiometric apatite structure, and some a hydroxyl-depleted apatite structure. The results of this study are largely the same as those previously obtained for rat dentin. However, the relative amounts of the various phosphorus species in human and rat dentin are dramatically different. In particular, stoichiometric apatite is more abundant in human dentin than in rat dentin, whereas the converse is true for disordered-phase orthophosphates. Furthermore, spatial proximity among all phosphorus species in human dentin is identical within experimental error, in contrast to what observed for rat dentin. Although it is not clear how these spectroscopic data could relate to the hierarchical structure or the mechanical properties of teeth, our data reveal that the molecular structures of human and rat dentin at different growth stages are not exactly the same.
Collapse
|
38
|
Sun R, Åhlén M, Tai CW, Bajnóczi ÉG, de Kleijne F, Ferraz N, Persson I, Strømme M, Cheung O. Highly Porous Amorphous Calcium Phosphate for Drug Delivery and Bio-Medical Applications. NANOMATERIALS (BASEL, SWITZERLAND) 2019; 10:E20. [PMID: 31861727 PMCID: PMC7022897 DOI: 10.3390/nano10010020] [Citation(s) in RCA: 24] [Impact Index Per Article: 4.8] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 11/28/2019] [Revised: 12/13/2019] [Accepted: 12/16/2019] [Indexed: 12/21/2022]
Abstract
Amorphous calcium phosphate (ACP) has shown significant effects on the biomineralization and promising applications in bio-medicine. However, the limited stability and porosity of ACP material restrict its practical applications. A storage stable highly porous ACP with Brunauer-Emmett-Teller surface area of over 400 m2/g was synthesized by introducing phosphoric acid to a methanol suspension containing amorphous calcium carbonate nanoparticles. Electron microscopy revealed that the porous ACP was constructed with aggregated ACP nanoparticles with dimensions of several nanometers. Large angle X-ray scattering revealed a short-range atomic order of <20 Å in the ACP nanoparticles. The synthesized ACP demonstrated long-term stability and did not crystallize even after storage for over 14 months in air. The stability of the ACP in water and an α-MEM cell culture medium were also examined. The stability of ACP could be tuned by adjusting its chemical composition. The ACP synthesized in this work was cytocompatible and acted as drug carriers for the bisphosphonate drug alendronate (AL) in vitro. AL-loaded ACP released ~25% of the loaded AL in the first 22 days. These properties make ACP a promising candidate material for potential application in biomedical fields such as drug delivery and bone healing.
Collapse
|
39
|
Dinh Nguyen T, Feng G, Yi X, Lyu Y, Lan Z, Xia J, Wu T, Jiang X. Six-month evaluation of novel bioabsorbable scaffolds composed of poly-L-lactic acid and amorphous calcium phosphate nanoparticles in porcine coronary arteries. J Biomater Appl 2019; 33:227-233. [PMID: 30096995 DOI: 10.1177/0885328218790332] [Citation(s) in RCA: 4] [Impact Index Per Article: 0.8] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/16/2022]
Abstract
Objective Using coronary angiography and intravascular ultrasound methods to evaluate the performance of the novel fully bioabsorbable scaffold (NFBS) composed of poly-L-lactic acid/amorphous calcium phosphate (PLLA/ACP) at six-month follow-up by comparing with PLLA scaffolds Methods Twelve PLLA/ACP scaffolds and 12 PLLA scaffolds were implanted into the coronary arteries of 12 miniature pigs. Quantitative coronary angiography (QCA) was used to measure the reference vessel diameter (RVD), mean lumen diameter (MLD) and late lumen loss (LLL). According to IVUS images, we calculated the strut malapposition rate (SMR) at post implantation, strut overlap rate (SOR), reference vessel area (RVA), mean stent area (MSA), mean lumen area (MLA) and luminal patency rate (LPR) at six-month follow-up. The radial strength of the scaffold was evaluated using a catheter tensile testing machine. Results QCA results indicated that, at six month, MLD of PLLA/ACP scaffolds was greater than those of PLLA scaffolds (2.47 ± 0.22 mm vs. 2.08 ± 0.25 mm, P < 0.05); LLL of PLLA/ACP scaffolds was less than those of PLLA scaffolds (0.42 ± 0.20 mm vs. 0.75 ± 0.22 mm, P < 0.05). IVUS results showed the SMR and SOR were all significantly less with the PLLA/ACP scaffolds than the PLLA scaffolds (5.84% ± 3.56% vs. 17.72% ± 4.86%, P < 0.05) (6.17% ± 4.63% vs. 17.65% ± 4.29%, P < 0.05). MSA, MLA and LPR of the PLLA/ACP scaffolds were all greater than those of PLLA scaffolds (6.35 ± 0.45 mm2 vs. 5.35 ± 0.51 mm2, P < 0.05) (4.76 ± 0.46 mm2 vs. 3.77 ± 0.46 mm2, P < 0.05) (78.01% ± 12.29% vs. 61.69% ± 9.76%, P < 0.05). Radial strength of PLLA/ACP scaffold at six month was greater than that of PLLA scaffold (76.33 ± 3.14 N vs. 67.67 ± 3.63 N). Conclusion The NFBS had less stent recoil, better lumen patency rate and greater radial strength than PLLA scaffolds. The results suggest the NFBS scaffolds can maintain the structural strength and functional performance, which are effective for up to six months when implanted in porcine coronary arteries.
Collapse
|
40
|
Shi Y, Shen D, Zheng H, Wu Z, Shao C, Zhang L, Pan H, Tang R, Fu B. Therapeutic Management of Demineralized Dentin Surfaces Using a Mineralizing Adhesive To Seal and Mineralize Dentin, Dentinal Tubules, and Odontoblast Processes. ACS Biomater Sci Eng 2019; 5:5481-5488. [PMID: 33464067 DOI: 10.1021/acsbiomaterials.9b00619] [Citation(s) in RCA: 11] [Impact Index Per Article: 2.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 12/27/2022]
Abstract
Dentin hypersensitivity is attributable to the exposed dentin and its patent tubules. We proposed the therapeutic management of demineralized dentin surfaces using a mineralizing adhesive to seal and remineralize dentin, dentinal tubules, and odontoblast processes. An experimental self-etch adhesive and a mineralizing adhesive consisting of the self-etch adhesive and 20 wt % poly-aspartic acid-stabilized amorphous calcium phosphate (PAsp-ACP) nanoparticles were prepared and characterized by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, transmission electron microscopy (TEM), and scanning electron microscopy. After 60 acid-etched midcoronal dentin disks were treated with distilled water (control), a desensitizing agent (Gluma), the experimental self-etch adhesive, and the mineralizing adhesive, dentin permeability was measured and mineralization was evaluated by Raman, FTIR, XRD, TEM, and selected-area electron diffraction, irrespective of abrasive and acidic challenges. In vitro cytotoxicity of the adhesive and the mineralizing adhesive was assessed by Cell Counting Kit-8. The mineralizing adhesive possessed excellent biocompatibility. We proposed a hybrid mineralization layer composed of the light-cured mineralizing adhesive and the mineralized dentin surfaces, as well as interiorly mineralized resin tags and odontoblast processes inside of the dentinal tubules. This hybrid mineralization not only reduced dentin permeability but also resisted abrasive and acidic attacks.
Collapse
|
41
|
Hoeher A, Mergelsberg S, Borkiewicz OJ, Dove PM, Michel FM. A new method for in situ structural investigations of nano-sized amorphous and crystalline materials using mixed-flow reactors. Acta Crystallogr A Found Adv 2019; 75:758-765. [PMID: 31475919 PMCID: PMC6718202 DOI: 10.1107/s2053273319008623] [Citation(s) in RCA: 17] [Impact Index Per Article: 3.4] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/18/2019] [Accepted: 06/17/2019] [Indexed: 11/29/2022] Open
Abstract
Structural investigations of amorphous and nanocrystalline phases forming in solution are historically challenging. Few methods are capable of in situ atomic structural analysis and rigorous control of the system. A mixed-flow reactor (MFR) is used for total X-ray scattering experiments to examine the short- and long-range structure of phases in situ with pair distribution function (PDF) analysis. The adaptable experimental setup enables data collection for a range of different system chemistries, initial supersaturations and residence times. The age of the sample during analysis is controlled by adjusting the flow rate. Faster rates allow for younger samples to be examined, but if flow is too fast not enough data are acquired to average out excess signal noise. Slower flow rates form older samples, but at very slow speeds particles settle and block flow, clogging the system. Proper background collection and subtraction is critical for data optimization. Overall, this MFR method is an ideal scheme for analyzing the in situ structures of phases that form during crystal growth in solution. As a proof of concept, high-resolution total X-ray scattering data of amorphous and crystalline calcium phosphates and amorphous calcium carbonate were collected for PDF analysis.
Collapse
|
42
|
Uskoković V, Marković S, Veselinović L, Škapin S, Ignjatović N, Uskoković DP. Insights into the kinetics of thermally induced crystallization of amorphous calcium phosphate. Phys Chem Chem Phys 2018; 20:29221-29235. [PMID: 30427330 PMCID: PMC6327086 DOI: 10.1039/c8cp06460a] [Citation(s) in RCA: 37] [Impact Index Per Article: 6.2] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/21/2022]
Abstract
Transformations between amorphous and crystalline apatite mechanistically govern some of the most essential processes in bone metabolism, including biomineralization and bone remodeling. Fundamental understanding of this phase transition can help us gain control over the formation and dissolution of boney tissues in vivo and utilize that knowledge for various therapeutic ends. Crystallization of hydroxyapatite (HAp) and two tricalcium phosphate (TCP) polymorphs from the metastable precursor, amorphous calcium phosphate (ACP) was here studied kinetically and mechanistically using thermal analyses, X-ray diffraction and Fourier-transform infrared spectroscopy. Crystallization was detected in the differential thermal analysis as the exothermic peak at 639.5 °C at the slowest heating regimen of 5 °C min-1, while a combination of different kinetics models, including Augis-Bennett, Borchardt-Daniels, Johnson-Mehl-Avrami, Kissinger, Ozawa and Piloyan, yielded activation energies in the 435-450 kJ mol-1 range. Dehydrated ACP required a significant energy input to transform to HAp, thus indirectly proving the key role that structural water plays in this process in a biological setting. The phase transformation at high temperatures involved preformed nuclei and was solely due to their 3D growth, contrasting the edge-controlled nucleation derived earlier as the mechanism of growth in the solution. Crystallization was in both cases accompanied by the formation of needle-shape crystals of HAp through aggregation of ultrafine spherical units of ACP. Relationship between crystallinity and the heating rate was detected only for the initially amorphous structure, indicating a more intense and coherent lattice ordering process in annealed ACP than in HAp. Despite that, crystallization disobeyed the rule of inverse proportionality between the thermal energy required for the relaxation of defects and the level of strain, as the recovery rate of the initially poorly crystalline HAp was higher than that of ACP.
Collapse
|
43
|
Gürlek C, Ertuğrul F, Nile C, Lappin DF, Buduneli N. Plaque Accumulation and Inflammation Adjacent to Restorations of Amorphous Calcium Phosphate-containing Composite in Early Childhood Caries. ORAL HEALTH & PREVENTIVE DENTISTRY 2018; 16:457-465. [PMID: 30460359 DOI: 10.3290/j.ohpd.a41361] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.2] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Subscribe] [Scholar Register] [Indexed: 11/06/2022]
Abstract
PURPOSE To evaluate the clinical, biochemical, and microbiological reactions to nanocomposite containing amorphous calcium phosphate (ACP) in comparison to a traditional composite restorative material in early childhood caries. MATERIALS AND METHODS Eighteen teeth were restored with the test material (ACP-containing resin) and 18 teeth were restored with the control material (traditional composite, TC) in fourteen paediatric patients using a split-mouth design. One caries- and restoration-free intact tooth in each patient was selected as the healthy control. Gingival crevicular fluid (GCF) and supragingival plaque samples were collected at baseline before the treatment and also on days 1, 7, 14 and 30 after treatment. Unstimulated whole saliva samples were obtained from each patient at baseline, and 1 and 6 months after restoration. GCF and saliva samples were assayed for IL-17A, IL-17F IL-17A/F, IL-17E, OPG and RANKL levels by ELISA, and plaque composition was assessed using RT-PCR. RESULTS Clinical evaluation indicated no statistically significant differences between the two restorative materials according to the FDI criteria surface lustre, material retention and marginal adaptation properties. Pro-inflammatory IL-17 levels decreased statistically significantly at 6 months compared to baseline and 1-month values (p < 0.05). The baseline pro-inflammatory IL-17 cytokine levels in GCF samples around the carious teeth were higher than those obtained around the healthy teeth (p < 0.05), but similar in GCF from the ACP-test and TC teeth. Microbiological findings were similar in the ACP and T groups. CONCLUSION It may be suggested that both ACP-containing and traditional resin composites show similar antimicrobial and biochemical effects in early childhood caries.
Collapse
|
44
|
Quan BD, Sone ED. The effect of polyaspartate chain length on mediating biomimetic remineralization of collagenous tissues. J R Soc Interface 2018; 15:rsif.2018.0269. [PMID: 30333243 DOI: 10.1098/rsif.2018.0269] [Citation(s) in RCA: 17] [Impact Index Per Article: 2.8] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/18/2018] [Accepted: 09/20/2018] [Indexed: 12/13/2022] Open
Abstract
Formation of hydroxyapatite (HAP) within collagen fibrils, as found in bone, dentine and cementum, is thought to be mediated by proteins rich in aspartate (Asp) and glutamate such as osteopontin and bone sialoprotein, respectively. Indeed polyaspartate (pAsp), a homopolymer analogue of such proteins, has been shown to induce intrafibrillar mineralization of collagen from solutions of calcium and phosphate that are supersaturated with respect to HAP. To elucidate the role of pAsp in mineralization of collagen, we explored the effect of pAsp chain length on in vitro HAP deposition in demineralized mouse periodontal tissue sections. Through characterization of both tissue sections and mineralizing solution, we show that chain length contributes to the effectiveness of pAsp in mediating intrafibrillar mineralization. This function appears to be associated with inhibition of otherwise kinetically favoured crystallization in the bulk solution, which allows for intrafibrillar crystallization, though this does not preclude the possibility of a more active role for pAsp in addition. Inhibition of crystallization in solution by pAsp occurs by slowing the growth of amorphous calcium phosphate and stabilization of this phase, rather than by sequestration of Ca2+ ions. These results suggest that the length of Asp-rich sequences of mineralizing proteins may be essential to their function, and could also be useful in optimization of mineralized tissue replacement synthesis.
Collapse
|
45
|
Effects of Amorphous Calcium Phosphate Administration on Dental Sensitivity during In-Office and At-Home Interventions. Dent J (Basel) 2018; 6:dj6040052. [PMID: 30275415 PMCID: PMC6313672 DOI: 10.3390/dj6040052] [Citation(s) in RCA: 7] [Impact Index Per Article: 1.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/04/2018] [Revised: 09/12/2018] [Accepted: 09/17/2018] [Indexed: 11/21/2022] Open
Abstract
Background. Tooth bleaching is the most frequently employed whitening procedure in clinics. The major side effect of tooth bleaching is dental sensitivity during and after the treatment. Here, we evaluated whether the administration of amorphous calcium phosphate (ACP), during in-office and at-home procedures may impact on dental sensitivity. Methods. Eighty patients, responding to the study requirements were enrolled according to the following criteria. Group 1 (n = 40), received in-office, 10% ACP prior to 30% professional hydrogen peroxide application. The whitening procedure continued at home using 10% carbamide peroxide with 15% ACP for 15 days. Group 2 (n = 40) received only 30% hydrogen peroxide application and continued the whitening procedures at home, using 10% carbamide hydroxide, without ACP- Casein phosphopeptides (CPP), for 15 days. Dental sensitivity was recorded with a visual analogue scale (VAS) at baseline, immediately after, and at 15 days after treatment in the two groups. Results. We observed that patients receiving ACP in the bleaching mixture experienced decreased dental sensitivity (* p ≤ 0.05), as detected by VAS scale analysis immediately following the procedures. Patients receiving ACP-CPP during at-home procedures showed a statistically significant (*** p ≤ 0.0001) reduction of dental sensitivity. Conclusions. We demonstrated that ACP-CPP administration, while exerting the same whitening effects as in control subjects receiving potassium fluoride (PF), had an impact on the reduction of dental sensitivity, improving patient compliance.
Collapse
|
46
|
Pei D, Sun J, Zhu C, Tian F, Jiao K, Anderson MR, Yiu C, Huang C, Jin C, Bergeron BE, Chen J, Tay FR, Niu L. Contribution of Mitophagy to Cell-Mediated Mineralization: Revisiting a 50-Year-Old Conundrum. ADVANCED SCIENCE (WEINHEIM, BADEN-WURTTEMBERG, GERMANY) 2018; 5:1800873. [PMID: 30356983 PMCID: PMC6193168 DOI: 10.1002/advs.201800873] [Citation(s) in RCA: 46] [Impact Index Per Article: 7.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 06/04/2018] [Indexed: 05/24/2023]
Abstract
Biomineralization in vertebrates is initiated via amorphous calcium phosphate (ACP) precursors. These precursors infiltrate the extracellular collagen matrix where they undergo phase transformation into intrafibrillar carbonated apatite. Although it is well established that ACP precursors are released from intracellular vesicles through exocytosis, an unsolved enigma in this cell-mediated mineralization process is how ACP precursors, initially produced in the mitochondria, are translocated to the intracellular vesicles. The present study proposes that mitophagy provides the mechanism for transfer of ACP precursors from the dysfunctioned mitochondria to autophagosomes, which, upon fusion with lysosomes, become autolysosomes where the mitochondrial ACP precursors coalesce to form larger intravesicular granules, prior to their release into the extracellular matrix. Apart from endowing the mitochondria with the function of ACP delivery through mitophagy, the present results indicate that mitophagy, triggered upon intramitochondrial ACP accumulation in osteogenic lineage-committed mesenchymal stem cells, participates in the biomineralization process through the BMP/Smad signaling pathway.
Collapse
|
47
|
Chu J, Feng X, Guo H, Zhang T, Zhao H, Zhang Q. Remineralization Efficacy of an Amelogenin-Based Synthetic Peptide on Carious Lesions. Front Physiol 2018; 9:842. [PMID: 30026702 PMCID: PMC6041723 DOI: 10.3389/fphys.2018.00842] [Citation(s) in RCA: 15] [Impact Index Per Article: 2.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/10/2018] [Accepted: 06/14/2018] [Indexed: 11/13/2022] Open
Abstract
Objective: The aim of this study was to evaluate the remineralization efficacy of an amelogenin-based peptide on initial enamel carious lesions in vitro. Furthermore, we attempted to provide insights into the possible mechanism of the remineralization, including determining the calcium-binding properties of the peptide and its effects on calcium phosphate mineralization. Methods: The peptide comprising the N-terminus and the C-terminus of porcine amelogenin was synthesized by Synpeptide Co., Ltd. Fifty specimens were randomly assigned to five immersing treatment groups for 12 days: remineralizing medium only; 12.5 μg/mL peptide + remineralizing medium; 25 μg/mL peptide + remineralizing medium; 50 μg/mL peptide + remineralizing medium; fluoride + remineralizing medium. After immersion, mean mineral loss before and after remineralization of each specimen was determined using micro-CT. Mean mineral gain after remineralization was calculated. Calcium binding properties were measured by Isothermal titration calorimetry (ITC). TEM and Fourier transform-infrared were used to determine the effects of the peptide on calcium phosphate mineralization. Results: A significant decrease in mineral loss after remineralization process in all groups was observed (p < 0.05). Treatment in remineralizing medium resulted in the lowest mineral gain while the fluoridated treatment exhibited the highest mineral gain among all groups. Inclusion of synthetic peptide in the remineralizing medium exhibited a higher mineral gain and the gain of 50 μg/mL group was greater than that of the 25 μg/mL group. No significant difference in mineral gain was observed between the remineralizing medium only group and the 12.5 μg/mL peptide group (p > 0.05). ITC values showed that the Ca2+-binding affinity of the peptide is about 9.914 × 104M−1. Furthermore, the peptide was found to inhibit calcium phosphate precipitation and stabilize amorphous calcium phosphate formation for more than 2 h and finally transform into ordered hydroxyapatite crystals. Conclusion: Specific concentrations of the amelogenin-based synthetic peptide promoted in vitro remineralization, with higher concentrations exhibiting significantly greater remineralization. This study presented evidence suggesting that the peptide may act as a Ca2+carrier as well as a regulating factor. When the stabilizing calcium and phosphorus ions bind with the peptide they become biologically available for the remineralization of deeper carious lesions, while also regulated by the peptide to transform into ordered hydroxyapatite crystals.
Collapse
|
48
|
Uskoković V, Tang S, Wu VM. On Grounds of the Memory Effect in Amorphous and Crystalline Apatite: Kinetics of Crystallization and Biological Response. ACS APPLIED MATERIALS & INTERFACES 2018; 10:14491-14508. [PMID: 29625010 DOI: 10.1021/acsami.8b02520] [Citation(s) in RCA: 21] [Impact Index Per Article: 3.5] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 06/08/2023]
Abstract
Memory effects, despite being intrinsic to biological systems, are rarely potentiated in biomaterials. By exploring the transition between amorphous calcium phosphate (ACP) and hydroxyapatite (HAp) from different empirical angles, here, we attempt to set the basis for elicitation of structural memory effects in CPs. Two CPs precipitated under different degrees of saturation (DS), yielding HAp at a low DS and ACP at a high DS, were shown to evolve into structures with a high level of crystallographic similarity after their prolonged aging in the solution and served as the basis for this study. Amorphous-to-crystalline transition was abrupt in both precipitates, indicating an autocatalytic process preceded by considerable nucleation lag times, but it was more dynamic and proceeded in multiple stages in the precipitate formed at a higher DS, involving a greater degree of lattice rearrangements. ACP was found to exist in one of the two stoichiometrically and crystallographically different forms, one of which, amounting to ≥60 wt %, resembled tricalcium phosphate and transformed to HAp through the surface dissolution/reprecipitation mechanism and the other one, amounting to ≤20 wt %, was apatitic, enabling the transformation of ACP to HAp via martensitic, bulk lattice reordering phenomena. Large density of stacking faults was responsible for the comparatively high lattice strain, the property to which biogenic apatite owes its ability to accommodate foreign ions and act as a mineral reservoir for the body. Being the precursor for biogenic apatite during biomineralization and a thermodynamically logical intermediate in the ripening of HAp per the Ostwald law of stages, ACP proved to be more prone to structural transformation than the final and the most stable of the CP phases in this sequence of events: HAp. Amorphized upon gelation, two CPs transformed into HAp, albeit at different rates, which were higher for the material that had been crystalline prior to amorphization than for the one that had initially been amorphous, indicating the presence of a definite memory effect. The two HAp powders with different histories of formation also elicited different biological responses, including a Runx2 transcription factor expression in MC3T3-E1 osteoblasts, cell uptake efficiency, and antibacterial activity, extending the memory effect in HAp to the biological domain. The biological response was typically indistinct between the final products and their respective precursors but markedly different between the two products obtained by following different formation paths, confirming the presence of the given memory effect. It is suggested that the key to explaining the difference in the response between the materials differing in their route of formation lies in the direct dependence between the DS at which precipitation occurs and the rate of exchange of hydrated ions and ionic clusters across the particle surface in contact with a solution.
Collapse
|
49
|
Allegrini S, da Silva AC, Tsujita M, Salles MB, Gehrke SA, Braga FJC. Amorphous calcium phosphate (ACP) in tissue repair process. Microsc Res Tech 2018. [PMID: 29532542 DOI: 10.1002/jemt.23013] [Citation(s) in RCA: 12] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 01/22/2023]
Abstract
Synthetic biomaterials submitted to new structural technologies have become ideal for the recovery of traumatized bone tissues and some bone substitutes such as bioactive glass, β-Tricalcium phosphate (β-TCP) and amorphous calcium phosphate (ACP) are being used in areas of tissue defects. For this study, ACP was produced in the form of fibers and then submitted to cytotoxicity testing. A sample of ACP was inserted into the mandibular region of a patient with a lost implant so after removal and curettage, the remaining bone site was filled with the ACP biomaterial. Preliminary cytotoxicity test was negative. After 15 weeks of healing, a titanium implant was inserted at the site. Clinical and radiographic follow-up was conducted for 12 months and sequential radiographic analyses revealed tissue formation resembling spongy bone. Images under immunohistochemistry demonstrated efficient deposition and osteoconduction of the newly deposited tissue. Residual portion of the CaO:P2 O5 outer layers served as a substrate for osteoid matrix deposition, aiding growth, and the results of fiber absorption favored maturation of the new bone tissue.
Collapse
|
50
|
Bienek DR, Frukhtbeyn SA, Giuseppetti AA, Okeke UC, Skrtic D. Antimicrobial Monomers for Polymeric Dental Restoratives: Cytotoxicity and Physicochemical Properties. J Funct Biomater 2018; 9:jfb9010020. [PMID: 29495522 PMCID: PMC5872106 DOI: 10.3390/jfb9010020] [Citation(s) in RCA: 7] [Impact Index Per Article: 1.2] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/19/2018] [Revised: 02/14/2018] [Accepted: 02/22/2018] [Indexed: 12/16/2022] Open
Abstract
A trend for the next generation of polymeric dental restoratives is to incorporate multifunctional capabilities to regulate microbial growth and remineralize tooth surfaces. Polymerizable 2-(methacryloyloxy)-N-(2-(methacryloyloxy)ethyl)-N,N-dimethylethan-1-aminium bromide (IDMA1) and N,N′-([1,1′-biphenyl]-2,2′-diylbis(methylene))bis(2-(methacryloyloxy)-N,N-dimethylethan-1-aminium) bromide (IDMA2), intended for utilization in bi-functional antimicrobial and remineralizing composites, were synthesized, purified with an ethanol-diethyl ether-hexane solvent system, and validated by nuclear magnetic resonance (1H and 13C NMR) spectroscopy, mass spectrometry, and Fourier-transform infrared spectroscopy. When incorporated into light-curable urethane dimethacrylate (UDMA)/polyethylene glycol-extended UDMA (PEG-U)/ethyl 2-(hydroxymethyl)acrylate (EHMA) (assigned UPE) resins, IDMAs did not affect the overall resins’ hydrophilicity/hydrophobicity balance (water contact angle: 60.8–65.5°). The attained degrees of vinyl conversion (DVC) were consistently higher in both IDMA-containing copolymers and their amorphous calcium phosphate (ACP) composites (up to 5% and 20%, respectively) reaching 92.5% in IDMA2 formulations. Notably, these high DVCs values were attained without an excessive increase in polymerization stress. The observed reduction in biaxial flexure strength of UPE-IDMA ACP composites should not prevent further evaluation of these materials as multifunctional Class V restoratives. In direct contact with human gingival fibroblasts, at biologically relevant concentrations, IDMAs did not adversely affect cell viability or their metabolic activity. Ion release from the composites was indicative of their strong remineralization potential. The above, early-phase biocompatibility and physicochemical tests justify further evaluation of these experimental materials to identify formulation(s) suitable for clinical testing. Successful completion is expected to yield a new class of restoratives with well-controlled bio-function, which will physicochemically, mechanically, and biologically outperform the conventional Class V restoratives.
Collapse
|