Electrospun fibrous scaffolds with multiscale and photopatterned porosity

Elastic three-dimensional poly (ε-caprolactone) nanofibre scaffold enhances migration, proliferation and osteogenic differentiation of mesenchymal stem cells

OBJECTIVES

We prepared 3D poly (ε-caprolactone) (PCL) nanofibre scaffolds and tested their use for seeding, proliferation, differentiation and migration of mesenchymal stem cell (MSCs).

MATERIALS AND METHODS

3D nanofibres were prepared using a special collector for common electrospinning; simultaneously, a 2D PCL nanofibre layer was prepared using a classic plain collector. Both scaffolds were seeded with MSCs and biologically tested. MSC adhesion, migration, proliferation and osteogenic differentiation were investigated.

RESULTS

The 3D PCL scaffold was characterized by having better biomechanical properties, namely greater elasticity and resistance against stress and strain, thus this scaffold will be able to find broad applications in tissue engineering. Clearly, while nanofibre layers of the 2D scaffold prevented MSCs from migrating through the conformation, cells infiltrated freely through the 3D scaffold. MSC adhesion to the 3D nanofibre PCL layer was also statistically more common than to the 2D scaffold (P < 0.05), and proliferation and viability of MSCs 2 or 3 weeks post-seeding, were also greater on the 3D scaffold. In addition, the 3D PCL scaffold was also characterized by displaying enhanced MSC osteogenic differentiation.

CONCLUSIONS

We draw the conclusion that all positive effects observed using the 3D PCL nanofibre scaffold are related to the larger fibre surface area available to the cells. Thus, the proposed 3D structure of the nanofibre layer will find a wide array of applications in tissue engineering and regenerative medicine.

Three-dimensional electrospun alginate nanofiber mats via tailored charge repulsions

The formation of 3D electrospun mat structures from alginate-polyethylene oxide (PEO) solution blends is reported. These unique architectures expand the capabilities of traditional electrospun mats for applications such as regenerative medicine, where a scaffold can help to promote tissue growth in three dimensions. The mat structures extend off the surface of the flat collector plate without the need of any modifications in the electrospinning apparatus, are self-supported when the electric field is removed, and are composed of bundles of nanofibers. A mechanism for the unique formations is proposed, based on the fiber-fiber repulsions from surface charges on the negatively charged alginate. Furthermore, the role of the electric field in the distribution of alginate within the nanofibers is discussed. X-ray photoelectron spectroscopy is used to analyze the surface composition of the electrospun nanofiber mats and the data is related to cast films made in the absence of the electric field. Further techniques to tailor the 3D architecture and nanofiber morphology by changing the surface tension and relative humidity are also discussed.

Injectable skeletal muscle matrix hydrogel promotes neovascularization and muscle cell infiltration in a hindlimb ischemia model

Peripheral artery disease (PAD) currently affects approximately 27 million patients in Europe and North America, and if untreated, may progress to the stage of critical limb ischemia (CLI), which has implications for amputation and potential mortality. Unfortunately, few therapies exist for treating the ischemic skeletal muscle in these conditions. Biomaterials have been used to increase cell transplant survival as well as deliver growth factors to treat limb ischemia; however, existing materials do not mimic the native skeletal muscle microenvironment they are intended to treat. Furthermore, no therapies involving biomaterials alone have been examined. The goal of this study was to develop a clinically relevant injectable hydrogel derived from decellularized skeletal muscle extracellular matrix and examine its potential for treating PAD as a stand-alone therapy by studying the material in a rat hindlimb ischemia model. We tested the mitogenic activity of the scaffold's degradation products using an in vitro assay and measured increased proliferation rates of smooth muscle cells and skeletal myoblasts compared to collagen. In a rat hindlimb ischemia model, the femoral artery was ligated and resected, followed by injection of 150 µL of skeletal muscle matrix or collagen 1 week post-injury. We demonstrate that the skeletal muscle matrix increased arteriole and capillary density, as well as recruited more desmin-positive and MyoD-positive cells compared to collagen. Our results indicate that this tissue-specific injectable hydrogel may be a potential therapy for treating ischemia related to PAD, as well as have potential beneficial effects on restoring muscle mass that is typically lost in CLI.

Electrospun polyvinyl alcohol-collagen-hydroxyapatite nanofibers: a biomimetic extracellular matrix for osteoblastic cells

The failure of prosthesis after total joint replacement is due to the lack of early implant osseointegration. In this study polyvinyl alcohol-collagen-hydroxyapatite (PVA-Col-HA) electrospun nanofibrous meshes were fabricated as a biomimetic bone-like extracellular matrix for the modification of orthopedic prosthetic surfaces. In order to reinforce the PVA nanofibers, HA nanorods and Type I collagen were incorporated into the nanofibers. We investigated the morphology, biodegradability, mechanical properties and biocompatibility of the prepared nanofibers. Our results showed these inorganic-organic blended nanofibers to be degradable in vitro. The encapsulated nano-HA and collagen interacted with the PVA content, reinforcing the hydrolytic resistance and mechanical properties of nanofibers that provided longer lasting stability. The encapsulated nano-HA and collagen also enhanced the adhesion and proliferation of murine bone cells (MC3T3) in vitro. We propose the PVA-Col-HA nanofibers might be promising modifying materials on implant surfaces for orthopedic applications.

Improved cellular infiltration into nanofibrous electrospun cross-linked gelatin scaffolds templated with micrometer-sized polyethylene glycol fibers

Gelatin-based nanofibrous scaffolds with a mean fiber diameter of 300 nm were prepared with and without micrometer-sized polyethylene glycol (PEG) fibers that served as sacrificial templates. Upon fabrication of the scaffolds via electrospinning, the gelatin fibers were crosslinked with glutaraldehyde, and the PEG templates were removed using tert-butanol to yield nanofibrous scaffolds with pore diameters ranging from 10 to 100 µm, as estimated with mercury intrusion porosimetry. Non-templated gelatin-based nanofibrous matrices had an average pore size of 1 µm. Fibroblasts were seeded onto both types of the gelatin-based nanofibrous surfaces and cultured for 14 days. For comparative purposes, chitosan-based and polyurethane-based macroporous scaffolds with pore sizes of 100 and 170 µm, respectively, were also included. The number of cells as a function of the depth into the scaffold was judged and quantitatively assessed using nuclei staining. Cell penetration up to a depth of 250 and 90 µm was noted in gelatin scaffolds prepared with sacrificial templates and gelatin-only nanofibrous scaffolds. Noticeably, scaffold preparation protocol presented here allowed the structural integrity to be maintained even with high template content (95%) and can easily be extended toward other classes of electrospun polymer matrices for tissue engineering.

Hydrogel design for cartilage tissue engineering: a case study with hyaluronic acid

Hyaline cartilage serves as a low-friction and wear-resistant articulating surface in load-bearing, diarthrodial joints. Unfortunately, as the avascular, alymphatic nature of cartilage significantly impedes the body's natural ability to regenerate, damage resulting from trauma and osteoarthritis necessitates repair attempts. Current clinical methods are generally limited in their ability to regenerate functional cartilage, and so research in recent years has focused on tissue engineering solutions in which the regeneration of cartilage is pursued through combinations of cells (e.g., chondrocytes or stem cells) paired with scaffolds (e.g., hydrogels, sponges, and meshes) in conjunction with stimulatory growth factors and bioreactors. A variety of synthetic and natural materials have been employed, most commonly in the form of hydrogels, and these systems have been tuned for optimal nutrient diffusion, connectivity of deposited matrix, degradation, soluble factor delivery, and mechanical loading for enhanced matrix production and organization. Even with these promising advances, the complex mechanical properties and biochemical composition of native cartilage have not been achieved, and engineering cartilage tissue still remains a significant challenge. Using hyaluronic acid hydrogels as an example, this review will follow the progress of material design specific to cartilage tissue engineering and propose possible future directions for the field.

Gradients with depth in electrospun fibrous scaffolds for directed cell behavior

A major obstacle in creating viable tissue-engineered constructs using electrospinning is the lack of complete cellularization and vascularization due to the limited porosity in these densely packed fibrous scaffolds. One potential approach to circumvent this issue is the use of various gradients of chemical and biophysical cues to drive the infiltration of cells into these structures. Toward this goal, this study focused on creating durotactic (mechanical) and haptotactic (adhesive) gradients through the thickness of electrospun hyaluronic acid (HA) scaffolds using a unique, yet simple, modification of common electrospinning protocols. Specifically, both mechanical (via cross-linking: ranging from 27-100% modified methacrylated HA, MeHA) and adhesive (via inclusion of the adhesive peptide RGD: 0-3 mM RGD) gradients were each fabricated by mixing two solutions (one ramping up, one ramping down) prior to electrospinning and fiber collection. Gradient formation was verified by fluorescence microscopy, FTIR, atomic force microscopy, and cellular morphology assessment of scaffolds at different points of collection (i.e., with scaffold thickness). To test further the functionality of gradient scaffolds, chick aortic arch explants were cultured on adhesive gradient scaffolds for 7 days, and low RGD-high RGD gradient scaffolds showed significantly greater cell infiltration compared with high RGD-low RGD gradients and uniform high RGD or uniform low RGD control scaffolds. In addition to enhanced infiltration, this approach could be used to fabricate graded tissue structures, such as those that occur at interfaces.

The influence of fibrous elastomer structure and porosity on matrix organization

Fibrous scaffolds are finding wide use in the field of tissue engineering, as they can be designed to mimic many native tissue properties and structures (e.g., cardiac tissue, meniscus). The influence of fiber alignment and scaffold architecture on cellular interactions and matrix organization was the focus of this study. Three scaffolds were fabricated from the photocrosslinkable elastomer poly(glycerol sebacate) (PGS), with changes in fiber alignment (non-aligned (NA) versus aligned (AL)) and the introduction of a PEO sacrificial polymer population to the AL scaffold (composite (CO)). PEO removal led to an increase in scaffold porosity and maintenance of scaffold anisotropy, as evident through visualization, mechanical testing, and mass loss studies. Hydrated scaffolds possessed moduli that ranged between ∼3-240 kPa, failing within the range of properties (<300 kPa) appropriate for soft tissue engineering. CO scaffolds were completely degraded as early as 16 days, whereas NA and AL scaffolds had ∼90% mass loss after 21 days when monitored in vitro. Neonatal cardiomyocytes, used as a representative cell type, that were seeded onto the scaffolds maintained their viability and aligned along the surface of the AL and CO fibers. When implanted subcutaneously in rats, a model that is commonly used to investigate in vivo tissue responses to biomaterials, CO scaffolds were completely integrated at 2 weeks, whereas ∼13% and ∼16% of the NA and AL scaffolds, respectively remained acellular. However, all scaffolds were completely populated with cells at 4 weeks post-implantation. Polarized light microscopy was used to evaluate the collagen elaboration and orientation within the scaffold. An increase in the amount of collagen was observed for CO scaffolds and enhanced alignment of the nascent collagen was observed for AL and CO scaffolds compared to NA scaffolds. Thus, these results indicate that the scaffold architecture and porosity are important considerations in controlling tissue formation.

Combined technologies for microfabricating elastomeric cardiac tissue engineering scaffolds

Polymer scaffolds that direct elongation and orientation of cultured cells can enable tissue engineered muscle to act as a mechanically functional unit. We combined micromolding and microablation technologies to create muscle tissue engineering scaffolds from the biodegradable elastomer poly(glycerol sebacate). These scaffolds exhibited well defined surface patterns and pores and robust elastomeric tensile mechanical properties. Cultured C2C12 muscle cells penetrated the pores to form spatially controlled engineered tissues. Scanning electron and confocal microscopy revealed muscle cell orientation in a preferential direction, parallel to micromolded gratings and long axes of microablated anisotropic pores, with significant individual and interactive effects of gratings and pore design.

Reconstructing the differentiation niche of embryonic stem cells using biomaterials

The biochemical cues and topographical architecture of the extracellular environment extensively influence ES cell fate. The microenvironment surrounding the developing embryo presents these instructive cues in a complex and interactive manner in order to guide cell fate decisions. Current stem cell research aims to reconstruct this multifaceted embryonic niche to recapitulate development in vitro. This review focuses on 2D and 3D differentiation niches created from natural and synthetic biomaterials to guide the differentiation of ES cells toward specific lineages. Biomaterials engineered to present specific physical constraints are also reviewed for their role in differentiation.

Electrospinning fibrous polymer scaffolds for tissue engineering and cell culture

As the field of tissue engineering evolves, there is a tremendous demand to produce more suitable materials and processing techniques in order to address the requirements (e.g., mechanics and vascularity) of more intricate organs and tissues. Electrospinning is a popular technique to create fibrous scaffolds that mimic the architecture and size scale of the native extracellular matrix. These fibrous scaffolds are also useful as cell culture substrates since the fibers can be used to direct cellular behavior, including stem cell differentiation (see extensive reviews by Mauck et al. and Sill et al. for more information). In this article, we describe the general process of electrospinning polymers and as an example, electrospin a reactive hyaluronic acid capable of crosslinking with light exposure (see Ifkovits et al. for a review on photocrosslinkable materials). We also introduce further processing capabilities such as photopatterning and multi-polymer scaffold formation. Photopatterning can be used to create scaffolds with channels and multi-scale porosity to increase cellular infiltration and tissue distribution. Multi-polymer scaffolds are useful to better tune the properties (mechanics and degradation) of a scaffold, including tailored porosity for cellular infiltration. Furthermore, these techniques can be extended to include a wide array of polymers and reactive macromers to create complex scaffolds that provide the cues necessary for the development of successful tissue engineered constructs.

Improved cellular infiltration in electrospun fiber via engineered porosity

Small pore sizes inherent to electrospun matrices can hinder efficient cellular ingrowth. To facilitate infiltration while retaining its extracellular matrix-like character, electrospinning was combined with salt leaching to produce a scaffold having deliberate, engineered delaminations. We made elegant use of a specific randomizing component of the electrospinning process, the Taylor Cone and the falling fiber beneath it, to produce a uniform, well-spread distribution of salt particles. After 3 weeks of culture, up to 4 mm of cellular infiltration was observed, along with cellular coverage of up to 70% within the delaminations. To our knowledge, this represents the first observation of extensive cellular infiltration of electrospun matrices. Infiltration appears to be driven primarily by localized proliferation rather than coordinated cellular locomotion. Cells also moved from the salt-generated porosity into the surrounding electrospun fiber matrix. Given that the details of salt deposition (amount, size, and number density) are far from optimized, the result provides a convincing illustration of the ability of mammalian cells to interact with appropriately tailored electrospun matrices. These layered structures can be precisely fabricated by varying the deposition interval and particle size conceivably to produce in vivo-like gradients in porosity such that the resulting scaffolds better resemble the desired final structure.