Dual-Interface Modulation with Covalent Organic Framework Enables Efficient and Durable Perovskite Solar Cells

A-D-A Molecule-Bridge Interface for Efficient Perovskite Solar Cells and Modules

As the photovoltaic field endeavors to transition perovskite solar cells (PSCs) to industrial applications, inverted PSCs, which incorporate fullerene as electron transport layers, have emerged as a compelling choice due to their augmented stability and cost-effectiveness. However, these attributes suffer from performance issues stemming from suboptimal electrical characteristics at the perovskite/fullerene interface. To surmount these hurdles, an interface bridging strategy (IBS) is proposed to attenuate the interface energy loss and enhance the interfacial stability by designing a series of A-D-A type perylene monoimide (PMI) derivatives with multifaceted advantages. In addition to passivating defects, the IBS plays a crucial role in facilitating the binding between perovskite and fullerene, thereby enhancing interface coupling and importantly, improving the formation of fullerene films. The PMI derivatives, functioning as bridges, serve as a protective barrier to enhance the device stability. Consequently, the IBS enables a remarkable efficiency of 24.62% for lab-scale PSCs and an efficiency of 18.73% for perovskite solar modules craft on 156 × 156 mm2 substrates. The obtained efficiencies represent some of the highest recorded for fullerene-based devices, showcasing significant progress in designing interfacial molecules at the perovskite/fullerene interface and offering a promising path to enhance the commercial viability of PSCs.

Implementation of a Multi-Functional-Group Strategy for Enhanced Performance of Perovskite Solar Cells through the Incorporation of 3-Amino-4-Phenylbutyric Acid Hydrochloride

Reducing the defect density of perovskite films during the crystallization process is critical in preparing high-performance perovskite solar cells (PSCs). Here, a multi-functional molecule, 3-phenyl-4-aminobutyric acid hydrochloride (APH), with three functional groups including a benzene ring, ─NH3 + and ─COOH, is added into the perovskite precursor solution to improve perovskite crystallization and device performance. The benzene ring increases the hydrophobicity of perovskites, while ─NH3 + and ─COOH passivate defects related to I- and Pb2+, respectively. Consequently, the power conversion efficiency (PCE) of the optimal device increased to 24.65%. Additionally, an effective area of 1 cm2 with a PCE of 22.45% is also prepared using APH as an additive. Furthermore, PSCs prepared with APH exhibit excellent stability by 87% initial PCE without encapsulation after exposure at room temperature under 25% humidity for 5000 h and retaining 70% of initial PCE after aging at 85 °C in an N2 environment for 864 h.

Multifunctional MOF@COF Nanoparticles Mediated Perovskite Films Management Toward Sustainable Perovskite Solar Cells

Although covalent organic frameworks (COFs) with high π-conjugation have recently exhibited great prospects in perovskite solar cells (PSCs), their further application in PSCs is still hindered by face-to-face stacking and aggregation issues. Herein, metal-organic framework (MOF-808) is selected as an ideal platform for the in situ homogeneous growth of a COF to construct a core-shell MOF@COF nanoparticle, which could effectively inhibit COF stacking and aggregation. The synergistic intrinsic mechanisms induced by the MOF@COF nanoparticles for reinforcing intrinsic stability and mitigating lead leakage in PSCs have been explored. The complementary utilization of π-conjugated skeletons and nanopores could optimize the crystallization of large-grained perovskite films and eliminate defects. The resulting PSCs achieve an impressive power conversion efficiency of 23.61% with superior open circuit voltage (1.20 V) and maintained approximately 90% of the original power conversion efficiency after 2000 h (30-50% RH and 25-30 °C). Benefiting from the synergistic effects of the in situ chemical fixation and adsorption abilities of the MOF@COF nanoparticles, the amount of lead leakage from unpackaged PSCs soaked in water (< 5 ppm) satisfies the laboratory assessment required for the Resource Conservation and Recovery Act Regulation.

Enhancing Ultraviolet Stability and Performance of Wide Bandgap Perovskite Solar Cells Through Ultraviolet Light-Absorbing Passivator

Ultraviolet light (UV) has caused tremendous damage to perovskite solar cells (PSCs), degrading the perovskite and shortening their lifetime. Defects act as non-radiative recombination sites, accelerate the degradation process, reduce the efficiency of the device and weaken the stability of solar cell. In this work, to realize efficient and stable p-i-n wide bandgap solar cells under UV, a synergetic strategy utilizing UV light-absorbing passivator, (Trifluoroacetyl) benzotriazole (TFABI), enhance UV photostability and regulate the defect passivation is proposed. By using TFABI, the degradation of the perovskite absorption layer under UV light is suppressed, spectral response is enhanced and the Pb vacancy defects are passivated. As a result, the target device achieves an efficiency of 21.54%, exhibiting excellent long-term stability under 365 nm UV irradiation. After 60 h of irradiation, it retains 85% of its initial value (60 mW cm-2 , RH 25-30%, 25 °C).

Improved Air Stability for High-Performance FACsPbI3 Perovskite Solar Cells via Bonding Engineering

Despite the fact that perovskite solar cells (PSCs) are widely popular due to their superb power conversion efficiency (PCE), their further applications are still restricted by low stability and high-density defects. Especially, the weak binding and ion-electron properties of perovskite crystals make them susceptible to moisture attack under environmental stress. Herein, we report an overall sulfidation strategy via introduction of 1-pentanethiol (PT) into the perovskite film to inhibit bulk defects and stabilize Pb ions. It has been confirmed that the thiol groups in PT can stabilize uncoordinated Pb ions and passivate iodine vacancy defects by forming strong Pb-S bonds, thus reducing nonradiative recombination. Moreover, the favorable passivation process also optimizes the energy-level arrangement, induces better perovskite crystallization, and enhances the charge extraction in the full solar cells. Consequently, the PT-modified inverted device delivers a champion PCE of 22.46%, which is superior to that of the control device (20.21%). More importantly, the PT-modified device retains 91.5% of its initial PCE after storage in air for 1600 h and over 85% of its initial PCE after heating at 85 °C for 800 h. This work provides a new perspective to simultaneously improve the performance and stability of PSCs to satisfy their commercial applications.