Facile fabrication of shape-controllable and reusable nanoporous catalytic aerogels based on Co-MOF and agarose for efficient decomposition of organic pollutants in water

Sulfate radical (SO4•-)-based advanced oxidation processes (SR-AOPs) have been studied to date by utilizing metal-organic frameworks as efficient catalysts to generate sulfate radicals by peroxymonosulfate (PMS) activation in water purification. It is important to select high-performance and reliable catalysts for efficient water remediation, and separation and recovery of catalysts are essential in the practical application of MOFs. Herein, we adapted thermally curable, shape-controllable, and cost-effective agarose (AG) as a smart matrix and ZIF-67, as a powerful catalyst to prepare nanoarchitectured aerogel (Z67@AG). This nanoporous aerogel composite can efficiently generate sulfate radicals and hydroxyl radicals by activating PMS in the nanopores. Z67@AG aerogel could be easily fabricated in various molds to make desired shapes. This approach enables its utilization for different filtering systems and demonstrates cost-effective and stable performance by mass production and reusability. In the SR-AOP, aerogel exhibited excellent catalytic decomposition performances of 95 % and 88 % efficiencies within 8 and 10 min for dye and levofloxacin, respectively. It is believed that the proposed highly catalytic nanoporous aerogel nanocomposite having cost-effectiveness, excellent catalytic activity, facile fabrication of desired shapes, and an excellent porous structure can be extended to the synthesis of various nanocomposites and emerging applications.

High specific surface area carbon aerogel derived from starch for methylene blue adsorption and supercapacitors

Starch based carbon aerogel has attracted significant attention due to the wide source, environmental friendliness and low price of raw materials. Here, starch based carbon aerogel was fabricated by graft reaction and cross-linking reaction of starch. The network structure of starch hydrogel was optimized through graft and cross-linking reaction. After freeze drying and high temperature carbonization, the obtained carbon aerogel that carbonized at 800 °C showed a specific surface area of 1508 m2·g-1 without activation which is far higher than that of other unactivated carbon aerogels. The starch based carbon aerogel carbonized at 800 °C exhibited superior methylene blue adsorption ability with a maximum adsorption capacity of 963.5 mg·g-1 as a result of its rich surface functional groups, high specific surface area, and reasonable pore size distribution. Furthermore, the carbon aerogel carbonized at 700 °C exhibited excellent electrochemical performance with a specific capacitance of 180.1 F·g-1 at a current density of 1 A·g-1as electrode materials for supercapacitors. Overall, this work provides a new method to prepare high performance starch based carbon aerogel.

Multiporous ZIF-8 carbon/cellulose composite beads: Highly efficient and scalable adsorbents for water treatment

Metal-organic framework (MOF) particles are one of the most promising adsorbents for removing organic contaminants from wastewater. However, powder-type MOF particles face challenges in terms of utilization and recovery. In this study, a novel bead-type adsorbent was prepared using activated carbon based on the zeolitic imidazolate framework-8 (AC-ZIF-8) and a regenerated cellulose hydrogel for dye removal. AC-ZIF-8 particles with a large surface area were obtained by carbonization and chemical activation with KOH. The AC-ZIF-8 powders were efficiently immobilized in hydrophilic cellulose hydrogel beads via cellulose dissolution/regeneration. The prepared AC-ZIF-8/cellulose hydrogel (AC-ZIF-8/CH) composite beads exhibit a large specific surface area of 1412.8 m2/g and an excellent maximum adsorption capacity of 565.13 mg/g for Rhodamine B (RhB). Moreover, the AC-ZIF-8/CH beads were effective over a wide range of pH, temperatures and for different types of dyes. These composite beads also offer economic benefits through desorption of dyes for recycling. The AC-ZIF-8/CH beads can be produced in substantial amounts and used as fillers in a fixed-bed column system, which can purify the continuous inflow of dye solutions. These findings suggest that our simple approach for preparing high-performance adsorbent beads will broaden the application of dye adsorbents, oil-water separation, and catalysts.

Surfactant-Free, Size-Controllable, and Scalable Green Synthesis of ZIF-8 Particles with Narrow Size Distribution by Tuning Key Reaction Parameters in Water Solvent

The chemical/physical properties and reliable performance of nanoporous materials are strongly influenced by the particle size and corresponding distribution. Among many types of MOFs, ZIF-8, is still widely used and many studies have been conducted to control the particle size and uniformity of ZIF-8 using surfactants and organic solvents. However, the use of surfactants and organic solvents process is expensive and may cause environmental pollution. For the first time, in this paper, a surfactant-free, size-controllable, and scalable green synthesis method of ZIF-8 particles is reported using four reaction parameters (temperature, concentration, pouring time, and reactant ratio) that affect the formation of nuclei and growth of ZIF-8 crystals. The as-synthesized ZIF-8 nanoparticles show great uniformity and controllable particle sizes in the wide range of 147-915 nm. In addition, a 2 L large-scale synthesis of ZIF-8 with narrow size distribution is developed by finely tuned particle size in water without any additives. To demonstrate the efficient utilization of nanopores according to the particle size and size distribution, an adsorption test is conducted on the ZIF-8 nanoparticles. This study will support the synthesis of size-controlled ZIF-8 with narrow size distribution and their composites for achieving high performance in the emerging applications.

Nitric Oxide Detection Using a Corona Phase Molecular Recognition Site on Chiral Single-Walled Carbon Nanotubes

Semiconducting single-walled carbon nanotubes (s-SWCNT) are structures that fluoresce in the near-infrared region. By coating SWCNT surfaces with polymeric materials such as single-chain DNA, changes in fluorescence emission occur in the presence of reagents. In this way, polymer-coated SWCNT structures allow them to be used as optical sensors for single molecule detection. Especially today, the inadequacy of the methods used in the detection of cellular molecules makes the early diagnosis of diseases such as cancer difficult at the single-molecule level. In this study, the detection of nitric oxide (NO) signals, which are a marker of cancer, was carried out at the single-molecule level. In this context, a sensor structure was formed by coating the 7,6-chiral s-SWCNT surface with ssDNA with different oligonucleotide lengths (AT). The sensor structure was characterized by using UV-vis spectroscopy and Raman spectroscopy microscopy. After formation of the sensor structure, a selectivity library was created using various molecules. As a result of the coating of the SWCNT (7,6) surface with DNA corona phase formation, Raman peaks at 195 and 276 cm-1 were observed to shift to the right. Additionally, the selectivity library results showed that the (AT)30 sequence can be used in NO detection. As a result of the studies using SWCNT (7.6)- (AT)30, the limit of detection (LOD) and limit of determination (LOQ) values of the sensor against NO were found to be 1.24 and 4.13 μM, respectively.

Multiscale Porous Carbon Materials by In Situ Growth of Metal-Organic Framework in the Micro-Channel of Delignified Wood for High-Performance Water Purification

Porous carbon materials are suitable as highly efficient adsorbents for the treatment of organic pollutants in wastewater. In this study, we developed multiscale porous and heteroatom (O, N)-doped activated carbon aerogels (CAs) based on mesoporous zeolitic imidazolate framework-8 (ZIF-8) nanocrystals and wood using 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO) oxidation, in situ synthesis, and carbonization/activation. The surface carboxyl groups in a TEMPO-oxidized wood (TW) can provide considerably large nucleation sites for ZIF-8. Consequently, ZIF-8, with excellent porosity, was successfully loaded into the TW via in situ growth to enhance the specific surface area and enable heteroatom doping. Thereafter, the ZIF-8-loaded TW was subjected to a direct carbonization/activation process, and the obtained activated CA, denoted as ZIF-8/TW-CA, exhibited a highly interconnected porous structure containing multiscale (micro, meso, and macro) pores. Additionally, the resultant ZIF-8/TW-CA exhibited a low density, high specific surface area, and excellent organic dye adsorption capacity of 56.0 mg cm-3, 785.8 m2 g-1, and 169.4 mg g-1, respectively. Given its sustainable, scalable, and low-cost wood platform, the proposed high-performance CA is expected to enable the substantial expansion of strategies for environmental protection, energy storage, and catalysis.

Nonacid Carbon Materials as Catalysts for Monoethanolamine Energy-Efficient Regeneration

In the CO₂ capture process, solid acid catalysts have been widely adopted to decrease energy consumption in the amine regeneration process owing to abundant acid sites. However, acid sites unavoidably degenerate in the basic amine solution. To address the challenge, nonacid carbon materials including carbon molecular sieves, porous carbon, carbon nanotubes, and graphene are first proposed to catalyze amine regeneration. It is found that carbon materials can significantly increase the CO₂ desorption amount by 47.1-72.3% and reduce energy consumption by 32-42%. In 20 stability experiments, CO₂ loading was stable with the max difference value of 0.01 mol CO₂/mol monoethanolamine (MEA), and no obvious increase in the relative heat duty (the maximum difference is 4%) occurred. The stability of carbon materials is superior to excellent solid acid catalysts, and the desorption performance is comparable. According to the results of theoretical calculation and experimental characterization, the electron-transfer mechanism of nonacid carbon materials is proposed, which is not only beneficial for MEA regeneration but also the probable reason for the stable catalytic activity. Owing to the excellent catalytic performance of carbon nanotube (CNT) in the HCO₃^- decomposition, nonacid carbon materials are quite promising to enhance the desorption performance of novel blend amines, which will further reduce the cost of carbon capture in the industry. This study provides a new strategy to develop stable catalysts used for amine energy-efficient regeneration.

Functionalized hierarchically porous carbon doped boron nitride for multipurpose and efficient treatment of radioactive sewage

In order to recycle Uranium (U) for the sustainable development of nuclear energy, diamide bipyridine (DABP) modified hierarchically porous carbon doped boron nitride (BCN-DABP) was synthesized as an adsorbent for the multipurpose removal of U. BCN-DABP displayed good adsorption performance for U in both weakly and highly acidic solutions. The hierarchically porous structure endowed BCN-DABP with ultrafast adsorption kinetics, and adsorption reached equilibrium within 180.0 and 0.5 min under pH = 4.0 and 2.00 mol L^-1 HNO₃, respectively. Moreover, combination of adsorption isotherm studies and DFT calculations showed that BCN-DABP possessed high adsorption capacities for U and displayed different adsorption performance under different conditions. BCN-DABP adsorbed UO₂²⁺ by chelation and electrostatic attraction under pH 4.0 and 2.00 mol L^-1 HNO₃, the maximum adsorption capacity under two conditions reached 818.7 and 1296.7 mg g^-1, respectively. As a result, BCN-DABP is expected to be used for the rapid and efficient removal of U in various kinds of contaminated water. Furthermore, excellent salinity tolerance, good adsorption selectivity, and outstanding radiation resistance also endowed BCN-DABP with great practical potential for removing U in radioactive contaminated water as well as high level liquid waste.

Recent Progress of Hollow Carbon Nanocages: General Design Fundamentals and Diversified Electrochemical Applications

Hollow carbon nanocages (HCNCs) consisting of sp2  carbon shells featured by a hollow interior cavity with defective microchannels (or customized mesopores) across the carbon shells, high specific surface area, and tunable electronic structure, are quilt different from the other nanocarbons such as carbon nanotubes and graphene. These structural and morphological characteristics make HCNCs a new platform for advanced electrochemical energy storage and conversion. This review focuses on the controllable preparation, structural regulation, and modification of HCNCs, as well as their electrochemical functions and applications as energy storage materials and electrocatalytic conversion materials. The metal single atoms-functionalized structures and electrochemical properties of HCNCs are summarized systematically and deeply. The research challenges and trends are also envisaged for deepening and extending the study and application of this hollow carbon material. The development of multifunctional carbon-based composite nanocages provides a new idea and method for improving the energy density, power density, and volume performance of electrochemical energy storage and conversion devices.

Mechanically Robust and Flexible GO/PI Hybrid Aerogels as Highly Efficient Oil Absorbents

Herein, mechanically robust and flexible graphene oxide/polyimide (GO/PI) hybrid aerogels (GIAs) were fabricated by a facile method, in which the mixed suspensions of the water-soluble polyimide precursor and graphene oxide (GO) sheets were freeze-dried, which was followed by a routine thermal imidation process. The porous GIAs obtained not only exhibit excellent elasticity and extremely low density values (from 33.3 to 38.9 mg.cm^-3), but they also possess a superior compressive strength (121.7 KPa). The GIAs could support a weight of up to 31,250 times of its own weight, and such a weight-carrying capacity is much higher than that of other typical carbon-based aerogels. Having such a porous structure, and high strength and toughness properties make GIAs ideal candidates for oil spill cleanup materials. The oil/organic solvents' absorption capacity ranges from 14.6 to 85, which is higher than that of most other aerogels (sponges). With their broad temperature tolerance and acidic stability, the unique multifunctional GIAs are expected to further extend their application range into extreme environments.

Monolithic carbon aerogels within foam framework for high-temperature thermal insulation and organics absorption

Carbon aerogels exhibit high porosity, good electrical conductivity, and low thermal conductivity, but their practical applications are greatly hindered by their tedious preparation and inherent structure brittleness. Herein, monolithic carbon aerogels (MCAs) with low density and large size are prepared via a facile sol-gel polymerization of phenolic resin within melamine foam (MF), followed by ambient pressure drying and co-carbonization. During ambient pressure drying process, the MF matrix can deliver supporting force to counteract against the solvent evaporation surface tension, thus inhibiting volume shrinkage and shape deformation. Upon co-carbonization process, the MF matrix and organic aerogel could pyrolyze and shrink cooperatively, which could effectively prevent the brittle fracture of monolith. Therefore, large-sized MCAs (up to 250 × 250 × 20 mm) with low densities of 0.12-0.22 g·cm^-3 are obtained. The as-obtained MCAs possess high compressive strength (2.50 MPa), ultra-low thermal conductivity (0.051 W·m^-1·K^-1 at 25 °C and 0.111 W·m^-1·K^-1 at 800 °C), and high-volume organic absorption capability (77.3-88.0%, V/V). This facile and low-cost method for the fabrication of large-sized monolithic carbon aerogels with excellent properties could envision enormous potential for high-temperature thermal insulation and organics absorption.

Fruit waste-derived cellulose and graphene-based aerogels: Plausible adsorption pathways for fast and efficient removal of organic dyes

A wide range of organic pollutants in industrial effluents, agricultural runoff, and domestic discharges are exacerbating water scarcity, leading to water-borne ailments, and adversely affecting the marine ecosystem and biodiversity. The efficient, sustainable, and cost-effective materials need to be addressed urgently for the removal of organic pollutants. Herein, ultra-light (0.018 g.cm^-3) and highly porous (96.4%) composite aerogel is prepared by gelatinization of graphene oxide with fruit waste-derived cellulose. The macroscopic porosity generated by interconnecting cellulosic skeleton and graphene oxide sheets via hydrogen bonding network provided ample avenues for transport and diffusion of organic dyes-enriched wastewater throughout the cellulose-graphene oxide composite aerogel (CGA). Consequently, organic dyes are efficiently adsorbed by easily accessible surface sites distributed throughout the CGA. The size, charge, and chemical structure of organic dyes along with textural features and accessible surface active sites of CGA governed the adsorption process. The spectroscopic analyses based on FTIR, Raman, and XPS measurements suggest electrostatic, n-π, π-π, cation-π interactions, dipole-dipole hydrogen, and Yoshida hydrogen linkages as major interactive pathways for the adsorption of organic dyes by the CGA. Moreover, the composite aerogel furnished an excellent recyclability for the adsorptive removal of organic pollutants from wastewater. The present work promises the potential of 2D nanostructured layered materials and fruit-waste-derived composite aerogels for sustainable utilization in wastewater treatment, which can be an excellent step towards water security.

Hierarchical porous metal–organic gels and derived materials: from fundamentals to potential applications

This review summarizes recent progress in the development and applications of metal–organic gels (MOGs) and their hybrids and derivatives dividing them into subclasses and discussing their synthesis, design and structure–property relationship.

Quantitative Coassembly for Precise Synthesis of Mesoporous Nanospheres with Pore Structure-Dependent Catalytic Performance

Precise synthesis of porous materials is essential for their applications. Self-assembly is a widely used strategy for synthesizing porous materials, but quantitative control of the assembly process still remains a great challenge. Here, a quantitative coassembly approach is developed for synthesizing resin/silica composite and its derived porous spheres. The assembly behaviors of the carbon and silica precursors are regulated without surfactants and the growth kinetics of the composite spheres are quantitatively controlled. This assembly approach enables the precise control of the size and pore structures of the derived carbon spheres. These carbon spheres provide a good platform to explore the structure-performance relationships of porous materials, and demonstrate their pore structure-dependent performance in catalytic water decontamination. This work provides a simple and robust approach for precise synthesis of porous spheres and brings insights into function-oriented design of porous materials.

Cellulose Nanofiber Composite with Bimetallic Zeolite Imidazole Framework for Electrochemical Supercapacitors

Cellulose nanofiber (CNF) and hybrid zeolite imidazole framework (HZ) are an emerging biomaterial and a porous carbonous material, respectively. The composite of these two materials could have versatile physiochemical characteristics. A cellulose nanofiber and cobalt-containing zeolite framework-based composite was prepared using an in-situ and eco-friendly chemical method followed by pyrolysis. The composite was comprised of cobalt nanoparticles decorated on highly graphitized N-doped nanoporous carbons (NPC) wrapped with carbon nanotubes (CNTs) produced from the direct carbonization of HZ. By varying the ratio of CNF in the composite, we determined the optimal concentration and characterized the derived samples using sophisticated techniques. Scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), and X-ray photoelectron spectroscopy (XPS) confirmed the functionalization of CNF in the metallic cobalt-covered N-doped NPC wrapped with CNTs. The CNF–HZNPC composite electrodes show superior electrochemical performance, which is suitable for supercapacitor applications; its specific capacitance is 146 F/g at 1 A/g. Furthermore, the composite electrodes retain a cycling stability of about 90% over 2000 charge–discharge cycles at 10 A/g. The superior electrochemical properties of the cellulose make it a promising candidate for developing electrodes for energy storage applications.

Electrochemical Applications of Ferrocene-Based Coordination Polymers

Ferrocene and its derivatives, especially ferrocene-based coordination polymers (Fc-CPs), offer the benefits of high thermal stability, two stable redox states, fast electron transfer, and excellent charge/discharge efficiency, thus holding great promise for electrochemical applications. Herein, we describe the synthesis and electrochemical applications of Fc-CPs and reveal how the incorporation of ferrocene units into coordination polymers containing other metals results in unprecedented properties. Moreover, we discuss the usage of Fc-CPs in supercapacitors, batteries, and sensors as well as further applications of these polymers, for example in electrocatalysts, water purification systems, adsorption/storage systems.

Ultralight covalent organic framework/graphene aerogels with hierarchical porosity

The fabrication of macroscopic objects from covalent organic frameworks (COFs) is challenging but of great significance to fully exploit their chemical functionality and porosity. Herein, COF/reduced graphene oxide (rGO) aerogels synthesized by a hydrothermal approach are presented. The COFs grow in situ along the surface of the 2D graphene sheets, which are stacked in a 3D fashion, forming an ultralight aerogel with a hierarchical porous structure after freeze-drying, which can be compressed and expanded several times without breaking. The COF/rGO aerogels show excellent absorption capacity (uptake of >200 g organic solvent/g aerogel), which can be used for removal of various organic liquids from water. Moreover, as active material of supercapacitor devices, the aerogel delivers a high capacitance of 269 F g⁻¹ at 0.5 A g⁻¹ and cycling stability over 5000 cycles.

Macroscopic architectures of covalent organic frameworks (COF) allow to fully exploit their chemical functionality and porosity but achieving three-dimensional hierarchical porous COF architectures remains challenging. Here, the authors present a COF/reduced graphene oxide aerogel which is synthesized by growing COF during a hydrothermal process along the surface of graphene sheets.

Practical MOF Nanoarchitectonics: New Strategies for Enhancing the Processability of MOFs for Practical Applications

Over the past decades, the development of porous materials has directly or indirectly affected industrial production methods. Metal-organic frameworks (MOFs) as an emerging class of porous materials exhibit some unique advantages, including controllable composition, a large surface area, high porosity, and so on. These attractive characteristics of MOFs have led to their potential applications in energy storage and conversion devices, drug delivery, adsorption and storage, sensors, and other areas. However, powdered MOFs have limited practical applications owing to poor processability, safety hazards from dust formation, and poor recyclability. In addition, the inherent micro/mesoporosities of MOFs also reduce the accessibility and diffusion kinetics for large molecules. To improve their processability for practical applications, MOFs are often deposited as MOF layers or films (i.e., MOF-coated composites) on supporting materials or are formed into 3D structured composites, such as aerogels and hydrogels. In this article, we review recent researches on these MOF composites, including their synthetic methods and potential applications in energy storage devices, heavy metal ion adsorption, and water purification. Finally, the future outlook and challenges associated with the large-scale fabrication of MOF-based composites for practical applications are discussed.

Co-Incorporated Mesoporous Carbon Material-Assisted Laser Desorption/Ionization Ion Source as an Online Interface of In Vivo Microdialysis Coupled with Mass Spectrometry

The combination of microdialysis and mass spectrometry (MS) provides the potential for rapidly monitoring diverse metabolites in vivo. Unfortunately, the high concentration of salt in biological microdialysates hindered the sensitive and online detection of these small molecular compounds. In this study, we synthesized Co-incorporated mesoporous carbon material (Co-NC) and developed a Co-NC-assisted laser desorption/ionization (LDI) ion source as an online interface of in vivo microdialysis coupled with MS for the direct analysis of diverse metabolites in microdialysates. The Co-NC could be used as a matrix for surface-assisted laser desorption/ionization mass spectrometry (SALDI MS) analysis of small molecular compounds, even under high concentration salt conditions. The Co-NC possessed the adsorption ability for small molecular compounds, and it was believed that the adsorption ability of Co-NC might separate the analytes from the salt in microdialysates at a microscopic level, which might facilitate the desorption and ionization of the analytes and finally improved the salt-tolerance ability as a matrix. Furthermore, the Co-NC-assisted LDI ion source as a novel interface of in vivo microdialysis coupled with MS has been applied to the online monitoring of liver metabolites from the CCl₄-induced liver injury rat model for the first time.