Tissue reactions induced by modified poly(vinyl alcohol) hydrogels in rabbit cornea

Heparin-grafted PVA hydrogels: a material for the optical part of artificial cornea

Heparin (Hep) was grafted to a poly(vinyl alcohol) (PVA) hydrogel surface by using the covalent grafting method. The structure of the modified hydrogel was determined from Fourier transform infrared attenuated total reflection and X-ray photoelectron spectroscopy. The thermal stability of the samples was investigated by thermogravimetry–differential thermal analysis. The effects of the concentration of (3-aminopropyl)triethoxysilane (kh550) and Hep on visible light transmittance, moisture content, equilibrium swelling, hydrophilicity and percentage of Hep sodium release of the composite hydrogel were studied. The visible light transmittance of the modified PVA hydrogel was above 94%. The time of swelling equilibrium was about 60 min and the equilibrium swelling ratio ranged from 3·0 to 3·5. The hydrophilicity was enhanced, and the static water contact angle decreased from 41 to 28°. The bioeffects of the PVA–kh550–Hep hydrogel were evaluated by studying cell adhesion and proliferation. During the adhesion assay in vitro, cell adhesion significantly decreased after the interfaces had been modified with Hep. The Cell Counting Kit-8 assay showed that the biocompatibility of the PVA–kh550–Hep hydrogel improved obviously compared to that of pure PVA. The experimental results demonstrated that the PVA–kh550–Hep hydrogel had good stability, bioactivity and biocompatibility, suggesting its potential applications in artificial corneas.

Property-based design: optimization and characterization of polyvinyl alcohol (PVA) hydrogel and PVA-matrix composite for artificial cornea

Each approach for artificial cornea design is toward the same goal: to develop a material that best mimics the important properties of natural cornea. Accordingly, the selection and optimization of corneal substitute should be based on their physicochemical properties. In this study, three types of polyvinyl alcohol (PVA) hydrogels with different polymerization degree (PVA1799, PVA2499 and PVA2699) were prepared by freeze-thawing techniques. After characterization in terms of transparency, water content, water contact angle, mechanical property, root-mean-square roughness and protein adsorption behavior, the optimized PVA2499 hydrogel with similar properties of natural cornea was selected as a matrix material for artificial cornea. Based on this, a biomimetic artificial cornea was fabricated with core-and-skirt structure: a transparent PVA hydrogel core, surrounding by a ringed PVA-matrix composite skirt that composed of graphite, Fe-doped nano hydroxyapatite (n-Fe-HA) and PVA hydrogel. Different ratio of graphite/n-Fe-HA can tune the skirt color from dark brown to light brown, which well simulates the iris color of Oriental eyes. Moreover, morphologic and mechanical examination showed that an integrated core-and-skirt artificial cornea was formed from an interpenetrating polymer network, no phase separation appeared on the interface between the core and the skirt.

Amniotic membrane immobilized poly(vinyl alcohol) hybrid polymer as an artificial cornea scaffold that supports a stratified and differentiated corneal epithelium

Poly(vinyl alcohol) (PVA) is a biocompatible, transparent hydrogel with physical strength that makes it promising as a material for an artificial cornea. In our previous study, type I collagen was immobilized onto PVA (PVA-COL) as a possible artificial cornea scaffold that can sustain a functional corneal epithelium. The cellular adhesiveness of PVA in vitro was improved by collagen immobilization; however, stable epithelialization was not achieved in vivo. To improve epithelialization in vivo, we created an amniotic membrane (AM)-immobilized polyvinyl alcohol hydrogel (PVA-AM) for use as an artificial cornea material. AM was attached to PVA-COL using a tissue adhesive consisting of collagen and citric acid derivative (CAD) as a crosslinker. Rabbit corneal epithelial cells were air-lift cultured with 3T3 feeder fibroblasts to form a stratified epithelial layer on PVA-AM. The rabbit corneal epithelial cells formed 3-5 layers of keratin-3-positive epithelium on PVA-AM. Occludin-positive cells were observed lining the superficial epithelium, the gap-junctional protein connexin43-positive cells was localized to the cell membrane of the basal epithelium, while both collagen IV were observed in the basement membrane. Epithelialization over implanted PVA-AM was complete within 2 weeks, with little inflammation or opacification of the hydrogel. Corneal epithelialization on PVA-AM in rabbit corneas improved over PVA-COL, suggesting the possibility of using PVA-AM as a biocompatible hybrid material for keratoprosthesis.

Calcium Alginate Provides a High Degree of Embolization in Aneurysm Models: A Specific Comparison to Coil Packing

OBJECTIVE

Although flexible, current coils do not fill intracranial aneurysms to a high degree, and questions remain regarding their thrombogenic capacity. We evaluated the usefulness of calcium alginate as an embolic material for endovascular embolization in aneurysm models.

METHODS

We assessed three endovascular methods of instilling calcium alginate into 10-mm sidewall and 7-mm bifurcation glass aneurysm models using a balloon catheter to seal the aneurysm orifice: 1) instillation of alginate and subsequent instillation of the reactive component calcium chloride (CaCl(2)) via a single-lumen catheter, 2) simultaneous instillation of alginate and CaCl(2) via a side-by-side double-lumen catheter, and 3) instillation of alginate mixed with CaCl(2) delivered from a concentric-tube microcatheter. A 13-mm sidewall silicon aneurysm model was used to measure and compare the volume of calcium alginate occupying the aneurysm models.

RESULTS

Instillation Method 1 did not achieve optimal filling of the aneurysm with calcium alginate. The percentage volumes of calcium alginate occupying the aneurysm were 69.2 +/- 7.7% and 84.6 +/- 5.4% for instillation Methods 2 and 3, respectively. In Method 3, calcium alginate began gelation upon leaving the catheter, entered the aneurysms in a strand form, and gelled to a mass that filled the aneurysm while conforming to its inner contour.

CONCLUSION

Calcium alginate fills aneurysm models to a significantly higher degree than published results of the space filled by coils. Instillation of calcium alginate, especially in strand form, may produce an embolization that better fills and conforms to the contour of aneurysms compared with coils.

Long-term implantation test and tumorigenicity of polyvinyl alcohol hydrogel plates

Two types of flat plates made from a polyvinyl alcohol (PVA) hydrogel with a water content of 80 and 20 (PVA-H80, PVA-H20), 20 x 10 x 1 mm in size, were subcutaneously implanted into each of 50 young, male Wistar rats. As a control, a sham operation was done on another set of 50 rats (Sham Op group). The shape and transparency of the PVA hydrogel were unchanged for up to 24 months. Tumors arose in 14 rats from the PVA-H80 group. In the PVA-H20 group, tumors appeared in 15 rats. The average tumor latency was 598 +/- 109 days in the PVA-H80 and 637 +/- 94 days in the PVA-H20. There was no difference in tumor incidence between the PVA-H20 and PVA-H80 groups (p < 0.05). In the Sham Op group, no malignant tumors appeared. Histopathologically, the tumors induced by hydrogel plates were malignant tumors resembling fibrosarcoma or malignant fibrous histiocytoma. This indicates that PVA hydrogel implants also induce solid state carcinogenesis at a similarly high rate to medical grade hydrophobic material reported in a previous study.