Impact of gamma irradiation on physico-chemical and electromagnetic interference shielding properties of Cu2O nanoparticles reinforced LDPE nanocomposite films

In the current work, cuprous oxide (Cu2O) nanoparticles coated with Tween 80 were successfully synthesized via the chemical reduction method. Nanocomposites composed of low-density polyethylene (LDPE) and different ratios of Cu2O nanoparticles were fabricated by the melt mixing process. 10% of ethyl vinyl acetate (EVA) as a compatibilizing agent was added to the molten LDPE matrix and the mixing process continued until homogenous nanocomposites were fabricated. To study the influence of ionizing radiation on the fabricated samples, the prepared species were exposed to 50 and 100 kGy of gamma rays. The synthesized Cu2O nanoparticles were investigated by transmission electron microscopy (TEM) and X-ray diffraction (XRD). XRD and TEM analysis illustrated the successful formation of spherical Cu2O nanoparticles with an average size of 16.8 nm. The as-prepared LDPE/Cu2O nanocomposites were characterized via different techniques such as mechanical, thermal, morphological, XRD, and FTIR. Electromagnetic interference shielding (EMI) of the different nanocomposite formulations was performed as a promising application for these materials in practical life. The electromagnetic shielding effectiveness (SE) of the produced samples was measured in the X-band of the radio frequency range from 8 to 12 GHz using the vector network analyzer (VNA) and a proper waveguide. All the samples were studied before and after gamma-ray irradiation under the same conditions of pressure and temperature. The shielding effectiveness increased significantly from 25 dB for unirradiated samples to 35 dB with samples irradiated with 100 kGy, which reflects 40% enhancement in the effectiveness of the shielding.

Recycled high-density polyethylene plastic reinforced with ilmenite as a sustainable radiation shielding material

In this work, recycled high-density polyethylene plastic (r-HDPE) reinforced with ilmenite mineral (Ilm) in different ratios (0, 15, 30, and 45 wt%) as a sustainable and flexible radiation shielding material was manufactured using the melt blending method. XRD patterns and FTIR spectra demonstrated that the polymer composite sheets were successfully developed. The morphology and elemental composition were addressed using SEM images and EDX spectra. Moreover, the mechanical characteristics of the prepared sheets were also studied. The gamma-ray attenuation characteristics for established r-HDPE + x% Ilm composite sheets were theoretically computed between 0.015 and 15 MeV using Phy-X/PSD software. Also, the mass attenuation coefficients have been compared to their values by the WinXCOM program. It is also shown that the shielding performance of the r-HDPE + 45% Ilm composite sheet is significantly greater than that of r-HDPE. As a result, the ilmenite-incorporated recycled high-density polyethylene sheets are suited for medical and industrial radiation shielding applications.

Short nylon tire cord and gamma irradiation impact on SBR/ultrasonic and mechanochemical devulcanized rubber blends

Devulcanization of discarded tire rubber (WR) has remained of prior attention to numerous researchers, aiming for unlimited commercial profits upon modification, especially to serve as a substituent for virgin rubber. In this concern, composites of styrene butadiene rubber (SBR) and devulcanized waste rubber, developed via two techniques: mechanochemical (DRm) and ultrasonic (DRus), and reinforced with short nylon tire cord (SNF), namely at a filling ratio of 3 and 5 phr were fabricated. All prepared specimens were exposed to various gamma radiation doses, namely 50, 100, and 150 kGy. The post-radiation characterization was investigated by FTIR and SEM techniques. Radiation-induced crosslinking density of the polymer composites was calculated and correlated with the different mechanical features. Furthermore, the TGA technique and activation energy measurement were implemented in studying the thermal behavior of the products. Incorporation of 5 phr SNF set out the thermal stability order: SBR/DRm/5 SNF > SBR/DRus/5 SNF > SBR/5 SNF. Ionizing irradiation of all composite–SNF formulations derived to a marked improvement in TS data as a result of creating further crosslinking within the polymeric matrix, reaching a maximum by the integral dose 150 kGy. The results were appreciably compared to a recently published study that applied reinforced tire fiber with polyester, as another cord utilized in the manufacture of tires. It is found that TS data observed by irradiation with 150 kGy of SBR/3 SNF, SBR/DRm/3 SNF, and SBR/DRus/3 SNF are respectively as follows: 3.7, 2.5, and 2.4 MPa, whereas the corresponding reported values for PTC reinforced counterpart blends were: 2, 1.7 and 1.8 MPa. Similarly, the TS respective values of SBR/5 SNF, SBR/DRm/5 SNF and SBR/DRus are 2.5, 1.9, and 2.2 MPa, whereas their counterparts reinforced with 5 phr PTC recorded 1.6, 1.8, and 1.2 MPa. SNF-reinforced SBR, SBR/DRm, and SBR/DRus were superior in their properties to PTC-reinforced counterpart specimens.