Compressive Fatigue Behavior of Gum and Filled SBR Vulcanizates

The influence of carbon black on physical mechanical properties, compressive fatigue life, and the temperature changes during compression fatigue process of styrene-butadiene rubber (SBR) vulcanizates were explored. A series of unfilled and filled SBR compounds were prepared, and the compressive fatigue behaviors of the vulcanizates were performed on a mechanical testing and simulation (MTS) machine. The top surfaces of the filled SBR were imaged using scanning electron microscopy (SEM) after 105 cycles of compressive fatigue. The filled SBR shows greater compressive fatigue resistance than the unfilled SBR. The incorporation of carbon black into SBR improves the creep resistance. The best compressive fatigue resistance for the filled SBR was achieved by the addition of 30 phr carbon black. With the increase of carbon black content, the energy dissipation and the heat build-up increase simultaneously. Furthermore, SEM images of the vulcanizates suggest that the crack propagation mechanism of the unfilled and the filled SBR was different. For the unfilled SBR, due to periodical compressive stress, the polymer chains can be destroyed, and the cracks can be easily initiated and propagated, showing serious damage on the top surfaces of the specimen. However, for the filled SBR, the carbon black agglomeration around the cracks can greatly delay the generation of the cracks, decrease the fatigue damage, and ultimately improve the fatigue resistance.

Effect of Thermal Aging on the Mechanical Properties of High Tenacity Polyester Yarn

Textile materials produced from a high tenacity industrial polyester fiber are most widely used in the mechanical rubber goods industry to reinforce conveyor belts, tire cords, and hoses. Reinforcement of textile rubber undergoes a vulcanization process to adhere the textile materials with the rubber and to enhance the physio-mechanical properties of the product. The vulcanization process has an influence on the textile material being used as a reinforcement. In this work, the effects of aging temperature and time on the high tenacity polyester yarn's mechanical and surface structural properties were investigated. An experiment was carried out on a pre-activated high tenacity polyester yarn of different linear densities, by aging the yarn specimens under various aging temperatures of 140, 160, 200, and 220 °C for six, twelve, and thirty-five minutes of aging time. The tensile properties and surface structural change in the yarns pre- and post-aging were studied. The investigation illustrates that aging time and temperature influence the surface structure of the fiber, tenacity, and elongation properties of the yarn. Compared to unaged yarn, an almost five times higher percentage of elongation was obtained for the samples aged at 220 °C for 6 min, while the lowest tenacity was obtained for the sample subjected to aging under 220 °C for 35 min.