One-Dimensional Co-Carbonate Hydroxide@Ni-MOFs Composite with Super Uniform Core-Shell Heterostructure for Ultrahigh Rate Performance Supercapacitor Electrode

Effect of synthesis temperature on the structural morphology of a metal-organic framework and the capacitor performance of derived cobalt-nickel layered double hydroxides

Three-dimensional interconnected nickel-cobalt layered double hydroxides (NiCo-LDHs) were prepared on nickel foam by ion exchange using a cobalt-based metal-organic framework (Co-MOF) as a template at different temperatures. The effects of the Co-MOF preparation temperature on the growth, mass, morphology, and electrochemical properties of the Co-MOF and derived NiCo-LDH samples were studied. The synthesis temperature from 30 to 50 °C gradually increased the mass of the active material and the thickness of the Co-MOF sheets grown on the nickel foam. The higher the temperature is, the larger the proportion of Co3+. β-Cobalt hydroxide (β-Co(OH)2) sheets were generated above 60 °C. The morphology and mass loading pattern of the derived flocculent layer clusters of NiCo-LDH were inherited from metal-organic frameworks (MOFs). The areal capacitance of NiCo-LDH shows an inverted U-shaped curve trend with increasing temperature. The electrode material synthesized at 50 °C had a tremendous specific capacitance of 7631 mF·cm-2 at a current density of 2 mA·cm-2. The asymmetric supercapacitor assembled with the sample and active carbon (AC) achieved an energy density of 55.0 Wh·kg-1 at a power density of 800.0 W·kg-1, demonstrating the great potential of the NiCo-LDH material for energy storage. This work presents a new strategy for designing and fabricating advanced green supercapacitor materials with large power and energy densities.

Efficient improvement in the electrochemical performance of petal-like lamellar NiMn-LDHs with affluent oxygen vacancies derived from Mn MOF-74

Supercapacitors (SCs) as a kind of novel energy storage devices have emerged to meet the urgent requirement of environmentally friendly clean energy storage equipment. However, unsatisfactory energy density and low operating voltage tremendously restrict their practical application. Herein, petal-like lamellar NiMn-layered double hydroxide (NiMn-LDH) was successfully fabricated through a simple Ni(NO3)2 etching method with Mn MOF-74 as a sacrificial template. This NiMn-LDH 3/NF electrode exhibited an improved specific capacitance of 1410.2 F g-1 at a current density of 1 A g-1 (Mn MOF-74/NF: 172.2) owing to its high redox activity, compositional flexibility and intercalating capability. Importantly, NiMn-LDH was further optimized via a facile hydroperoxide treatment to harvest NiMn-LDH (O-LDH) with abundant oxygen vacancies, exhibiting remarkable improvement in specific capacitance (990%) compared to original MOF-74 before modification. The preparation of O-LDH enriches the electrode material engineering strategy and achieves improved electrochemical performance for application in new-generation SCs.

In situ synthesis of layered nickel organophosphonates for efficient aqueous nickel-zinc battery cathodes

Aqueous nickel-zinc (Ni-Zn) batteries have received increasing research interests because of their reliable safety and economical-friendliness. However, the retarded ionic diffusion, low capacity and limited stability of traditional Ni-based cathodes greatly impedes the practical application of Ni-Zn batteries. Herein, two metal organophosphonate materials of Ni methylphosphonate (Ni-MPA) and Ni phenylphosphonate (Ni-PPA) directly grown on Ni foam are constructed successfully through one step solvothermal technique. These two self-supported Ni organophosphonates featured hybrid two-dimensional (2D) structures consisting of alternating inorganic and organic layers, where the inorganic layers are formed by six-coordinated Ni2+ bridged by oxygen atoms and capped by organophosphonate groups, availing to provide rich open redox reaction sites, rapid ion diffusion and structural flexibility. The research results reveal that the organic groups in phosphonic acid ligands have important influence on their electrochemical properties. Consequently, the Ni-MPA electrode exhibits a higher specific capacity of 2.27 mAh/cm2 compared to that of the Ni-PPA electrode (1.1 mAh/cm2) at 3.0 mA/cm2; however, it demonstrates a more rapid transformation rate into Ni(OH)2 in an alkaline solution. Furthermore, the constructed Ni-MPA//Zn battery can deliver an impressive areal energy density of 2.95 mWh/cm2, good rate performance as well as a long-term cycling stability.

Emerging Pristine MOF-Based Heterostructured Nanoarchitectures: Advances in Structure Evolution, Controlled Synthesis, and Future Perspectives

Metal-organic frameworks (MOFs) can be customized through modular assembly to achieve a wide range of potential applications, based on their desired functionality. However, most of the initially reported MOFs are limited to microporous systems and are not sufficiently stable, which restricts their popularization. Heterogeneity is introduced into a simple MOF framework to create MOF-based heterostructures with fascinating properties and interesting functions. Heterogeneity can be introduced into the MOFs via postsynthetic/ligand exchange. Although the ligand exchange has shown potential, it is difficult to precisely control the degree of exchange or position. Among the various synthesis strategies, hierarchical assembly is particularly attractive for constructing MOF-based heterostructures, as it can achieve precise regulation of MOF-based heterostructured nanostructures. The hierarchical assembly significantly expands the compositional diversity of MOF-based heterostructures, which has high elasticity for lattice matching during the epitaxial growth of MOFs. This review focuses on the synthetic evolution mechanism of hierarchical assemblies of MOF-based nanoarchitectures. Subsequently, the precise control of pore structure, pore size, and morphology of MOF-based nanoarchitectures by hierarchical assembly is emphasized. Finally, possible solutions to address the challenges associated with heterogeneous interfaces are presented, and potential opportunities for innovative applications are proposed.

Controlled Synthesis of Flower-like Hierarchical NiCo-Layered Double Hydroxide Integrated with Metal-Organic Framework-Derived Co@C for Supercapacitors

Layered double hydroxides (LDHs) have come to the foreground recently, considering their unique layered structure and short ion channels when they act as electrode materials for supercapacitors (SCs). However, due to their poor rate and cycle performance, they are not highly sought after in the market. Therefore, a flower-like hierarchical NiCo-LDH@C nanostructure with flake NiCo-LDH anchored on the carbon skeleton has emerged here, which is constructed by calcination and hydrothermal reaction and applying flake ZIF-67 as a precursor. In this structure, NiCo-LDH grows outward with abundant and homogeneously distributed Co nanoparticles on Co@C as nucleation sites, forming a hierarchical structure that is combined tightly with the carbon skeleton. The flower-like hierarchical nanostructures formed by the composite of metal-organic frameworks (MOFs) and LDHs have successfully enhanced the cycle and rate performance of LDH materials on the strength of strong structural stability, large specific surface area, and unique cooperative effect. The NiCo-LDH@C electrode displays superb electrochemical performance, with a specific capacitance of 2210.6 F g^-1 at 1 A g^-1 and 88.8% capacitance retention at 10 A g^-1. Furthermore, the asymmetric supercapacitor (ASC) constructed with NiCo-LDH@C//RGO reveals a remarkable energy density of 45.02 W h kg^-1 with a power density of 799.96 W kg^-1. This project aims to propose a novel avenue to exploit NiCo-LDH electrode materials and provide theory and methodological guidance for deriving complex structures from MOF derivatives.

Recent advancements in zero- to three-dimensional carbon networks with a two-dimensional electrode material for high-performance supercapacitors

Supercapacitors have gained significant attention owing to their exceptional performance in terms of energy density and power density, making them suitable for various applications, such as mobile devices, electric vehicles, and renewable energy storage systems. This review focuses on recent advancements in the utilization of 0-dimensional to 3-dimensional carbon network materials as electrode materials for high-performance supercapacitor devices. This study aims to provide a comprehensive evaluation of the potential of carbon-based materials in enhancing the electrochemical performance of supercapacitors. The combination of these materials with other cutting-edge materials, such as Transition Metal Dichalcogenides (TMDs), MXenes, Layered Double Hydroxides (LDHs), graphitic carbon nitride (g-C₃N₄), Metal-Organic Frameworks (MOFs), Black Phosphorus (BP), and perovskite nanoarchitectures, has been extensively studied to achieve a wide operating potential window. The combination of these materials synchronizes their different charge-storage mechanisms to attain practical and realistic applications. The findings of this review indicate that hybrid composite electrodes with 3D structures exhibit the best potential in terms of overall electrochemical performance. However, this field faces several challenges and promising research directions. This study aimed to highlight these challenges and provide insights into the potential of carbon-based materials in supercapacitor applications.

From 1D to 2D: Controllable Preparation of 2D Ni-MOFs for Supercapacitors

Controllable modulation strategies between one-dimensional (1D) and two-dimensional (2D) structures have been rarely reported for metal-organic frameworks (MOFs). Here, 1D, 1D/2D, and 2D Ni-MOFs can be facilely prepared by adjusting the ratio of Ni²⁺ and the pyromellitic acid linker. A low-dimensional structure can shorten the transmission distance, while MOFs with a high Ni²⁺ content can supply rich active sites for oxidation-reduction reactions. The 2D structure Ni-MOF with an optimized Ni²⁺/pyromellitic acid ratio presents a good performance of 1036 F g^-1 at a current density of 1 A g^-1 with a comparable rate performance of 62% at 20 A g^-1. The study may offer a facile design to control the structure of MOFs for employing in electrochemical energy storage.

Designed formation of C/Fe3O4@Ni(OH)2 cathode with enhanced pseudocapacitance for asymmetric supercapacitors

The rational design and synthesis of advanced electrode materials are significant for the applications of supercapacitors. Ferroferric oxide (Fe₃O₄), with its high theoretical capacitance is a renowned cathode material. Nevertheless, its low electronic conductivity and poor cycling stability during a long-term charge/discharge process limit its large-scale applications. In this work, the precise modulation of multiple components was reported to enhance electrochemical performance. The ternary heterostructures were fabricated by wrapping ultrathin nickel hydroxide (Ni(OH)₂) nanosheets on the surfaces of Fe₃O₄ nanoparticles-loaded on sodium carboxymethyl cellulose (CMC)-derived porous carbon, named as C/Fe₃O₄@Ni(OH)₂. Due to the large specific surface area and excellent conductivity of CMC-derived porous carbon and the abundant reaction sites of Ni(OH)₂ nanosheets, the optimized C/Fe₃O₄@Ni(OH)₂-1.0 sample exhibited the highest specific capacitance of 3072F g^-1 at a current density of 0.5 A g^-1. Furthermore, the assembled asymmetric supercapacitor (ASC) with activated carbon and C/Fe₃O₄@Ni(OH)₂-1.0 as the negative and positive electrodes, respectively, showed an energy density of 123 W h kg^-1 at 381 W kg^-1, and a long-life stability with an excellent capacitance retention of 90.04 % after 10,000 cycles. The route for preparing composite electrode materials proposed in this work provides a reference for realizing high-performance energy storage devices.

Advances of Electroactive Metal-Organic Frameworks

The preparation of electroactive metal-organic frameworks (MOFs) for applications of supercapacitors and batteries has received much attention and remarkable progress during the past few years. MOF-based materials including pristine MOFs, hybrid MOFs or MOF composites, and MOF derivatives are well designed by a combination of organic linkers (e.g., carboxylic acids, conjugated aromatic phenols/thiols, conjugated aromatic amines, and N-heterocyclic donors) and metal salts to construct predictable structures with appropriate properties. This review will focus on construction strategies of pristine MOFs and hybrid MOFs as anodes, cathodes, separators, and electrolytes in supercapacitors and batteries. Descriptions and discussions follow categories of electrochemical double-layer capacitors (EDLCs), pseudocapacitors (PSCs), and hybrid supercapacitors (HSCs) for supercapacitors. In contrast, Li-ion batteries (LIBs), Lithium-sulfur batteries (LSBs), Lithium-oxygen batteries (LOBs), Sodium-ion batteries (SIBs), Sodium-sulfur batteries (SSBs), Zinc-ion batteries (ZIBs), Zinc-air batteries (ZABs), Aluminum-sulfur batteries (ASBs), and others (e.g., LiSe, NiZn, H⁺ , alkaline, organic, and redox flow batteries) are categorized for batteries.