Innovative root-end filling materials based on calcium-silicates and calcium-phosphates

Evaluation of the Shear Bond Strength of Immediate and Delayed Restorations of Various Calcium Silicate-Based Materials with Fiber-Reinforced Composite Resin Materials

Due to significant tissue loss in teeth requiring pulp treatments, hermetic restoration of the remaining dental tissues is one of the most crucial factors in determining the treatment's success. The adhesion of composite resins to calcium silicate cements (CSCs) is considered challenging. Consequently, it is crucial to identify the optimal method for obtaining optimal adhesion. The aim of the present study is to evaluate the shear bond strength (SBS) values of immediate and delayed restorations with fiber-reinforced composites on powder-liquid, premixed, and resin-containing flowable CSCs. In the present study, the SBS values obtained after immediate (14 min) and delayed (7 days) restorations of three different CSCs (NeoMTA2, NeoPutty, and TheraCal PT) with three different resin composite materials (EverX FlowTM, EverX PosteriorTM, and Filtek Z550) were compared. The fracture types were evaluated using a stereomicroscope and SEM. TheraCal PT had the highest SBS values for both immediate and delayed restorations, and the comparison with other materials showed a statistically significant difference (p = 0.001). In contrast, there was no statistically significant difference between the SBS values of NeoMTA and NeoPutty (p > 0.05). In both immediate and delayed restorations, there was no statistically significant difference between nanohybrid and fiber-reinforced composites (p > 0.05). The simple use and strong bonding ability of TheraCal PT with composite resins may provide support for the idea that it is suitable for pulpal interventions. Nevertheless, due to the in vitro nature of this study, additional in vitro and clinical studies are required to investigate the material's physical, mechanical, and biological properties for use in clinical applications.

Comparative Biocompatibility and Odonto-/Osteogenesis Effects of Hydraulic Calcium Silicate-Based Cements in Simulated Direct and Indirect Approaches for Regenerative Endodontic Treatments: A Systematic Review

BACKGROUND

Regenerative dentistry is the operation of restoring dental, oral and maxillofacial tissues. Currently, there are no guidelines for the ideal cement/material in regenerative endodontic treatments (RET). Hydraulic calcium silicate-based cements (hCSCs) are currently the material of choice for RET.

OBJECTIVES

This systematic review was conducted to gather all of the different direct and indirect approaches of using hCSCs in RET in vitro and in vivo, and to ascertain if there are any superiorities to indirect approaches.

METHODS AND MATERIALS

This systematic review was conducted according to the 2020 PRISMA guidelines. The study question according to the PICO format was as follows: Comparison of the biological behavior (O) of stem cells (P) exposed to hCSCs through direct and indirect methods (I) with untreated stem cells (C). An electronic search was executed in Scopus, Google Scholar, and PubMed.

RESULTS

A total of 78 studies were included. Studies were published between 2010 and 2022. Twenty-eight commercially available and eighteen modified hCSCs were used. Seven exposure methods (four direct and three indirect contacts) were assessed. ProRoot MTA and Biodentine were the most used hCSCs and had the most desirable results. hCSCs were either freshly mixed or set before application. Most studies allowed hCSCs to set in incubation for 24 h before application, which resulted in the most desirable biological outcomes. Freshly mixed hCSCs had the worst outcomes. Indirect methods had significantly better viability/proliferation and odonto-/osteogenesis outcomes.

CONCLUSION

Biodentine and ProRoot MTA used in indirect exposure methods result in desirable biological outcomes.

The effect of acidity on the physicochemical properties of two hydraulic calcium silicate-based cements and two calcium phosphate silicate-based cements

BACKGROUND

Bioceramic cements have been widely used in endodontic treatment. This study aimed to compare the microhardness, elastic modulus, internal microstructure and chemical compositions of Biodentine, WMTA, ERRM Putty, iRoot FS and IRM after exposure to PBS, butyric acid, and butyric acid followed by PBS.

METHODS

Specimens of each material were prepared and randomly divided into 5 subgroups (n = 5): subgroup A: PBS (pH = 7.4) for 4 days, subgroup B: PBS (pH = 7.4) for 14 days, subgroup C: butyric acid (pH = 5.4) for 4 days, subgroup D: butyric acid (pH = 5.4) for 14 days, subgroup E: butyric acid for 4 days followed by 10 days in contact with PBS. The surface microhardness, elastic modulus, internal morphologic and chemical compositions of specimens were analyzed.

RESULTS

The microhardness and elastic modulus values of all materials were significantly higher in the presence of PBS compared to exposure to butyric acid, with the same setting time (P < 0.01). After 4-day exposure to butyric acid followed by 10-day exposure to PBS, the microhardness values returned to the same level as 4-day exposure to PBS (P > 0.05). Biodentine showed significantly higher microhardness and elastic modulus values than other materials, while IRM displayed the lowest (P < 0.01).

CONCLUSION

Biodentine seems the most suitable bioceramic cements when applied to an infected area with acidic pH. Further storage at neutral pH, e.g. PBS reverses the adverse effects on bioceramic cements caused by a low pH environment.

Evaluation of interfacial adaptation and penetration of bioceramic-based sealers in oval root canals: A confocal laser scanning microscope study

To assess the interfacial adaptation and penetration depth of three different bioceramic-based sealers (CeraSeal, EndoSeal MTA, Nishika Canal Sealer BG) compared to an epoxy resin-based sealer (AH Plus) in oval root canals. Fourty extracted single-rooted mandibular premolar with oval canal were prepared and randomly allocated according to the obturation into; CeraSeal, EndoSeal MTA, Nishika Canal Sealer BG and AH Plus. The roots were sectioned at 3, 6 and 9 mm from the apex. The sealer adaptation and the penetration depth were evaluated under confocal laser scanning microscope. One-way ANOVA and Repeated measure ANOVA were used to statistically analyze the data. Nishika Canal Sealer BG showed significantly higher sealer adaptation than EndoSeal MTA (P < .001) at apical and middle thirds. Meanwhile, AH Plus showed significantly higher sealer adaptation than EndoSeal MTA (P = 0.011) at middle third. For sealer penetration, Nishika Canal Sealer BG showed the longest sealer penetration that was significant compared to AH Plus (P < .001) and EndoSeal MTA (P < .001) whereas CeraSeal was significantly higher than EndoSeal MTA (P = 0.029) at coronal third. For AH Plus, there was a significant less sealer penetration at coronal third compared to apical and middle thirds (P < .05). Whereas for EndoSeal MTA, the coronal third has significant less penetration compared to the middle third (P = 0.032). Endoseal has the lowest adaptation and penetration depth. Nishika Canal Sealer BG has better adaptation and penetration depth using single cone obturation technique in oval canal. RESEARCH HIGHLIGHTS: All the tested root canal sealers have some percentage of gaps and vary in their penetration capability into dentinal tubules. Nishika Canal Sealer BG has significantly better sealer adaptation to root dentinal walls than that of EndoSeal MTA at the apical and middle third but not significantly different from other type of sealers used. Nishika Canal Sealer BG has significantly better penetration depth than AH Plus and EndoSeal MTA at the coronal third of radicular dentin.

Calcium Silicate-Based Sealer Dentinal Tubule Penetration-A Systematic Review of In Vitro Studies

The aim of this systematic review was to perform a qualitative synthesis of in vitro studies which evaluate and compare the penetration of calcium silicate-based sealers into dentinal tubules. A systematic advanced search was performed in Scopus, Embase, Medline (via PubMed), Web of Science, and Cochrane databases on the 1 December 2022. In vitro studies that compared the tubular penetration of at least two calcium silicate-based sealers in extracted human teeth were eligible. PRILE 2021 guidelines were used for the assessment of the risk of bias included studies. The search identified a total of 680 preliminary records, among which 12 studies were eligible for review. The most used methodology to evaluate sealer penetration was the use of a fluorochrome together with the tested sealers and the analysis of their penetration under confocal laser microscopy. Regarding the results of the included studies, calcium silicate-based sealers exhibit a favorable dentinal tubule penetration. Tubular penetration, however, can be affected by factors such as the irrigation protocol, sealer activation, the filling method used, and root canal morphology. EndoSequence BC Sealer showed the highest sealer penetration among the tested sealers. The influence of different fluorochromes on the results of dentinal tubule penetration studies should also be further explored. The in vitro nature of the included studies limits the applicability of the results into the clinical setting. Prospero registration: CRD42022383896.

A Micro-CT Analysis of Initial and Long-Term Pores Volume and Porosity of Bioactive Endodontic Sealers

The evaluation of the porosities within the interface of root canals obturated with endodontics materials is extremely important for the long-term success of endodontic treatments. The aim of this study was to compare initial and long-term volume of pores (total, open, closed) and porosity (total, regional) of three bioactive endodontic sealers: GuttaFlow Bioseal, Total Fill BC Sealer, and BioRoot RCS. Root canals were obturated with three “bioactive” sealers using the single-cone technique. The volume of open and closed pores and porosity were calculated using a micro-computed tomography (MCT) method. The measurements were performed after 7 days (initial) and after 6 months (long-term) of incubation. Statistical significance was considered at p < 0.05. The total volume of pores remained unchanged after the 6-month storage. GuttaFlow Bioseal exhibited significantly higher long-term volume in open pores than Total Fill BC Sealer. The total porosity in all the tested sealers presented no statistically significant change after the 6-month storage, except for BioRoot RCS. The total porosity values of this latter material significantly increased after long-term incubation, especially in the apical region. In conclusion, the use of bioactive sealers with excessive tendency to create porosities both in shorth- and long-term periods of storage may compromise the long-term success of endodontic treatments.

Complicated Crown Fracture of Permanent Incisors: A Conservative Treatment Case Report and a Narrative Review

Dental trauma may have a severe impact on the social and psychological wellbeing of a patient. Most cases of dental injuries involve anterior teeth, especially the maxillary upper incisors. Crown fractures, with or without pulp exposure, are the most common trauma in permanent dentition. There are many methods of management, in which the initial state of the pulp, the time since the injury, and the presence of an accompanying injury play a key role. This case report aimed at showing a possible conservative treatment after complicated tooth fracture that consisted of partial pulpotomy followed by adhesive reattachment of the tooth fragment using a technique based on heated resin composite. Such a specific procedure represents a conservative approach to traumatic coronal lesions, providing a suitable opportunity to maintain the tooth vitality, aesthetics, and function. Indeed, reattachment of tooth fragment using a composite/adhesive is a simple technique to achieve excellent results in terms of aesthetic and function.

Can the Concentration of Citric Acid Affect Its Cytotoxicity and Antimicrobial Activity?

Background: There has been no unanimity concerning the ideal concentration of citric acid for safe use in clinical practice. This study evaluated the cytotoxicity and the antibacterial activity in infected dentinal tubules of 10% and 1% citric acid (CA) solutions. Methods: The cytotoxicity of CA solutions in DMEM (diluted 1/10, 1/100) was assessed in L-929 fibroblasts. A broth macrodilution method (MIC and MBC) was used to assess CA antibacterial concentration. The antimicrobial activity of CA solutions was also evaluated after their final rinse inside root canals in previously Enterococcus faecalis-contaminated dentinal tubules. Ten infected dentine samples were rinsed for 5 min with 5% NaOCl and subsequently with 1% citric acid for 3 min. Another 10 were rinsed with 5% NaOCl and 10% citric acid for 3 min; the remaining four specimens were utilized as positive controls. Two uncontaminated specimens were used as negative controls. After LIVE/DEAD BacLight staining, the samples were assessed using CLSM to analyze the percentage of residual live and dead cells. Results: Both undiluted and diluted CA solutions showed severe toxicity; no changes from normal morphology were displayed when diluted 1/100. The MIC and MBC of CA were 6.25 mg/mL and 12.50 mg/mL, respectively. CA solutions demonstrated significantly low levels of bacterial counts than the positive control group, reporting a value of 9.3% for the 10% solution versus the 1% solution (35.2%). Conclusions: Despite its valuable antimicrobial properties, the cytotoxic effects of citric acid should be considered during endodontic treatment.

Dislodgement pushout resistance of five bioceramic root-end filling materials

This study evaluated the dislodgement push-out resistance of five bioceramic materials. One hundred single-rooted teeth with one canal had the apical 3 mm and crown resected to create a 14 mm standardized length. The canals were instrumented to an apical size 80 with a 3 mm root-end preparation made with ultrasonic diamonds. The prepared roots were randomly divided into 5 root-end restorative groups (n=20). ProRoot MTA, Biodentine, EndoSequence Root Repair Material, EndoSequence Fast Set Putty, and EndoSequence BC Sealer with each material placed following manufacturer's instructions and stored at 100% humidity for 2 weeks. An apical-to-coronal static testing load with the identified dislodgement force converted into MPa with mean results analyzed with Kruskal-Wallis and Dunn's post hoc tests (α=0.05). ProRoot MTA and Biodentine displayed similar push-out stress resistance and exhibited significantly greater stress resistance than the similar Endosequence materials. However, all materials failed cohesively and were not dislodged from the root canal surface.

Pilot Evaluation of Sealer-Based Root Canal Obturation Using Epoxy-Resin-Based and Calcium-Silicate-Based Sealers: A Randomized Clinical Trial

The purpose of this randomized controlled clinical trial was to assess the short-term clinical effectiveness of sealer-based root canal obturation using calcium-silicate-based sealer (CSBS) and epoxy-resin-based sealer (ERBS). A total of eighty patients (eighty teeth) were enrolled and seventy-two patients (seventy-two teeth) were randomly assigned into four different sealer groups: AH Plus (AH, Dentsply Sirona), ADseal (AD, Meta Biomed), CeraSeal (CS, Meta Biomed), or EndoSeal TCS (ES, Maruchi). At the first visit, root canal treatment was performed using ProTaper. Next, the NiTi file system and passive ultrasonic irritation was applied with 2.5% NaOCl. At the second visit, the teeth were obturated with a sealer-based obturation technique using the assigned sealer. The quality of filling obturation was evaluated with postoperative radiographs in terms of the presence of voids and sealer extrusion. The patients were recalled at 1-week, 1-month, and 3-month intervals, and pain levels were measured using visual analog scales (VAS), and clinical examination performed with percussion and palpation. Radiographs were also taken. The results were statistically compared by using the χ2 test or Fisher exact test. Among the 80 teeth included, 72 teeth received allocated intervention and 71 teeth were included in the analysis (98.6% recall). There was no significant difference among the sealers in void and sealer extrusion (p > 0.05). Postoperative pain was not indicated prominently regardless of the type of sealer. For a 3-month follow-up period, all cases were maintained successfully except for one case from AD. According to the findings, there was no significant difference between CSBS and ERBS in terms of postoperative pain or the healing process, and the variation in filling quality appears to be linked to the properties of each product.

Herbal Medications in Endodontics and Its Application-A Review of Literature

Herbal products are gaining popularity in dental and medical practice nowadays due to their biocompatibility, higher antimicrobial activity, antioxidant and anti-inflammatory properties. Herbal medicine has experienced rapid growth in recent years due to its beneficial properties, ease of availability, and lack of side effects. As pathogenic bacteria become more resistant to antibiotics and chemotherapeutic agents, researchers are becoming more interested in alternative products and treatment choices for oral diseases. As a result, natural phytochemicals separated from plants and utilized in traditional medicine are suitable substitutes for synthetic chemicals. The aim of this review article is to list and understand several herbal alternatives that are currently accessible for use as efficient endodontic medicaments. The herbal products used in endodontics have several advantages, including safety, ease of use, increased storability, low cost, and a lack of microbial tolerance. However, preclinical and clinical testing and interactions with other materials and adverse effects are required for these herbal products.

Novel Bioactive Adhesive Monomer CMET Promotes Odontogenic Differentiation and Dentin Regeneration

This study aimed to evaluate the in vitro effect of the novel bioactive adhesive monomer CMET, a calcium salt of 4-methacryloxyethyl trimellitate acid (4-MET), on human dental pulp stem cells (hDPSCs) and its capacity to induce tertiary dentin formation in a rat pulp injury model. Aqueous solutions of four tested materials [4-MET, CMET, Ca(OH)₂, and mineral trioxide aggregate (MTA)] were added to the culture medium upon confluence, and solvent (dH₂O) was used as a control. Cell proliferation was assessed using the Cell Counting Kit-8 assay, and cell differentiation was evaluated by real-time quantitative reverse transcription-polymerase chain reaction. The mineralization-inducing capacity was evaluated using alizarin red S staining and an alkaline phosphatase activity assay. For an in vivo experiment, a mechanical pulp exposure model was prepared on Wistar rats; damaged pulp was capped with Ca(OH)₂ or CMET. Cavities were sealed with composite resin, and specimens were assessed after 14 and 28 days. The in vitro results showed that CMET exhibited the lowest cytotoxicity and highest odontogenic differentiation capacity among all tested materials. The favorable outcome on cell mineralization after treatment with CMET involved p38 and c-Jun N-terminal kinases signaling. The nuclear factor kappa B pathway was involved in the CMET-induced mRNA expression of odontogenic markers. Similar to Ca(OH)₂, CMET produced a continuous hard tissue bridge at the pulp exposure site, but treatment with only CMET produced a regular dentinal tubule pattern. The findings suggest that (1) the evaluated novel bioactive adhesive monomer provides favorable biocompatibility and odontogenic induction capacity and that (2) CMET might be a very promising adjunctive for pulp-capping materials.

Sealing ability and microbial leakage of root-end filling materials: MTA versus epoxy resin: A systematic review and meta-analysis

Objectives

The purpose of this systematic review of the literature is to investigate which of the epoxy-based cements and those based on Tricalciumsilicate (MTA, Bioceramic) have the best sealing capacity through the analysis of studies that have provided a survey model in vitro of bacteria leakage.

Source

The articles were identified using electronic databases such as PubMed, Scopus, the search was conducted between 8.12.2020 and 31.12.2020 and a last search was conducted on 2.12.2021.

Study selection

678 records were identified and after removing the duplicates we obtain 481 records, with the first phase of screening and selection of records we reached 204 and with the application of the inclusion and exclusion criteria we selected 31 articles, only 9 studies made a direct comparison between the two endodontic cement categories and presented data that could be included in the metaanalysis.

Data

The meta-analysis of first outcome shows an odds ratio of 2.70 C.I.(Confidence Interval) [1.54, 4.73], the test for overall effect has a p value = 0.0005 with a heterogeneity index of I 2 of 9%; The second outcome meta-analysis shows an Odds Ratio of 1.50 C.I. (Confidence Interval) [0.92, 2.46] with a p value of 0.10 with an I 2 of 79%.

Conclusion

the sealing ability is higher for epoxy resins than for tricalcium silicate-based cements, for observation periods longer than 90 days.

Clinical relevance

The knowledge of the cement that determines the best sealing ability and resistance to microbial leakage, can be of help for the dentist who has to face clinical situations such as endodontic retreatments whose failure is determined by the persistence of bacteria in the endodontic canals.

Experimental Dental Composites Containing a Novel Methacrylate-Functionalized Calcium Phosphate Component: Evaluation of Bioactivity and Physical Properties

The aim of this study was to synthesize and characterize a novel methacrylate-functionalized calcium phosphate (MCP) to be used as a bioactive compound for innovative dental composites. The characterization was accomplished by attenuated total reflectance Fourier-transform infrared spectroscopy (ATR-FTIR), scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). The incorporation of MCP as a bioactive filler in esthetic dental composite formulations and the ability of MCP containing dental composites to promote the precipitation of hydroxyapatite (HAp) on the surfaces of those dental composites was explored. The translucency parameter, depth of cure, degree of conversion, ion release profile, and other physical properties of the composites were studied with respect to the amount of MCP added to the composites. Composite with 3 wt.% MCP showed the highest flexural strength and translucency compared to the control composite and composites with 6 wt.% and 20 wt.% MCP. The progress of the surface precipitation of hydroxyapatite on the MCP containing dental composites was studied by systematically increasing the MCP content in the composite and the time of specimen storage in Dulbecco's phosphate-buffered solution with calcium and magnesium. The results suggested that good bioactivity properties are exhibited by MCP containing composites. A direct correlation between the percentage of MCP in a composite formulation, the amount of time the specimen was stored in PBS, and the deposition of hydroxyapatite on the composite's surface was observed.

A Comparative Study of Biocompatibility in Rat Connective Tissue of a New Mineral Trioxide Compound (Theracal) versus MTA and a Bioactive G3 Glass

The aim of this paper was to assess the differences in tissue response to implantation during 15, 30 and 45 days in the subcutaneous connective tissue of Wistar rats from three biomaterials: Angelus MTA^®, Theracal LC^®, and Angelus MTA^® to which 25% bioglass G3 was added. Twenty-four Wistar rats were used, the materials were inserted into the rat’s dorsal area in silicone tubes 5 mm long by 1.5 mm diameter. Histological reaction was assessed at 15, 30, and 45 days after implantation. They were then stained with hematoxylin eosin and evaluated by two observers. Data were analyzed using Fisher’s exact test and Mann–Whitney’s U test was used to determine the association between variables. Angelus MTA induced the formation of dystrophic calcifications twice as much as Theracal LC (p < 0.05). The addition of G3 did not affect the greater or lesser occurrence of calcifications (p > 0.05). Theracal LC and MTA plus G3 caused an inflammatory reaction, which was chronic at 15 days and decreased in intensity, almost disappearing after 45 days. Theracal LC, as well as Angelus MTA plus G3, were well tolerated when implanted in the subcutaneous connective tissue of rat. Histologically, no inconvenience was found for the use by direct contact of Theracal LC, and the mixture of MTA with 25% bioactive glass G3, in the tissue of Wistar rats.

Metallothionein 3 Promotes Osteoblast Differentiation in C2C12 Cells via Reduction of Oxidative Stress

Metallothioneins (MTs) are intracellular cysteine-rich proteins, and their expressions are enhanced under stress conditions. MTs are recognized as having the ability to regulate redox balance in living organisms; however, their role in regulating osteoblast differentiation is still unclear. In this research, we found that the expression of MT3, one member of the MT protein family, was specifically upregulated in the differentiation process of C2C12 myoblasts treated with bone morphogenetic protein 4 (BMP4). Transfection with MT3-overexpressing plasmids in C2C12 cells enhanced their differentiation to osteoblasts, together with upregulating the protein expression of bone specific transcription factors runt-related gene 2 (Runx2), Osterix, and distal-less homeobox 5 (Dlx5). Additionally, MT3 knockdown performed the opposite. Further studies revealed that overexpression of MT3 decreased reactive oxygen species (ROS) production in C2C12 cells treated with BMP4, and MT3 silencing enhanced ROS production. Treating C2C12 cells with antioxidant N-acetylcysteine also promoted osteoblast differentiation, and upregulated Runx2/Osterix/Dlx5, while ROS generator antimycin A treatment performed the opposite. Finally, antimycin A treatment inhibited osteoblast differentiation and Runx2/Osterix/Dlx5 expression in MT3-overexpressing C2C12 cells. These findings identify the role of MT3 in osteoblast differentiation and indicate that MT3 may have interesting potential in the field of osteogenesis research.

Physicochemical and Antibacterial Properties of Novel, Premixed Calcium Silicate-Based Sealer Compared to Powder-Liquid Bioceramic Sealer

The aim of this study was to compare the physicochemical properties, filling ability, and antibacterial activity of a premixed calcium silicate-based sealer to those of a powder–liquid bioceramic sealer. Ceraseal (CS) and BioRoot (BR) materials were analyzed using scanning electron microscopy and energy-dispersive X-ray spectroscopy at 7 and 14 d of immersion in distilled water. The filling ability of the two sealers as well as the water contact angle, solubility, flow, roughness, crystalline microstructure, pH, and compressive strength were also evaluated. The antibacterial activity was assessed through an agar diffusion as well as through direct tests. All the results were statistically analyzed using one-way or two-way analysis of variance tests. Statistically significant lower void percentages were observed for CS at 2 and 8 mm from the working length (WL) compared to those for the BR group, whilst no significant difference was observed at 5 mm from the WL. BR sealer showed higher alkaline pH, rougher surface, lower water contact angle values, lower flowability, and higher solubility compared to CS. BR showed globular and needle-like crystalline microstructure, whilst CS had globular and flower-like crystalline microstructure up to 72 h. No statistical difference was found for the compressive strength between the two sealers. BR and CS showed no antibacterial effect against Enterococcus faecalis after 3 h, whilst both sealers showed antibacterial capacity after 24 and 72 h. BR demonstrated higher antibacterial activity after 24 h. In conclusion, the use of bioceramic sealers may play an important role in controlling bacterial growth. Moreover, CS may have superior filling ability and lower solubility than the BioRoot sealer due to its specific chemical composition and mixing method.

Micro-computed tomography high resolution evaluation of dimensional and morphological changes of 3 root-end filling materials in simulated physiological conditions

The aim of this study was to evaluate volumetric and morphological stability of 3 root-end filling materials in addition to porosity and interface voids, using micro-computed tomography (µCT) in high resolution and a highly accurate approach for image analysis. Following root-end resection and apical preparation, two-rooted maxillary premolars were divided into three groups, according to the filling materials: White MTA Angelus, Biodentine, and IRM. Samples were scanned by µCT at 5 µm after the setting time and at time intervals of 7 and 30 days after immersion in phosphate-buffered saline (PBS). Volumetric and morphological changes besides material porosity and interface voids were evaluated by comparing initial values and those obtained after immersion. Data were analyzed statistically, using ANOVA and t-tests (α = 0.05). All materials showed volumetric stability. Regarding the morphological changes, Biodentine had a significant thickness reduction after storage in PBS when compared with MTA. Biodentine also showed an increase in porosity, as well as in percentage and thickness of voids after 30 days of immersion. In conclusion, µCT in high resolution and an accurate image analysis approach may be used to evaluate morphological changes of endodontic materials. Although Biodentine showed suitable adaptability and lower values of porosity than MTA, after PBS immersion there was a dimensional reduction of this material, besides an increase in porosity and interface voids.