In search of representative models of human bone-forming cells for cytocompatibility studies

Guidance on the assessment of biocompatibility of biomaterials: Fundamentals and testing considerations

BACKGROUND

Assessing the biocompatibility of materials is crucial for ensuring the safety and well-being of patients by preventing undesirable, toxic, immune, or allergic reactions, and ensuring that materials remain functional over time without triggering adverse reactions. To ensure a comprehensive assessment, planning tests that carefully consider the intended application and potential exposure scenarios for selecting relevant assays, cell types, and testing parameters is essential. Moreover, characterizing the composition and properties of biomaterials allows for a more accurate understanding of test outcomes and the identification of factors contributing to cytotoxicity. Precise reporting of methodology and results facilitates research reproducibility and understanding of the findings by the scientific community, regulatory agencies, healthcare providers, and the general public.

AIMS

This article aims to provide an overview of the key concepts associated with evaluating the biocompatibility of biomaterials while also offering practical guidance on cellular principles, testing methodologies, and biological assays that can support in the planning, execution, and reporting of biocompatibility testing.

Sirtuin 3-activated superoxide dismutase 2 mediates fluoride-induced osteoblastic differentiation in vitro and in vivo by down-regulating reactive oxygen species

Skeletal fluorosis is a chronic metabolic bone disease caused by long-term excessive fluoride intake. Abnormal differentiation of osteoblasts plays an important role in disease progression. Research on the mechanism of fluoride-mediated bone differentiation is necessary for the prevention and treatment of skeletal fluorosis. In the present study, a rat model of fluorosis was established by exposing it to drinking water containing 50 mg/L F-. We found that fluoride promoted Runt-related transcription factor 2 (RUNX2) as well as superoxide dismutase 2 (SOD2) and sirtuin 3 (SIRT3) expression in osteoblasts of rat bone tissue. In vitro, we also found that 4 mg/L sodium fluoride promoted osteogenesis-related indicators as well as SOD2 and SIRT3 expression in MG-63 and Saos-2 cells. In addition, we unexpectedly discovered that fluoride suppressed the levels of reactive oxygen species (ROS) and mitochondrial reactive oxygen species (mtROS) in osteoblasts. When SOD2 or SIRT3 was inhibited in MG-63 cells, fluoride-decreased ROS and mtROS were alleviated, which in turn inhibited fluoride-promoted osteogenic differentiation. In conclusion, our results suggest that SIRT3/SOD2 mediates fluoride-promoted osteoblastic differentiation by down-regulating reactive oxygen species.

In vitroassessment of a gallium-doped glass polyalkenoate cement: chemotherapeutic potential, cytotoxicity and osteogenic effects

Metastatic bone lesions are often osteolytic, which causes advanced-stage cancer sufferers to experience severe pain and an increased risk of developing a pathological fracture. Gallium (Ga) ion possesses antineoplastic and anti-bone resorption properties, suggesting the potential for its local administration to impede the growth of metastatic bone lesions. This study investigated the chemotherapeutic potential, cytotoxicity, and osteogenic effects of a Ga-doped glass polyalkenoate cement (GPC) (C-TA2) compared to its non-gallium (C-TA0) counterpart. Ion release profiles revealed a biphasic pattern characterized by an initial burst followed by a gradually declining release of ions. C-TA2 continued to release Ga steadily throughout the experimentation period (7 d) and exhibited prolonged zinc (Zn) release compared to C-TA0. Interestingly, the Zn release from both GPCs appeared to cause a chemotherapeutic effect against H1092 lung cancer cellsin vitro, with the prolonged Zn release from C-TA2 extending this effect. Unfortunately, both GPCs enhanced the viability of HCC2218 breast cancer cells, suggesting that the chemotherapeutic effects of Zn could be tied to cellular differences in preferred Zn concentrations. The utilization of SAOS-2 and MC3T3 cell lines as bone cell models yielded conflicting results, with the substantial decline in MC3T3 viability closely associated with silicon (Si) release, indicating cellular variations in Si toxicity. Despite this ambiguity, both GPCs exhibited harmful effects on the osteogenesis of primary rat osteoblasts, raising concerns about excessive burst Zn release. While Ga/Zn-doped GPCs hold promise for treating metastatic bone lesions caused by lung cancers, further optimization is required to mitigate cytotoxicity on healthy bone.

Evaluation of Cytocompatibility of PEEK-Based Composites as a Function of Manufacturing Processes

The biocompatible polymer polyetheretherketone (PEEK) is a suitable candidate to be part of potential all-polymer total joint replacements, provided its use is associated with better osseointegration, mechanical performance, and wear resistance. Seeking to meet the aforementioned requirements, respectively, we have manufactured a PEEK composite with different fillers: carbon fibers (CF), hydroxyapatite particles (HA) and graphene platelets (GNP). The mechanical outcomes of the composites with combinations of 0, 1.5, 3.0 wt% GNP, 5 and 15 wt% HA and 30% of wt% CF concentrations pointed out that one of the best filler combinations to achieve the previous objectives was 30 wt% CF, 8 wt% HA and 2 wt% of GNP. The study compares the bioactivity of human osteoblasts on this composite prepared by injection molding with that on the material manufactured by the Fused Filament Fabrication 3D additive technique. The results indicate that the surface adhesion and proliferation of human osteoblasts over time are better with the composite obtained by injection molding than that obtained by 3D printing. This result is more closely correlated with morphological parameters of the composite surface than its wettability behavior.

Human cells with osteogenic potential in bone tissue research

Bone regeneration after injury or after surgical bone removal due to disease is a serious medical challenge. A variety of materials are being tested to replace a missing bone or tooth. Regeneration requires cells capable of proliferation and differentiation in bone tissue. Although there are many possible human cell types available for use as a model for each phase of this process, no cell type is ideal for each phase. Osteosarcoma cells are preferred for initial adhesion assays due to their easy cultivation and fast proliferation, but they are not suitable for subsequent differentiation testing due to their cancer origin and genetic differences from normal bone tissue. Mesenchymal stem cells are more suitable for biocompatibility testing, because they mimic natural conditions in healthy bone, but they proliferate more slowly, soon undergo senescence, and some subpopulations may exhibit weak osteodifferentiation. Primary human osteoblasts provide relevant results in evaluating the effect of biomaterials on cellular activity; however, their resources are limited for the same reasons, like for mesenchymal stem cells. This review article provides an overview of cell models for biocompatibility testing of materials used in bone tissue research.

In vitro static and dynamic cell culture study of novel bone scaffolds based on 3D-printed PLA and cell-laden alginate hydrogel

The aim of this paper was to design and fabricate a novel composite scaffold based on the combination of 3D-printed PLA-based triply minimal surface structures (TPMS) and cell-laden alginate hydrogel. This novel scaffold improves the low mechanical properties of alginate hydrogel and can also provide a scaffold with a suitable pore size, which can be used in bone regeneration applications. In this regard, an implicit function was used to generate some Gyroid TPMS scaffolds. Then the fused deposition modeling (FDM) process was employed to print the scaffolds. Moreover, the micro-CT technique was employed to assess the microstructure of 3D-printed TPMS scaffolds and obtain the real geometries of printed scaffolds. The mechanical properties of composite scaffolds were investigated under compression tests experimentally. It was shown that different mechanical behaviors could be obtained for different implicit function parameters. In this research, to assess the mechanical behavior of printed scaffolds in terms of the strain-stress curves on, two approaches were presented: equivalent volume and finite element-based volume. Results of strain-stress curves showed that the finite-element based approach predicts a higher level of stress. Moreover, the biological response of composite scaffolds in terms of cell viability, cell proliferation, and cell attachment was investigated. In this vein, a dynamic cell culture system was designed and fabricated, which improves mass transport through the composite scaffolds and applies mechanical loading to the cells, which helps cell proliferation. Moreover, the results of the novel composite scaffolds were compared to those without Alginate, and it was shown that the composite scaffold could create more viability and cell proliferation in both dynamic and static cultures. Also, it was shown that scaffolds in dynamic cell culture have a better biological response than in static culture. In addition, Scanning electron microscopy was employed to study the cell adhesion on the composite scaffolds, which showed excellent attachment between the scaffolds and cells.

Biological Response to Bioinspired Microporous 3D-Printed Scaffolds for Bone Tissue Engineering

The scaffold is a key element in the field of tissue engineering, especially when large defects or substitutions of pathological tissues or organs need to be clinically addressed. The expected outcome is strongly dependent on the cell–scaffold interaction and the integration with the surrounding biological tissue. Indeed, mimicking the natural extracellular matrix (ECM) of the tissue to be healed represents a further optimization that can limit a possible morphological mismatch between the scaffold and the tissue itself. For this aim, and referring to bone tissue engineering, polylactic acid (PLA) scaffolds were 3D printed with a microstructure inspired by the trabecular architecture and biologically evaluated by means of human osteosarcoma SAOS-2 cells. The cells were seeded on two types of scaffolds differing for the designed pore size (i.e., 400 and 600 µm), showing the same growth exponential trend found in the control and no significant alterations in the actin distribution. The microporous structure of the two tested samples enhanced the protein adsorption capability and mRNA expression of markers related to protein synthesis, proliferation, and osteoblast differentiation. Our findings demonstrate that 3D-printed scaffolds support the adhesion, growth, and differentiation of osteoblast-like cells and the microporous architecture, mimicking the natural bone hierarchical structure, and favoring greater bioactivity. These bioinspired scaffolds represent an interesting new tool for bone tissue engineering and regenerative medicine applications.

The Effect of Low-Temperature Thermal Processing on Bovine Hydroxyapatite Bone Substitutes, toward Bone Cell Interaction and Differentiation

Ideal bone grafting scaffolds are osteoinductive, osteoconductive, and encourage osteogenesis through the remodeling processes of bone resorption, new bone formation, and successful integration or replacement; however, achieving this trifecta remains challenging. Production methods of bone grafts, such as thermal processing, can have significant effects on the degree of cell-surface interactions via wide-scale changes in the material properties. Here, we investigated the effects of small incremental changes at low thermal processing temperatures on the degree of osteoclast and osteoblast attachment, proliferation, and differentiation. Bovine bone scaffolds were prepared at 100, 130, 160, 190, and 220 °C and compared with a commercial control, Bio-Oss^®. Osteoclast attachment and activity were significantly higher on lower temperature processed bone and were not present ≥190 °C. The highest osteoblast proliferation and differentiation were obtained from treatments at 130 and 160 °C. Similarly, qRT²-PCR assays highlighted osteoblasts attached to bone processed at 130 and 160 °C as demonstrating the highest osteogenic gene expression. This study demonstrated the significant effects of small-scale processing changes on bone graft materials in vitro, which may translate to a tailored approach of cellular response in vivo.

High-performance bilayer composites for the replacement of osteochondral defects

Two novel bilayer constructs for the repair of osteochondral defects were developed from nanofibers and ceramic particles embedded into PVA matrices, exhibiting multiple promising properties similar to those of corresponding natural tissues.

Osteoblast function in patients with idiopathic osteonecrosis of the femoral head : implications for a possible novel therapy

Aims

To investigate whether idiopathic osteonecrosis of the femoral head (ONFH) is related to impaired osteoblast activities.

Methods

We cultured osteoblasts isolated from trabecular bone explants taken from the femoral head and the intertrochanteric region of patients with idiopathic ONFH, or from the intertrochanteric region of patients with osteoarthritis (OA), and compared their viability, mineralization capacity, and secretion of paracrine factors.

Results

Osteoblasts from the intertrochanteric region of patients with ONFH showed lower alkaline phosphatase (ALP) activity and mineralization capacity than osteoblasts from the same skeletal site in age-matched patients with OA, as well as lower messenger RNA (mRNA) levels of genes encoding osteocalcin and bone sialoprotein and higher osteopontin expression. In addition, osteoblasts from patients with ONFH secreted lower osteoprotegerin (OPG) levels than those from patients with OA, resulting in a higher receptor activator of nuclear factor kappa-light-chain-enhancer of activated B cells (NF-κB) ligand (RANKL)-to-OPG ratio. In patients with ONFH, osteoblasts from the femoral head showed reduced viability and mineralized nodule formation compared with osteoblasts from the intertrochanteric region. Notably, the secretion of the pro-resorptive factors interleukin-6 and prostaglandin E₂ as well as the RANKL-to-OPG ratio were markedly higher in osteoblast cultures from the femoral head than in those from the intertrochanteric region.

Conclusion

Idiopathic ONFH is associated with a reduced mineralization capacity of osteoblasts and increased secretion of pro-resorptive factors.

Cite this article: Bone Joint Res 2021;10(9):619–628.

Development of Si doped nano hydroxyapatite reinforced bilayer chitosan nanocomposite barrier membranes for guided bone regeneration

Guided Bone Regeneration (GBR) is a widely used process for the treatment of periodontal defects to prevent the formation of surrounding soft tissue at the periodontal defect and to provide hard tissue regeneration. Recently GBR designs have focused on the development of resorbable natural polymer-based barrier membranes due to their biodegradability and excellent biocompatibility. The aim of this study is to fabricate a novel bilayer nanocomposite membrane with microporous sublayer composed of chitosan and Si doped nanohydroxyapatite particles (Si-nHap) and chitosan/PEO nanofiber upper layer. Bilayer membrane was designed to prevent epithelial and fibroblastic cell migration and growth impeding bone formation with its upper layer and to support osteogenic cell bioactivity at the defect site with its sublayer. Microporous and nanofiber layers were fabricated by using freeze-drying and electrospinning techniques respectively. The effect of Si-nHap content on the morphological, mechanical and physical properties of the composites were investigated using SEM, AFM, micro-Ct, compression test, water uptake capacity and enzymatic degradation study. Antimicrobial properties of nanocomposite membranes were investigated with tube dilution and disk diffusion methods. In vitro cytotoxicity of bilayer membranes was evaluated. Saos-2 and NIH/3T3 proliferation studies were carried out on each layer. In vitro bioactivity of Saos-2 and NIH/3T3 cells were evaluated with ALP activity and hydroxyproline content respectively. Results showed that Si-nHap incorporation enhanced the mechanical and physical properties as well as controlling biodegradability of the polymer matrix. Besides, Si-nHap loading induced the bioactivity of Saos-2 cells by enhancing cell attachment, spreading and biomineralization on the material surface. Thus, results supported that designed bilayer nanocomposite membranes can be used as a potential biomaterial for guided bone regeneration in periodontal applications.

Human osteoblast and fibroblast response to oral implant biomaterials functionalized with non-thermal oxygen plasma

Plasma-treatment of oral implant biomaterials prior to clinical insertion is envisaged as a potential surface modification method for enhanced implant healing. To investigate a putative effect of plasma-functionalized implant biomaterials on oral tissue cells, this investigation examined the response of alveolar bone osteoblasts and gingival fibroblasts to clinically established zirconia- and titanium-based implant surfaces for bone and soft tissue integration. The biomaterials were either functionalized with oxygen-plasma in a plasma-cleaner or left untreated as controls, and were characterized in terms of topography and wettability. For the biological evaluation, the cell adhesion, morphogenesis, metabolic activity and proliferation were examined, since these parameters are closely interconnected during cell-biomaterial interaction. The results revealed that plasma-functionalization increased implant surface wettability. The magnitude of this effect thereby depended on surface topography parameters and initial wettability of the biomaterials. Concerning the cell response, plasma-functionalization of smooth surfaces affected initial fibroblast morphogenesis, whereas osteoblast morphology on rough surfaces was mainly influenced by topography. The plasma- and topography-induced differential cell morphologies were however not strong enough to trigger a change in proliferation behaviour. Hence, the results indicate that oxygen plasma-functionalization represents a possible cytocompatible implant surface modification method which can be applied for tailoring implant surface wettability.

A Novel Strategy to Coat Dopamine-Functionalized Titanium Surfaces With Agarose-Based Hydrogels for the Controlled Release of Gentamicin

Introduction

The use of spinal implants for the treatment of back disorders is largely affected by the insurgence of infections at the implantation site. Antibacterial coatings have been proposed as a viable solution to limit such infections. However, despite being effective at short-term, conventional coatings lack the ability to prevent infections at medium and long-term. Hydrogel-based drug delivery systems may represent a solution controlling the release of the loaded antibacterial agents while improving cell integration. Agarose, in particular, is a biocompatible natural polysaccharide known to improve cell growth and already used in drug delivery system formulations. In this study, an agarose hydrogel-based coating has been developed for the controlled release of gentamicin (GS).

Methods

Sand blasted Ti6Al4V discs were grafted with dopamine (DOPA) solution. After, GS loaded agarose hydrogels have been produced and additioned with tannic acid (TA) and calcium chloride (CaCl₂) as crosslinkers. The different GS-loaded hydrogel formulations were deposited on Ti6Al4V-DOPA surfaces, and allowed to react under UV irradiation. Surface topography, wettability and composition have been analyzed with profilometry, static contact angle measurement, XPS and FTIR spectroscopy analyses. GS release was performed under pseudo-physiological conditions up to 28 days and the released GS was quantified using a specific ELISA test. The cytotoxicity of the produced coatings against human cells have been tested, along with their antibacterial activity against S. aureus bacteria.

Results

A homogeneous coating was obtained with all the hydrogel formulations. Moreover, the coatings presented a hydrophilic behavior and micro-scale surface roughness. The addition of TA in the hydrogel formulations showed an increase in the release time compared to the normal GS-agarose hydrogels. Moreover, the GS released from these gels was able to significantly inhibit S. aureus growth compared to the GS-agarose hydrogels. The addition of CaCl₂ to the gel formulation was able to significantly decrease cytotoxicity of the TA-modified hydrogels.

Conclusions

Due to their surface properties, low cytotoxicity and high antibacterial effects, the hereby proposed gentamicin-loaded agarose-hydrogels provide new insight, and represent a promising approach for the surface modification of spinal implants, greatly impacting their application in the orthopedic surgical scenario.

ZnO Nanosheet-Coated TiZrPdSiNb Alloy as a Piezoelectric Hybrid Material for Self-Stimulating Orthopedic Implants

A Ti-based alloy (Ti₄₅Zr₁₅Pd₃₀Si₅Nb₅) with already proven excellent mechanical and biocompatibility features has been coated with piezoelectric zinc oxide (ZnO) to induce the electrical self-stimulation of cells. ZnO was grown onto the pristine alloy in two different morphologies: a flat dense film and an array of nanosheets. The effect of the combined material on osteoblasts (electrically stimulable cells) was analyzed in terms of proliferation, cell adhesion, expression of differentiation markers and induction of calcium transients. Although both ZnO structures were biocompatible and did not induce inflammatory response, only the array of ZnO nanosheets was able to induce calcium transients, which improved the proliferation of Saos-2 cells and enhanced the expression of some early differentiation expression genes. The usual motion of the cells imposes strain to the ZnO nanosheets, which, in turn, create local electric fields owing to their piezoelectric character. These electric fields cause the opening of calcium voltage gates and boost cell proliferation and early differentiation. Thus, the modification of the Ti₄₅Zr₁₅Pd₃₀Si₅Nb₅ surface with an array of ZnO nanosheets endows the alloy with smart characteristics, making it capable of electric self-stimulation.

A review of in vitro cell culture testing methods for bioactive glasses and other biomaterials for hard tissue regeneration

Bioactive glasses are used to regenerate bone by a mechanism which involves surface degradation, the release of ions such as calcium, soluble silica and phosphate and the precipitation of a biomimetic apatite surface layer on the glass. One major area of bioactive glass research is the incorporation of therapeutically active ions to broaden the application range of these materials. When developing such new compositions, in vitro cell culture studies are a key part of their characterisation. However, parameters of cell culture studies vary widely, and depending on the intended use of bioactive glass compositions, different layouts, cell types and assays need to be used. The aim of this publication is to provide materials scientists, particularly those new to cell culture studies, with a tool for selecting the most appropriate assays to give insight into the properties of interest.

Test conditions can significantly affect the results of in vitro cytotoxicity testing of degradable metallic biomaterials

In vitro cytotoxicity testing is an indispensable part of the development of new biomaterials. However, the standard ISO 10993-5 enables variability in the testing conditions, which makes the results of the test incomparable. We studied the influence of media composition on the results of the cytotoxicity test. Solutions of ZnCl₂ served as simulated extracts and we also used extracts of three types of Zn-based and Mg-based degradable metals. We incubated the cells with the solutions prepared in two types of media with two concentrations of serum (5 and 10%). We compared the toxic effect of the extracts on L929 murine fibroblast-derived cell line, which is recommended by ISO standard and on “osteoblast-like cells” U-2 OS. We also compared two methods of exposition: solutions were added either to a sub-confluent layer or to the cell suspension. We evaluated the metabolic activity of the cells using the resazurin test. We found out that in vitro cytotoxicity is dramatically influenced by the concentration of serum and by the type of the medium as well as by the type of exposition and type of cells. Therefore, when performing in vitro cytotoxicity testing of biomaterials, the authors should carefully specify the conditions of the test and comparison of different studies should be carried out with caution.

Human osteoblast-like SAOS-2 cells on submicron-scale fibers coated with nanocrystalline diamond films

A unique composite nanodiamond-based porous material with a hierarchically-organized submicron-nano-structure was constructed for potential bone tissue engineering. This material consisted of submicron fibers prepared by electrospinning of silicon oxide (SiO_x), which were oxygen-terminated (O-SiO_x) and were hermetically coated with nanocrystalline diamond (NCD) films. The NCD films were then terminated with hydrogen (H-NCD) or oxygen (O-NCD). The materials were tested as substrates for the adhesion, growth and osteogenic differentiation of human osteoblast-like Saos-2 cells. The number and the spreading area of the initially adhered cells, their growth rate during 7 days after seeding and the activity of alkaline phosphatase (ALP) were significantly higher on the NCD-coated samples than on the uncoated O-SiO_x samples. In addition, the concentration of type I collagen was significantly higher in the cells on the O-NCD-coated samples than on the bare O-SiO_x samples. The observed differences could be attributed to the tunable wettability of NCD and to the more appropriate surface morphology of the NCD-coated samples in contrast to the less stable, rapidly eroding bare SiO_x surface. The H-NCD coatings and the O-NCD coatings both promoted similar initial adhesion of Saos-2 cells, but the subsequent cell proliferation activity was higher on the O-NCD-coated samples. The concentration of beta-actin, vinculin, type I collagen and alkaline phosphatase (ALP), the ALP activity, and also the calcium deposition tended to be higher in the cells on the O-NCD-coated samples than on the H-NCD-coated samples, although these differences did not reach statistical significance. The improved cell performance on the O-NCD-coated samples could be attributed to higher wettability of these samples (water drop contact angle less than 10°), while the H-NCD-coated samples were hydrophobic (contact angle >70°). NCD-coated porous SiO_x meshes can therefore be considered as appropriate scaffolds for bone tissue engineering, particularly those with an O-terminated NCD coating.

Beta-Titanium Alloy Covered by Ferroelectric Coating–Physicochemical Properties and Human Osteoblast-Like Cell Response

Beta-titanium alloys are promising materials for bone implants due to their advantageous mechanical properties. For enhancing the interaction of bone cells with this perspective material, we developed a ferroelectric barium titanate (BaTiO3) coating on a Ti39Nb alloy by hydrothermal synthesis. This coating was analyzed by scanning electron and Raman microscopy, X-ray diffraction, piezoresponse force microscopy, X-ray photoelectron spectroscopy, nanoindentation, and roughness measurement. Leaching experiments in a saline solution revealed that Ba is released from the coating. A progressive decrease of Ba concentration in the material was also found after 1, 3, and 7 days of cultivation of human osteoblast-like Saos-2 cells. On day 1, the Saos-2 cells adhered on the BaTiO3 film in higher initial numbers than on the bare alloy, but they were less spread, and their initial proliferation rate was slower. These cells also contained a lower amount of beta1-integrins and vinculin, i.e., molecules involved in cell adhesion, and produced a lower amount of collagen I. This cell behavior was attributed to a higher surface roughness of BaTiO3 film rather than to its potential cytotoxicity, because the cell viability on this film was very high, reaching almost 99%. The amount of alkaline phosphatase, an enzyme involved in bone matrix mineralization, was similar in cells on the BaTiO3-coated and uncoated alloy, and on day 7, the cells on BaTiO3 film attained a higher final cell population density. These results indicate that after some improvements, particularly in its roughness and stability, the hydrothermal ferroelectric BaTiO3 film could be promising coating for improved osseointegration of bone implants.

Extensive early mineralization of pre-osteoblasts, inhibition of osteoclastogenesis and faster peri-implant bone healing in osteoporotic rat model: principle effectiveness of bone-specific delivery of Tibolone as evaluated in vitro and in vivo

Hydrophobic drug molecules pose a significant challenge in immobilization on super-hydrophobic metallic surfaces like conventional titanium implants. Pre-coating surface modifications may yield a better platform with improved wettability for such purposes. Such modifications, as depicted in this study, were hypothesized to provide the requisite roughness to assist deposition of polymers like silk fibroin (SF) as a drug-binding matrix in addition to significant improvement in early protein adsorption, which facilitates faster cellular adhesion and proliferation. A silk-based localized drug delivery module was developed on the titanium surface and tested for its surface roughness, wettability, biocompatibility and in vitro differentiation potential of cells cultured on the coated metallic surfaces with/without external supplementation of the active metabolite of Tibolone. Conditioning of the matrix-coated implants with osteogenic as well as osteoclastogenic media supplemented with Tibolone stimulated the expression of early osteogenic gene and calcium deposition in the extracellular matrix. Significant inhibition in resorptive activity was also observed in the presence of the drug. To assess the efficacy of localized delivery of Tibolone via topographically modified titanium implants for inducing early peri-implant bone formation, osteoporosis was artificially induced in rats subjected to bilateral ovariectomy and implants were placed thereafter. Bone-specific release of Tibolone through the biomimetic matrix in osteoporotic rats collectively indicated significant improvement in peri-implant bone growth after 2 and 4 weeks (p < 0.05 compared to dummy-coated implants). These findings demonstrate for the first time that Tibolone released from SF matrix-coated implants can accelerate the biological stability of bone fixtures.

Laser Ablated Periodic Nanostructures on Titanium and Steel Implants Influence Adhesion and Osteogenic Differentiation of Mesenchymal Stem Cells

Metal implants used in trauma surgeries are sometimes difficult to remove after the completion of the healing process due to the strong integration with the bone tissue. Periodic surface micro- and nanostructures can directly influence cell adhesion and differentiation on metallic implant materials. However, the fabrication of such structures with classical lithographic methods is too slow and cost-intensive to be of practical relevance. Therefore, we used laser beam interference ablation structuring to systematically generate periodic nanostructures on titanium and steel plates. The newly developed laser process uses a special grating interferometer in combination with an industrial laser scanner and ultrashort pulse laser source, allowing for fast, precise, and cost-effective modification of metal surfaces in a single step process. A total of 30 different periodic topologies reaching from linear over crossed to complex crossed nanostructures with varying depths were generated on steel and titanium plates and tested in bone cell culture. Reduced cell adhesion was found for four different structure types, while cell morphology was influenced by two different structures. Furthermore, we observed impaired osteogenic differentiation for three structures, indicating reduced bone formation around the implant. This efficient way of surface structuring in combination with new insights about its influence on bone cells could lead to newly designed implant surfaces for trauma surgeries with reduced adhesion, resulting in faster removal times, reduced operation times, and reduced complication rates.

In Vitro Production of Calcified Bone Matrix onto Wool Keratin Scaffolds via Osteogenic Factors and Electromagnetic Stimulus

Pulsed electromagnetic field (PEMF) has drawn attention as a potential tool to improve the ability of bone biomaterials to integrate into the surrounding tissue. We investigated the effects of PEMF (frequency, 75 Hz; magnetic induction amplitude, 2 mT; pulse duration, 1.3 ms) on human osteoblast-like cells (SAOS-2) seeded onto wool keratin scaffolds in terms of proliferation, differentiation, and production of the calcified bone extracellular matrix. The wool keratin scaffold offered a 3D porous architecture for cell guesting and nutrient diffusion, suggesting its possible use as a filler to repair bone defects. Here, the combined approach of applying a daily PEMF exposure with additional osteogenic factors stimulated the cells to increase both the deposition of bone-related proteins and calcified matrix onto the wool keratin scaffolds. Also, the presence of SAOS-2 cells, or PEMF, or osteogenic factors did not influence the compression behavior or the resilience of keratin scaffolds in wet conditions. Besides, ageing tests revealed that wool keratin scaffolds were very stable and showed a lower degradation rate compared to commercial collagen sponges. It is for these reasons that this tissue engineering strategy, which improves the osteointegration properties of the wool keratin scaffold, may have a promising application for long term support of bone formation in vivo.

The Effects of Biomaterial Implant Wear Debris on Osteoblasts

Aseptic loosening subsequent to periprosthetic osteolysis is the leading cause for the revision of arthroplasty failure. The biological response of macrophages to wear debris has been well established, however, the equilibrium of bone remodeling is not only dictated by osteoclastic bone resorption but also by osteoblast-mediated bone formation. Increasing evidence shows that wear debris significantly impair osteoblastic physiology and subsequent bone formation. In the present review, we update the current state of knowledge regarding the effect of biomaterial implant wear debris on osteoblasts. The interaction of osteoblasts with osteoclasts and macrophages under wear debris challenge, and potential treatment options targeting osteoblasts are also presented.

Development and Biocompatibility of Collagen-Based Composites Enriched with Nanoparticles of Strontium Containing Mesoporous Glass

In the last years bone tissue engineering has been increasingly indicated as a valid solution to meet the challenging requirements for a healthy bone regeneration in case of bone loss or fracture. In such a context, bioactive glasses have already proved their great potential in promoting the regeneration of new bone tissue due to their high bioactivity. In addition, their composition and structure enable us to incorporate and subsequently release therapeutic ions such as strontium, enhancing the osteogenic properties of the material. The incorporation of these inorganic systems in polymeric matrices enables the formulation of composite systems suitable for the design of bone scaffolds or delivery platforms. Among the natural polymers, type I collagen represents the main organic phase of bone and thus is a good candidate to develop biomimetic bioactive systems for bone tissue regeneration. However, alongside the specific composition and structure, the key factor in the design of new biosystems is creating a suitable interaction with cells and the host tissue. In this scenario, the presented study aimed at combining nano-sized mesoporous bioactive glasses produced by means of a sol–gel route with type I collagen in order to develop a bioactive hybrid formulation suitable for bone tissue engineering applications. The designed system has been fully characterized in terms of physico-chemical and morphological analyses and the ability to release Sr²⁺ ions has been studied observing a more sustained profile in presence of the collagenous matrix. With the aim to improve the mechanical and thermal stability of the resulting hybrid system, a chemical crosslinking approach using 4-star poly (ethylene glycol) ether tetrasuccinimidyl glutarate (4-StarPEG) has been explored. The biocompatibility of both non-crosslinked and 4-StarPEG crosslinked systems was evaluated by in vitro tests with human osteoblast-like MG-63 cells. Collected results confirmed the high biocompatibility of composites, showing a good viability and adhesion of cells when cultured onto the biomaterial samples.

Permanently hydrophilic, piezoelectric PVDF nanofibrous scaffolds promoting unaided electromechanical stimulation on osteoblasts

Biomimetic functional scaffolds for tissue engineering should fulfil specific requirements concerning structural, bio-chemical and electro-mechanical characteristics, depending on the tissue that they are designed to resemble. In bone tissue engineering, piezoelectric materials based on poly(vinylidene fluoride) (PVDF) are on the forefront, due to their inherent ability to generate surface charges under minor mechanical deformations. Nevertheless, PVDF's high hydrophobicity hinders sufficient cell attachment and expansion, which are essential in building biomimetic scaffolds. In this study, PVDF nanofibrous scaffolds were fabricated by electrospinning to achieve high piezoelectricity, which was compared with drop-cast membranes, as it was confirmed by XRD and FTIR measurements. Oxygen plasma treatment of the PVDF surface rendered it hydrophilic, and surface characterization revealed a long-term stability. XPS analysis and contact angle measurements confirmed an unparalleled two-year stability of hydrophilicity. Osteoblast cell culture on the permanently hydrophilic PVDF scaffolds demonstrated better cell spreading over the non-treated ones, as well as integration into the scaffold as indicated by SEM cross-sections. Intracellular calcium imaging confirmed a higher cell activation on the piezoelectric electrospun nanofibrous scaffolds. Combining these findings, and taking advantage of the self-stimulation of the cells due to their attachment on the piezoelectric PVDF nanofibers, a 3D tissue-like functional self-sustainable scaffold for bone tissue engineering was fabricated.

Heat-treated carbon coatings on poly (l-lactide) foils for tissue engineering

Carbon-based materials have emerged as promising candidates for a wide variety of biomedical applications, including tissue engineering. We have developed a simple but unique technique for patterning carbon-based substrates in order to control cell adhesion, growth and phenotypic maturation. Carbon films were deposited on PLLA foils from distances of 3 to 7 cm. Subsequent heat-treatment (60 °C, 1 h) created lamellar structures with dimensions decreasing from micro- to nanoscale with increasing deposition distance. All carbon films improved the spreading and proliferation of human osteoblast-like MG 63 cells, and promoted the alignment of these cells along the lamellar structures. Similar alignment was observed in human osteoblast-like Saos-2 cells and in human dermal fibroblasts. Type I collagen fibers produced by Saos-2 cells and fibroblasts were also oriented along the lamellar structures. These structures increased the activity of alkaline phosphatase in Saos-2 cells. Carbon coatings also supported adhesion and growth of vascular endothelial and smooth muscle cells, particularly flatter non-heated carbon films. On these films, the continuity of the endothelial cell layer was better than on heat-treated lamellar surfaces. Heat-treated carbon-coated PLLA is therefore more suitable for bone and skin tissue engineering, while carbon-coated PLLA without heating is more appropriate for vascular tissue engineering.

Phenotypic stability of the human MG-63 osteoblastic cell line at different passages

One of the most popular cell lines in osteogenesis studies is the human osteoblastic line MG-63. For cell biological investigation, it is important that the cells remain stable in their phenotype over several passages in cell culture. MG-63 cells can be used to provide fundamental insights into cell--material interaction. The aim of this study is to present a systematic characterization of the physiological behavior of MG-63 cells in the range of passages 5-30. Significant cell physiology processes during the first 24 h, including cell morphology, availability of adhesion receptors, cell cycle phases, as well as the expression of the signaling proteins Akt, GSK3a/b, IkB-α, ERK1/2, p38-MAPK, and intracellular calcium ion mobilization, remained stable over the entire range of passages P5-P30. Due to these stable characteristics in a wide range of cell culture passages, MG-63 cells can be considered as a suitable in vitro model to analyze the biocompatibility and biofunctionality of implant materials.

lncRNA HOTAIR Inhibits Mineralization in Osteoblastic Osteosarcoma Cells by Epigenetically Repressing ALPL

HOTAIR is a lncRNA that plays critical role in gene regulation and chromatin dynamics through epigenetic mechanisms. In this work we studied the physiological role of HOTAIR during the process of mineralization using osteoblastic osteosarcoma cells focusing in ALPL (Tissue Non-Specific Alkaline Phosphatase), a pivotal gene that controls bone formation. HOTAIR knockdown resulted in upregulation of ALPL, increase of alkaline phosphatase (ALP) activity, and enhanced mineralization in osteoblastic SaOS-2 cells cultured in mineralizing medium. Luciferase assays using reporter vectors containing ALPL promoter showed that HOTAIR repression increases ALPL promoter activity. Furthermore, HOTAIR knockdown increased histone H3K4 methylation levels at ALPL promoter region, suggesting that ALPL repression by HOTAIR is regulated by epigenetic mechanisms. This work supports that physiological bone formation is epigenetically regulated by a lncRNA.

Cobalt and Titanium nanoparticles influence on human osteoblast mitochondrial activity and biophysical properties of their cytoskeleton

We investigated the biophysical effects (cell elasticity and spring constant) caused on Saos-2 human osteoblast-like cells by nanosized metal (Co and Ti) wear debris, as well as the adhesive characteristics of cells after exposure to the metal nanoparticles. Cell mitochondrial activity was investigated using the MTT assays; along with LDH assay, metal uptake, cell apoptosis and mineralisation output (alizarin red assay) of the cells. Osteoblasts mitochondrial activity was not affected by Ti nanoparticles at concentrations up to 1 mg/ml and by Cobalt nanoparticles at concentrations < 0.5 mg/ml; however elasticity and spring constant were significantly modified by the exposure to nanoparticles of these metals in agreement with the alteration of cell conformation (shape), as result of the exposure to simulated wear debris, demonstrated by fluorescence images after actin staining.

Porous Heat-Treated Polyacrylonitrile Scaffolds for Bone Tissue Engineering

Heat-treated polyacrylonitrile (HT-PAN), also referred to as black orlon (BO), is a promising carbon-based material used for applications in tissue engineering and regenerative medicine. To the best of our knowledge, no such complex bone morphology-mimicking three-dimensional (3D) BO structure has been reported to date. We report that BO can be easily made into 3D cryogel scaffolds with porous structures, using succinonitrile as a porogen. The cryogels possess a porous morphology, similar to bone tissue. The prepared scaffolds showed strong osteoconductive activity, providing excellent support for the adhesion, proliferation, and mitochondrial activity of human bone-derived cells. This effect was more apparent in scaffolds prepared from a matrix with a higher content of PAN (i.e., 10% rather than 5%). The scaffolds with 10% of PAN also showed enhanced mechanical properties, as revealed by higher compressive modulus and higher compressive strength. Therefore, these scaffolds have a robust potential for use in bone tissue engineering.

Substrate Microarchitecture Shapes the Paracrine Crosstalk of Stem Cells with Endothelial Cells and Osteoblasts

We examined the hypothesis that substrate microarchitecture regulates the crosstalk between human mesenchymal stem cells (hMSC) and cell types involved in bone regeneration. Compared with polyester flat substrates having uniformly distributed homogenous pores (2D), three-dimensional polystyrene substrates with randomly oriented and interconnected pores of heterogeneous size (3D) stimulated the stromal secretion of IGF-1 while lessened the production of VEGFR-1, MCP-1 and IL-6. The medium conditioned by hMSC cultured in 3D substrates stimulated tube formation by human endothelial cells (hEC) to a higher extent than medium from 2D cultures. 3D co-cultures of hMSC and hEC contained higher secreted levels of IGF-1, EGF and FGF-2 than 2D co-cultures, resulting in increased hEC proliferation and migration. Substrate microarchitecture influenced the secretion of factors related to bone remodeling as the ratio RANKL to OPG, and the levels of M-CSF and IL-6 were higher in 3D co-cultures of hMSC and human osteoblasts (hOB) than in 2D co-cultures. Cytokine microenvironment in 3D co-cultures stimulated osteoblast matrix reorganization while demoted the late steps of osteoblastic maturation. Altogether, data in this study may unveil a new role of scaffold microarchitecture during bone regeneration, as modulator of the paracrine relationships that hMSC establish with hEC and hOB.

Paracrine interactions between mesenchymal stem cells and macrophages are regulated by 1,25-dihydroxyvitamin D3

Mesenchymal stem cells (MSC) modulate the macrophage-mediated inflammatory response through the secretion of soluble factors. In addition to its classical effects on calcium homeostasis, 1,25-dihydroxyvitamin D3 (1,25D3) has emerged as an important regulator of the immune system. The present study investigates whether 1,25D3 modulates the paracrine interactions between MSC and macrophages. 1,25D3 stimulated MSC to produce PGE₂ and VEGF and regulated the interplay between macrophages and MSC toward reduced pro-inflammatory cytokine production. Conditioned media (CM) from co-cultures of macrophages and MSC impaired MSC osteogenesis. However, MSC cultured in CM from 1,25D3-treated co-cultures showed increased matrix maturation and mineralization. Co-culturing MSC with macrophages prevented the 1,25D3-induced increase in RANKL levels, which correlated with up-regulation of OPG secretion. MSC seeding in three-dimensional (3D) substrates potentiated their immunomodulatory effects on macrophages. Exposure of 3D co-cultures to 1,25D3 further reduced the levels of soluble factors related to inflammation and chemotaxis. As a consequence of 1,25D3 treatment, the recruitment of monocytes toward CM of 3D co-cultures decreased, while the osteogenic maturation of MSC increased. These data add new insights into the pleiotropic effects of 1,25D3 on the crosstalk between MSC and macrophages and highlight the role of the hormone in bone regeneration.

Cytokine, Chemokine, and Growth Factor Profile Characterization of Undifferentiated and Osteoinduced Human Adipose-Derived Stem Cells

Bone is the second most manipulated tissue after blood. Adipose-derived stem cells (ASCs) may become a convenient source of MSC for bone regenerative protocols. Surprisingly, little is known about the most significant biomolecules these cells produce and release after being osteoinduced. Therefore, the present study aimed at dosing 13 candidates chosen among the most representative cytokines, chemokines, and growth factors within the conditioned media of osteodifferentiated and undifferentiated ASCs. Two acknowledged osteoblastic cell models, that is, MG-63 and SaOs-2 cells, were compared. Notably, IL-6, IL-8, MCP-1, and VEGF were highly produced and detectable in ASCs. In addition, while IL-6 and IL-8 seemed to be significantly induced by the osteogenic medium, no such effect was seen for MCP-1 and VEGF. Overall SaOS-2 had a poor expression profile, which may be consistent with the more differentiated phenotype of SaOs-2 compared to ASCs and MG-63. Instead, in maintaining medium, MG-63 displayed a very rich production of IL-12, MCP-1, IP-10, and VEGF, which were significantly reduced in osteogenic conditions, with the only exception of MCP-1. The high expression of MCP-1 and VEGF, even after the osteogenic commitment, may support the usage of ASCs in bone regenerative protocols by recruiting both osteoblasts and osteoclasts of the host.

Adhesion and differentiation of Saos-2 osteoblast-like cells on chromium-doped diamond-like carbon coatings

Diamond-like carbon (DLC) thin films are promising for use in coating orthopaedic, dental and cardiovascular implants. The problem of DLC layers lies in their weak layer adhesion to metal implants. Chromium is used as a dopant for improving the adhesion of DLC films. Cr-DLC layers were prepared by a hybrid technology, using a combination of pulsed laser deposition (PLD) from a graphite target and magnetron sputtering. Depending on the deposition conditions, the concentration of Cr in the DLC layers moved from zero to 10.0 at.%. The effect of DLC layers with 0.0, 0.9, 1.8, 7.3, 7.7 and 10.0 at.% Cr content on the adhesion and osteogenic differentiation of human osteoblast-like Saos-2 cells was assessed in vitro. The DLC samples that contained 7.7 and 10.0 at.% of Cr supported cell spreading on day 1 after seeding. On day three after seeding, the most apparent vinculin-containing focal adhesion plaques were also found on samples with higher concentrations of chromium. On the other hand, the expression of type I collagen and alkaline phosphatase at the mRNA and protein level was the highest on Cr-DLC samples with a lower concentration of Cr (0-1.8 at.%). We can conclude that higher concentrations of chromium supported cell adhesion; however DLC and DLC doped with a lower concentration of chromium supported osteogenic cell differentiation.

Antibacterial ability and osteogenic activity of porous Sr/Ag-containing TiO2 coatings

Implant-associated infection and poor osseointegration remains a major clinical challenge in Ti-based implant materials. A versatile strategy to endow Ti-based implants with long-term antibacterial ability as well as better osteogenic activity is highly desirable for high quality implantation. Strontium (Sr) has been shown to be a significant element to favor bone growth by promoting new bone formation and inhibiting bone resorption. In this study, a novel duplex-treatment technique encompassing magnetron sputtering with micro-arc oxidation is utilized to fabricate porous Sr/Ag-containing TiO2 coatings loaded with different concentrations of Ag and Sr. All coatings are porous with pore size less than 5 µm. Ag is primarily distributed homogeneously inside the pores, and the concentrations of Ag in Sr/Ag-containing TiO2 coatings with low and high Ag contents are 0.40 at.% and 0.83 at.% respectively. We have demonstrated that this kind of coating displays long-lasting antibacterial ability even up to 28 d due to the incorporation of Ag. Further, Sr/Ag-containing TiO2 coatings with optimum Ag and Sr contents revealed good cytocompatibility, enhanced osteoblast spreading and osseointegration, which stemmed primarily from the synergistic effect exerted by the porous surface topography and the bioactive element Sr. However, this study has also identified, for the first time, that proper addition of Ag would further facilitate osteogenic effects. Besides, Sr may be able to alleviate the potential cytotoxic effect of excessive Ag. Thus, integration of optimum functional elements Ag and Sr into Ti-based implant materials would be expected to expedite osseointegration while simultaneously sustaining long-term antibacterial activity, which would provide new insights for relevant fundamental investigations and biomedical applications.

Choice of osteoblast model critical for studying the effects of electromagnetic stimulation on osteogenesis in vitro

The clinical benefits of electromagnetic field (EMF) therapy in enhancing osteogenesis have been acknowledged for decades, but agreement regarding the underlying mechanisms continues to be sought. Studies have shown EMFs to promote osteoblast-like cell proliferation, or contrarily, to induce differentiation and enhance mineralization. Typically these disparities have been attributed to methodological differences. The present paper argues the possibility that the chosen osteoblast model impacts stimulation outcome. Phenotypically immature cells, particularly at low seeding densities, appear to be prone to EMF-amplified proliferation. Conversely, mature cells at higher densities seem to be predisposed to earlier onset differentiation and mineralization. This suggests that EMFs augment ongoing processes in cell populations. To test this hypothesis, mature SaOS-2 cells and immature MC3T3-E1 cells at various densities, with or without osteo-induction, were exposed to sinusoidal 50 Hz EMF. The exposure stimulated the proliferation of MC3T3-E1 and inhibited the proliferation of SaOS-2 cells. Baseline alkaline phosphatase (ALP) expression of SaOS-2 cells was high and rapidly further increased with EMF exposure, whereas ALP effects in MC3T3-E1 cells were not seen until the second week. Thus both cell types responded differently to EMF stimulation, corroborating the hypothesis that the phenotypic maturity and culture stage of cells influence stimulation outcome.

Effect of Surface Modifications of Ti40Zr10Cu38Pd12 Bulk Metallic Glass and Ti-6Al-4V Alloy on Human Osteoblasts In Vitro Biocompatibility

The use of biocompatible materials, including bulk metallic glasses (BMGs), for tissue regeneration and transplantation is increasing. The good mechanical and corrosion properties of Ti40Zr10Cu38Pd12 BMG and its previously described biocompatibility makes it a potential candidate for medical applications. However, it is known that surface properties like topography might play an important role in regulating cell adhesion, proliferation and differentiation. Thus, in the present study, Ti40Zr10Cu38Pd12 BMG and Ti6-Al-4V alloy were surface-modified electrochemically (nanomesh) or physically (microscratched) to investigate the effect of material topography on human osteoblasts cells (Saos-2) adhesion, proliferation and differentiation. For comparative purposes, the effect of mirror-like polished surfaces was also studied. Electrochemical treatments led to a highly interconnected hierarchical porous structure rich in oxides, which have been described to improve corrosion resistance, whereas microscratched surfaces showed a groove pattern with parallel trenches. Cell viability was higher than 96% for the three topographies tested and for both alloy compositions. In all cases, cells were able to adhere, proliferate and differentiate on the alloys, hence indicating that surface topography plays a minor role on these processes, although a clear cell orientation was observed on microscratched surfaces. Overall, our results provide further evidence that Ti40Zr10Cu38Pd12 BMG is an excellent candidate, in the present two topographies, for bone repair purposes.

The effect of silver or gallium doped titanium against the multidrug resistant Acinetobacter baumannii

Implant-related infection of biomaterials is one of the main causes of arthroplasty and osteosynthesis failure. Bacteria, such as the rapidly-emerging Multi Drug Resistant (MDR) pathogen Acinetobacter Baumannii, initiate the infection by adhering to biomaterials and forming a biofilm. Since the implant surface plays a crucial role in early bacterial adhesion phases, titanium was electrochemically modified by an Anodic Spark Deposition (ASD) treatment, developed previously and thought to provide osseo-integrative properties. In this study, the treatment was modified to insert gallium or silver onto the titanium surface, to provide antibacterial properties. The material was characterized morphologically, chemically, and mechanically; biological properties were investigated by direct cytocompatibility assay, Alkaline Phosphatase (ALP) activity, Scanning Electron Microscopy (SEM), and Immunofluorescent (IF) analysis; antibacterial activity was determined by counting Colony Forming Units, and viability assay. The various ASD-treated surfaces showed similar morphology, micrometric pore size, and uniform pore distribution. Of the treatments studied, gallium-doped specimens showed the best ALP synthesis and antibacterial properties. This study demonstrates the possibility of successfully doping the surface of titanium with gallium or silver, using the ASD technique; this approach can provide antibacterial properties and maintain high osseo-integrative potential.

Effect of Fluoride-Modified Titanium Surface on Early Adhesion of Irradiated Osteoblasts

Objective. The present study aimed to investigate the effect of fluoride-modified titanium surface on adhesion of irradiated osteoblasts. Materials and Methods. Fluoride-modified surface was obtained and the morphology, roughness, and chemical composition of the surface were evaluated by scanning electron microscopy, atomic force microscopy, and X-ray photoelectron spectroscopy, respectively. The adhesion of irradiated osteoblast-like cells, in terms of number, area, and fluorescence intensity on the titanium surface, was evaluated using immunofluorescence staining. Results. Numerous nanosize pits were seen only in the F-TiO surface. The pits were more remarkable and uniform on F-TiO surface than on TiO surface; however, the amplitude of peaks and bottoms on F-TiO surface appeared to be smaller than on TiO surface. The Sa value and Sdr percentage of TiO surfaces were significantly higher than those of F-TiO surface. The concentrations of main elements such as titanium, oxygen, and carbon were similar on both surfaces. The number of irradiated osteoblasts adhered on the control surface was larger than on fluoride-modified surface. Meanwhile, the cells on the fluoride-modified surface formed more actin filaments. Conclusions. The fluoride-modified titanium surface alters the adhesion of irradiated osteoblasts. Further studies are needed to investigate the proliferation, differentiation, maturation, gene expression, and cytokine production of irradiated osteoblasts on fluoride-modified titanium surface.

Osteogenic cell differentiation on H-terminated and O-terminated nanocrystalline diamond films

Nanocrystalline diamond (NCD) films are promising materials for bone implant coatings because of their biocompatibility, chemical resistance, and mechanical hardness. Moreover, NCD wettability can be tailored by grafting specific atoms. The NCD films used in this study were grown on silicon substrates by microwave plasma-enhanced chemical vapor deposition and grafted by hydrogen atoms (H-termination) or oxygen atoms (O-termination). Human osteoblast-like Saos-2 cells were used for biological studies on H-terminated and O-terminated NCD films. The adhesion, growth, and subsequent differentiation of the osteoblasts on NCD films were examined, and the extracellular matrix production and composition were quantified. The osteoblasts that had been cultivated on the O-terminated NCD films exhibited a higher growth rate than those grown on the H-terminated NCD films. The mature collagen fibers were detected in Saos-2 cells on both the H-terminated and O-terminated NCD films; however, the quantity of total collagen in the extracellular matrix was higher on the O-terminated NCD films, as were the amounts of calcium deposition and alkaline phosphatase activity. Nevertheless, the expression of genes for osteogenic markers – type I collagen, alkaline phosphatase, and osteocalcin – was either comparable on the H-terminated and O-terminated films or even lower on the O-terminated films. In conclusion, the higher wettability of the O-terminated NCD films is promising for adhesion and growth of osteoblasts. In addition, the O-terminated surface also seems to support the deposition of extracellular matrix proteins and extracellular matrix mineralization, and this is promising for better osteoconductivity of potential bone implant coatings.

Microstructure and cytotoxicity evaluation of duplex-treated silver-containing antibacterial TiO₂ coatings

Implant-related infection is one of the most common and serious complications associated with biomedical implantation. To prevent bacterial adhesion, a series of porous TiO2 coatings with different concentrations of silver (designated as M0, M1, M2 and M3) were prepared on pure titanium substrates by a duplex-treatment technique combining magnetron sputtering with micro-arc oxidation. All coatings are porous with pore size less than 5 μm and the concentrations of silver in the M0, M1, M2 and M3 are 0, 0.95, 1.36 and 1.93 wt.%, respectively. Silver is found to be distributed throughout the thickness of the coatings by scanning electron microscopy. The release of silver from the TiO2 coatings was confirmed by an inductively-coupled plasma mass spectroscopy. The antibacterial effects of these coatings were tested against Gram-positive Staphylococcus aureus (S. aureus) and Gram-negative Escherichia coli (E. coli), and the cytotoxicity was evaluated using the mouse pre-osteoblast cells. The results indicate that the antibacterial activities of TiO2 coatings are greatly improved due to the incorporation of silver. No cytotoxic effect is found for the M1 surfaces from the observation of pre-osteoblast cell by MTT assay and fluorescence microscopy. Although the M2 and M3 coatings appeared to be toxic for pre-osteoblast cells after 1 day in culture, the cell viability on M2 and M3 surfaces was greatly raised after culturing for 2 days. Our results suggested that the TiO2 coatings incorporated with an optimum amount of silver can possess excellent antibacterial activities without cytotoxic effect, which has promising applications in biomedical devices.

Conditioned media from microvascular endothelial cells cultured in simulated microgravity inhibit osteoblast activity

Background and Aims. Gravity contributes to the maintenance of bone integrity. Accordingly, weightlessness conditions during space flight accelerate bone loss and experimental models in real and simulated microgravity show decreased osteoblastic and increased osteoclastic activities. It is well known that the endothelium and bone cells cross-talk and this intercellular communication is vital to regulate bone homeostasis. Because microgravity promotes microvascular endothelial dysfunction, we anticipated that the molecular cross-talk between endothelial cells exposed to simulated microgravity and osteoblasts might be altered. Results. We cultured human microvascular endothelial cells in simulated microgravity using the rotating wall vessel device developed by NASA. Endothelial cells in microgravity show growth inhibition and release higher amounts of matrix metalloproteases type 2 and interleukin-6 than controls. Conditioned media collected from microvascular endothelial cells in simulated microgravity were used to culture human osteoblasts and were shown to retard osteoblast proliferation and inhibit their activity. Discussion. Microvascular endothelial cells in microgravity are growth retarded and release high amounts of matrix metalloproteases type 2 and interleukin-6, which might play a role in retarding the growth of osteoblasts and impairing their osteogenic activity. Conclusions. We demonstrate that since simulated microgravity modulates microvascular endothelial cell function, it indirectly impairs osteoblastic function.

Interaction of human osteoblast-like Saos-2 and MG-63 cells with thermally oxidized surfaces of a titanium-niobium alloy

An investigation was made of the adhesion, growth and differentiation of osteoblast-like MG-63 and Saos-2 cells on titanium (Ti) and niobium (Nb) supports and on TiNb alloy with surfaces oxidized at 165°C under hydrothermal conditions and at 600°C in a stream of air. The oxidation mode and the chemical composition of the samples tuned the morphology, topography and distribution of the charge on their surfaces, which enabled us to evaluate the importance of these material characteristics in the interaction of the cells with the sample surface. Numbers of adhered MG-63 and Saos-2 cells correlated with the number of positively-charged (related with the Nb₂O₅ phase) and negatively-charged sites (related with the TiO₂ phase) on the alloy surface. Proliferation of these cells is correlated with the presence of positively-charged (i.e. basic) sites of the Nb₂O₅ alloy phase, while cell differentiation is correlated with negatively-charged (acidic) sites of the TiO₂ alloy phase. The number of charged sites and adhered cells was substantially higher on the alloy sample oxidized at 600°C than on the hydrothermally treated sample at 165°C. The expression values of osteoblast differentiation markers (collagen type I and osteocalcin) were higher for cells grown on the Ti samples than for those grown on the TiNb samples. This was more particularly apparent in the samples treated at 165°C. No considerable immune activation of murine macrophage-like RAW 264.7 cells on the tested samples was found. The secretion of TNF-α by these cells into the cell culture media was much lower than for either cells grown in the presence of bacterial lipopolysaccharide, or untreated control samples. Thus, oxidized Ti and TiNb are both promising materials for bone implantation; TiNb for applications where bone cell proliferation is desirable, and Ti for induction of osteogenic cell differentiation.