Bioactive low-shrinkage-stress nanocomposite suppresses S. mutans biofilm and preserves tooth dentin hardness

Novel Resin-Based Antibacterial Root Surface Coating Material to Combat Dental Caries

Root caries caused by cariogenic bacteria are a burden on a large number of individuals worldwide, especially the elderly. Applying a protective coating to exposed root surfaces has the potential to inhibit the development of caries, thus preserving natural teeth. This study aimed to develop a novel antibacterial coating to combat root caries and evaluate its effectiveness using the antibacterial monomer dimethylaminohexadecyl methacrylate (DMAHDM). DMAHDM was synthesized and incorporated into a resin consisting of 55.8% urethane dimethacrylate (UDMA) and 44.2% TEG-DVBE (UV) at a 10% mass fraction of glass filler. Multiple concentrations of DMAHDM were tested for their impact on the resin's mechanical and physical properties. S. mutans biofilms grown on resin disks were analyzed for antibacterial efficacy. Cytotoxicity was assessed against human gingival fibroblasts (HGFs). The results showed an 8-log reduction in colony-forming units (CFUs) against S. mutans biofilm (mean ± sd; n = 6) (p < 0.05) when 5% DMAHDM was incorporated into the UV resin. There was a 90% reduction in metabolic activity and lactic acid production. A low level of cytotoxicity against HGF was observed without compromising the physical and mechanical properties of the resin. This coating material demonstrated promising physical properties, potent antibacterial effects, and low toxicity, suggesting its potential to protect exposed roots from caries in various dental procedures and among elderly individuals with gingival recession.

Preparation and performance evaluation of a novel orthodontic adhesive incorporating composite dimethylaminohexadecyl methacrylate-Polycaprolactone fibers

This study addressed enamel demineralization, a common complication in fixed orthodontic treatment, by evaluating a novel orthodontic adhesive with DMAHDM-PCL composite fibers. These fibers, produced through electrospinning, were incorporated into orthodontic adhesive to create experimental formulations at different concentrations and a control group. The study assessed antimicrobial properties, biosafety, and mechanical characteristics. New orthodontic adhesive exhibited significant bacteriostatic effects, reducing bacterial biofilm activity and concentrations. Incorporating 1% and 3% DMAHDM-PCL did not affect cytocompatibility. Animal tests confirmed no inflammatory irritation. Shear bond strength and adhesive residual index results indicated that antimicrobial fibers didn't impact bonding ability. In conclusion, orthodontic adhesives with 3% DMAHDM-PCL fibers are potential antimicrobial bonding materials, offering a comprehensive solution to enamel demineralization in orthodontic patients.

Reinforced dentin remineralization via a novel dual-affinity peptide

OBJECTIVES

In light of the constantly flowing saliva, anti-caries remineralization agents are inclined to be taken away. Owing to their limited residence time, the remineralization effect is not as desirable as expected. Hence, our study aimed to synthesize a novel peptide (DGP) with high affinity to both collagen fibrils and hydroxyapatite, and investigated its dentin remineralization efficacy in vitro and anti-caries capability in vivo.

METHODS

DGP was synthesized through Fmoc solid-phase reaction. The binding ability and interaction mechanism of DGP to demineralized dentin were investigated. Dentin specimens were demineralized, then treated with DGP and deionized water respectively. The specimens were incubated in artificial saliva and in-vitro remineralization effectiveness was analyzed after 14 days. The rat caries model was established to further scrutinize the in-vivo efficacy of caries prevention.

RESULTS

DGP possesses an enhanced adhesion force of 12.29 ± 1.12 nN to demineralized dentin. The favorable adsorption capacity is ascribed to the stable hydrogen bonds between S2P-101 and ASP-100 of DGP and GLY33 and PRO-16 of collagen fibers. Abundant mineral deposits and remarkable tubule occlusion were observed in the DGP group. DGP-treated dentin obtained notable microhardness recovery and higher mineral content after a 14-day remineralization regimen. DGP also demonstrated potent caries prevention in vivo, with substantially fewer carious lesions and significantly lower Keyes scoring.

SIGNIFICANCE

DGP proves to possess a high affinity to demineralized dentin regardless of saliva flowing, thus enhancing remineralization potency significantly in vitro and in vivo, potential for dental caries prevention and combatting initial dentin caries clinically.

Antimicrobial dental composites with K18-methyl methacrylate and K18-filler

OBJECTIVE

To determine the effects of using K18-methyl methacrylate (K18-MMA) and K18-Filler on composite cure, esthetic, mechanical, polymerization shrinkage, and antimicrobial properties.

METHODS

K18-MMA (0-20% w/w) was used to replace TEGDMA in a 70:30 Bis-GMA:TEGDMA composite filled to 70% w/w with barium glass or K18-Filler. Composite degree of cure (Rockwell15T hardness and near Infrared FTIR), hydrophilicity (contact angle measurements), translucency (transparency parameter measurements, TP), mechanical (3-point bend test), polymerization shrinkage (volumetric shrinkage and shrinkage stress), and antimicrobial properties (colony counting assay) against Streptococcus mutans, Streptococcus sanguinis, and Candida albicans were determined.

RESULTS

All experimental groups had comparable degrees of cure (near Infrared FTIR and Rockwell15T Hardness), TP, moduli, polymerization volumetric shrinkages and shrinkage stresses to those of controls (Bonferroni corrected p > 0.0018). Only one group (15% K18-MMA+K18-Filler) had significantly different (lower) contact angles as compared to that of controls (Bonferroni corrected p < 0.0018). Most of the K18-Filler-containing composites had significantly lower ultimate transverse strengths (UTS) than controls (Bonferroni corrected p < 0.0018). Controls had significantly greater S mutans colony counts than 15% and 20% w/w K18-MMA+K18-Filler groups, and greater S sanguinis and C albicans colony counts than K18-containing groups. Of the composites with that provided significant antimicrobial properties against S. mutans, S. sanguinis, and C. albicans, only the 20% K18-MMA+K18-Filler group had significantly lower UTS than controls.

SIGNIFICANCE

Composites with K18-MMA and K18-Filler with comparable physical properties to control composites and significant antimicrobial properties have been developed. K18-MMA and K18-Filler seem to be suitable for incorporation into commercial dental resins.

Synergistic effect of ion-releasing fillers on the remineralization and mechanical properties of resin-dentin bonding interfaces

In modern restorative dentistry, adhesive resin materials are vital for achieving minimally invasive, esthetic, and tooth-preserving restorations. However, exposed collagen fibers are found in the hybrid layer of the resin-dentin bonding interface due to incomplete resin penetration. As a result, the hybrid layer is susceptible to attack by internal and external factors such as hydrolysis and enzymatic degradation, and the durability of dentin bonding remains limited. Therefore, efforts have been made to improve the stability of the resin-dentin interface and achieve long-term clinical success. New ion-releasing adhesive resin materials are synthesized by introducing remineralizing ions such as calcium and phosphorus, which continuously release mineral ions into the bonding interface in resin-bonded restorations to achieve dentin biomimetic remineralization and improve bond durability. As an adhesive resin material capable of biomimetic mineralization, maintaining excellent bond strength and restoring the mechanical properties of demineralized dentin is the key to its function. This paper reviews whether ion-releasing dental adhesive materials can maintain the mechanical properties of the resin-dentin bonding interface by supplementing the various active ingredients required for dentin remineralization from three aspects: phosphate, silicate, and bioactive glass.

Recurrent caries models to assess dental restorations: A scoping review

OBJECTIVES

To review the literature on recurrent caries models used to evaluate restorative materials, compare reported methodology and parameters, and devise specific recommendations to be considered in future investigations.

DATA

The following were extracted: study design, sample characteristics, source of teeth, name of restorations compared including controls, recurrent caries model type, type of demineralizing and remineralizing solutions, type of biofilm used, methods to detect recurrent caries.

SOURCES

Literature searches were performed in OVID Medline, EMBASE, SCOPUS, and Cochrane Library.

STUDY SELECTION

For a study to be included, it had to examine dental materials for tooth restoration purposes only with a valid control group and evaluate restorative dental materials regardless of the form of the teeth caries model used or nature of the tooth structure used. A total of 91 studies were included. Most of the studies presented were in vitro. Human teeth were the main source of specimens utilized. Around 88% of the studies used specimens without an artificial gap, and 44% used a chemical model. S. mutans was the main bacterial species used in microbial caries models.

CONCLUSION

The findings of this review provided an insight into the performance of available dental materials assessed using different recurrent caries models, yet this review cannot be used as a guideline for material selection. Selecting the appropriate restorative material relies on several patient-related factors such as microbiota, occlusion, and diet that are not comprehensively taken into consideration in recurrent caries models and thus hinder reliable comparison.

CLINICAL SIGNIFICANCE

Due to the heterogenicity of variables among studies on the performance of dental restorative materials, this scoping review aimed to provide insights for dental researchers concerning the available recurrent caries models, testing methods used, and aspects of comparison between these materials including their characteristics and limitations.

Engineered Biomaterials Trigger Remineralization and Antimicrobial Effects for Dental Caries Restoration

Dental caries is the most prevalent chronic disease globally, significantly impacting individuals' quality of life. A key reason behind the failure of implanted restorations is their biological inactivity, meaning they are unable to form crosslinks with the surrounding tooth structures, thus making patients susceptible to implant loss and recurrent tooth decay. For the treatment of caries, antibacterial medicine and remineralization are effective means of treating the recurrence of caries. Owing to the rapid progression in the biomaterials field, several biomaterials have been reported to display antimicrobial properties and aid in dentin remineralization. Bioactive materials hold considerable potential in diminishing biofilm accumulation, inhibiting the process of demineralization, enabling dentin remineralization, and combating bacteria related to caries. Bioactive materials, such as fluoride, amorphous calcium phosphate, bioactive glass, collagen, and resin-based materials, have demonstrated their effectiveness in promoting dentin remineralization and exerting antibacterial effects on dental caries. However, the concentration of fluoride needs to be strictly controlled. Although amorphous calcium phosphate can provide the necessary calcium and phosphorus ions for remineralization, it falls short in delivering the mechanical strength required for oral mastication. Resin-based materials also offer different advantages due to the complexity of their design. In this review, we delve into the application of advanced bioactive materials for enhancing dentin remineralization and antibacterial properties. We eagerly anticipate future developments in bioactive materials for the treatment of dental caries.

Novel Dental Low-Shrinkage-Stress Composite with Antibacterial Dimethylaminododecyl Methacrylate Monomer

OBJECTIVES

Current dental resins exhibit polymerization shrinkage causing microleakage, which has the potential to cause recurrent caries. Our objectives were to create and characterize low-shrinkage-stress (LSS) composites with dimethylaminododecyl methacrylate (DMADDM) as an antibacterial agent to combat recurrent caries.

METHODS

Triethylene glycol divinylbenzyl ether and urethane dimethacrylate were used to reduce shrinkage stress. DMADDM was incorporated at different mass fractions (0%, 1.5%, 3%, and 5%). Flexural strength, elastic modulus, degree of conversion, polymerization stress, and antimicrobial activity were assessed.

RESULTS

The composite with 5% DMADDM demonstrated higher flexural strength than the commercial group (p < 0.05). The addition of DMADDM in BisGMA-TEGDMA resin and LSS resin achieved clinically acceptable degrees of conversion. However, LSS composites exhibited much lower polymerization shrinkage stress than BisGMA-TEGDMA composite groups (p < 0.05). The addition of 3% and 5% DMADDM showed a 6-log reduction in Streptococcus mutans (S. mutans) biofilm CFUs compared to commercial control (p < 0.001). Biofilm biomass and lactic acid were also substantially decreased via DMADDM (p < 0.05).

CONCLUSIONS

The novel LSS dental composite containing 3% DMADDM demonstrated potent antibacterial action against S. mutans biofilms and much lower polymerization shrinkage-stress, while maintaining excellent mechanical characteristics. The new composite is promising for dental applications to prevent secondary caries and increase restoration longevity.

Smart Dental Materials Intelligently Responding to Oral pH to Combat Caries: A Literature Review

Smart dental materials are designed to intelligently respond to physiological changes and local environmental stimuli to protect the teeth and promote oral health. Dental plaque, or biofilms, can substantially reduce the local pH, causing demineralization that can then progress to tooth caries. Progress has been made recently in developing smart dental materials that possess antibacterial and remineralizing capabilities in response to local oral pH in order to suppress caries, promote mineralization, and protect tooth structures. This article reviews cutting-edge research on smart dental materials, their novel microstructural and chemical designs, physical and biological properties, antibiofilm and remineralizing capabilities, and mechanisms of being smart to respond to pH. In addition, this article discusses exciting and new developments, methods to further improve the smart materials, and potential clinical applications.

Comparison of collagen features of distinct types of caries-affected dentin

OBJECTIVES

To compare the biodegradability, mechanical behavior, and physicochemical features of the collagen-rich extracellular matrix (ECM) of artificial caries-affected dentin (ACAD), natural caries-affected dentin (NCAD) and sound dentin (SD).

METHODS

Dentin specimens from human molars were prepared and assigned into groups according to the type of dentin: ACAD, NCAD, or SD. ACAD was produced by incubation of demineralized SD with Streptococcus mutans in a chemically defined medium (CDM) with 1% sucrose for 7 days at 37 °C under anaerobic conditions. Specimens were assessed to determine collagen birefringence, biodegradability, mechanical behavior, and chemical composition. Data were individually processed and analyzed by ANOVA and post-hoc tests (α = 0.05).

RESULTS

CDM-based biofilm challenge reduced loss, storage, and complex moduli in ACAD (p < 0.001), while the damping capacity remained unaffected (p = 0.066). Higher red and lower green birefringence were found in ACAD and NCAD when compared with SD (p < 0.001). Differently to ACAD, SD and NCAD presented higher biodegradability to exogenous proteases (p = 0.02). Chemical analysis of the integrated areas of characteristic bands that assess mineral quality (carbonate/phosphate and crystallinity index), mineral to matrix (phosphate/amide I) and post-translational modifications (amide III/CH₂, pentosidine/CH₂, and pentosidine/amide III) (p<0.05) showed that NCAD was significantly different from SD while ACAD exhibited intermediate values.

CONCLUSIONS

CDM-based biofilm challenge produced a dentin ECM with decreased mechanical properties and increased collagen maturity. The compositional and structural conformation of the ACAD suggested that CDM-based biofilm challenge showed potential to produce artificial lesions by revealing a transitional condition towards mimicking critical features of NCAD.

CLINICAL SIGNIFICANCE

This study highlights the importance of developing a tissue that mimics the features of natural caries-affected dentin ECM for in vitro studies. Our findings suggested the potential of a modified biofilm challenge protocol to produce and simulate a relevant substrate, such as caries-affected dentin.

Current Strategies to Control Recurrent and Residual Caries with Resin Composite Restorations: Operator- and Material-Related Factors

This review addresses the rationale of recurrent and/or residual caries associated with resin composite restorations alongside current strategies and evidence-based recommendations to arrest residual caries and restrain recurrent caries. The PubMed and MEDLINE databases were searched for composite-associated recurrent/residual caries focusing on predisposing factors related to materials and operator’s skills; patient-related factors were out of scope. Recurrent caries and fractures are the main reasons for the failure of resin composites. Recurrent and residual caries are evaluated differently with no exact distinguishment, especially for wall lesions. Recurrent caries correlates to patient factors, the operator’s skills of cavity preparation, and material selection and insertion. Material-related factors are significant. Strong evidence validates the minimally invasive management of deep caries, with concerns regarding residual infected dentin. Promising technologies promote resin composites with antibacterial and remineralizing potentials. Insertion techniques influence adaptation, marginal seal, and proximal contact tightness. A reliable diagnostic method for recurrent or residual caries is urgently required. Ongoing endeavors cannot eliminate recurrent caries or precisely validate residual caries. The operator’s responsibility to precisely diagnose original caries and remaining tooth structure, consider oral environmental conditions, accurately prepare cavities, and select and apply restorative materials are integral aspects. Recurrent caries around composites requires a triad of attention where the operator’s skills are cornerstones.

Enhancing adhesive-dentin interface stability of primary teeth: From ethanol wet-bonding to plant-derived polyphenol application

OBJECTIVES

To investigate whether the adhesive-dentin interface stability of primary teeth would be enhanced by epigallocatechin-3-gallate (EGCG) with ethanol wet-bonding.

METHODS

Non-caries primary molars were sliced to achieve a flat dentin surface and etched then randomly distributed into five groups in accordance with different treatments: group 1, no treatment; group 2, applying absolute ethanol wet-bonding for 60 s; groups 3-5, applying 0.1%, 0.5%, and 1% (w/v) EGCG-incorporating ethanol wet-bonding (0.1%, 0.5%, and 1% EGCG) for 60 s. Singlebond universal adhesive was then applied followed by resin composite construction. Microtensile bond strength, fracture mode, and nanoleakage at adhesive-dentin interface were evaluated after 24 h of water storage or 10,000 times of thermocycling. Zymography of hybrid layer, biofilm formation of Streptococcus mutans by CLSM, FESEM, and MTT test, and cytotoxicity by CCK-8 assay were respectively assessed.

RESULTS

Irrespective of thermocycling, the dentin bond strength was preserved with reduced nanoleakage in the 0.5% and 1% EGCG groups. Furthermore, the activity of endogenous proteases and the growth of Streptococcus mutans biofilm were inhibited after treatment with 0.5% and 1% EGCG/ethanol solutions (groups 4 and 5). CCK-8 results of the 0.1% and 0.5% EGCG groups showed acceptable biocompatibility.

CONCLUSIONS

Treatment by EGCG/ethanol solutions effectively enhanced the bond stability of primary teeth at the adhesive-dentin interface.

CLINICAL SIGNIFICANCE

Synergistic application of EGCG and ethanol wet-bonding suggesting a promising strategy to improve dentin bonding durability with bacterial biofilm inhibition, thus increasing resin-based restorations' service life in primary dentition.

Effects of thermal cycling on mechanical and antibacterial durability of bioactive low-shrinkage-stress nanocomposite

OBJECTIVES

Recent studies developed low-shrinkage-stress composite with remineralizing and antibacterial properties to combat secondary caries and increase restoration longevity. However, their long-term durability in thermal cycling is unclear. The objectives of this study were to develop an antibacterial, remineralizing and low-shrinkage-stress composite, and to investigate its durability in thermal cycling for 20,000 cycles, equivalent to two years of clinical life.

METHODS

The resin consisted of urethane dimethacrylate (UDMA) and triethylene glycol divinylbenzyl ether (TEG-DVBE). Composites were made with 5% dimethylaminohexadecyl methacrylate (DMAHDM) and 20% of nanoparticles of amorphous calcium phosphate (NACP). Composites were thermal cycled at 5°C and 55°C for 20,000 cycles. A human salivary biofilm model was used to evaluate antibiofilm activity before and after thermal cycling.

RESULTS

After 20,000 cycles, the flexural strength of bioactive low-shrinkage-stress composite matched commercial control with no antibacterial activity (p > 0.05). Surface roughness was clinically acceptable at less than 0.2 μm. UV+NACP+DMAHDM composite reduced the total microorganisms, total streptococci, and mutans streptococci by 2-5 logs, compared to commercial composite. Biofilm lactic acid production was reduced by 11 folds. The antibacterial performance was maintained after thermal cycling, with no decrease after 20,000 cycles.

CONCLUSIONS

Bioactive low-shrinkage-stress composite possessed good mechanical properties that matched commercial composite both before and after thermal cycling. The new composite had potent antibacterial activity, which was maintained and did not decrease after thermal cycling.

CLINICAL SIGNIFICANCE

The new bioactive low-shrinkage-stress composite could reduce polymerization shrinkage stress and release calcium and phosphate ions, with good mechanical properties and strong antibacterial function that were durable after thermal cycling. These properties indicate great potential for inhibiting recurrent caries and increasing the restoration longevity.

Novel bioactive adhesive containing dimethylaminohexadecyl methacrylate and calcium phosphate nanoparticles to inhibit metalloproteinases and nanoleakage with three months of aging in artificial saliva

OBJECTIVES

The objectives of this study were to: (1) develop a multifunctional adhesive via dimethylaminohexadecyl methacrylate (DMAHDM) and nanoparticles of amorphous calcium phosphate (NACP); and (2) investigate its ability to provide metalloproteinases (MMPs) deactivation and remineralization for long-term dentin bonding durability.

METHODS

DMAHDM and NACP were incorporated into Adper™ Single Bond 2 Adhesive (SB2) at mass fractions of 5% and 20%, respectively. Degree of conversion and contact angle were measured. Endogenous MMP activity of the demineralized dentin beams, Masson's trichrome staining, nano-indentation, microtensile bond strength and interfacial nanoleakage analyses were investigated after 24 h and 3 months of storage aging in artificial saliva.

RESULTS

Adding DMAHDM and NACP did not compromise the degree of conversion and contact angle of SB2 (p > 0.05). DMAHDM and NACP incorporation reduced the endogenous MMP activity by 53 %, facilitated remineralization, and increased the Young's modulus of hybrid layer by 49 % after 3 months of aging in artificial saliva, compared to control. For SB2 Control, the dentin bond strength decreased by 38 %, with greater nanoleakage expression, after 3 months of aging (p < 0.05). However, DMAHDM+NACP group showed no loss in bond strength, with much less nanoleakage, after 3 months of aging (p > 0.05).

SIGNIFICANCE

DMAHDM+NACP adhesive greatly reduced MMP-degradation activity in demineralized dentin, induced remineralization at adhesive-dentin interface, and maintained the dentin bond strength after aging, without adversely affecting polymerization and dentin wettability. This new adhesive has great potential to help eliminate secondary caries, prevent hybrid layer degradation, and increase the resin-dentin bond longevity.

Dental Materials for Oral Microbiota Dysbiosis: An Update

The balance or dysbiosis of the microbial community is a major factor in maintaining human health or causing disease. The unique microenvironment of the oral cavity provides optimal conditions for colonization and proliferation of microbiota, regulated through complex biological signaling systems and interactions with the host. Once the oral microbiota is out of balance, microorganisms produce virulence factors and metabolites, which will cause dental caries, periodontal disease, etc. Microbial metabolism and host immune response change the local microenvironment in turn and further promote the excessive proliferation of dominant microbes in dysbiosis. As the product of interdisciplinary development of materials science, stomatology, and biomedical engineering, oral biomaterials are playing an increasingly important role in regulating the balance of the oral microbiome and treating oral diseases. In this perspective, we discuss the mechanisms underlying the pathogenesis of oral microbiota dysbiosis and introduce emerging materials focusing on oral microbiota dysbiosis in recent years, including inorganic materials, organic materials, and some biomolecules. In addition, the limitations of the current study and possible research trends are also summarized. It is hoped that this review can provide reference and enlightenment for subsequent research on effective treatment strategies for diseases related to oral microbiota dysbiosis.

Retention of Intrafibrillar Minerals Improves Resin-Dentin Bond Durability

The concept of extrafibrillar demineralization involves selective removal of apatite crystallites from the extrafibrillar spaces of mineralized dentin without disturbing the intrafibrillar minerals within collagen. This helps avoiding activation of endogenous proteases and enables air-drying of partially demineralized dentin without causing collapse of completely demineralized collagen matrix that adversely affects resin infiltration. The objective of the present study was to evaluate the potential of quaternized carboxymethyl chitosan (QCMC)-based extrafibrillar demineralization in improving resin-dentin bond durability. Isothermal titration calorimetry indicated that QCMC synthesized by quaternization of O-carboxymethyl chitosan had moderate affinity for Ca²⁺ (binding constant: 8.9 × 10⁴ M^-1). Wet and dry bonding with the QCMC-based demineralization produced tensile bond strengths equivalent to the phosphoric acid (H₃PO₄)-based etch-and-rinse technique. Those bond strengths were maintained after thermocycling. Amide I and PO₄^3- mappings of QCMC-conditioned dentin were performed with atomic force microscope-infrared spectroscopy (AFM-IR). Whereas H₃PO₄-etched dentin exhibited an extensive reduction in PO₄^3- signals corresponding to apatite depletion, QCMC-conditioned dentin showed scattered dark areas and bright PO₄^3- streak signals. The latter were consistent with areas identified as collagen fibrils in the amide I mapping and were suggestive of the presence of intrafibrillar minerals in QCMC-conditioned dentin. Young's modulus mapping of QCMC-demineralized dentin obtained by AFM-based amplitude modulation-frequency modulation recorded moduli that were the same order of magnitude as those in mineralized dentin and at least 1 order higher than H₃PO₄-etched dentin. In situ zymography of the gelatinolytic activity within hybrid layers created with QCMC conditioning revealed extremely low signals before and after thermocycling, compared with H₃PO₄-etched dentin for both wet and dry bonding. Confocal laser scanning microscopy identified the antibacterial potential of QCMC against Streptococcus mutans and Enterococcus faecalis biofilms. Taken together, the QCMC-based demineralization retains intrafibrillar minerals, preserves the elastic modulus of collagen fibrils, reduces endogenous proteolytic activity, and inhibits bacteria biofilms to extend dentin bond durability.

Autopolymerizing acrylic repair resin containing low concentration of dimethylaminohexadecyl methacrylate to combat saliva-derived bacteria

Biofilm accumulation on the polymethyl methacrylate (PMMA) restorations negatively affect the prognosis of the provisional restorations or the following treatment. This study developed a novel antibacterial PMMA resin containing low concentration of dimethylaminohexadecyl methacrylate (DMAHDM). Four resins were tested: (1) PMMA resin (Control), (2) 1.25% DMAHDM, (3) 2.5% DMAHDM, (4) 5% DMAHDM. Adding 1.25% DMAHDM into the PMMA resin did not influence the mechanical properties, degree of conversion, monomer releasing, and color stability of the specimens (p > 0.05). The incorporation of DMAHDM into PMMA resin could greatly prevent saliva-derived biofilms adhesion compared with the control group (p < 0.05). The metabolism level of saliva-derived biofilms on the 1.25%, 2.5%, and 5% DMAHDM resins were reduced by 20%, 54%, and 62%, respectively. And the mechanism of DMAHDM disturbing the integrity of bacterial cell walls was confirmed by flow cytometric analysis. Adding 1.25% and 2.5% DMAHDM did not compromise cytocompatibility of the modified resin (p > 0.05). Therefore, novel PMMA resin containing low concentration DMAHDM is promising as a future antimicrobial provisional restoration material for preventing microbial-induced complications in clinical settings. Graphical abstract.

Low-Shrinkage Resin Matrices in Restorative Dentistry-Narrative Review

Dimethacrylate-based resin composites restorations have become widely-used intraoral materials in daily dental practice. The increasing use of composites has greatly enhanced modern preventive and conservative dentistry. They have many superior features, especially esthetic properties, bondability, and elimination of mercury and galvanic currents. However, polymeric materials are highly susceptible to polymerization shrinkage and stresses that lead to microleakage, biofilm formation, secondary caries, and restoration loss. Several techniques have been investigated to minimize the side effects of these shrinkage stresses. The primary approach is through fabrications and modification of the resin matrices. Therefore, this review article focuses on the methods for testing the shrinkage, as well as formulations of resinous matrices available to reduce polymerization shrinkage and its associated stress. Furthermore, this article reviews recent cutting-edge developments on bioactive low-shrinkage-stress nanocomposites to effectively inhibit the growth and activities of cariogenic pathogens and enhance the remineralization process.

Minimally-invasive dentistry via dual-function novel bioactive low-shrinkage-stress flowable nanocomposites

The objectives of this in vitro study were to develop a novel low-shrinkage-stress flowable nanocomposite with antibacterial properties through the incorporation of dimethylaminohexadecyl methacrylate (DMAHDM) and nanoparticles of amorphous calcium phosphate (NACP), and investigate the mechanical and oral biofilm properties, to be used in minimally-invasive techniques.

METHODS

The light-cured low-shrinkage-stress flowable resin was formulated by mixing urethane dimethacrylate (UDMA) and triethylene glycol divinylbenzyl ether (TEG-DVBE) at a 1:1 mass ratio. Different mass fractions of glass, and either 5% DMAHDM or 20%NACP or both were incorporated. Paste flowability, ultimate micro tensile strength and surface roughness were evaluated. The antibacterial response of DMAHDM resin was assessed by using biofilms of human saliva-derived microcosm model. Virtuoso flowable composite was used as a control.

RESULTS

(45% resin+5% DMAHDM+20% NACP+30% glass) formula yielded the needed outcomes. It had flow rate within the range of ISO requirement. The micro tensile strength was (39.1 ± 4.3) MPa, similar to (40.1 ± 4.0) MPa for commercial control (p > 0.05). The surface roughness values of the novel composite (0.079 ± 0.01) µm similar to commercial composite (0.09 ± 0.02) µm (p > 0.05). Salivary microcosm biofilm colony forming unit values were reduced by 5-6 logs (p < 0.05). Biofilm metabolic activity was also substantially reduced, compared to control composite (p < 0.05).

SIGNIFICANCE

The novel bioactive flowable nanocomposite achieved strong antibacterial activities without compromising the mechanical properties. It is promising to be used as pit and fissure sealants, and as fillings in conservative cavities to inhibit recurrent caries and increase restoration longevity.

Magnetic-Responsive Photosensitizer Nanoplatform for Optimized Inactivation of Dental Caries-Related Biofilms: Technology Development and Proof of Principle

Conventional antibiotic therapies for biofilm-trigged oral diseases are becoming less efficient due to the emergence of antibiotic-resistant bacterial strains. Antimicrobial photodynamic therapy (aPDT) is hampered by restricted access to bacterial communities embedded within the dense extracellular matrix of mature biofilms. Herein, a versatile photosensitizer nanoplatform (named MagTBO) was designed to overcome this obstacle by integrating toluidine-blue ortho (TBO) photosensitizer and superparamagnetic iron oxide nanoparticles (SPIONs) via a microemulsion method. In this study, we reported the preparation, characterization, and application of MagTBO for aPDT. In the presence of an external magnetic field, the MagTBO microemulsion can be driven and penetrate deep sites inside the biofilms, resulting in an improved photodynamic disinfection effect compared to using TBO alone. Besides, the obtained MagTBO microemulsions revealed excellent water solubility and stability over time, enhanced the aPDT performance against S. mutans and saliva-derived multispecies biofilms, and improved the TBO's biocompatibility. Such results demonstrate a proof-of-principle for using microemulsion as a delivery vehicle and magnetic field as a navigation approach to intensify the antibacterial action of currently available photosensitizers, leading to efficient modulation of pathogenic oral biofilms.

Size Dependence of Particulate Calcium Phosphate Fillers in Dental Resin Composites

Resin composites that consist of polymeric resins and functional fillers are commonly used as restorative materials for dental caries. Various types of calcium phosphates (CaPs) are studied as remineralizing fillers in the formulation of dental resin composites, which are generally inhibitory to demineralization of teeth, but the performance of resin composites has not yet been investigated comprehensively with respect to the size of CaP particles. In this study, the same tricalcium phosphate (TCP) particles within two different size ranges, the as-received TCP particles (TCP) and those resulted from grinding (TCP-G), were tested to determine the size dependence of CaP fillers in dental resin composites. The buffering capability, mechanical properties, ion release, antibacterial performance, and remineralization effect of TCP/TCP-G-containing composites were experimentally characterized and compared against two other commercial dental materials. The integration of micrometer-sized TCP particles resulted in a similar buffering effect and Ca²⁺/PO₄ ^3- release behaviors compared to the resin composite containing much smaller TCP-G particles. The flexural strength of the TCP-G resin composite was lower than that of the TCP composite after immersion in water for 30 days. However, the TCP-G composite facilitated crystal deposition toward better gap-closing performance at the dentin-composite interface. This study explored detailed insights about the size effect of CaP fillers, which is useful for the development of functional dental resin composites and their clinical translation.

A comprehensive review of the antibacterial activity of dimethylaminohexadecyl methacrylate (DMAHDM) and its influence on mechanical properties of resin-based dental materials

The repetitive restorative cycle should be avoided, aiming at the smallest number of restorations' replacements to ensure greater tooth longevity. Antibacterial materials associated with the control of caries etiological factors can help improve restoration's durability. This review aimed to analyze the results of in vitro studies that added Dimethylaminohexadecyl methacrylate (DMAHDM), an antibacterial monomer, to restorative materials. The PubMed, SCOPUS, Web of Science, and Biblioteca Virtual em Saúde databases were screened for studies published between 2015 and 2020. After full-text reading, 24 articles were included in the final sample. DMAHDM has demonstrated antibacterial efficacy against several bacteria related to dental caries and periodontal diseases, causing a transition in the biofilm balance without inducing resistance. When DMAHDM was included in acrylic resin, the material cytotoxicity increased, and changes in mechanical properties were observed. In contrast, resin composites had their mechanical properties maintained in most studies; however, toxicity was not examined. The association between DMAHDM and 2-methacryloyloxyethyl phosphorylcholine or silver nanoparticles improved the antibacterial effect. Besides, the association with nanoparticles of amorphous calcium phosphate or nanoparticles of calcium fluoride can provide remineralization capacity. There is a lack of information on the cytotoxicity and bacteria resistance induction, and further studies are needed to address this.

Novel low-shrinkage-stress bioactive nanocomposite with anti-biofilm and remineralization capabilities to inhibit caries

Background/purpose

A common reason for dental composite restoration failure is recurrent caries at the margins. Our objectives were to: (1) develop a novel low-shrinkage-stress, antibacterial and remineralizing resin composite; (2) evaluate the effects of dimethylaminohexadecyl methacrylate (DMAHDM) on mechanical properties, biofilm inhibition, calcium (Ca) and phosphate (P) ion release, degree of conversion, and shrinkage stress on the new low-shrinkage-stress resin composite for the first time.

Material and methods

The resin consisted of urethane dimethacrylate (UDMA) and triethylene glycol divinylbenzyl ether (TEG-DVBE) with high resistance to salivary hydrolytic degradation. Composites were made with 0%–8% of DMAHDM for antibacterial activity, and 20% of nanoparticles of amorphous calcium phosphate (NACP) for remineralization. Mechanical properties and Streptococcus mutans biofilm growth on composites were assessed. Ca and P ion releases, degree of conversion and shrinkage stress were evaluated.

Results

Adding 2–5% DMAHDM and 20% NACP into the low-shrinkage-stress composite did not compromise the mechanical properties (p > 0.05). The incorporation of DMAHDM greatly reduced S. mutans biofilm colony-forming units by 2–5 log and lactic acid production by 7 folds, compared to a commercial composite (p < 0.05). Adding 5% DMAHDM did not compromise the Ca and P ion release. The low-shrinkage-stress composite maintained a high degree of conversion of approximately 70%, while reducing the shrinkage stress by 37%, compared to a commercial control (p < 0.05).

Conclusion

The bioactive low-shrinkage-stress composite reduced the polymerization shrinkage stress, without compromising other properties. Increasing the DMAHDM content increased the antibacterial effect in a dose-dependent manner.

Intelligent pH-responsive dental sealants to prevent long-term microleakage

OBJECTIVES

Microleakage is a determinant factor of failures in sealant application. In this study, DMAEM (dodecylmethylaminoethyl methacrylate), a pH-responsive antibacterial agent, was incorporated into resin-based sealant for the first time. The objectives of this study were to: (1) investigate the long-term performance of DMAEM-modified sealants against oral microbial-aging; and (2) investigate the long-term preventive effect of DMAEM-modified sealants on microleakage.

METHODS

Depth-of-cure and cytotoxicity of DMAEM-modified sealants were measured. Then, an aging model using biofilm derived from the saliva of high caries experience children was conducted. After aging, microhardness and surface roughness were measured. Biofilm activity, lactic acid production and exopolysaccharide (EPS) production were measured. 16S rRNA gene sequencing were also performed. The effects of DMAEM on microleakage were tested using an in vitro microleakage assessment.

RESULTS

The addition of DMAEM with a mass fraction of 2.5-10% did not affect depth-of-cure values and cytotoxicity of sealants. Adding 2.5-10% DMAEM did not affect the surface roughness and microhardness after aging. Compared to control, adding 2.5-10% DMAEM reduced biofilm metabolic activity by more than 80%. The lactic acid production and EPS production were reduced by 50% in DMAEM groups. DMAEM-modified sealants maintained the microbial diversity of biofilm after aging, they also inhibited the growth of lactobacillus. The 5% and 10% DMAEM groups exhibited a significant reduction in microleakage compared to control.

SIGNIFICANCE

The long-term antibacterial activities against oral microbial-aging and the long-term microecosystem-regulating capabilities enabled DMAEM-modified sealant to prevent microleakage in sealant application and thus prevent dental caries.

Recent Progress in Antimicrobial Strategies for Resin-Based Restoratives

Repairing tooth defects with dental resin composites is currently the most commonly used method due to their tooth-colored esthetics and photocuring properties. However, the higher than desirable failure rate and moderate service life are the biggest challenges the composites currently face. Secondary caries is one of the most common reasons leading to repair failure. Therefore, many attempts have been carried out on the development of a new generation of antimicrobial and therapeutic dental polymer composite materials to inhibit dental caries and prolong the lifespan of restorations. These new antimicrobial materials can inhibit the formation of biofilms, reduce acid production from bacteria and the occurrence of secondary caries. These results are encouraging and open the doors to future clinical studies on the therapeutic value of antimicrobial dental resin-based restoratives. However, antimicrobial resins still face challenges such as biocompatibility, drug resistance and uncontrolled release of antimicrobial agents. In the future, we should focus on the development of more efficient, durable and smart antimicrobial dental resins. This article focuses on the most recent 5 years of research, reviews the current antimicrobial strategies of composite resins, and introduces representative antimicrobial agents and their antimicrobial mechanisms.

Sustained Antibacterial Effect and Wear Behavior of Quaternary Ammonium Contact-Killing Dental Polymers after One-Year of Hydrolytic Degradation

This study intended to investigate the long-term antibacterial effect, mechanical performance, and surface topography of new anticaries dental composites. While most artificial aging studies of dental resins lasted for 30–90 days, this study prolonged the water-aging to one year to be more clinically relevant. The base resin was loaded with dimethylaminohexadecyl methacrylate (DMAHDM) at 3 or 5 wt.% and nano-sized amorphous calcium phosphate (NACP) at 20 wt.%. Composites were subjected to one-year water storage and wear. Following water aging, samples were evaluated for flexural strength, elastic modulus, and microbiological assays. Biofilm plate counting method, metabolic assay, colorimetric quantification of lactic acid, and Baclight bacterial viability assay were measured after one year. Topography changes (ΔRa, ΔRq, ΔRv, ΔRt) were examined after wear and observed by scanning electron microscopy. Biofilm assays and topography changes data were analyzed via one-way ANOVA and Tukey’s tests. Mechanical properties and normalized data were verified using a t-test. The flexural strength values for the formulations that contained 5% DMAHDM-20% NACP, 3% DMAHDM, and 5% DMAHDM were reduced significantly (p < 0.05) in relation to the baseline but the values were still above the ISO standards. No significant differences were observed between the groups concerning the topography changes, except for the ΔRt, where there was a significant increase in the 5% DMAHDM-20% NACP group. All the groups demonstrated robust biofilm-inhibition, with slightly reduced antibacterial properties following water aging. The aged samples reduced the total microorganisms, total streptococci, and mutans streptococci by 1.5 to 3-log, compared to the experimental control. The new formulations containing DMAHDM and NACP were able to sustain the antibacterial performance after one-year of aging. Mechanical properties and surface topography were slightly affected over time.

Long-term antibacterial activity and cytocompatibility of novel low-shrinkage-stress, remineralizing composites

A low-shrinkage-stress (LSS), antibacterial and remineralizing nanocomposite was recently developed; however, validation of its long-term antibacterial potency in modulating human salivary-derived biofilm is an unmet need. This study aimed to evaluate the antibacterial effect of the bioactive LSS composite before and after aging in acidic solution for 90 days using a multi-species biofilm model, and to evaluate its cytotoxicity. The LSS composite consisted of urethane dimethacrylate (UDMA) and triethylene glycol divinylbenzyl ether (TEG-DVBE), 3% dimethylaminohexadecyl methacrylate (DMAHDM) and 20% nanoparticles of amorphous calcium phosphate (NACP). Biofilm colony-forming units (CFU), lactic acid production, and confocal laser scanning microscopy (3D biofilm) were evaluated before and after three months of aging. Cytotoxicity was assessed against human gingival fibroblasts (HGF). The new LSS composite presented the lowest biofilm CFU, lactic acid and biofilm biomass, compared to controls (n = 6, p < 0.05). Importantly, the new composite exhibited no significant difference in antibacterial performance before and after 90-day-aging, demonstrating long-term antibacterial activity (p > 0.1). The LSS antibacterial and remineralizing composite presented a low cell viability at original extract that has increased with further dilutions. In conclusion, this study spotlighted that the new bioactive composite not only had a low shrinkage stress, but also down-regulated the growth of oral biofilms, reduced acid production, maintained antibacterial activity after the 90-day-aging, and did not compromise the cytocompatibility.