Quantitative nano-mechanical mapping AFM-based method for elastic modulus and surface roughness measurements of model polymer infiltrated ceramics

In vitro profiling and molecular dynamics simulation studies of berberine loaded MCM-41 mesoporous silica nanoparticles to prevent neuronal apoptosis

Neuronal loss in Alzheimer's disease has been reported to display features of apoptosis, pyroptosis (programmed necrosis), or necroptosis. This study thoroughly examines the production and characterization of MCM-41 based berberine (BBR)-loaded porous silica nanoparticles (MSNs) by a modified Stöber method, focusing on their possible role in inhibiting the apoptotic process. Particle size, polydispersity index, morphology, drug loading, zeta potential, entrapment efficiency, and drug release were examined. The formulation was analyzed using various spectroscopic techniques. The surface area was computed by the Brunauer-Emmett-Teller plot. Computational models were developed for molecular dynamics simulation studies. A small PDI value indicated an even distribution of particles at nanoscale sizes (80-100 nm). Results from XRD and SEAD experiments confirmed the amorphous nature of BBR in nanoparticles. Nanoparticles had high entrapment (75.21 ± 1.55%) and drug loading (28.16 ± 2.5%) efficiencies. A negative zeta potential value (-36.861.1 mV) indicates the presence of silanol groups on the surface of silica. AFM findings reveal bumps due to the surface drug that contributed to the improved roughness of the MSNs-BBR surface. Thermal gravimetric analysis confirmed the presence of BBR in MSNs. Drug release was controlled by simple diffusion or quasi-diffusion. Molecular dynamics simulations confirmed the existence of diffused drug molecules. Cellular studies using SH-SY-5Y cells revealed dose-dependent growth inhibition. Fragmented cell nuclei and nuclear apoptotic bodies in DAPI-stained cells exposed to nanoparticles showed an increase in apoptotic cells. Flow cytometry analysis demonstrated a lower red-to-green ratio in SH-SY-5Y cells treated with nanoparticles. This suggests improved mitochondrial health, cellular viability restoration, and prevention of the apoptotic process. This study provides essential data on the synthesis and potential of MSNs loaded with BBR, which may serve as a viable therapeutic intervention for conditions associated with apoptosis.

The Contribution of Scanning Force Microscopy on Dental Research: A Narrative Review

Scanning force microscopy (SFM) is one of the most widely used techniques in biomaterials research. In addition to imaging the materials of interest, SFM enables the mapping of mechanical properties and biological responses with sub-nanometer resolution and piconewton sensitivity. This review aims to give an overview of using the scanning force microscope (SFM) for investigations on dental materials. In particular, SFM-derived methods such as force-distance curves (scanning force spectroscopy), lateral force spectroscopy, and applications of the FluidFM® will be presented. In addition to the properties of dental materials, this paper reports the development of the pellicle by the interaction of biopolymers such as proteins and polysaccharides, as well as the interaction of bacteria with dental materials.

Bacterial adhesion to composite resins produced by additive and subtractive manufacturing

The aim of this study was to evaluate the surface roughness and contact angle of composite resins produced by CAD/CAM milling and three-dimensional (3D) printing for permanent restorations as well as the adhesion of S. mutans and S. sanguinis bacteria to these composites. Three CAD/CAM milling composite resins (Vita Enamic-VE, Cerasmart-CE, Lava Ultimate-LU) and three 3D printing resins (Varseo Smile Crown plus-VSC, Saremco print Crowntech-SPC, Formlabs 3B Permanent crown-FLP) were selected. Twenty samples were prepared for each group. Using a contact profilometer, the surface roughness was determined, and an optical goniometer was used to quantify the contact angle. To evaluate the bacterial adhesion, composite specimens were immersed in mucin containing artificial saliva. All samples were incubated for 24 h at 37°C in 5% CO2. CFUs were determined by counting colonies after the incubation period. Surface roughness values of test samples were the highest in the Group VSC [0.46 (0.14) µm], whereas the lowest values were found in the Group LU [0.23 (0.05) µm]. There was no statistically significant difference between the groups in contact angle values (p > 0.05). The S. mutans adhesion extent on the Group SPC was statistically higher compared to all other materials with p < 0.05. For S. sanguinis, the lowest bacterial adhesion value was recorded in Group CE (3.00 × 104 CFU/ml) and statistically significant differences were found with Group VE and VSC (p < 0.05). Different digital manufacturing techniques and material compositions can affect the surface roughnesses of composite resins. All composite resin samples have hydrophobic characteristics. Microbial adhesion of the tested composite resins may be varied depending on the bacterial species. S. mutans showed much more adhesion to these materials than S. sanguinis.

Effect of thickness, translucency, and substrates on the masking ability of a polymer-infiltrated ceramic-network material

OBJECTIVE

The aim of this in vitro study is to evaluate the masking ability of polymer-infiltrated ceramic-network materials (PICN) with different translucencies and thicknesses on multiple types of substrates.

MATERIALS AND METHODS

Ceramic samples were prepared of VITA ENAMIC blocks in two different translucencies (2M2-T, 2M2-HT) in a thickness range of 0.5-2.5 mm (±0.05 mm). Layered specimens were obtained using composite substrates in nine shades and transparent try-in paste. Spectral reflectance of specimens was measured using a Konica Minolta CM-3720d spectrophotometer and D65 standard illumination. CIEDE2000 color difference (ΔE00 ) between two samples was evaluated using 50%:50% perceptibility and acceptability thresholds. Specular component of the reflection was examined with Specular Component Excluded (SCE) and Included (SCI) settings. Statistical evaluation was performed by linear regression analysis, Kruskal-Wallis test, and multiplicative effect analysis.

RESULTS

An increase in thickness of 0.5 mm reduces ΔE00 of HT samples to 73.5%, of T samples to 60.5% (p < 0.0001). Five substrates with HT specimens, and three substrates with T specimens had significantly different results from average (p < 0.05). There is a significant difference between SCE and SCI data depending on the wavelength (p < 0.0001).

CONCLUSIONS

Masking ability of PICN materials is influenced by the thickness and translucency of the ceramic, and by the substrate. Reflection of the examined PICN material is characterized by both diffuse and specular reflection.

CLINICAL SIGNIFICANCE

Although PICN materials have been available on the market for 10 years now, there is a lack of information regarding their masking ability. Acquiring in-depth data and thereby practical experience of the factors affecting the esthetics of PICN materials is essential for creating perfectly lifelike restorations.

Evaluation of Physical-Chemical Properties of Contemporary CAD/CAM Materials with Chromatic Transition "Multicolor"

The use of materials for computer-aided design/computer-aided manufacturing (CAD/CAM) has been rapidly increasing in daily practice. However, one of the main issues regarding modern CAD/CAM materials is their aging in the oral environment, which may lead to significant changes in their overall properties. The aim of this study was to compare the flexural strength, water sorption, cross-link density (softening ratio%), surface roughness, and SEM analysis of three modern CAD/CAM "multicolor" composites. Grandio (Grandio disc multicolor-VOCO GmbH, Cuxhaven, Germany), Shofu (Shofu Block HC-Shofu Inc., Kyoto, Japan), and Vita (Vita Enamic multiColor-Vita Zahnfabrik, Bad Sackingen, Germany) were tested in this study. They were prepared in stick-shaped specimens and submitted to different tests after several aging protocols, such as thermocycling and mechanical cycle loading challenge. Further disc-shaped specimens were also created and tested for water sorption, cross-link density, surface roughness, and SEM ultramorphology, before and after storage in an ethanol-based solution. For flexural strength and ultimate tensile strength, Grandio showed the greatest values both at baseline and after aging (p < 0.05). Grandio and Vita Enamic presented the highest modulus of elasticity and the lowest water sorption (p < 0.05). A significant reduction (p < 0.05) in microhardness after ethanol storage (softening ratio%) was observed especially in Shofu. Grandio had the lowest roughness parameters compared to the other tested CAD/CAM materials, while ethanol storage significantly increased the Ra and RSm values in Shofu (p < 0.05). Despite the comparable modulus of elasticity of Vita and Grandio, this latter showed greater flexural strength and ultimate tensile strength both at baseline and after aging. Hence, Grandio and Vita Enamic may be employed for the anterior teeth and for those restorations requiring load-bearing capacity. Conversely, aging seems to affect several properties of Shofu, so its use for permanent restorations should be well-pondered based on the clinical situation.

Pre-cementation treatment of glass-ceramics with vacuum impregnated resin coatings

OBJECTIVE

The study aimed to investigate the effectiveness of a vacuum impregnation process to eliminate the porosity at the ceramic-resin interface to optimize the reinforcement of a glass-ceramic by resin cementation.

METHODS

100 leucite glass-ceramic disks (1.0 ± 0.1 mm thickness) were air-abraded, etched with 9.6 % HF acid, and silanated. Specimens were randomly allocated to 5 groups (n = 20). Group A received no further treatment (uncoated control). Groups B and D were resin-coated under atmospheric pressure, whereas groups C and E were resin-coated using vacuum impregnation. The polymerized resin-coating surfaces of specimens in groups B and C were polished to achieve a resin thickness of 100 ± 10 µm, while in groups D and E no resin-coating modification was performed prior to bi-axial flexure strength (BFS) determination. Optical microscopy was undertaken on the fracture fragments to identify the failure mode and origin. Comparisons of BFS group means were made by a one-way analysis of variance (ANOVA) and post-hoc Tukey test at α = 0.05.

RESULTS

All resin-coated sample groups (B-E) showed a statistically significant increase in mean BFS compared with the uncoated control (p < 0.01). There was a significant difference in BFS between the ambient and vacuum impregnated unpolished groups (D and E) (p < 0.01), with the greatest strengthening achieved using a vacuum impregnation technique.

SIGNIFICANCE

Results highlight the opportunity to further develop processes to apply thin conformal resin coatings, applied as a pre-cementation step to strengthen dental glass-ceramics.

AFM Analysis of a Three-Point Flexure Tested, 3D Printing Definitive Restoration Material for Dentistry

Background: Three-dimensional printing is a rapidly developing technology across all industries. In medicine recent developments include 3D bioprinting, personalized medication and custom prosthetics and implants. To ensure safety and long-term usability in a clinical setting, it is essential to understand material specific properties. This study aims to analyze possible surface changes of a commercially available and approved DLP 3D printed definitive restoration material for dentistry after three-point flexure testing. Furthermore, this study explores whether Atomic Force Microscopy (AFM) is a feasible method for examination of 3D printed dental materials in general. This is a pilot study, as there are currently no studies that analyze 3D printed dental materials using an AFM. Methods: The present study consisted of a pretest followed by the main test. The resulting break force of the preliminary test was used to determine the force used in the main test. The main test consisted of atomic force microscopy (AFM) surface analysis of the test specimen followed by a three-point flexure procedure. After bending, the same specimen was analyzed with the AFM again, to observe possible surface changes. Results: The mean root mean square (RMS) roughness of the segments with the most stress was 20.27 nm (±5.16) before bending, while it was 26.48 nm (±6.67) afterward. The corresponding mean roughness (Ra) values were 16.05 nm (±4.25) and 21.19 nm (±5.71) Conclusions: Under three-point flexure testing, the surface roughness increased significantly. The p-value for RMS roughness was p = 0.003, while it was p = 0.006 for Ra. Furthermore, this study showed that AFM surface analysis is a suitable procedure to investigate surface changes in 3D printed dental materials.

Effect of Sintering and Infiltration Conditions on Nanoscale Dual Network SiO2/Polymethyl Metacrylate Composites Mimicking Human Enamel

OBJECTIVE

The aim of this study was to achieve facile sintering conditions and rapid penetration of organic substances into the structure of sintered silica network on the nano-scale in order to prepare polymer infiltrated ceramic network mimicking human enamel.

METHODS

Stepwise temperature programming (stepwise isothermal firing) was used to create a cohesive ceramic network containing interconnected pores, which is essential to provide polymer/ceramic dual networks. Liquid phase self-penetration, ultrasonic irradiation assisted liquid phase penetration and vapor phase penetration routes were used to infiltrate methyl methacrylate monomers and benzoyl peroxide reagent into the porous silica blocks.

RESULTS

The use of stepwise isothermal firing route, in comparison with high temperature sintering methods, significantly reduces the time and temperature required for the preliminary preparation of the SiO₂ samples and reaching the appropriate interconnected porous structure. The most appropriate method for monomer and oxidant reagents infiltration is to use liquid phase infiltration assisted by ultrasound irradiation of pre-sintered nano-silica blocks. It was found that the amount of infiltrated monomer and oxidizing agent, degree of conversion of the monomer to the polymer and surface hardness of the samples strongly depend on the infiltration route.

CLINICAL SIGNIFICANCE

The use of inexpensive silica nanoparticles and low temperature sintering and the use of ultrasound waves to quickly and effectively penetrate methyl methacrylate monomers and increase the polymerization efficiency lead to the preparation of composites with a transparent appearance and mechanical properties similar to human tooth enamel.