Partial replacement effect of montmorillonite with cellulose nanowhiskers on polylactic acid nanocomposites

Structure and Properties of Polylactic Acid Biocomposite Films Reinforced with Cellulose Nanofibrils

Polylactic acid (PLA) is one of the most promising biodegradable and recyclable thermoplastic biopolymer derived from renewable feedstock. Nanocellulose reinforced PLA biocomposites have received increasing attention in academic and industrial communities. In the present study, cellulose nanofibrils (CNFs) was liberated by combined enzymatic pretreatment and high-pressure homogenization, and then subsequently incorporated into the PLA matrix to synthesize PLA/CNF biocomposite films via solution casting and melt compression. The prepared PLA/CNF biocomposite films were characterized in terms of transparency (UV-Vis spectroscopy), chemical structure (attenuated total reflectance-Fourier transform infrared, ATR-FTIR; X-ray powder diffraction, XRD), thermal (thermogravimetric analyzer, TGA; differential scanning calorimetry, DSC), and tensile properties. With 1.0–5.0 wt % additions of CNF to the PLA matrix, noticeable improvements in thermal and physical properties were observed for the resulting PLA/CNF biocomposites. The 2.5 wt % addition of CNF increased the tensile strength by 8.8%. The T_onset (initial degradation temperature) and T_max (maximum degradation temperature) after adding 5.0 wt % CNF was increased by 20 °C, and 10 °C, respectively in the nitrogen atmosphere. These improvements were attributed to the good dispersibility and improved interfacial interaction of CNF in the PLA matrix.

Effects of molecular weight and crystallizability of polylactide on the cellulose nanocrystal dispersion quality in their nanocomposites

This study investigated how cellulose nanocrystals (CNC) dispersion quality and its percolation network formation could be influenced when using polylactide (PLA) with various molecular weights and crystallizability. In this context, systematic rheological experiments were conducted on PLA/CNC nanocomposites prepared through solution casting method using dimethylformamide (DMF) as the solvent. It was found that lower CNC percolation concentrations could be obtained when a PLA matrix possesses lower molecular weight as the shorter chains and CNCs interpenetration could be facilitated during their dissolution in the solvent. On the other hand, the CNC percolation concentration was further lowered when the PLA with higher crystallizability was used. During the solvent evaporation step that occurred at 85 °C, the isothermal heterogeneous crystallization of PLA around the dispersed CNCs could prevent the driving force of the CNCs towards their re-agglomeration. Therefore, the finest CNC dispersion was appeared in the highly crystallizable low molecular weight PLA through which the rheological properties were dramatically improved and the thermal stability was significantly extended to higher temperatures. The crystallization behavior of the prepared nanocomposites was also analyzed using differential scanning calorimeter and X-ray diffractometer. The thermal degradation behavior of the PLA/CNC nanocomposites were examined through thermogravimetric and rheological analysis.