Preparation and characterization of poly(3-hydroxybutyrate)/chitosan composite films using acetic acid as a solvent

Better Ce (III) Sorption Properties of Unprocessed Chitinous Waste from Hermetia illucens than Commercial Chitosans

Insect farming generates a new type of chitinous waste in the form of dead specimens that have died of natural causes and insect moults (puparia), particularly large amounts of which are generated during the rearing of holometabolous insects. Following the circular economy paradigm, we treated waste in the form of puparia and dead adults of H. illucens as a valuable material, i.e., as sources of chitin, and tested it as a sorbent for cerium, a lanthanide of great industrial importance. For comparison, non-treated, raw insect materials and commercial chitosans were also investigated. Chitin extracted from H. illucens showed an adsorption capacity at the same level as commercially available, marine-source chitin (approximately 6 mg Ce·g-1). However, more interestingly, raw materials exhibited much higher adsorption capacities-dead adults were similar to commercial chitosans (approximately 32 mg Ce·g-1), while puparia demonstrated twice the performance (approximately 60 mg Ce·g-1). This indicates that unprocessed waste can be used as environmentally friendly, cost-effective Ce biosorbents with comparable or even better sorption capacity than chitosans, whose production requires intense chemical processing.

The Effect of Acetic Acid as a Solvent on the Structure and Properties of Poly(3-hydroxybutyrate)-Based Dried Gels

Poly(3-hydroxybutyrate) (PHB) is a microbially derived polyhydroxyalkanoate that is widely used in biomedical applications. In this study, we investigated the use of acetic acid (aa) as an alternative environmentally friendly solvent for the preparation of gels from PHB (PHB aa) and compared their characteristics with PHB products dissolved in chloroform (PHB chl) using such methods as DSC, FTIR, SEM, rheometry, biodegradation, and cytocompatibility assay. A slight decrease in the degree of the crystallinity of the PHB from 61% to 50.8% was found when the acetic acid was used. This resulted in a greater mass loss for the PHB aa (11%) during enzymatic degradation over 180 days. Gels prepared from PHB in the different solvents showed differences in the microstructure and porosity of the samples, which affected their viscoelastic properties. The storage modulus (G') for the PHB aa gels was higher by 35% compared to that for the PHB chl, and Young's modulus in compression was 101.5 and 41.3 kPa for the PHB aa and PHB chl, respectively. The porosity of the PHB aa was 97.7%, which was 5.2% higher than that for the PHB chl. The presence of low molecular weight polymers in the PHB aa had an effect on mesenchymal stem cells' viability, expressed as a threefold increase in the number of attached cells after 7 days of incubation compared to the PHB chl. Thus, the proposed method of PHB-based materials' preparation is a promising, more environmentally friendly analog of the extensively used method of preparation from chloroform.

Evaluation of Chemical and Biological Properties of Biodegradable Composites Based on Poly(3-hydroxybutyrate) and Chitosan

In this study, composite films and scaffolds of polyester poly(3-hydroxybutyrate) and polysaccharide chitosan obtained via a simple and reproducible blending method using acetic acid as a solvent were considered. The degradation process of the films was studied gravimetrically in a model biological medium in the presence of enzymes in vitro for 180 days. The kinetics of weight reduction depended on the amount of chitosan in the composition. The biocompatibility of the films was evaluated using the Alamar blue test and fluorescence microscopy. The materials were non-cytotoxic, and the addition of poly(3-hydroxybutyrate) to chitosan improved its matrix properties on mesenchymal stem cells. Then, the 3D composites were prepared by freeze-drying. Their structure (using SEM), rheological behavior, moisture absorption, and porosity were investigated. The addition of different amounts of chitosan allowed us to vary the chemical and biological properties of poly(3-hydroxybutyrate) materials and their degradation rate, which is extremely important in the development of biomedical poly(3-hydroxybutyrate) materials, especially implantable ones.