Limited Evidence Supports Polished Monolithic Zirconia as Less Likely to Cause Antagonist Enamel Wear Compared to Other Prosthetic Materials

Effect of ceramic materials and tooth preparation design on computer-aided design and computer-aided manufacturing endocrown adaptation and retentive strength: An in vitro study

OBJECTIVES

To evaluate how various tooth preparation designs impact the adaptation-both at the margins and internally-and the retentive strength of computer-aided design and computer-aided manufacturing (CAD/CAM) produced endocrowns.

MATERIALS AND METHODS

60 extracted human mandibular first molars were endodontically treated and assigned into three groups (n = 20) according to the tooth preparation design: Group N: butt joint design, Group F and F1 received 1- and 2-mm circumferential ferrule preparation, respectively. Endocrowns were milled using either lithium disilicate glass-ceramic (IPS emax ceramic) or monolithic zirconia. The internal and marginal adaptation of the endocrowns were evaluated using the replica technique. After cementation, the endocrowns of all test groups were dislodged axially at 0.5 mm/min using a universal testing machine. A 2-way ANOVA and the independent samples t-test (α = .05) were performed to statistically analyze the data.

RESULTS

The effect of changing the design of the tooth preparation (butt joint, ferrule) on the marginal and internal gap was shown to be statistically significant (p < .05); the lower gap values were recorded at the axial followed by cervical, marginal, and pulpal floor walls in both ceramic groups regardless of the teeth preparation design. The ANOVA test revealed similar average removal forces and stresses for the two types of tested ceramic materials.

CONCLUSION

IPS emax ceramic adapted better than monolithic zirconia ceramic, regardless of the preparation design. Ferrule preparation design is more retentive than butt joint preparation, regardless of the type of ceramic material used.

Revolution of Current Dental Zirconia: A Comprehensive Review

The aim of this article is to comprehensively review the revolution of dental zirconia (Zir), including its types, properties, applications, and cementation procedures. A comprehensive search of PubMed and Embase was conducted. The search was limited to manuscripts published in English. The final search was conducted in October 2021. Newly developed monolithic Zir ceramics have substantially enhanced esthetics and translucency. However, this material must be further studied in vitro and in vivo to determine its long-term ability to maintain its exceptional properties. According to the literature, monolithic translucent Zir has had promising results and a high survival rate. Thus, the utilization of this material is indicated when strength and esthetics are needed. Both the materials and methods used for cementation of monolithic Zir have significantly improved, encouraging dentists to use this material, especially when a conservative approach is required. Zir restorations showed promising outcomes, particularly for monolithic Zir crowns supported with implant and fixed dental prostheses.