Hsu CH, Ng DQ, Lin YP. Release of lead, copper, zinc from the initial corrosion of brass water meter in drinking water: Influences of solution composition and electrochemical characterization. ENVIRONMENTAL POLLUTION (BARKING, ESSEX : 1987) 2024; 352:124154. [PMID: 38750810 DOI: 10.1016/j.envpol.2024.124154] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 01/10/2024] [Revised: 04/13/2024] [Accepted: 05/12/2024] [Indexed: 05/18/2024]
Abstract
Corrosion of brass plumbing materials may lead to metal release and deteriorate the drinking water quality. In this study, the initial corrosion of brass coupon cut from commercially available water meter was investigated. High rates of Pb, Cu and Zn release from the brass coupon were found during the early stage of corrosion (0-5 d) due to general corrosion and galvanic corrosion. The corrosion current density (Icorr) increased and resistance (RF) decreased during this period indicating that severe corrosion had occurred. In a later stage (5-30 d), a decreased Icorr and an increased RF were observed due to the development of a denser layer of Pb and Cu corrosion products which regulated the release of soluble Pb and Cu. The release of Zn continued and no significant Zn precipitation was found. Overall, particulate Pb, particulate Cu and soluble Zn dominated in the metal release during the initial corrosion of brass. The release of Pb, Cu and Zn was enhanced by a lower pH. Free chlorine was found to slightly reduce the release of Pb but promote the release of Cu and Zn. The presence of Pb on the brass surfaces was found to alleviate the dezincification process. A conceptual model based on metal release profile and electrochemical characterization was proposed to describe the initial corrosion of brass in typical drinking water.
Collapse
Affiliation(s)
- Ching-Hsuan Hsu
- Graduate Institute of Environmental Engineering, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei, 10617, Taiwan.
| | - Ding-Quan Ng
- Department of Environmental Engineering and Management, Chaoyang University of Technology, No. 168, Jifeng E. Rd, Wufeng District, Taichung, 41349, Taiwan
| | - Yi-Pin Lin
- Graduate Institute of Environmental Engineering, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei, 10617, Taiwan; NTU Research Center for Future Earth, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei, 10617, Taiwan.
| |
Collapse
|
2
|
Guo X, Ji X, Liu Z, Feng Z, Zhang Z, Du S, Li X, Ma J, Sun Z. Complex impact of metals on the fate of disinfection by-products in drinking water pipelines: A systematic review. WATER RESEARCH 2024; 261:121991. [PMID: 38941679 DOI: 10.1016/j.watres.2024.121991] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 04/16/2024] [Revised: 06/14/2024] [Accepted: 06/21/2024] [Indexed: 06/30/2024]
Abstract
Metals in the drinking water distribution system (DWDS) play an important role on the fate of disinfection by-products (DBPs). They can increase the formation of DBPs through several mechanisms, such as enhancing the proportion of reactive halogen species (RHS), catalysing the reaction between natural organic matter (NOM) and RHS through complexation, or by increasing the conversion of NOM into DBP precursors. This review comprehensively summarizes these complex processes, focusing on the most important metals (copper, iron, manganese) in DWDS and their impact on various DBPs. It organizes the dispersed 'metals-DBPs' experimental results into an easily accessible content structure and presents their underlying common or unique mechanisms. Furthermore, the practically valuable application directions of these research findings were analysed, including the toxicity changes of DBPs in DWDS under the influence of metals and the potential enhancement of generalization in DBP model research by the introduction of metals. Overall, this review revealed that the metal environment within DWDS is a crucial factor influencing DBP levels in tap water.
Collapse
Affiliation(s)
- Xinming Guo
- State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150096, China
| | - Xiaoyue Ji
- State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150096, China
| | - Zihan Liu
- State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150096, China
| | - Zhuoran Feng
- State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150096, China
| | - ZiFeng Zhang
- International Joint Research Center for Persistent Toxic Substances (IJRC-PTS), State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150090, China
| | - Shuang Du
- Institute of NBC Defense. PLA Army, P.O.Box1048, Beijing 102205 China
| | - Xueyan Li
- Suzhou University Science & Technology, School of Environmental Science & Engineering, Suzhou 215009, China
| | - Jun Ma
- State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150096, China
| | - Zhiqiang Sun
- State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150096, China.
| |
Collapse
|
3
|
Wang JW, Yu CH, Hou WC, Hsiao TC, Lin YP. Characterization of Fe-Containing and Pb-Containing Nanoparticles Resulting from Corrosion of Plumbing Materials in Tap Water Using a Hyphenated ATM-DMA-spICP-MS System. ENVIRONMENTAL SCIENCE & TECHNOLOGY 2024; 58:2038-2047. [PMID: 38241248 PMCID: PMC10832032 DOI: 10.1021/acs.est.3c07592] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Subscribe] [Scholar Register] [Received: 09/27/2023] [Revised: 12/15/2023] [Accepted: 01/05/2024] [Indexed: 01/21/2024]
Abstract
Single-particle inductively coupled plasma mass spectrometry (spICP-MS) has been used to characterize metallic nanoparticles (NPs) assuming that all NPs are spherical and composed of pure element. However, environmental NPs generally do not meet these criteria, suggesting that spICP-MS may underestimate their true sizes. This study employed a system hyphenating the atomizer (ATM), differential mobility analyzer (DMA), and spICP-MS to characterize metallic NPs in tap water. Its performance was validated by using reference Au nanoparticles (AuNPs) and Ag-shelled AuNPs. The hyphenated system can determine the actual size and metal composition of both NPs with additional heating after ATM, while stand-alone spICP-MS misidentified the Ag-shelled AuNPs as smaller individual AgNPs and AuNPs. Dissolved metal ions could introduce artifact NPs after heating but could be eliminated by centrifugation. The hyphenated system was applied to characterize Fe-containing and Pb-containing NPs resulting from the corrosion of plumbing materials in tap water. The mode sizes of Fe-containing and Pb-containing NPs were determined to be 110 and 100 nm and the particle number concentrations were determined to be 4.99 × 107 and 1.40 × 106 #/mL, respectively. Cautions should be paid to potential changes in particle size induced by heating for metallic NPs with a low melting point or a high organic content.
Collapse
Affiliation(s)
- Jing-Wen Wang
- Graduate
Institute of Environmental Engineering, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei 10617, Taiwan
| | - Chia-Hung Yu
- Graduate
Institute of Environmental Engineering, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei 10617, Taiwan
| | - Wen-Che Hou
- Department
of Environmental Engineering, National Cheng
Kung University, No. 1 University Road, Tainan City 70101, Taiwan
| | - Ta-Chih Hsiao
- Graduate
Institute of Environmental Engineering, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei 10617, Taiwan
| | - Yi-Pin Lin
- Graduate
Institute of Environmental Engineering, National Taiwan University, No. 1, Sec. 4, Roosevelt Road, Taipei 10617, Taiwan
- NTU
Research Center for Future Earth, National
Taiwan University, No.
1, Sec. 4, Roosevelt Road, Taipei 10617, Taiwan
| |
Collapse
|
4
|
Oliveira IM, Gomes IB, Plácido A, Simões LC, Eaton P, Simões M. The impact of potassium peroxymonosulphate and chlorinated cyanurates on biofilms of Stenotrophomonas maltophilia: effects on biofilm control, regrowth, and mechanical properties. BIOFOULING 2023; 39:691-705. [PMID: 37811587 DOI: 10.1080/08927014.2023.2254704] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 06/07/2023] [Accepted: 08/27/2023] [Indexed: 10/10/2023]
Abstract
The activity of two chlorinated isocyanurates (NaDCC and TCCA) and peroxymonosulphate (OXONE) was evaluated against biofilms of Stenotrophomonas maltophilia, an emerging pathogen isolated from drinking water (DW), and for the prevention of biofilm regrowth. After disinfection of pre-formed 48 h-old biofilms, the culturability was reduced up to 7 log, with OXONE, TCCA, and NaDCC showing more efficiency than free chlorine against biofilms formed on stainless steel. The regrowth of biofilms previously exposed to OXONE was reduced by 5 and 4 log CFU cm-2 in comparison to the unexposed biofilms and biofilms exposed to free chlorine, respectively. Rheometry analysis showed that biofilms presented properties of viscoelastic solid materials, regardless of the treatment. OXONE reduced the cohesiveness of the biofilm, given the significant decrease in the complex shear modulus (G*). AFM analysis revealed that biofilms had a fractured appearance and smaller bacterial aggregates dispersed throughout the surface after OXONE exposure than the control sample. In general, OXONE has been demonstrated to be a promising disinfectant to control DW biofilms, with a higher activity than chlorine. The results also show the impact of the biofilm mechanical properties on the efficacy of the disinfectants in biofilm control.
Collapse
Affiliation(s)
- I M Oliveira
- LEPABE - Laboratory for Process Engineering, Environment, Biotechnology and Energy, Faculty of Engineering, University of Porto, Porto, Portugal
- ALiCE - Associate Laboratory in Chemical Engineering, Faculty of Engineering, University of Porto, Porto, Portugal
| | - I B Gomes
- LEPABE - Laboratory for Process Engineering, Environment, Biotechnology and Energy, Faculty of Engineering, University of Porto, Porto, Portugal
- ALiCE - Associate Laboratory in Chemical Engineering, Faculty of Engineering, University of Porto, Porto, Portugal
| | - A Plácido
- REQUIMTE/LAQV - Associated Laboratory for Green Chemistry of the Network of Chemistry and Technology, Department of Chemistry and Biochemistry, Faculty of Sciences, University of Porto, Porto, Portugal
| | - L C Simões
- CEB - Centre of Biological Engineering, University of Minho, Braga, Portugal
- LABBELS - Associate Laboratory in Biotechnology, Bioengineering and Microelectromechanical Systems, Braga/Guimarães, Portugal
| | - P Eaton
- REQUIMTE/LAQV - Associated Laboratory for Green Chemistry of the Network of Chemistry and Technology, Department of Chemistry and Biochemistry, Faculty of Sciences, University of Porto, Porto, Portugal
- The Bridge, School of Chemistry, University of Lincoln, Lincoln, UK
| | - M Simões
- LEPABE - Laboratory for Process Engineering, Environment, Biotechnology and Energy, Faculty of Engineering, University of Porto, Porto, Portugal
- ALiCE - Associate Laboratory in Chemical Engineering, Faculty of Engineering, University of Porto, Porto, Portugal
| |
Collapse
|
5
|
Chang L, Lee JHW, Fung YS. Prediction of lead leaching from galvanic corrosion of lead-containing components in copper pipe drinking water supply systems. JOURNAL OF HAZARDOUS MATERIALS 2022; 436:129169. [PMID: 35739706 DOI: 10.1016/j.jhazmat.2022.129169] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 02/08/2022] [Revised: 05/13/2022] [Accepted: 05/14/2022] [Indexed: 06/15/2023]
Abstract
Galvanic corrosion is one of the main reasons for pipe degradation and lead contamination in drinking water systems. The electrical connection of dissimilar metals in corrosive tap water accelerates the dissolution rate of lead from leaded materials. This paper reports an electrochemistry based model to predict lead leaching from a copper pipe fitted with leaded connections. The corrosion of lead at the metal-electrolyte interface depends on the charge transfer and the electric field across the interface. The electric potential field and the mass transport process are dynamically coupled for corrosion propagation in stagnant water; they are respectively governed by the conservation of charge and reactant mass. Using polarization parameters for the electrodes as a function of concentration of oxidizing agents, a dynamic electrochemical model is developed to predict lead leaching from galvanic corrosion. The predicted lead and copper leaching curves are in good agreement with the experimental data for a lead-soldered coupled copper pipe, a brass valve coupled copper pipe, and a pure copper pipe. The findings offer a quantitative understanding on galvanic corrosion in drinking water supply systems and a practical modeling framework for prediction of lead leaching in tap water as a function of stagnation time.
Collapse
Affiliation(s)
- Lu Chang
- Department of Civil and Environmental Engineering, The Hong Kong University of Science and Technology, Clear Water Bay, Hong Kong, China
| | - Joseph H W Lee
- Macao Environmental Research Institute, Macau University of Science and Technology, Taipa, Macao, China.
| | - Y S Fung
- Department of Chemistry, The University of Hong Kong, Pokfulam Road, Hong Kong, China
| |
Collapse
|
6
|
Zhu G, Li Y, Zhang G. Interaction between crevice and galvanic corrosion of X65 carbon steel in the CO2-saturated NaCl solution under the coupling of crevice and galvanic effects. J Electroanal Chem (Lausanne) 2022. [DOI: 10.1016/j.jelechem.2022.116482] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 10/18/2022]
|
7
|
Zhang H, Liu D, Zhao L, Wang J, Xie S, Liu S, Lin P, Zhang X, Chen C. Review on corrosion and corrosion scale formation upon unlined cast iron pipes in drinking water distribution systems. J Environ Sci (China) 2022; 117:173-189. [PMID: 35725069 DOI: 10.1016/j.jes.2022.04.024] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/24/2022] [Revised: 04/12/2022] [Accepted: 04/21/2022] [Indexed: 06/15/2023]
Abstract
The qualified finished water from water treatment plants (WTPs) may become discolored and deteriorated during transportation in drinking water distribution systems (DWDSs), which affected tap water quality seriously. This water stability problem often occurs due to pipe corrosion and the destabilization of corrosion scales. This paper provides a comprehensive review of pipe corrosion in DWDSs, including corrosion process, corrosion scale formation, influencing factors and monitoring technologies utilized in DWDSs. In terms of corrosion process, corrosion occurrence, development mechanisms, currently applied assays, and indices used to determine the corrosion possibility are summarized, as well as the chemical and bacterial influences. In terms of scale formation, explanations for the nature of corrosion and scale formation mechanisms are discussed and its typical multilayered structure is illustrated. Furthermore, the influences of water quality and microbial activity on scale transformation are comprehensively discussed. Corrosion-related bacteria at the genus level and their associated corrosion mechanism are also summarized. This review helps deepen the current understanding of pipe corrosion and scale formation in DWDSs, providing guidance for water supply utilities to ensure effective measures to maintain water quality stability and guarantee drinking water safety.
Collapse
Affiliation(s)
- Haiya Zhang
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, School of Environment, Tsinghua University, Beijing 100084, China; State Key Laboratory of Environmental Criteria and Risk Assessment, Chinese Research Academy of Environmental Sciences, Beijing 100012, China
| | - Dibo Liu
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, School of Environment, Tsinghua University, Beijing 100084, China
| | - Lvtong Zhao
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, School of Environment, Tsinghua University, Beijing 100084, China
| | - Jun Wang
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, School of Environment, Tsinghua University, Beijing 100084, China; Research Institute for Environmental Innovation (Suzhou), Tsinghua, Suzhou 215163, China
| | - Shuguang Xie
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, College of Environmental Sciences and Engineering, Peking University, Beijing 100871, China
| | - Shuming Liu
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, School of Environment, Tsinghua University, Beijing 100084, China
| | - Pengfei Lin
- Research Institute for Environmental Innovation (Suzhou), Tsinghua, Suzhou 215163, China
| | - Xiaojian Zhang
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, School of Environment, Tsinghua University, Beijing 100084, China; Research Institute for Environmental Innovation (Suzhou), Tsinghua, Suzhou 215163, China
| | - Chao Chen
- State Key Joint Laboratory of Environmental Simulation and Pollution Control, School of Environment, Tsinghua University, Beijing 100084, China; Research Institute for Environmental Innovation (Suzhou), Tsinghua, Suzhou 215163, China.
| |
Collapse
|