Effects of water and microbial-based aging on the performance of three dental restorative materials

Formulation of arginine-loaded mesoporous silica nanoparticles (Arg@MSNs) modified orthodontic adhesive

OBJECTIVES

The objective of this study was to synthesize arginine loaded mesoporous silica nanoparticles (Arg@MSNs), develop a novel orthodontic adhesive using Arg@MSNs as modifiers, and investigate the adhesive performance, antibacterial activity, and biocompatibility.

METHODS

Arg@MSNs were synthesized by immobilizing arginine into MSNs and characterized using transmission electron microscope (TEM), dynamic light scattering (DLS), and Fourier Transform Infrared Spectrometer (FT-IR). Arg@MSNs were incorporated into Transbond XT adhesive with different mass fraction to form functional adhesives. The degree of conversion (DC), arginine release behavior, adhesive performance, antibacterial activity against Streptococcus mutans biofilm, and cytotoxicity were comprehensively evaluated.

RESULTS

TEM, DLS, and FT-IR characterizations confirmed the successful preparation of Arg@MSNs. The incorporation of Arg@MSNs did not significantly affect DC and exhibited clinically acceptable bonding strength. Compared to the commercial control, the Arg@MSNs modified adhesives greatly suppressed the metabolic activity and polysaccharide production while increased the biofilm pH values. The cell counting kit (CCK)-8 test indicated no cytotoxicity.

CONCLUSIONS

The novel orthodontic adhesive containing Arg@MSNs exhibited significantly enhanced antibacterial activities and inhibitory effects on acid production compared to the commercial adhesive without compromising their bonding strength or biocompatibility.

CLINICAL SIGNIFICANCE

The novel orthodontic adhesive containing Arg@MSNs exhibits potential clinical benefits in preventing demineralization of enamel surfaces around or beneath orthodontic brackets due to its enhanced antibacterial activities and acid-producing inhibitory effects.

Effect of Prolonged Water Aging on the Bond Strength and Marginal Seal of Three Novel Restorative Materials

AIM

To assess and contrast the shear bond strength (SBS) and microbial leakage of Cention-N, Fuji IX, and nanohybrid composite restorative materials after being exposed to prolonged water aging.

MATERIALS AND METHODS

A total of 30 self-curing acrylic blocks were prepared for SBS analysis. Extracted teeth were affixed on the acrylic resin to incorporate the root section. To expose the occlusal dentin, 3 mm of the midcoronal portion was sectioned. The sectioned samples were allocated into the following three groups: Group I: Fuji IX; group II: Filtek Z350; and group III: Cention-N. Cylindrical plastic tubing was used to place each material as directed by the manufacturer and water aging for 7, 14, and 28 days at 37°C. Also, a universal testing machine (UTM) was utilized for testing followed by a scanning electron microscope (SEM). For microleakage analysis, a total of 30 class-V cavities were prepared. The prepared samples were allotted to respective groups; Later, 200 thermocycles at 5°C and 55°C were applied for 30 seconds to mimic the oral environment. The root apices sealed with sticky wax and the exception of a 1-mm around the edges of the restorations were then painted twice with clear nail varnish and submerged in 0.5% basic fuchsin dye at 37°C. Samples were washed, dried, and sectioned longitudinally followed by stereomicroscopic evaluation.

RESULTS

Groups I (0.083), group II (0.083), and group III (0.102) did not show significant variation in the SBS after water degradation. At the end of 28 days of water aging, group III showed 33.3% adhesive failure and 66.7% mixed failure mode. For marginal leakage in group III, the mean and standard deviation (SD) were 334.90 ± 418.454 with the p = 0.001 showing a significant difference compared to groups I and II.

CONCLUSION

Compared to nanohybrid composite and Fuji IX, Cention-N showed a superior SBS after being exposed to water aging and exhibited lesser marginal leakage.

CLINICAL SIGNIFICANCE

Cention-N outperformed in its marginal adaptation with superior shear resistance and can be considered as an alternative bulk filling material.

Effects of Bio-Aging on Mechanical Properties and Microbial Behavior of Different Resin Composites

Under challenging oral environments, the overall performance of resin composites is affected by bio-aging. This study investigated the effects of saliva biofilm-induced bio-aging on the mechanical properties and microbial behavior of composites with different filler types. Microhybrid, nanohybrid, nano-filled and nano-filled flowable composites were bio-aged with saliva biofilm for 30 days. Surface morphology, roughness, mechanical and aesthetic properties were determined. A 48 h saliva biofilm model was used to evaluate the microbial behavior of different composites in vitro. Biofilm metabolic activity, lactic acid production and live/dead bacterial staining were tested. Six volunteers were selected to wear intra-oral appliances with composite slabs for 24 h and biofilms were collected and analyzed using 16S rRNA sequencing to assess the biofilm formation over those materials in situ. Although there were increasing trends, surface roughness, water resorption and material solubility had no significant changes for all groups after bio-aging (p > 0.05). There were no significant changes in elastic modulus for all groups after aging (p > 0.05). However, a decrease in flexural strength in all groups was observed (p < 0.05), except for the nanoflow composite group (p > 0.05). The Vickers hardness remained stable in all groups after aging (p > 0.05), except for the nano-filled group (p < 0.05). The nanoflow composite showed distinct color changes compared to the micro-hybrid group after aging (p < 0.05). Biofilm metabolic activity and lactic acid production in vitro increased slightly after bio-aging in all groups, but with no statistical significance (p > 0.05). The Shannon index diversity of biofilms in situ decreased after aging (p < 0.05), while no significant difference was shown in species composition at the genus level in all groups (p > 0.05). Resin composites with different sized fillers displayed a relatively stable mechanical performance and uncompromised microbial behavior both in vitro and in situ after 30 days of bio-aging. Based on the results, composites with different filler types can be selected flexibly according to clinical needs. However, a longer time for bio-aging is still needed to confirm the mechanical properties and microbial behaviors of composites in the long run.

Modification of glass-ionomer cement properties by quaternized chitosan-coated nanoparticles

Glass ionomers (GICs), because of their qualities, are in a good position to be modified to resist masticatory stresses as permanent posterior restoration and prevent recurrent caries. The purpose of the present study was to evaluate the effect of adding quaternized chitosan-coated mesoporous silica nanoparticles (HTCC@MSNs) to conventional GIC on its mechanical properties, antimicrobial activity and fluoride release and the effect of 1- and 3-month water aging on the studied properties. HTCC@MSNs was synthesized, added to commercially available conventional GIC at 1%, 3%, and 5% by weight forming three experimental groups and compared with plain GIC as a control group. Flexural strength, modulus, Vickers microhardness and wear volumes were evaluated. Antibacterial activity was tested against Streptococcus mutans and fluoride release in de-ionized water was measured. All properties were evaluated before and after one- and three-month aging (n = 10 specimens per test/per time). Two-way ANOVA was used for statistical analysis. Characterization confirmed successful preparation of HTCC@MSNs. The flexural strength, modulus, hardness and wear resistance of the GICs improved significantly by adding 1-3% HTCC@MSNs, while 5% HTCC@MSNs group showed no significant difference compared to control group. Bacterial inhibition zones and fluoride release increased proportionally to the amount of filler added. Mechanical properties were improved by artificial aging. Fluoride release values, and bacterial inhibition zones decreased with aging for all groups. HTCC@MSNs as a filler with the optimized proportion provides strengthening and antibacterial effect. In addition, aging is an important factor to be considered in evaluating experimental fillers.

The Bio-Aging of Biofilms on Behalf of Various Oral Status on Different Titanium Implant Materials

The properties of titanium implants are affected by bio-aging due to long-term exposure to the oral microenvironment. This study aimed to investigate probable changes in titanium plates after different biofilm bio-aging processes, representing various oral status. Titanium plates with different surface treatments were used, including polish, sandblasted with large grit and acid etched (SLA), microarc oxidation (MAO), and hydroxyapatite coating (HA). We established dual-species biofilms of Staphylococcus aureus (S. aureus)-Candida albicans (C. albicans) and saliva biofilms from the healthy and patients with stage III-IV periodontitis, respectively. After bio-aging with these biofilms for 30 days, the surface morphology, chemical composition, and water contact angles were measured. The adhesion of human gingival epithelial cells, human gingival fibroblasts, and three-species biofilms (Streptococcus sanguis, Porphyromonas gingivalis, and Fusobacterium nucleatum) were evaluated. The polished specimens showed no significant changes after bio-aging with these biofilms. The MAO- and SLA-treated samples showed mild corrosion after bio-aging with the salivary biofilms. The HA-coated specimens were the most vulnerable. Salivary biofilms, especially saliva from patients with periodontitis, exhibited a more distinct erosion on the HA-coating than the S. aureus-C. albicans dual-biofilms. The coating became thinner and even fell from the substrate. The surface became more hydrophilic and more prone to the adhesion of bacteria. The S. aureus-C. albicans dual-biofilms had a comparatively mild corrosion effect on these samples. The HA-coated samples showed more severe erosion after bio-aging with the salivary biofilms from patients with periodontitis compared to those of the healthy, which emphasized the importance of oral hygiene and periodontal health to implants in the long run.

Surface degradation and biofilm formation on hybrid and nanohybrid composites after immersion in different liquids

PURPOSE

This study evaluated the association of surface degradation and formation of Streptococcus mutans (S. mutans) biofilm in resin-based composites (RBCs) after storage in different acidic liquids.

METHODS

To evaluate microhardness and surface micromorphology, hybrid and nanohybrid RBC discs were stored in artificial gastric acid, cola drink, orange juice, artificial saliva, and distilled water for three intervals of 15 min per day for 7, 15, and 30 days. After 30 days of storage, surface roughness was analyzed, and the RBC discs were placed in a biofilm reactor inoculated with S. mutans to evaluate surface biofilm formation.

RESULTS

As compared with nanohybrid RBCs, roughness and surface microhardness values were significantly lower (P < 0.05) for hybrid RBCs stored in artificial gastric acid, followed by specimens stored in cola drink and orange juice. Artificial gastric acid caused greater surface degradation, which increased the biomass of S. mutans on the surface of both RBC types.

CONCLUSION

Surface degradation of hybrid and nanohybrid RBCs correlated with the pH of the liquid, while S. mutans biofilm formation was associated with increased surface roughness in hybrid RBCs.

The First Step in Standardizing an Artificial Aging Protocol for Dental Composites—Evaluation of Basic Protocols

The clinical performance of a dental restoration is strongly influenced by the complex and dynamically-changing oral environment; however, no standard procedure exists to evaluate this lifetime. This research provides an in-depth analysis of the effect of different aging procedures on the flexural strength (FS), diametral tensile strength (DTS) and hardness (HV) of selected dental materials (Resin F, Flow-Art and Arkon). Material structure was evaluated by scanning electron microscopy. It was found that each aging protocol had some influence on the tested properties, with continual erosion and degradation being observed. Greater mechanical degradation was observed for Resin F (neat resin) after the applied aging protocols, suggesting that a resin matrix is more susceptible for degradation. The most aggressive aging protocol was Protocol 5: 0.1 M NaOH, seven days, 60 °C. Further studies on the effect of artificial aging on dental materials should include a study of the thermal and chemical factors. A standardized aging procedure is crucial for improving the resistance of dental resin composite to oral conditions and their clinical performance.

The Effect of a Green Smoothie on Microhardness, Profile Roughness and Color Change of Dental Restorative Materials

Acidic drinks are known to exert negative effects on the surface properties of dental restorative materials. However, the effect of increasingly popular green smoothie drinks has not been addressed so far. The present study investigated the effect of cyclic immersions (5 min daily over 30 days) in a green smoothie drink on the surface properties of contemporary dental restorative materials, including resin composites, an alkasite, and a glass hybrid. Vickers microhardness, profile roughness, and perceptible color change in the CIE L* a* b* color space were evaluated as clinically relevant properties of the material surface. After 30-day green smoothie immersion, microhardness values either decreased by 8–28% (for resin composites) or increased by up to 91% (for glass hybrid). The increase in profile roughness (Ra parameter) of smoothie-immersed specimens was 7–26 times higher compared to the control group. The perceptible color change (ΔE*) in the smoothie group was 3–8 times higher compared to the control group. Overall, this study demonstrated that daily exposure of dental restorations made from resin composites, alkasites, and glass hybrid materials to a green smoothie drink can significantly accelerate material degradation, which is reflected as surface softening, as well as higher roughness and higher perceptible color change.

Novel Giomers Incorporated with Antibacterial Quaternary Ammonium Monomers to Inhibit Secondary Caries

The objective of this study was to develop novel modified giomers by incorporating the antibacterial quaternary ammonium monomers (QAMs), dimethylaminododecyl methacrylate (DMADDM) or dimethylaminohexadecyl methacrylate (DMAHDM) into a commercial giomer. The material performances including mechanical properties, surface characteristics, color data, cytotoxicity and fluoride release of the novel giomers were evaluated. Antibacterial activity against severe early childhood caries (S-ECC) saliva-derived biofilms was assessed by lactic acid production measurement, MTT assay, biofilm staining and 16S rRNA sequencing. A rat model was developed and the anti-caries effect was investigated by micro-CT scanning and modified Keyes’ scoring. The results showed that the material properties of the QAMs groups were comparable to those of the control group. The novel giomers significantly inhibited lactic acid production and biofilm viability of S-ECC saliva-derived biofilms. Furthermore, caries-related genera such as Streptococcus and Lactobacillus reduced in QAMs groups, which showed their potential to change the microbial compositions. In the rat model, lesion depth, mineral loss and scoring of the QAMs groups were significantly reduced, without side effects on oral tissues. In conclusion, the novel giomers incorporated with antibacterial QAMs could inhibit the cariogenic biofilms and help prevent secondary caries, with great potential for future application in restorative treatment.

Intelligent pH-responsive dental sealants to prevent long-term microleakage

OBJECTIVES

Microleakage is a determinant factor of failures in sealant application. In this study, DMAEM (dodecylmethylaminoethyl methacrylate), a pH-responsive antibacterial agent, was incorporated into resin-based sealant for the first time. The objectives of this study were to: (1) investigate the long-term performance of DMAEM-modified sealants against oral microbial-aging; and (2) investigate the long-term preventive effect of DMAEM-modified sealants on microleakage.

METHODS

Depth-of-cure and cytotoxicity of DMAEM-modified sealants were measured. Then, an aging model using biofilm derived from the saliva of high caries experience children was conducted. After aging, microhardness and surface roughness were measured. Biofilm activity, lactic acid production and exopolysaccharide (EPS) production were measured. 16S rRNA gene sequencing were also performed. The effects of DMAEM on microleakage were tested using an in vitro microleakage assessment.

RESULTS

The addition of DMAEM with a mass fraction of 2.5-10% did not affect depth-of-cure values and cytotoxicity of sealants. Adding 2.5-10% DMAEM did not affect the surface roughness and microhardness after aging. Compared to control, adding 2.5-10% DMAEM reduced biofilm metabolic activity by more than 80%. The lactic acid production and EPS production were reduced by 50% in DMAEM groups. DMAEM-modified sealants maintained the microbial diversity of biofilm after aging, they also inhibited the growth of lactobacillus. The 5% and 10% DMAEM groups exhibited a significant reduction in microleakage compared to control.

SIGNIFICANCE

The long-term antibacterial activities against oral microbial-aging and the long-term microecosystem-regulating capabilities enabled DMAEM-modified sealant to prevent microleakage in sealant application and thus prevent dental caries.

Anti-bacterial and anti-microbial aging effects of resin-based sealant modified by quaternary ammonium monomers

OBJECTIVES

Pit and fissure sealant is used in the prevention of dental caries. However, commercial pit and fissure sealant lacks persistent antibacterial properties. Dimethylaminododecyl methacrylate (DMADDM) was added to pit and fissure sealants to give it sustainable antibacterial properties and anti-microbial aging properties.

METHODS

Resin-based sealant was used as a control. Novel sealants were made with DMADDM. Atomic force microscope observation, curing depth, cytotoxicity, lactic acid measurement, hardness and microleakage were measured. Saliva-derived biofilms were grown on sealants. Biofilm metabolic activity, lactic acid production and biomass accumulation were measured.

RESULTS

Incorporating DMADDM did not increase the cytotoxicity or change the physical properties when the mass fraction of the DMADDM was 2.5-10%. The modification decreased the amount of bacterial biofilm, metabolic activity, lactic acid production and exopolysaccharide (EPS) in the saliva biofilms. It also provided anti-microbial aging properties.

CONCLUSION

The incorporation of DMADDM improved the antibacterial and anti-microbial aging effects of the material. It demonstrated a sustained antibacterial effect. The antibacterial and anti-microbial aging modification might be a potential choice for future clinical applications to inhibit dental caries, especially for children at high caries risk.

CLINICAL SIGNIFICANCE

The antibacterial and anti-microbial aging modification might be a potential choice for future clinical applications to prevent dental caries, especially for individuals at high caries risk.

Effect of water aging on the anti-biofilm properties of glass ionomer cement containing fluoro-zinc-silicate fillers

A previous study has reported that a novel fluoro-zinc-silicate glass ionomer cement (Caredyne Restore) showed superior anti-biofilm effects by interfering with bacterial adhesion. However, the active ions may degrade with time. This study aimed to assess the valid anti-biofilm effects of Caredyne Restore after being aged by water immersion for 3 weeks. Streptococcus mutans biofilm was allowed to grow on the surface before and after water aging for 24 h using a modified Robbins device flow-cell system. The results showed water aging promoted biofilm formation. Insufficient amount of fluoride and zinc ions were released from Caredyne Restore after water aging under neutral pH condition. An acidic pH is needed to exert effective anti-biofilm properties. As the release of active ions from Caredyne Restore will gradually decrease after the restoration,  the restoration may not prevent biofilm formation after 3 weeks while neutral pH is maintained by the buffering capacity of saliva.

Interaction between the Oral Microbiome and Dental Composite Biomaterials: Where We Are and Where We Should Go

Dental composites are routinely placed as part of tooth restoration procedures. The integrity of the restoration is constantly challenged by the metabolic activities of the oral microbiome. This activity directly contributes to a less-than-desirable half-life for the dental composite formulations currently in use. Therefore, many new antimicrobial dental composites are being developed to counteract the microbial challenge. To ensure that these materials will resist microbiome-derived degradation, the model systems used for testing antimicrobial activities should be relevant to the in vivo environment. Here, we summarize the key steps in oral microbial colonization that should be considered in clinically relevant model systems. Oral microbial colonization is a clearly defined developmental process that starts with the formation of the acquired salivary pellicle on the tooth surface, a conditioned film that provides the critical attachment sites for the initial colonizers. Further development includes the integration of additional species and the formation of a diverse, polymicrobial mature biofilm. Biofilm development is discussed in the context of dental composites, and recent research is highlighted regarding the effect of antimicrobial composites on the composition of the oral microbiome. Future challenges are addressed, including the potential of antimicrobial resistance development and how this could be counteracted by detailed studies of microbiome composition and gene expression on dental composites. Ultimately, progress in this area will require interdisciplinary approaches to effectively mitigate the inevitable challenges that arise as new experimental bioactive composites are evaluated for potential clinical efficacy. Success in this area could have the added benefit of inspiring other fields in medically relevant materials research, since microbial colonization of medical implants and devices is a ubiquitous problem in the field.

The Effect of Simulated Field Storage Conditions on Dental Restorative Materials for Military Field Use

INTRODUCTION

Dental readiness, one critical component of medical readiness, is adversely impacted by dental emergencies. Many dental emergencies require restorative materials such as glass ionomers, resins, and zinc oxide eugenols to remedy them. The Authorized Dental Allowance List (ADAL) and Authorized Medical Allowance List (AMAL) contain the equipment and materials used by Navy dentists to treat Sailors and Marines. These supplies are subjected to harsh storage conditions on deployments. Much is known about how materials behave when stored at room temperature, but less is known about how their properties are affected after exposure to high temperatures and humidity. We subjected five dental restorative materials to storage in aggravated conditions, and then tested them to determine which products are more robust.

MATERIALS AND METHODS

Unopened packages of Fuji Triage, Fuji IX GP (both GC America Inc., Alsip, Illinois), TPH Spectra ST Low Viscosity, Intermediate Restorative Material (both Dentsply Sirona, York, Pennsylvania), and Herculite XRV (Kerr Corporation, Orange, California) were exposed to 0, 5, or 10 days' storage at 30-60°C with 95% relative humidity. After storage in these aggravated conditions, we tested the compressive strength, hardness, elastic modulus, flexural strength, flexural modulus, sorption, and solubility of each material.

RESULTS

The physical properties of all materials were affected by storage in aggravated conditions, though the properties of some materials degraded more than others. Both glass ionomers, Fuji Triage (P = 0.0012) and Fuji IX GP (P = 0.0031), and the composite Herculite XRV (P = 0.0253) lost compressive strength after 5 or 10 days in aggravated conditions. The hardness values for all materials were affected (P < 0.05) by the aggravated conditions, though the elastic modulus of TPH Spectra was not affected (P > 0.05). None of the materials lost flexural strength (P > 0.05) or had changes in their flexural modulus (P > 0.05). The water sorption behavior of Fuji Triage (P = 0.0426) and Fuji IX GP (P = 0.0201) changed after 10 days of aggravated storage, and the solubility of all materials was altered by the harsh conditions.

CONCLUSION

Some materials degrade more than others in aggravated conditions. Both resin composite materials were more resistant to high temperatures and humidity levels than the glass ionomers tested. These changes in physical characteristics should be considered when reviewing or optimizing the ADAL/AMAL for different projected operational environments.

Effect of Polyols and Selected Dental Materials on the Ability to Create a Cariogenic Biofilm-On Children Caries-Associated Streptococcus Mutans Isolates

Secondary caries is a disease associated with the formation of biofilm on the border of the tooth and dental filling. Its development is strongly influenced by the dietary sweet foods and the type of dental material. The aim of the study was to assess the effect of sweeteners on the ability of clinical Streptococcus mutans strains to form biofilm on dental materials. Strains were isolated from plaque samples from 40 pediatric patients from the 3-6 ICADS II group. The ability to form biofilm was tested on composite and glass ionomer dental materials used for milk teeth filling in the presence of sucrose, xylitol, sorbitol, and erythritol. The bacterial film mass after 12, 24, 48, and 72 h and the number of bacterial colonies significantly decreased (p < 0.01) compared to the initial value for 5% erythritol and sorbitol on examined materials. A greater inhibitory effect was noted for glass ionomers compared to composites. Sucrose and xylitol supported biofilm formation, while erythritol had the best inhibitory effect. The use of fluoride-releasing glass ionomers exerted an effect synergistic to erythritol, i.e., inhibited plaque formation and the amount of cariogenic S. mutans. Selection of proper type of dental material together with replacing sucrose with polyols can significantly decrease risk of secondary caries development. Erithritol in combination with glass ionomer seems to be the most effective in secondary caries prevention.

Flexural strength and surface microhardness of materials used for temporary dental disocclusion submitted to thermal cycling: An in vitro study

OBJECTIVE

The objective of this study was to evaluate the effect of temperature variation on surface microhardness and resistance to flexion of different materials used for making a temporary dental disocclusion.

METHODS

One hundred specimens were made of the following materials (n=20): glass ionomer cement (GIC); compomer (CP); composite resin (CR); Blue colour resin composite for temporary dental disocclusion (BTDD); ultraviolet colour resin composite for temporary dental disocclusion (UVTDD). They were stored in distilled water for 24hours and, subsequently, half of the specimens in each group were subjected to thermal cycling (n=10). All samples were subjected to the microhardness test (HMV-2000) and the flexural strength analysis (INSTRON). The data were submitted to parametric statistical analysis (ANOVA) and Tukey's complementary test with a significance level of 5%. In the mechanical tests, all materials except the GIC showed a statistically significant difference between the groups subjected to thermal cycling and not submitted, and thermal cycling (P<0.05) was responsible for the reduction of the values found, except for GIC.

RESULTS

In the mechanical tests, all materials except the GIC showed a statistically significant difference between the groups subjected to thermal cycling and not submitted, and thermal cycling (P<0.05) was responsible for the reduction of the values found, except for GIC. For microhardness, the highest average was found for BTDD and UVTDD (P≤0.05). As for the resistance, the flexion was found that in the groups not submitted to thermal cycling there was no statistically significant difference for all materials, except for GIC, for the groups with thermal cycling the materials BTDD and UVTDD showed a statistically significant difference from GIC, however, they did not differ statistically from the CP and CR groups.

CONCLUSION

BTDD and UVTDD presented higher average results of surface microhardness and, in the resistance test, the flexion of these materials behaved similarly to the CP and the CR studied. The temperature variation has an effect on the properties of these materials.

Flexural Performance of Direct Resin Composite Restorative Materials Past Expiration Date

Objective  This study' s purpose was to examine the flexural properties of five direct restorative resin composites stored up to 30 months after the expiration date.

Materials and Methods  Ambient-stored materials had pre-expiration date baseline flexure strength values as per ISO 4049 ( n = 20). All materials were used per manufacturer guidelines, photopolymerized on both sides using a LED-based visible light curing unit, and stored in 0.2M phosphate buffered saline. At 24 hours, specimens were stressed to failure in three-point bend at a 0.5 mm/min cross head speed. Additional samples were made at 3, 6, 9, 12, 15, 18, 24, and 30 months past expiration date. Young’s modulus (flexural) was ascertained using the linear slope of the stress-stain curve.

Statistical Analysis  The mean data was found to contain a non-normal distribution and irregular variance which was compared using Kruskal–Wallis with Dunn’s posthoc testing.

Also, Pearson’s correlation analysis was used to identify possible similar degradation behavior between products within both flexure strength and modulus determinations. A 95% level of confidence (α = 0.05) was used.

Results  Materials maintained similar to baseline flexure strength and modulus for up to 15 months past expiration date with two materials being similar at 30 months. However, clinicians were still advised to follow expiration dates, as resin composite degradation mechanisms are complex and vital constituents might degrade that are not overtly identified by clinical handling characteristics. No dental shelf life standards exist and manufacturers are requested to provide protocol information used in determining shelf life expiration.

Anti-caries effect of resin infiltrant modified by quaternary ammonium monomers

OBJECTIVES

Resin infiltrant is used in early enamel caries. However, commercial resin infiltrant lacks persistent antibacterial activity. Dimethylaminododecyl methacrylate (DMADDM) was added to resin infiltrant to give it sustainable antibacterial properties and inhibit demineralization.

METHODS

After the application of resin infiltrant to bovine enamel, cytotoxicity, surface roughness, and aesthetics were assessed. A multi-species biofilm was incubated on the enamel disk before and one month after microbial-aging. After a 48-h anaerobic incubation, biomass accumulation, metabolic activity, and lactic acid were analyzed using a crystal violet assay, an MTT (3-(4,5-dimethyl-thiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay, and a lactic acid assay. Biofilm structure and composition were determined by live/dead staining, exopolysaccharide (EPS) staining, scanning electron microscopy (SEM), and quantitative polymerase chain reaction (qPCR). The depth and content of demineralization were tested by transverse microradiography (TMR).

RESULTS

Incorporating DMADDM did not increase the cytotoxicity or change the physical properties when the mass fraction of the DMADDM was 2.5-10 %. The modification decreased the amount of bacterial biofilm, metabolic activity, lactic acid production, EPS, and the proportion of Streptococcus mutans in the biofilms. It also provided anti-demineralization effects. The surface roughness and antibacterial ability were not changed after one month of microbial-aging.

CONCLUSION

The incorporation of DMADDM improved the antibacterial and anti-demineralization effects of the material. It demonstrated a sustained antibacterial effect.

CLINICAL SIGNIFICANCE

The antibacterial modification might be a potential choice for future clinical applications to inhibit early enamel caries.

Effects of surface coating on the flexural strength of fluoridereleasing restorative materials after water aging for one year

Purpose:

To evaluate the effects of surface coating and one-year water storage on the flexural strength of fluoride-releasing restorative materials.

Materials and methods:

Forty specimens were prepared from each material; GCP Glass Fill (GCP), Amalgomer CR (AHL), Zirconomer (Shofu), Fuji IX GP Capsule (GC), Beautifil II (Shofu), Estelite Σ Quick (Tokuyama) and reliaFIL LC (AHL). The specimens were randomly divided into two groups; surface coated with G-Coat Plus (GC) and uncoated. Each group was subdivided into two groups stored in distilled water at 37◦C for 24 h and 1 year before testing (n=10). The flexural strength was evaluated using three-point bending test according to the ISO 4049:2009 standard using a universal testing machine. After flexural strength test, a cross-section of the coated specimens was evaluated with scanning electron microscopy (SEM).

Results:

A significant increase was observed on the flexural strength of Amalgomer CR, Zirconomer and Fuji IX GP after 24 h when G-Coat Plus was applied (p<0.05). This significant increase was observed on the flexural strength of only Amalgomer CR and Zirconomer after 1 year (p<0.05). The highest flexural strength was obtained with Beautifil II, Estelite Σ Quick and reliaFIL LC after 24 h and 1 year (p<0.05). After 1 year, there was decrease on the flexural strength of the other materials except Beautifil II, Estelite Σ Quick and reliaFIL LC.

Conclusion:

The resin coating improved the flexural strength of some glass ionomer-based materials but the water aging decreased the same physical properties.

The effect of ionizing radiation on properties of fluoride-releasing restorative materials

The purpose of this study was to evaluate the effect of ionizing radiation from high energy X-ray on fluoride release, surface roughness, flexural strength, and surface chemical composition of the materials. The study groups comprised five different restorative materials: Beautifil II, GCP Glass Fill, Amalgomer CR, Zirconomer, and Fuji IX GP. Twenty disk-shaped specimens (8x2 mm) for fluoride release and 20 bar-shaped specimens (25 x 2x 2 mm) for flexural strength were prepared from each material. Each material group was divided into two subgroups: irradiated (IR) and non-irradiated (Non-IR). The specimens from IR groups were irradiated with 1.8 Gy/day for 39 days (total IR = 70.2 Gy). The amount of fluoride released into deionized water was measured using a fluoride ion-selective electrode and ion analyzer after 24 hours and on days 2, 3, 7, 15, 21, 28, 35, and 39 (n = 10). The flexural strength was evaluated using the three-point bending test (n = 10). After the period of measurement of fluoride release, seven specimens (n = 7) from each group were randomly selected to evaluate surface roughness using AFM and one specimen was randomly selected for the SEM and EDS analyses. Data were analyzed with two-way ANOVA and Tukey tests (p = 0.05). The irradiation significantly increased fluoride release and surface roughness for Amalgomer CR and Zirconomer groups (p < 0.05). No significant change in flexural strength of the materials was observed after irradiation (p > 0.05). The ionizing radiation altered the amount of fluoride release and surface roughness of only Amalgomer CR and Zirconomer. The effect could be related to the chemical compositions of materials.

Two-staged time-dependent materials for the prevention of implant-related infections

Infection is a main cause of implant failure. Early implant-related infections often occur in the first 4 weeks post-operation. Inhibiting bacterial adhesion and biofilm formation at the early stage and promoting subsequent implant osseointegration are important for implant success. Our previous studies demonstrated that dimethylaminododecyl methacrylate (DMADDM) provided dental materials with antibacterial effects. In the present study, DMADDM and hydroxyapatite (HA) are loaded on to the titanium (Ti) surface via poly dopamine (PDA) self-polymerization. This local DMADDM-delivery Ti is referred as Ti-PHD. Here we report the two-staged capability of Ti-PHD: (1) in the first stage, releasing DMADDM during the high-infection-risk initial period post-implantation for 4 weeks; (2) then in the second stage, enhancing osteogenesis and promoting osseointegration. Ti-PHD has a porous surface with higher average roughness and greater hydrophilicity than pure Ti. Its biocompatibility is verified in vitro and in vivo. During the first 4 weeks of release, both DMADDM remaining on Ti surface and DMADDM released into the soaking medium greatly reduced the adherence and growth of pathogens. This is further confirmed by the prevention of bone destruction in a rat osteomyelitis model. After releasing DMADDM for 4 weeks, Ti-PHD promotes osteogenic differentiation of human bone marrow mesenchymal stem cells (hBMSCs) and new bone formation around the implants in vivo. This article represents the first report on the two-staged, time-dependent antibacterial and osteogenesis effects of Ti-PHD, demonstrating its potential for clinical applications to inhibit implant-associated infections. STATEMENT OF SIGNIFICANCE: The present study develops a two-staged time-dependent system for local dimethylaminododecyl methacrylate (DMADDM) delivery via Ti implant (referred to as Ti-PHD). DMADDM and hydroxyapatite (HA) are loaded on to the Ti surface with poly dopamine (PDA). Ti-PHD can release DMADDM during the high-risk period of infection in the first stage, and then promote osseointegration and new bone formation in the second stage. This bioactive and therapeutic Ti is promising to inhibit infections and enhance implant success.

Effect of Novel Micro-Arc Oxidation Implant Material on Preventing Peri-Implantitis

Dental implants occasionally fail for many reasons, especially peri-implantitis. The adhesion of bacteria to the surface of titanium is the initial factor in peri-implantitis. Therefore, the aim of this study was to assess the effect of a novel micro-arc oxidation (MAO) titanium on bacteria inhibition and regulation through periodontitis, and on a healthy saliva-derived biofilm, in vitro. MAO, sandblasting and acid etching (SLA), machined titanium and plasma-sprayed hydroxyapatite (HA) were selected for further study. The metabolic activity and biomass accumulation were tested using MTT (3-(4,5-Dimethyl-thiazol-2-yl)-2,5-diphenyltetrazolium bromide) and crystal violet assay after 24 h of anaerobic incubation. The structure was determined by scanning electron microscopy (SEM) and live/dead staining. Moreover, 16S rDNA sequencing was used to assess the microbial community. The results showed that biofilms on MAO were thinner compared to HA and SLA. In the periodontitis group, the biofilm accumulation and metabolic activity reached the highest levels in the HA group (p < 0.05); MAO titanium had the smallest biofilm accumulation and higher live/dead ratio; and the relative abundance of Lactobacillus in the SLA, HA and MAO groups increased significantly compared to the machined group (p < 0.05). In the healthy group, the relative abundance of Lactobacillus in the MAO group increased significantly compared to the other three groups (p < 0.05); the amount and metabolism activity of bacteria in the MAO group was lower (p < 0.05); MAO titanium had the least biofilm accumulation and a higher live/dead ratio. In conclusion, the novel MAO titanium had the ability to combat peri-implantitis by inhibiting the biofilm and regulating the microbial ecosystem to healthier conditions.

The effect of aging methods on the fracture toughness and physical stability of an oxirane/acrylate, ormocer, and Bis-GMA-based resin composites

PURPOSE

To determine the effect of aging methods on the fracture toughness of a conventional Bis-GMA-based resin composite (Filtek Supreme), an ormocer-based resin composite (Admira), and an experimental hydrophobic oxirane/acrylate interpenetrating network resin system (OASys)-based composite.

METHODS

A 25 × 5 × 2.8-mm stainless-steel mold with 2.5 mm single-edge center notch, following ASTM standards [E399-90], was used to fabricate 135 specimens (n = 15) of the composite materials and randomly distributed into groups. For the baseline group, specimens were fabricated and then tested after 24-h storage in water. For the biofilm challenge, specimens were randomly placed in a six-well tissue culture plate and kept at 37 °C with bacterial growth media (Brain Heart Infusion (BHI); Streptococcus mutans) changed daily for 15 days. For the water storage challenge, specimens were kept in 5 ml of deionized distilled autoclaved water for 30 days at 37 °C. μCT evaluation by scanning the specimens was performed before and after the proposed challenge. Fracture toughness (K_Ic) testing was carried out following the challenges.

RESULTS

μCT surface area and volume analyses showed no significant changes regardless of the materials tested or the challenge. Filtek and Admira fracture toughness was significantly lower after the biofilm and water storage challenges. OASys mean fracture toughness values after water aging were significantly higher than that of baseline. Toughness values for OASys composites after biofilm aging were not statistically different when compared to either water or baseline values.

CONCLUSION

The fracture toughness of Bis-GMA and ormocer-based dental resin composites significantly decreased under water and bacterial biofilm assault. However, such degradation in fracture toughness was not visible in OASys-based composites.

CLINICAL SIGNIFICANCE

Current commercial dental composites are affected by the oral environment, which might contribute to the long-term performance of these materials.

Effects of theobromine addition on chemical and mechanical properties of a conventional glass ionomer cement

In vitro effect of 1% theobromine addition on the physical and chemical properties of conventional glass ionomer (GIC) cement was investigated. Conventional GIC (GIC-C) and 1% theobromine added to GIC (GIC-THEO) specimens were compared regarding the microhardness (n = 10), sorption (n = 5), solubility (n = 5), color change (n = 10), fluoride release in saliva (n = 10) and the amount of biofilm deposition (n = 20). Compared against conventional GIC, adding 1% theobromine increased microhardness (p < 0.05), while its sorption, solubility, color and fluoride release to saliva (p > 0.05) remained unchanged. On the other hand, Streptococcus mutans biofilm amount deposited on its surface decreased statistically when theobromine was added to GIC (p < 0.05). Based on the results, it could be concluded that 1% theobromine addition to GIC can be a good strategy as it keeps some of its properties and improves microhardness and biofilm deposits strengthening its role in the preventive approach of dentistry.

Effects of water aging on the mechanical and anti-biofilm properties of glass-ionomer cement containing dimethylaminododecyl methacrylate

OBJECTIVES

The aims of this study were to investigate the effects of water aging for up to 6months on the mechanical and anti-biofilm properties of a novel antibacterial glass ionomer cement (GIC) containing dimethylaminododecyl methacrylate (DMADDM).

METHODS

GIC specimens (n=180) which contained DMADDM (0wt.%, 1.1wt.% or 2.2wt.%) were prepared. The mechanical properties surface roughness, microhardness and the surface charge density of ammonium groups were measured before and after water aging for 3 and 6months at 37°C. Further six months aged specimens (n=216) were worn by 6 volunteers in their oral cavities for 24h and 72h. Biofilm formation was analyzed and rated by fluorescence microscopy (FM) and by scanning electron microscopy (SEM). Biofilm viability was analyzed by FM.

RESULTS

Water aging did not show any adverse effects on the surface roughness and hardness of the material. The surface charge density of the GIC samples containing DMADDM decreased due to the aging procedure, however, was still higher than that of the GIC without DMADDM. In situ biofilm formation was significantly reduced after 24h on DMADDM containing GIC (p<0.05). FM results showed a higher ratio of red/green fluorescence on GIC-DMADDM samples.

SIGNIFICANCE

Incorporating DMADDM into GIC affected the material properties in a tolerable manner even after 6months of storage in water. The new GIC is a promising material to affect the biofilm formation on the surface of restorations.

Influence of Dental Prosthesis and Restorative Materials Interface on Oral Biofilms

Oral biofilms attach onto both teeth surfaces and dental material surfaces in oral cavities. In the meantime, oral biofilms are not only the pathogenesis of dental caries and periodontitis, but also secondary caries and peri-implantitis, which would lead to the failure of clinical treatments. The material surfaces exposed to oral conditions can influence pellicle coating, initial bacterial adhesion, and biofilm formation, due to their specific physical and chemical characteristics. To define the effect of physical and chemical characteristics of dental prosthesis and restorative material on oral biofilms, we discuss resin-based composites, glass ionomer cements, amalgams, dental alloys, ceramic, and dental implant material surface properties. In conclusion, each particular chemical composition (organic matrix, inorganic filler, fluoride, and various metallic ions) can enhance or inhibit biofilm formation. Irregular topography and rough surfaces provide favorable interface for bacterial colonization, protecting bacteria against shear forces during their initial reversible binding and biofilm formation. Moreover, the surface free energy, hydrophobicity, and surface-coating techniques, also have a significant influence on oral biofilms. However, controversies still exist in the current research for the different methods and models applied. In addition, more in situ studies are needed to clarify the role and mechanism of each surface parameter on oral biofilm development.

The effect of artificial aging on Martens hardness and indentation modulus of different dental CAD/CAM restorative materials

OBJECTIVES

To determine the Martens hardness parameters for five different classes of CAD/CAM restorative materials after storage in water and thermo-cycling.

MATERIALS AND METHODS

Lithium disilicate ceramic IPS e.max CAD (EX), silicate ceramic IPS Empress CAD (EC), a polymer infiltrated interpenetrating network material (hybrid material) VITA Enamic (VE), two compact filled composites Lava Ultimate (LU), experimental material (EM), two low filled resin composites Katana Avencia (KA), Ambarino High-Class (AH) and ultra-low/unfilled acrylic polymers CAD-Temp (CT), Telio CAD (TC), breCAM.HIPC (BC) were tested. Specimens were stored in water at 37 °C for 30, 60, 90, 120 days and afterwards thermo-cycled (30,000×, 5 °C/55 °C). Martens hardness (HM) and indentation modulus (E_IT) were longitudinally investigated after each storage time. For structural analysis, each material was analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX).

RESULTS

The groups of unfilled polymers/ultra-low filled composite (CT, TC, BC) followed by low (KA, AH) and compact filled resin composites (LU, EM) showed the lowest HM and E_IT values (p < 0.001). The highest values presented ceramics (EX, EC) followed by hybrid material (VE) (p < 0.001). High influence on the Martens hardness parameters was exerted by the aging duration (HM: η_P² = 0.108, p < 0.001; E_IT: η_P² = 0.074, p < 0.001). Structural analyses of resin composites revealed big differences in shape, size and distribution of filler particles.

CONCLUSIONS

The tested CAD/CAM materials showed differences in Martens hardness and indentation modulus pursuant to the material class. Ceramics showed highest values, followed by the hybrid material. For resin composites the Martens hardness and indentation modulus increased with the filler content. Artificial aging affected CAD/CAM materials differently. Some materials tested are prone to aging, the Martens hardness and indentation modulus decreased after thermo-cycling.