Environmentally safe bioadditive allows degradation of refractory poly(lactic acid) in seawater: Effect of poly(aspartic acid-co-l-lactide) on the hydrolytic degradation of PLLA at different salinity and pH conditions

Generation of Microplastics from Biodegradable Packaging Films Based on PLA, PBS and Their Blend in Freshwater and Seawater

Biodegradable polymers and their blends have been advised as an eco-sustainable solution; however, the generation of microplastics (MPs) from their degradation in aquatic environments is still not fully grasped. In this study, we investigated the formation of bio-microplastics (BMPs) and the changes in the physicochemical properties of blown packaging films based on polylactic acid (PLA), polybutylene succinate (PBS) and a PBS/PLA 70/30 wt% blend after degradation in different aquatic media. The tests were carried out in two temperature/light conditions to simulate degradation in either warm water, under sunlight exposure (named Warm and Light-W&L), and cold deep water (named Cold and Dark-C&D). The pH changes in the aqueous environments were evaluated, while the formed BMPs were analyzed for their size and shape alongside with variations in polymer crystallinity, surface and mechanical properties. In W&L conditions, for all the films, the hydrolytic degradation led to the reorganization of the polymer crystalline phases, strong embrittlement and an increase in hydrophilicity. The PBS/PLA 70/30 blend exhibited increased resistance to degradation with respect to the neat PLA and PBS films. In C&D conditions, no microparticles were observed up to 12 weeks of degradation.

Visualization of isothermal crystallization and phase separation in poly[(R)-3-hydroxybutyrate]/poly(L-lactic acid) by low-frequency Raman imaging

The visualization of the variation of the inter/intra molecular interaction (C = O⋯CH3) between poly[(R)-3-hydroxybutyrate] (PHB) and poly-L-lactic acid (PLLA) in the PHB/PLLA miscible blend during phase separation and crystallization process was successfully investigated using Raman imaging. Images of the blend were developed using high- and low-frequency Raman spectra acquired during the isothermal crystallization of the blend, and both of them were compared. The low-frequency region allowed to observe the changes in the hydrogen bonds between the molecular chains in the blend during phase separation and crystallization via a band at 75 cm-1 derived from PHB. The imaging results obtained using the band at 75 cm-1 due to hydrogen bonding (C = O⋯CH3) between molecular chains were in good agreement with the results obtained using the C = O stretching band at 1720 cm-1. Herein, we demonstrated that the low-frequency region of the Raman spectrum is more sensitive to detecting the start of the phase separation and crystallization of PHB than the corresponding high-frequency region.

Fabrication and evaluation of 3D printed poly(l-lactide) copolymer scaffolds for bone tissue engineering

The application of poly(L-lactic acid) (PLLA) in tissue engineering is limited due to its brittleness and uncontrollable degradation rate. In this study, the flexible p-dioxanone (PDO) and highly reactive glycolide (GA) units were introduced into PLLA segments by chemical modification to prepare poly(l-lactide-ran-p-dioxanone-ran-glycolide) (PLPG) copolymers. The copolymers were then processed into the PLPG scaffold by a 3D printing technology. The physicochemical properties of the PLPG copolymers were studied by NMR, DSC, XRD, GPC, and SEM. Furthermore, the mechanical properties, degradation properties, and biocompatibility of the PLPG scaffolds were also studied. The results showed that introducing PDO and GA units disrupted the regularity of PLLA, decreasing the crystallinity of the PLPG copolymers. However, introducing PDO and GA units could effectively improve the mechanical and degradation properties of the PLLA scaffolds. In vitro cell culture experiments indicated that the PLPG scaffolds supported proliferation, growth, and differentiation of MC3T3-E1 cells. The PLPG scaffolds reported herein, with controllable degradation rates and mechanical performance, may find applications in bone tissue engineering.

Fluorescence tracing the degradation process of biodegradable PBAT: Visualization and high sensitivity

Biodegradable plastics have emerged as a potential solution to the mounting plastic pollution crisis. However, current methods for evaluating the degradation of these plastics are limited in detecting structural changes rapidly and accurately, particularly for PBAT, which contains worrying benzene rings. Inspired by the fact that the aggregation of conjugated groups can endow polymers with intrinsic fluorescence, this work found that PBAT emits a bright blue-green fluoresces under UV irradiation. More importantly, we pioneered a degradation evaluation approach to track the degradation process of PBAT via fluorescence. A blue shift of fluorescence wavelength as the thickness and molecular weight of PBAT film decreased during degradation in an alkali solution was observed. Additionally, the fluorescence intensity of the degradation solution increased gradually as the degradation progressed, and was found to be exponentially correlated with the concentration of benzene ring-containing degradation products following filtration with the correlation coefficient is up to 0.999. This study proposes a promising new strategy for monitoring the degradation process with visualization and high sensitivity.

Controlled and Accelerated Hydrolysis of Polylactide (PLA) through Pentaerythritol Phosphites with Acid Scavengers

This study provides insight into the accelerated hydrolysis of polyester PLA through the addition of phosphites based on pentaerythritol. To control hydrolysis and ensure processing stability, different types of phosphites and combinations of phosphites with acid scavengers were studied. Therefore, commercially available PLA was compounded with selected additives on a twin-screw extruder, and hydrolysis experiments were performed at 23 °C, 35 °C and 58 °C in deionized water. Hydrolysis of PLA was evaluated by the melt volume rate (MVR) and size-exclusion chromatography (SEC). For example, after 4 days of water storage at 58 °C, the number average molecular weight of the PLA comparison sample was reduced by 31.3%, whereas PLA compounded with 0.8% phosphite P1 had a 57.7% lower molecular weight. The results are in good agreement with the expected and tested stability against hydrolysis of the investigated phosphite structures. ³¹P-NMR spectroscopy was utilized to elucidate the hydrolysis of phosphites in the presence of lactic acid. With the addition of phosphites based on pentaerythritol, the hydrolysis rate can be enhanced, and faster biodegradation behavior of biodegradable polyesters is expected. Accelerated biodegradation is beneficial for reducing the residence time of polymers in composting facilities or during home composting and as litter or microplastic residues.

Comparative Study of Crystallization, Mechanical Properties, and In Vitro Cytotoxicity of Nanocomposites at Low Filler Loadings of Hydroxyapatite for Bone-Tissue Engineering Based on Poly(l-lactic acid)/Cyclo Olefin Copolymer

A poly(l-lactic acid)/nanohydroxyapatite (PLLA/nHA) scaffold works as a bioactive, osteoconductive scaffold for bone-tissue engineering, but its low degradation rate limits embedded HA in PLLA to efficiently interact with body fluids. In this work, nano-hydroxyapatite (nHA) was added in lower filler loadings (1, 5, 10, and 20 wt%) in a poly(l-lactic acid)/cyclo olefin copolymer10 wt% (PLLA/COC10) blend to obtain novel poly(l-lactic acid)/cyclo olefin copolymer/nanohydroxyapatite (PLLA/COC10-nHA) scaffolds for bone-tissue regeneration and repair. Furthermore, the structure-activity relationship of PLLA/COC10-nHA (ternary system) nanocomposites in comparison with PLLA/nHA (binary system) nanocomposites was systematically studied. Nanocomposites were evaluated for structural (morphology, crystallization), thermomechanical properties, antibacterial potential, and cytocompatibility for bone-tissue engineering applications. Scanning electron microscope images revealed that PLLA/COC10-nHA had uniform morphology and dispersion of nanoparticles up to 10% of HA, and the overall nHA dispersion in matrix was better in PLLA/COC10-nHA as compared to PLLA/nHA. Fourier transformation infrared spectroscopy (FTIR), powder X-ray diffraction (XRD), and differential scanning calorimetry (DSC) studies confirmed miscibility and transformation of the α-crystal form of PLLA to the ά-crystal form by the addition of nHA in all nanocomposites. The degree of crystallinity (%) in the case of PLLA/COC10-nHA 10 wt% was 114% higher than pure PLLA/COC10 and 128% higher than pristine PLLA, indicating COC and nHA are acting as nucleating agents in the PLLA/COC10-nHA nanocomposites, causing an increase in the degree of crystallinity (%). Moreover, PLLA/COC10-nHA exhibited 140 to 240% (1-20 wt% HA) enhanced mechanical properties in terms of ductility as compared to PLLA/nHA. Antibacterial activity results showed that 10 wt% HA in PLLA/COC10-nHA showed substantial activity against P. aeruginosa, S. aureus, and L. monocytogenes. In vitro cytocompatibility of PLLA/COC10 and PLLA nanocomposites with nHA osteoprogenitor cells (MC3T3-E1) and bone mesenchymal stem cells (BMSC) was evaluated. Both cell lines showed two- to three-fold enhancement in cell viability and 10- to 30-fold in proliferation upon culture on PLLA/COC10-nHA as compared to PLLA/nHA composites. It was observed that the ternary system PLLA/COC10-nHA had good dispersion and interfacial interaction resulting in improved thermomechanical and enhanced osteoconductive properties as compared to PLLA/nHA.

Comprehensive exploration of natural degradation of poly(lactic acid) blends in various degradation media: A review

Poly(lactic acid) (PLA), a bio-based polyester, has been extensively investigated in the recent past owing to its excellent mechanical properties. Several studies have been conducted on PLA blends, with a focus on improving the brittleness of PLA to ensure its suitability for various applications. However, the increasing use of PLA has increased the contamination of PLA-based products in the environment because PLA remains intact even after three years at sea or in soil. This review focuses on analyzing studies that have worked on improving the degradation properties of PLA blends and studies how other additives affect degradation by considering different degradation media. Factors affecting the degradation properties, such as surface morphology, water uptake, and crystallinity of PLA blends, are highlighted. In natural, biotic, and abiotic media, water uptake plays a crucial role in determining biodegradation rates. Immiscible blends of PLA with other polymer matrices cause phase separation, increasing the water absorption. The susceptibility of PLA to hydrolytic and enzymatic degradation is high in the amorphous region because it can be easily penetrated by water. It is essential to study the morphology, water absorption, and structural properties of PLA blends to predict the biodegradation properties of PLA in the blends.

Poly(aspartic acid) in Biomedical Applications: From Polymerization, Modification, Properties, Degradation, and Biocompatibility to Applications

Poly(aspartic acid) (PASP) is an anionic polypeptide that is a highly versatile, biocompatible, and biodegradable polymer that fulfils key requirements for use in a wide variety of biomedical applications. The derivatives of PASP can be readily tailored via the amine-reactive precursor, poly(succinimide) (PSI), which opens up a large window of opportunity for the design and development of novel biomaterials. PASP also has a strong affinity with calcium ions, resulting in complexation, which has been exploited for bone targeting and biomineralization. In addition, recent studies have further verified the biocompatibility and biodegradability of PASP-based polymers, which is attributed to their protein-like structure. In light of growing interest in PASP and its derivatives, this paper presents a comprehensive review on their synthesis, characterization, modification, biodegradation, biocompatibility, and applications in biomedical areas.