Development of a novel porous polyvinyl formal (PVF) microfibrous scaffold for nerve tissue engineering

Carboxymethyl cellulose-agarose-gelatin: A thermoresponsive triad bioink composition to fabricate volumetric soft tissue constructs

Polysaccharide based hydrogels have been predominantly utilized as ink materials for 3D bioprinting due to biocompatibility and cell responsive features. However, most hydrogels require extensive crosslinking due to poor mechanical properties leading to limited printability. To improve printability without using cytotoxic crosslinkers, thermoresponsive bioinks could be developed. Agarose is a thermoresponsive polysaccharide with upper critical solution temperature (UCST) for sol-gel transition at 35-37 °C. Therefore, we hypothesized that a triad of carboxymethyl cellulose(C)-agarose(A)-gelatin(G) could be a suitable thermoresponsive ink for printing since they undergo instantaneous gelation without any addition of crosslinkers after bioprinting. The blend of agarose-carboxymethyl cellulose was mixed with 1% w/v, 3% w/v and 5% w/v gelatin to optimize the triad ratio for hydrogel formation. It was observed that a blend (C2-A0.5-G1 and C2-A1-G1) containing 2% w/v carboxymethyl cellulose, 0.5% or 1% w/v agarose and 1% w/v gelatin formed better hydrogels with higher stability for up to 21 days in DPBS at 37 °C. Further, C2-A0.5-G1 and C2-A1-G1hydrogels showed higher storage modulus 762 ± 182 Pa & 2452 ± 430 Pa, higher porosity of 96.98 ± 2% & 98.2 ± 0.8% and swellability of 1518 ± 68% & 1587 ± 25% respectively. To evaluate the in vitro potential of these bioink formulations, indirect and direct cytotoxicity were determined using NCTC clone 929 (mouse fibroblast cells) and HADF (primary human adult dermal fibroblast) cells as per the ISO 10993-5 standards. Importantly, the printability of these bioinks was confirmed using extrusion bioprinting by successfully printing different complex 3D patterns.

Hyaluronic Acid as Bioink and Hydrogel Scaffolds for Tissue Engineering Applications

Bioprinting is an additive manufacturing technique that focuses on developing living tissue constructs using bioinks. Bioink is crucial in determining the stability of printed patterns, which remains a major challenge in bioprinting. Thus, the choices of bioink composition, modifications, and cross-linking methods are being continuously researched to augment the clinical translation of bioprinted constructs. Hyaluronic acid (HA) is a naturally occurring polysaccharide with the repeating unit of N-acetyl-glucosamine and d-glucuronic acid disaccharides. It is present in the extracellular matrix (ECM) of tissues (skin, cartilage, nerve, muscle, etc.) with a wide range of molecular weights. Due to the nature of its chemical structure, HA could be easily subjected to chemical modifications and cross-linking that would enable better printability and stability. These interesting properties have made HA an ideal choice of bioinks for developing tissue constructs for regenerative medicine applications. In this Review, the physicochemical properties, reaction chemistry involved in various cross-linking strategies, and biomedical applications of HA have been elaborately discussed. Further, the features of HA bioinks, emerging strategies in HA bioink preparations, and their applications in 3D bioprinting have been highlighted. Finally, the current challenges and future perspectives in the clinical translation of HA-based bioinks are outlined.

Titanium dioxide (TiO2) nanoparticles reinforced polyvinyl formal (PVF) nanocomposites as chemiresistive gas sensor for sulfur dioxide (SO2) monitoring

The present work reports the preparation of polyvinyl formal (PVF)/Titanium dioxide (TiO₂) nanocomposite films using a solution casting method followed by the characterization of the synthesized PVF/TiO₂ nanocomposite films using various analytical techniques namely FTIR, XRD, UV-vis, SEM and TGA analysis. The results obtained from different analyses confirmed that the TiO₂ NPs was fine dispersed within the PVF matrix and there exists well compatibility among the polymer matrix and the nanofiller. The pristine TiO₂ NPs based fabricated chemiresistive sensor exhibits the maximum sensitivity of 50.25% at 370 °C where as PVF/TiO₂ nanocomposite sensor showed the enhanced sensitivity of 83.75% at a relatively low operating temperature of 150 °C towards 600 ppm sulfur dioxide (SO₂) gas. The 25 wt% PVF/TiO₂ nanocomposite film sensor exhibited good sensitivity (∼83.75%), selectivity, rapid response time (66 s)/recovery time (107 s), and long-term stability of 60 days for SO₂ gas detection. The fabricated PVF/TiO₂ nanocomposite film sensors in our work possesses the advantages of low power consumption, cost-effective, and distinguished sensing abilities for SO₂ detection makes it possible for potential applications. Thus, the fabricated chemiresistive sensors based on TiO₂ NPs reinforced PVF nanocomposites films are evaluated and experimental results to show an excellent behavior towards SO₂ gas detection for industrial processes control and environmental monitoring applications.

Fabrication and evaluation of porous and conductive nanofibrous scaffolds for nerve tissue engineering

Peripheral nerve repair is still one of the major clinical challenges which has received a great deal of attention. Nerve tissue engineering is a novel treatment approach that provides a permissive environment for neural cells to overcome the constraints of repair. Conductivity and interconnected porosity are two required characteristics for a scaffold to be effective in nerve regeneration. In this study, we aimed to fabricate a conductive scaffold with controlled porosity using polycaprolactone (PCL) and chitosan (Chit), FDA approved materials for the use in implantable medical devices. A novel method of using tetrakis (hydroxymethyl) phosphonium chloride (THPC) and formaldehyde was applied for in situ synthesis of gold nanoparticles (AuNPs) on the scaffolds. In order to achieve desirable porosity, different percentage of polyethylene oxide (PEO) was used as sacrificial fiber. Fourier transform infrared spectroscopy (FTIR) and field emission scanning electron microscopy (FE-SEM) results demonstrated the complete removing of PEO from the scaffolds after washing and construction of interconnected porosities, respectively. Elemental and electrical analysis revealed the successful synthesis of AuNPs with uniform distribution and small average diameter on the PCL/Chit scaffold. Contact angle measurements showed the effect of porosity on hydrophilic properties of the scaffolds, where the porosity of 75-80% remarkably improved surface hydrophilicity. Finally, the effect of conductive nanofibrous scaffold on Schwann cells morphology and vaibility was investigated using FE-SEM and MTT assay, respectively. The results showed that these conductive scaffolds had no cytotoxic effect and support the spindle-shaped morphology of cells with elongated process which are typical of Schwann cell cultures.

Topographical and Biomechanical Guidance of Electrospun Fibers for Biomedical Applications

Electrospinning is gaining increasing interest in the biomedical field as an eco-friendly and economic technique for production of random and oriented polymeric fibers. The aim of this review was to give an overview of electrospinning potentialities in the production of fibers for biomedical applications with a focus on the possibility to combine biomechanical and topographical stimuli. In fact, selection of the polymer and the eventual surface modification of the fibers allow selection of the proper chemical/biological signal to be administered to the cells. Moreover, a proper design of fiber orientation, dimension, and topography can give the opportunity to drive cell growth also from a spatial standpoint. At this purpose, the review contains a first introduction on potentialities of electrospinning for the obtainment of random and oriented fibers both with synthetic and natural polymers. The biological phenomena which can be guided and promoted by fibers composition and topography are in depth investigated and discussed in the second section of the paper. Finally, the recent strategies developed in the scientific community for the realization of electrospun fibers and for their surface modification for biomedical application are presented and discussed in the last section.

The Evolving Neural Tissue Engineering Landscape of India

The healthcare sector in India is witnessing unprecedented advancement. Tissue engineering has become an integral part of healthcare and medicine, particularly where treatments involve functional restoration of any injured or deceased part of the body. Not falling behind much with the progressing medical and healthcare sector of India, tissue engineering is also gaining momentum in the country. Out of several arenas of tissue engineering, India has made its mark in orthopedic and bone regeneration, cosmetic and skin regeneration, and very importantly neural regeneration. There are several articles reviewing the progress and prospects of orthopedic and skin regeneration research in India. However, there is no systematic review on progress, prospects, and pitfalls associated with neural tissue engineering in Indian context. The existing ones mainly focus on the technical advancements in the field from a global perspective. Therefore, it is worthwhile to have an organized look at the evolving neural tissue engineering landscape of India. This review will walk the readers systematically through different aspects of the topic. The review starts with an introduction to the nervous system to help readers appreciate the complexity that must be dealt with while engineering neural tissue. This is followed with a global picture of the neural tissue engineering, prominent research groups working on neural tissue engineering in India, factors that have and are currently molding the prospects of this field, and concluding with an overall perspective on present and future of neural tissue engineering in India.

Interactions at scaffold interfaces: Effect of surface chemistry, structural attributes and bioaffinity

Effective regenerative medicine relies on understanding the interplay between biomaterial implants and the adjoining cells. Scaffolds contribute by presenting sites for cellular adhesion, growth, proliferation, migration, and differentiation which lead to regeneration of tissues over desired periods of time. The fabrication and recruitment of scaffolds often fail to consider the interactions that occur at the interfaces, thereby risking rejection. This lack of knowledge on interfacial microenvironments and related exchanges often causes reduced cellular interactions, poor cell survival and intervention failure. Successful regenerative therapy requires scaffolds with bespoke biocompatibility, optimum pore structure, and cues for cell attachments. These factors determine the development of cellular affinity in scaffolds. For biomedical applications, a detailed understanding of scaffolds and their interfaces is required for better tuning of biomaterials to suit the microenvironments. In this review, we discuss the role of biointerfaces with a focus on surface chemistry, pore structure, scaffold hydro-affinity and their biointeractions. An understanding of the effect of scaffold interfacial properties is crucial for enhancing the progress of tissue engineering towards clinical applications.

Vapor-Assisted Crosslinking of a FK/PVA/PEO Nanofiber Membrane

Herein, we demonstrate a three-component FK/PVA/PEO nanofiber membrane by electrospinning and vapor-assisted crosslinking. We have used feather-derived-keratin (FK), poly (vinyl alcohol) (PVA), and poly (ethylene oxide) (PEO) as membrane components and citric acid/glyoxal as the crosslinker. The structural, thermal, hydrophobicity, and mechanical properties of the as-prepared and crosslinked FK/PVA/PEO nanofiber membranes have been systematically investigated. The results suggest that the nanofiber membrane’s vapor-assisted crosslinking by citric acid has shown better performances than that of glyoxal used as a crosslinker. These results exhibit that non-toxic citric acid can be used as a crosslinking agent to modify the performance of keratin-based membranes. This study opens up further avenues for post-synthesis modification of polymeric membranes for a wide range of applications.