Development of a fiber-reinforced material for fiber posts: Evaluation of stress distribution, fracture load, and failure mode of restored roots

Minimum residual root dentin thickness of mandibular premolars restored with a post: A finite element analysis study

STATEMENT OF PROBLEM

Thin root dentin after post space preparation will increase the risk of root fracture. However, the minimum residual root dentin thickness to be preserved after post space preparation is unclear.

PURPOSE

The purpose of this finite element analysis (FEA) study was to measure the residual root dentin thicknesses and analyze the stress distributions of post-restored mandibular premolars.

MATERIAL AND METHODS

The cone beam computed tomography (CBCT) data of 90 first and second mandibular premolars from Chinese participants (44 men, 46 women; aged between 20 and 79 years) were analyzed. Cross-sections 5 to 9 mm from the radiologic apex were used to measure the buccolingual and mesiodistal root diameters. The probability that the residual thickness of the buccolingual and mesiodistal root walls would be no less than 0.5, 0.6, 0.7, 0.8, 0.9, and 1 mm after post space preparation with a #2 Peeso reamer was calculated. Six 3-dimensional finite element models of cast post-restored mandibular premolars with 0.5, 0.6, 0.7, 0.8, 0.9, and 1 mm mesial and distal root dentin thicknesses were established. A static force of 100 N was applied to the buccal cusp tip at 45, 60, 75, and 90 degrees to the long axis of the tooth, and the maximum tensile stress and von Mises stress were analyzed. The Bonferroni post hoc test (αcorrected=.003) was used for multiple comparisons.

RESULTS

The buccolingual root diameter of mandibular premolars was wider than the mesiodistal root diameter. The probabilities that the mesiodistal residual root dentin thickness of mandibular first and second premolars at 5 mm from the apex would be no less than 1 mm after post space preparation with a #2 Peeso reamer were only 10% and 28%, respectively. The maximum tensile stress was at a minimum when the mesial and distal residual root dentin thickness was 0.6 mm in the external cervical dentin adjacent to the crestal bone and 1 mm in the apical dentin corresponding to the apex of the post. The maximum tensile stress of the mandibular premolar model with 0.6-mm mesial and distal residual root dentin thicknesses was lower than that with 0.9 mm and 1.0 mm thicknesses (Pcorrected<.001).

CONCLUSIONS

Short posts or smaller instruments for post space preparation are recommended to obtain a 1-mm residual root dentin thickness in the mesiodistal direction of mandibular premolars. If a 1-mm thickness cannot be preserved, a minimum residual root dentin thickness of 0.6 to 0.9 mm in the mesiodistal direction should be retained.

Evaluation of mechanical properties of anatomically customized fiber posts using E-glass short fiber-reinforced composite to restore weakened endodontically treated premolars

OBJECTIVE

This study was conducted to assess the influence of combining different forms of fiber-reinforced composites (FRC) on the mechanical behavior and bond strength of compromised endodontically treated teeth (ETT).

MATERIALS AND METHODS

Eighty extracted human premolar teeth were randomly divided into five experimental groups according to the type of intra-radicular restoration and the canal preparation design which was either non-flared (Group 1), flared (Groups 2-5), closed-apex (Groups 1,3,5) or open-apex (Groups 2,4). Standard prefabricated fiber posts were used as intra-radicular restoration for Groups 1-3 while Groups 4-5 were restored with anatomically customized relined fiber posts. After composite core fabrication, all samples were sent for an artificial aging process. Fracture resistance and push-out bond strength tests were then carried out through a universal testing machine followed by mode of failure analysis via a stereomicroscope and scanning electron microscope.

RESULTS

Pairwise Log-Rank comparisons revealed that the survival rate of Group 2 and Group 3 was significantly lower than all other groups after artificial aging. The highest fracture resistance value (1796 N) was recorded in Group 5 and was significantly higher than that of the other groups (p < 0.05), while Group 2 exhibited the lowest fracture resistance (758 N), which was significantly lower compared to the other groups. Group 5 and Group 4 demonstrated a significantly higher push-out bond strength, at all root thirds, than Group 3, Group 2, and Group 1 (p < 0.05). The most frequently observed failure mode in the tested groups occurred between the resin cement and radicular dentin.

CONCLUSION

The use of short fiber-reinforced composite (SFRC) to reline the prefabricated FRC post has been proven to have superior fracture resistance with favorable failure patterns and increased push-out bond strength values compared to standard prefabricated FRC posts.

Numerical Study of the Mechanical Behaviour of Wedge-Shaped Defect Filling Materials

This paper deals with direct restorations of teeth with non-carious cervical lesions (NCCL). NCCL defects are capable of gradual growth and are accompanied by the degradation of the surrounding tissue. Direct restorative treatment, in which the cavity is filled with a cementing agent, is considered to be an accessible and common treatment option. The study included simulations of the teeth without lesions, the teeth with V and U lesions and the tooth-restorative system. Parameterised numerical tooth models were constructed. Two cases with defect depths of 0.8 mm and ~1.7 mm and three variants with fillet radii of the defect end of 0.1, 0.2 and 0.3 mm were considered. The effect of two biomaterials for restorations was studied, namely Herculite XRV (Kerr Corp, Orange, CA, USA) and Charisma (Heraeus Kulzer GmbH, Hanau, Germany). The models were deformed with a vertical load of 100 to 1000 N from the antagonist tooth. The tooth-restorative system was considered, taking into consideration the contact interaction in the interface areas with the tooth tissues. Within the limits of the research, the character of the distribution of the deformation characteristics and their dependence on the level of loading, the depth of the defect and the radius of the curvature of the "wedge" were established.

Numerical Modeling of a New Type of Prosthetic Restoration for Non-Carious Cervical Lesions

The paper considers a new technology for the treatment of non-carious cervical lesions (NCCLs). The three parameterized numerical models of teeth are constructed: without defect, with a V-shaped defect, and after treatment. A new treatment for NCCL has been proposed. Tooth tissues near the NCCLs are subject to degradation. The main idea of the technology is to increase the cavity for the restoration of NCCLs with removal of the affected tissues. The new treatment method also allows the creation of a playground for attaching the gingival margin. The impact of three biomaterials as restorations is studied: CEREC Blocs; Herculite XRV; and Charisma. The models are deformed by a vertical load from the antagonist tooth from 100 to 1000 N. The tooth-inlay system is considered, taking into account the contact interaction. Qualitative patterns of tooth deformation before and after restoration were established for three variants of the inlay material.