Improved Blood Compatibility and Endothelialization of Titanium Oxide Nanotube Arrays on Titanium Surface by Zinc Doping

A CO-releasing coating based on carboxymethyl chitosan-functionalized graphene oxide for improving the anticorrosion and biocompatibility of magnesium alloy stent materials

Due to its biofunctions similar to NO, the CO gas signaling molecule has gradually shown great potential in cardiovascular biomaterials for regulating the in vivo performances after the implantation and has received increasing attention. To construct a bioactive surface with CO-releasing properties on the surface of magnesium-based alloy to augment the anticorrosion and biocompatibility, graphene oxide (GO) was firstly modified using carboxymethyl chitosan (CS), and then CO-releasing molecules (CORM401) were introduced to synthesize a novel biocompatible nanomaterial (GOCS-CO) that can release CO in the physiological environments. The GOCS-CO was further immobilized on the magnesium alloy surface modified by polydopamine coating with Zn2+ (PDA/Zn) to create a bioactive surface capable of releasing CO in the physiological environment. The outcomes showed that the CO-releasing coating can not only significantly enhance the anticorrosion and abate the corrosion degradation rate of the magnesium alloy in a simulated physiological environment, but also endow it with good hydrophilicity and a certain ability to adsorb albumin selectively. Owing to the significant enhancement of anticorrosion and hydrophilicity, coupled with the bioactivity of GOCS, the modified sample not only showed excellent ability to prevent platelet adhesion and activation and reduce hemolysis rate but also can promote endothelial cell (EC) adhesion, proliferation as well as the expression of nitric oxide (NO) and vascular endothelial growth factor (VEGF). In the case of CO release, the hemocompatibility and EC growth behaviors were further significantly improved, suggesting that CO molecules released from the surface can significantly improve the hemocompatibility and EC growth. Consequently, the present study provides a novel surface modification method that can simultaneously augment the anticorrosion and biocompatibility of magnesium-based alloys, which will strongly promote the research and application of CO-releasing bioactive coatings for surface functionalization of cardiovascular biomaterials and devices.

An Antibacterial Bionic Periosteum with Angiogenesis-Neurogenesis Coupling Effect for Bone Regeneration

The periosteum, rich in neurovascular networks, bone progenitor cells, and stem cells, is vital for bone repair. Current artificial periosteal materials face challenges in mechanical strength, bacterial infection, and promoting osteogenic differentiation and angiogenesis. To address these issues, we adjusted the electrospinning ratio of poly-ε-caprolactone and chitosan and incorporated Zn doping whitlockite with polydopamine coating into a nanofiber membrane. After a series of characterizations, optimal results were achieved with a poly-ε-caprolactone: chitosan ratio of 8:1 and 5% nanoparticle content. In vitro cell experiments and in vivo calvarial defect models, the sustained release of Mg2+ and Ca2+ promoted vascularization and new bone formation, respectively, while the release of Zn2+ was conducive to antibacterial and cooperated with Mg2+ to promote neurovascularization. Consequently, this antibacterial bionic periosteum with an angiogenesis-neurogenesis coupling effect demonstrates a promising potential for bone repair applications.

A 3D-Printed Scaffold for Repairing Bone Defects

The treatment of bone defects has always posed challenges in the field of orthopedics. Scaffolds, as a vital component of bone tissue engineering, offer significant advantages in the research and treatment of clinical bone defects. This study aims to provide an overview of how 3D printing technology is applied in the production of bone repair scaffolds. Depending on the materials used, the 3D-printed scaffolds can be classified into two types: single-component scaffolds and composite scaffolds. We have conducted a comprehensive analysis of material composition, the characteristics of 3D printing, performance, advantages, disadvantages, and applications for each scaffold type. Furthermore, based on the current research status and progress, we offer suggestions for future research in this area. In conclusion, this review acts as a valuable reference for advancing the research in the field of bone repair scaffolds.

Mesoscopic Model for Reversible Adsorption Stage of Albumin and Fibrinogen on TiO2 Surface

The competitive behavior of proteins in the reversible adsorption stage plays a crucial role in determining the composition of the protein layer and the subsequent biological responses to the biomaterial. However, such competitive adsorption is a mesoscopic process at physiological protein concentration, and neither a macroscopic experiment nor microscopic MD (molecular dynamics) simulation is suitable to clarify it. Here, we proposed a mesoscopic DPD (dissipative particle dynamics) model to illustrate the competitive process of albumin and fibrinogen on TiO2 surface with its parameters deduced from our previous MD simulation, and proved the model well retained the diffusion and adsorption properties of proteins in the competitive adsorption on the plane surface. We then applied the model to the competitive adsorption on the surfaces with different nanostructures and observed that when the nanostructure size is much larger than that of protein, the increase in surface area is the main influencing factor; when the nanostructure size is close to that of protein, the coordination between the nanostructure and the size and shape of protein significantly affects the competitive adsorption process. The model has revealed many mechanical phenomena observed in previous experimental studies and has the potential to contribute to the development of high-performance biomaterials.

Preparation and Properties of GO/ZnO/nHAp Composite Microsphere Bone Regeneration Material

The purpose of this study is to explore the possibility of using graphene-zinc oxide-hydroxyapatite (GO/ZnO/nHAp) composite microspheres as bone regeneration materials by making use of the complementary advantages of nanocomposites, so as to provide reference for the clinical application of preventing and solving bacterial infection after implantation of synthetic materials. Firstly, GO/ZnO composites and hydroxyapatite nanoparticles were synthesized using the hydrothermal method, and then GO/ZnO/nHAp composite microspheres were prepared via high-temperature sintering. The graphene-zinc oxide-calcium phosphate composite microspheres were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), energy dispersion spectroscopy (EDS), water contact angle measurement, degradation and pH determination, and differential thermal analysis (DiamondTG/DTA). The biocompatibility, osteogenic activity, and antibacterial activity of GO/ZnO/nHAp composite microspheres were further studied. The results of the cell experiment and antibacterial experiment showed that 0.5% and 1% GO-ZnO-nHAp composite microspheres not only had good biocompatibility and osteogenic ability but also inhibited Escherichia coli and Staphylococcus aureus by more than 45% and 70%. Therefore, GO/ZnO/nHAp composite microspheres have good physical and chemical properties and show good osteogenic induction and antibacterial activity, and this material has the possibility of being used as a bone regeneration material.

Unravelling Surface Modification Strategies for Preventing Medical Device-Induced Thrombosis

The use of biomaterials in implanted medical devices remains hampered by platelet adhesion and blood coagulation. Thrombus formation is a prevalent cause of failure of these blood-contacting devices. Although systemic anticoagulant can be used to support materials and devices with poor blood compatibility, its negative effects such as an increased chance of bleeding, make materials with superior hemocompatibility extremely attractive, especially for long-term applications. This review examines blood-surface interactions, the pathogenesis of clotting on blood-contacting medical devices, popular surface modification techniques, mechanisms of action of anticoagulant coatings, and discusses future directions in biomaterial research for preventing thrombosis. In addition, this paper comprehensively reviews several novel methods that either entirely prevent interaction between material surfaces and blood components or regulate the reaction of the coagulation cascade, thrombocytes, and leukocytes.

Mechanical and Biological Properties of Titanium and Its Alloys for Oral Implant with Preparation Techniques: A Review

Dental implants have revolutionised restorative dentistry, offering patients a natural-looking and durable solution to replace missing or severely damaged teeth. Titanium and its alloys have emerged as the gold standard among the various materials available due to their exceptional properties. One of the critical advantages of titanium and its alloys is their remarkable biocompatibility which ensures minimal adverse reactions within the human body. Furthermore, they exhibit outstanding corrosion resistance ensuring the longevity of the implant. Their mechanical properties, including hardness, tensile strength, yield strength, and fatigue strength, align perfectly with the demanding requirements of dental implants, guaranteeing the restoration's functionality and durability. This narrative review aims to provide a comprehensive understanding of the manufacturing techniques employed for titanium and its alloy dental implants while shedding light on their intrinsic properties. It also presents crucial proof-of-concept examples, offering tangible evidence of these materials' effectiveness in clinical applications. However, despite their numerous advantages, certain limitations still exist necessitating ongoing research and development efforts. This review will briefly touch upon these restrictions and explore the evolving trends likely to shape the future of titanium and its alloy dental implants.

Titanium Surface-Grafted Zwitterionic Polymers with an Anti-Polyelectrolyte Effect Enhances Osteogenesis

Zwitterionic polymers have attracted considerable attention because of their anti-adsorption and unique anti-polyelectrolyte effects and was widely used in surface modification. In this study, zwitterionic copolymers (poly (sulfobetaine methacrylate-co-butyl acrylate) (pSB) coating on the surface of a hydroxylated titanium sheet using surface-initiated atom transfer radical polymerization (SI-ATRP) was successfully constructed. X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR) and Water contact angle (WCA) analysis proved the successful preparation of the coating. The swelling effect caused by the anti-polyelectrolyte effect was reflected in the simulation experiment in vitro, and this coating can promote the proliferation and osteogenesis of MC3T3-E1. Therefore, this study provides a new strategy for designing multifunctional biomaterials for implant surface modifications.

Copper and Zinc Co-doped Titanium Dioxide Nanotubes Arrays on Controlling Nitric Oxide Releasing and Regulating the Inflammatory Responses for Cardiovascular Biomaterials

BACKGROUND

Titanium dioxide (TiO₂) nanotubes arrays have shown tremendous application foreground due to their unique characters of structure and performance. However, the single bio-function is still the limit on cardiovascular biomaterials.

METHODS

The loadability function provides the possibility for the TiO₂ nanotubes arrays to realize composite multifunction. The copper can catalyze the release of nitric oxide to promote the proliferation of endothelium cells and improve the anticoagulant. Also, zinc can adjust the inflammatory responses to improve anti-inflammation.

RESULTS

In this patent work, we co-doped the copper and zinc onto TiO₂ nanotubes arrays to estimate the hemocompatibility, cytocompatibility and responses of inflammation. The results showed that copper and zinc could introduce better multi-biofunctions to the TiO₂ nanotubes arrays for the application in cardiovascular biomaterials.

CONCLUSION

In summary, the NTs@Cu/Zn sample as a new composite material in this study had significant biocompatibility in vascular implantation and can be used as a potential material for polymer- free drug-eluting stents.

Reduced restenosis and enhanced re-endothelialization of functional biodegradable vascular scaffolds by everolimus and magnesium hydroxide

BACKGROUND

Coronary artery disease is a cardiovascular disease with a high mortality and mortality rate in modern society. Vascular stent insertion to restore blood flow is essential to treat this disease. A fully biodegradable vascular scaffold (BVS) is a vascular poly (L-lactic acid) (PLLA) stent that is receiving growing interest as this is biodegradable in the body and does not require secondary removal surgery. However, acidic byproducts composed of PLLA produced during the biodegradation of the BVS can induce an inflammatory response. Magnesium hydroxide, a basic inorganic particle, neutralizes the acidic byproducts of PLLA.  METHODS: In this study, we investigated using a BVS coated with everolimus and surface-modified magnesium hydroxide that suppresses smooth muscle cell proliferation and protects endothelial cells, respectively. The various characteristics of the functional stent were evaluated using in vitro and in vivo analyses.  RESULTS: The BVS was successfully prepared with evenly coated everolimus and surface-modified magnesium hydroxide. A neutral pH value was maintained by magnesium hydroxide during degradation, and everolimus was released for one month. The coated BVS effectively inhibited protein adsorption and platelet adhesion, demonstrating excellent blood compatibility. In vitro analysis showed that BVS protects endothelial cells with magnesium hydroxide and selectively inhibits smooth muscle cell proliferation via everolimus treatment. The functional BVS was inserted into porcine coronary arteries for 28 days, and the results demonstrated that the restenosis and inflammation greatly decreased and re-endothelialization was enhanced as compared to others.

CONCLUSIONS

This study provides new insights into the design of drug-incorporated BVS stent for coronary artery disease.

Calcium-doped zinc oxide nanocrystals as an innovative intracanal medicament: a pilot study

Objectives

This study investigated the cytotoxicity, radiopacity, pH, and dentinal tubule penetration of a paste of 1.0% calcium-doped zinc oxide nanocrystals (ZnO:1.0Ca) combined with propylene glycol (PRG) or polyethylene glycol and propylene glycol (PEG-PRG).

Materials and Methods

The pastes were prepared by mixing calcium hydroxide [Ca(OH)2] or ZnO:1.0Ca with PRG or a PEG-PRG mixture. The pH was evaluated after 24 and 96 hours of storage in deionized water. Digital radiographs were acquired for radiopacity analysis and bubble counting of each material. The materials were labeled with 0.1% fluorescein and applied to root canals, and images of their dentinal tubule penetration were obtained using confocal laser scanning microscopy. RAW264.7 macrophages were placed in different dilutions of culture media previously exposed to the materials for 24 and 96 hours and tested for cell viability using the MTT assay. Analysis of variance and the Tukey test (α = 0.05) were performed.

Results

ZnO:1.0Ca materials showed lower viability at 1:1 and 1:2 dilutions than Ca(OH)2 materials (p < 0.0001). Ca(OH)2 had higher pH values than ZnO:1.0Ca at 24 and 96 hours, regardless of the vehicle (p < 0.05). ZnO:1.0Ca pastes showed higher radiopacity than Ca(OH)2 pastes (p < 0.01). No between-material differences were found in bubble counting (p = 0.0902). The ZnO:1.0Ca pastes had a greater penetration depth than Ca(OH)2 in the apical third (p < 0.0001).

Conclusions

ZnO:1.0Ca medicaments presented higher penetrability, cell viability, and radiopacity than Ca(OH)2. Higher values of cell viability and pH were present in Ca(OH)2 than in ZnO:1.0Ca.

Rational design of dual-functional surfaces on polypropylene with antifouling and antibacterial performances via a micropatterning strategy

The hydrophobicity and inertness of the polypropylene (PP) material surface usually lead to serious biofouling and bacterial infections, which hamper its potential application as a biomedical polymer. Many strategies have been developed to improve its antifouling or antibacterial properties, yet designing a surface to achieve both antifouling and antibacterial performances simultaneously remains a challenge. Herein, we construct a dual-function micropatterned PP surface with antifouling and antibacterial properties through plasma activation, photomask technology and ultraviolet light-induced graft polymerization. Based on the antifouling agent poly(2-methacryloyloxyethyl phosphate choline) (PMPC) and the antibacterial agent quaternized poly(N,N-dimethylamino)ethyl methacrylate (QPDMAEMA), two different micropatterning structures have been successfully prepared: PP-PMPC-QPDMAEMA in which QPDMAEMA is the micropattern and PMPC is the coating polymer, and PP-QPDMAEMA-PMPC in which PMPC is the micropattern and QPDMAEMA is the coating polymer. The composition, elemental distribution and surface morphology of PP-PMPC-QPDMAEMA and PP-QPDMAEMA-PMPC have been thoroughly characterized by Fourier transform infrared (FT-IR) spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), respectively. Compared with pristine PP, the two types of micropatterned PP films exhibit good surface hydrophilicity as characterized by water contact angle measurements. The results of anti-protein adsorption, platelet adhesion and antibacterial evaluation showed that PP-PMPC-QPDMAEMA and PP-QPDMAEMA-PMPC had good anti-protein adsorption properties, especially for lysozyme (Lyz). They can effectively prevent platelet adhesion, and the anti-platelet adhesion performance of PP-QPDMAEMA-PMPC is slightly better than that of the PP-PMPC-QPDMAEMA sample. The sterilization rate of S. aureus and E. coli is as high as 95% for the two types of micropatterned PP films. Due to the rational design of micropatterns on the PP surface, the two classes of dual-functional PP materials realize both the resistance of protein and platelet adhesion, and the killing of bacteria at the same time. We anticipate that this work could provide a design strategy for the construction of multifunctional biomedical polymer materials.

Cellular studies and sustained drug delivery via nanostructures fabricated on 3D printed porous Neovius lattices of Ti6Al4V ELI

Site-specific drug delivery has the potential to reduce drug dosage by 3 to 5-folds. Given the propensity of drugs used in the treatment of tuberculosis and cancers, the increased drug dosages via oral ingestion for several months to a few years of medication is often detrimental to the health of patients. In this study, the sustained delivery of drugs with multiscale structured novel Neovius lattices was achieved. 3D Neovius Open Cell Lattices (NOCL) with porosities of 40, 45, and 50 % were fabricated layer-by-layer on the laser bed fusion process. Micron-sized Ti6Al4V Eli powder was used for 3D printing. The Young's modulus achieved from the novel Neovius lattices were in the range of 1.2 to 1.6 GPa, which is comparable to human cortical bone and helps to improve implant failure due to the stress shielding effect. To provide sustained drug delivery, nanotubes (NTs) were fabricated on NOCLs via high-voltage anodisation. The osteogenic agent icariin was loaded onto the NOCL-NT samples and their release profiles were studied for 7 days. A significantly steady and slow release rate of 0.05% per hour of the drug was achieved using NOCL-NT. In addition, the initial burst release of NOCL-NT was 4 fold lower than that of the open-cell lattices without nanotubes. Cellular studies using MG63 human osteoblast-like cells were performed to determine their biocompatibility and osteogenesis which were analysed using Calcein AM staining and Alamar Blue after 1, 5, and 7 days. 3D printed NOCL samples with NTs and with Icariin loaded NTs demonstrated a significant increase in cell proliferation as compared to as printed NOCL samples.

Effects of Zinc Ions Released From Ti-NW-Zn Surface on Osteogenesis and Angiogenesis In Vitro and in an In Vivo Zebrafish Model

Zinc-modified titanium materials have been widely applied in oral implants. Among them, our previous studies have also successfully prepared a novel acid-etched microstructured titanium surface modified with zinc-containing nanowires (Ti-NW-Zn) and proved its excellent biocompatibility. It is well known that the functional regulation between angiogenesis and osteogenesis is of great importance for bone remodeling around implants. However, there are few reports concerning the biological safety of zinc ions released from materials and the appropriate concentration of released zinc ions which was more conducive to angiogenesis and bone regeneration. In this study, we investigated the effects of zinc ions released from Ti-NW-Zn surfaces on angiogenesis and osteogenesis using the zebrafish model and revealed the relationship between angiogenesis and osteogenesis via HUVECs and MC3T3-E1s in vitro. We found that the zinc ions released from Ti-NW-Zn surfaces, with a concentration lower than median lethal concentrations (LCs) of zebrafish, were biologically safe and promote osteogenesis and angiogenesis in vivo. Moreover, the proper concentration of zinc ions could induce the proliferation of HUVECs and osteogenic differentiation. The positive effects of the appropriate concentration of zinc ions on osteoblast behaviors might be regulated by activating the MAPK/ERK signaling pathway. These aspects may provide new sights into the mechanisms underlying zinc-modified titanium surfaces between osteogenesis and angiogenesis, to lay the foundation for further improving the materials, meanwhile, promoting the applications in dentistry.

Endothelialization strategy of implant materials surface: The newest research in recent 5 years

In recent years, more and more metal or non-metal materials have been used in the treatment of cardiovascular diseases, but the vascular complications after transplantation are still the main factors restricting the clinical application of most grafts, such as acute thrombosis and graft restenosis. Implant materials have been extensively designed and surface optimized by researchers, but it is still too difficult to avoid complications. Natural vascular endodermis has excellent function, anti-coagulant and anti-intimal hyperplasia, and it is also the key to maintaining the homeostasis of normal vascular microenvironment. Therefore, how to promote the adhesion of endothelial cells (ECs) on the surface of cardiovascular materials to achieve endothelialization of the surface is the key to overcoming the complications after implant materialization. At present, the surface endothelialization design of materials based on materials surface science, bioactive molecules, and biological function intervention and feedback has attracted much attention. In this review, we summarize the related research on the surface modification of materials by endothelialization in recent years, and analyze the advantages and challenges of current endothelialization design ideas, explain the relationship between materials, cells, and vascular remodeling in order to find a more ideal endothelialization surface modification strategy for future researchers to meet the requirements of clinical biocompatibility of cardiovascular materials.

Electrodeposited dopamine/strontium-doped hydroxyapatite composite coating on pure zinc for anti-corrosion, antimicrobial and osteogenesis

Zinc-based biometal is expected to become a new generation of biodegradable implants. Due to its antibacterial and biocompatibility in vivo, zinc metals is recently considered to be the most promising biodegradable metal, However, cytotoxicity is the thorny problem that currently restrict its application, due to the excessive Zn ions released during degradation. In order to solve these problems, dopamine modified strontium-doped hydroxyapatite coating (SrHA/PDA) was fabricated on alkali-treated pure zinc to improve its corrosion rate and cytocompatibility by electrodeposition for the first time. The obtained coating showed a dense structure and high crystallinity, which was attributed to the attraction of Ca²⁺ ions by polydopamine. The results showed that the SrHA/PDA coating delayedthe degradation rate of zinc metal, which reduced the release of Zn²⁺, thereby reducing its cytotoxicity. Additionally, electrochemical tests showed that SrHA/PDA coating can reduce the corrosion rate of pure zinc. In vitro cell viability showed that even at high Zn²⁺ concentrations (3.11 mg/L), preosteoblasts (MC3T3-E1) cells proliferated at a high rate on SrHA/PDA, thus confirming that Sr²⁺ counteracted the cytotoxic effects of Zn²⁺ and promoted cell differentiation. Moreover, the SrHA/PDA coating still maintained excellent antibacterial effects against pathogenic bacterial strains (Escherichia coli and Staphylococcus aureus). Mild pH changes had no significant effect on the viability of cells and bacterias. Collectively, the present study elucidated that by coating SrHA/PDA/Zn(OH)₂ on Zn, a controllable corrosion rate, original antibacterial properties and better cell compatibility can be achieved. This provided a new strategy for the surface modification of biodegradable Zn.

Surface modification strategies to improve titanium hemocompatibility: a comprehensive review

Titanium and its alloys are widely used in different biomaterial applications due to their remarkable mechanical properties and bio-inertness. However, titanium-based materials still face some challenges, with an emphasis on hemocompatibility. Blood-contacting devices such as stents, heart valves, and circulatory devices are prone to thrombus formation, restenosis, and inflammation due to inappropriate blood-implant surface interactions. After implantation, when blood encounters these implant surfaces, a series of reactions takes place, such as protein adsorption, platelet adhesion and activation, and white blood cell complex formation as a defense mechanism. Currently, patients are prescribed anticoagulant drugs to prevent blood clotting, but these drugs can weaken their immune system and cause profound bleeding during injury. Extensive research has been done to modify the surface properties of titanium to enhance its hemocompatibility. Results have shown that the modification of surface morphology, roughness, and chemistry has been effective in reducing thrombus formation. The main focus of this review is to analyze and understand the different modification techniques on titanium-based surfaces to enhance hemocompatibility and, consequently, recognize the unresolved challenges and propose scopes for future research.

Double-edged sword: Therapeutic efficacy versus toxicity evaluations of doped titanium implants

Titanium-based orthopaedic/dental implants modified with various metal-doping strategies can enhance local therapy and bioactivity. Intentional or unintentional (because of loading and wear) release of metal ions/nanoparticles (NPs) from metal-doped implants can be therapeutic or cause adverse local tissue reactions, compromising long-term survival. Strategies to incorporate metals into implants, such as superficial or deep loading inside nano-engineered surfaces, including nanotubes, and the physiochemical characteristics of the released species significantly influence both their therapeutic and cytotoxic potential. In this review, we compare and contrast this 'double-edged sword' to arrive at an improved understanding of metal-doped implants to enable controlled therapy while minimising cytotoxicity concerns.

Different Cell and Tissue Behavior of Micro-/Nano-Tubes and Micro-/Nano-Nets Topographies on Selective Laser Melting Titanium to Enhance Osseointegration

Background and Purpose

Micro-/nano-tubes (TNTs) and micro-/nano-nets (TNNs) are the common and sensible choice in the first step of combined modifications of titanium surface for further functionalization in the purpose of extended indications and therapeutic effect. It is important to recognize the respective biologic reactions of these two substrates for guiding a biologically based first-step selection.

Materials and Methods

TNTs were produced by anodic oxidation and TNNs were formed by alkali-heat treatment. The original selective laser melting (SLM) titanium surface was set as control. Surface characterization was evaluated by scanning electron microscopy, surface roughness, and water contact angle measurements. Osteoclastogenesis and osteogenesis were measured. MC3T3-E1 cells and RAW 264.7 cells were used for in vitro assay in terms of adhesion, proliferation, and differentiation. In vivo assessments were taken on Beagle dogs with micro-CT and histological analysis.

Results

TNN and TNT groups performed decreased roughness and increased hydrophilicity compared with SLM group. For biological detections, the highest ALP activity and osteogenesis-related genes expression were observed in TNT group followed by TNN group (P <0.05). Interestingly, when it comes to the osteoclastogenesis, TNNs displayed lowest TRAP activity and osteoclastogenesis-related genes expression and TNTs were lower than SLM but higher than TNNs (P <0.05). BV/TV around implants was highest in TNT group after 4 weeks (P <0.05). HE, ALP and TRAP staining showed that osteogenic and osteoclastic activity around TNTs were both higher than TNNs (P <0.05).

Conclusion

TNNs and TNTs have dual advantages in promotion of osteogenesis and inhibition of osteoclastogenesis. Furthermore, TNNs showed better capability in inhibiting osteoclast activity while TNTs facilitated stronger osteogenesis. Our results implied that TNT substrates would take advantage in early application after implantation, while diseases with inappropriate osteoclast activity would prefer TNN substrates, which will guide a biologically based first-step selection on combined modification for different clinical purposes.

Loading Gentamicin and Zn2+ on TiO2 Nanotubes to Improve Anticoagulation, Endothelial Cell Growth, and Antibacterial Activities

Titanium and its alloys are widely used in blood-contacting implantable and interventional medical devices; however, their biocompatibility is still facing great challenges. In the present study, in order to improve the biocompatibility and antibacterial activities of titanium, TiO2 nanotubes were firstly in situ prepared on the titanium surface by anodization, followed by the introduction of polyacrylic acid (PAA) and gentamicin (GS) on the nanotube surface by layer-by-layer assembly, and finally, zinc ions were loaded on the surface to further improve the bioactivities. The nanotubes displayed excellent hydrophilicity and special nanotube-like structure, which can selectively promote the albumin adsorption, enhance the blood compatibility, and promote the growth of endothelial cells to some degree. After the introduction of PAA and GS, although the superhydrophilicity cannot be achieved, the results of platelet adhesion, cyclic guanosine monophosphate (cGMP) activity, hemolysis rate, and activated partial thromboplastin time (APTT) showed that the blood compatibility was improved, and the blood compatibility was further enhanced after zinc ion loading. On the other hand, the modified surface showed good cytocompatibility to endothelial cells. The introduction of PAA and zinc ions not only promoted the adhesion and proliferation of endothelial cells but also upregulated expression of vascular endothelial growth factor (VEGF) and nitric oxide (NO). The slow and continuous release of GS and Zn2+ over 14 days can significantly improve the antibacterial properties. Therefore, the present study provides an effective method for the surface modification of titanium-based blood-contacting materials to simultaneously endow with good blood compatibility, endothelial growth behaviors, and antibacterial properties.

Immobilization of bioactive complex on the surface of magnesium alloy stent material to simultaneously improve anticorrosion, hemocompatibility and antibacterial activities

Magnesium alloy represents one of the most potential biodegradable vascular stent materials due to its good biodegradability, biocompatibility and suitable mechanical properties, whereas the rapid degradation in physiological environment and the limited biocompatibility remain the challenges. In this study, graphene oxide (GO) was firstly functionalized by chitosan (GOCS), followed by loading zinc ions and propranolol to obtain GOCS@Zn/Pro complex, which was finally covalently immobilized on the self-assembled modified magnesium alloy surface to enhance the corrosion resistance and biocompatibility. The multi-functional coating can significantly improve the corrosion resistance and reduce the degradation rate of the magnesium alloy. Furthermore, the coating can significantly inhibit platelet adhesion and activation, reduce hemolysis rate, prolong activated partial thromboplastin time (APTT), and thus improve the blood compatibility of the magnesium alloy. In addition, the modified magnesium alloy can not only significantly promote the endothelial cell adhesion and proliferation, up-regulate the expression of vascular endothelial growth factor (VEGF) and nitric oxide (NO), but also endow the materials with good antibacterial properties. Therefore, the method of the present study can be used to modify magnesium alloy stent materials to simultaneously enhance corrosion resistance and blood compatibility, promote endothelialilization, and inhibit infections.

Nanointeraction: The profound influence of nanostructured and nano-drug delivery biomedical implant surfaces on cell behavior

Nanostructured surfaces feature promising biological properties on biomaterials attracting large interest at basic research, implant industry development, and bioengineering applications. Thou, nanoscale interactions at a molecular and cellular level are not yet completely understood and its biological and clinical implications need to be further elucidated. As follows, the aim of this comprehensive review was to evaluate nanostructured surfaces at biomedical implants focusing on surface development, nanostructuration, and nanoengineered drug delivery systems that can induce specific cell interactions in all relevant aspects of biological, reparative, anti-bacterial, anti-inflammatory and clinical processes. The methods and the physio-chemical properties involved in nanotopography performance, the main cellular characteristics involved at surface/cell interaction, and a summary of results and outlooks reported in studies applying nanostructured surfaces and nano-drug delivery systems is presented. The future prospects and commercial translation of this developing field, particularly concerning multifunctional nanostructured surfaces and its clinical implications are further discussed. At a cellular level, nanostructured biomedical implant surfaces can enhance osteogenesis by targeting osteoblasts, osteocytes, and mesenchymal cells, stimulate fibroblast/epithelial cells proliferation and adherence, inhibit bacterial cell proliferation and biofilm accumulation, and act as immune-modulating surfaces targeting macrophages and reducing pro-inflammatory cytokine expression. Moreover, several methodological options to create drug-delivery systems on metallic implant surfaces are available, however, the clinical translation is yet incomplete. The efficiency of which nanostructured/nano-delivery surfaces may target specific cell interactions and favor clinical outcomes needs to be further elucidated in pre-clinical and clinical studies, along with engineering solutions for commercial translation and approval of controlling agencies.

Surface Engineering of Cardiovascular Devices for Improved Hemocompatibility and Rapid Endothelialization

Cardiovascular devices have been widely applied in the clinical treatment of cardiovascular diseases. However, poor hemocompatibility and slow endothelialization on their surface still exist. Numerous surface engineering strategies have mainly sought to modify the device surface through physical, chemical, and biological approaches to improve surface hemocompatibility and endothelialization. The alteration of physical characteristics and pattern topographies brings some hopeful outcomes and plays a notable role in this respect. The chemical and biological approaches can provide potential signs of success in the endothelialization of vascular device surfaces. They usually involve therapeutic drugs, specific peptides, adhesive proteins, antibodies, growth factors and nitric oxide (NO) donors. The gene engineering can enhance the proliferation, growth, and migration of vascular cells, thus boosting the endothelialization. In this review, the surface engineering strategies are highlighted and summarized to improve hemocompatibility and rapid endothelialization on the cardiovascular devices. The potential outlook is also briefly discussed to help guide endothelialization strategies and inspire further innovations. It is hoped that this review can assist with the surface engineering of cardiovascular devices and promote future advancements in this emerging research field.